CN106098132A - A kind of yellow gold conductor cable for aerospace - Google Patents
A kind of yellow gold conductor cable for aerospace Download PDFInfo
- Publication number
- CN106098132A CN106098132A CN201610379277.9A CN201610379277A CN106098132A CN 106098132 A CN106098132 A CN 106098132A CN 201610379277 A CN201610379277 A CN 201610379277A CN 106098132 A CN106098132 A CN 106098132A
- Authority
- CN
- China
- Prior art keywords
- aerospace
- conductor
- copper
- yellow gold
- gold conductor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of yellow gold conductor cable for aerospace, it is characterised in that include split conductor core, oversheath;Per share described insulated wire cores is made up of conductor and insulating barrier, is filled with inserts between described insulated wire cores, and per share described insulated wire cores is sequentially provided with internal shield, external shielding layer, flame-retardant layer, waterproof layer from the inside to the outside;Described conductor is yellow gold conductor, is made up of following material by weight: copper 10 100 parts;Silver 0.1 100 parts;Graphene 0.01 100 parts.Wired signal transmission of the present invention is reliable, capacity of resisting disturbance strong, have good electric conductivity, wearability and resistance fusion welding, can ensure that aerospace equipment is properly functioning in special environment, improves the safety of aerospace equipment.
Description
Technical field
The present invention relates to power cable technical field, specifically a kind of yellow gold conductor aerospace
Cable.
Electric wire is that electric power or information are transferred at one the wire at another.Along with science and technology development, electric wire
Cable application field is more and more extensive, and cable classification has power cable, controls cable, compensating cable, shielded cable, high temperature
Cable, computer cable, signal cable, coaxial cable, fire-resisting cable, cable for ship, mine cable, aluminium alloy cable, aviation
Space flight cable etc., along with the development of Aero-Space science and technology, more and more higher to the performance requirement of electric wire in aircraft, in order to
Guarantee that aerospace equipment is properly functioning in special environment, need develop that the transmission of a kind of signal is reliable, capacity of resisting disturbance is strong,
Electric performance stablity cable.
Summary of the invention
It is an object of the invention to provide that the transmission of a kind of signal is reliable, capacity of resisting disturbance strong, the yellow gold of electric performance stablity
Conductor cable for aerospace.
The present invention solves technical problem and adopts the following technical scheme that
A kind of yellow gold conductor cable for aerospace, its feature is, including split conductor core, oversheath;Often
Insulated wire cores described in Gu is made up of conductor and insulating barrier, is filled with inserts, per share described insulation between described insulated wire cores
Core is sequentially provided with internal shield, external shielding layer, flame-retardant layer, waterproof layer from the inside to the outside;Described conductor is yellow gold conductor, presses
Weight portion is made up of following material: copper 10-100 part;Silver 0.1-100 part;Graphene 0.01-100 part.
Further, described yellow gold conductor is preferably by weight: copper 95-100 part;Silver 0.1-10 part;Graphene
0.01-10 part.
Further, described yellow gold conductor is preferably by weight: copper 99.5 parts;Silver 0.49 part;Graphene 0.01 part.
Further, described yellow gold conductor is preferably by weight: copper 90 parts;Silver 9 parts;Graphene 1 part.
Further, described internal shield is preferably proof copper-wire braided screen layer.
Further, described external shielding layer is preferably copper strips lapped shielding layer.
Further, described flame-retardant layer be flame-retardant layer be wrapped Muscovitum belt.
Compared with the prior art, the present invention has the beneficial effect that:
Wired signal transmission of the present invention is reliable, capacity of resisting disturbance strong, have good electric conductivity, wearability and anti-melting welding
Property, can ensure that aerospace equipment is properly functioning in special environment, improve the safety of aerospace equipment.
Accompanying drawing explanation
Fig. 1 is Aero-Space construction of cable schematic diagram of the present invention.
Reference: 1 conductor, 2 insulating barriers, 3 internal shields, 4 external shielding layers, 5 flame-retardant layers, 6 waterproof layers, 7 oversheaths.
Detailed description of the invention
By detailed description of the invention, technical solution of the present invention is further explained explanation below in conjunction with accompanying drawing.
Embodiment 1
A kind of yellow gold conductor cable for aerospace, including split conductor core, oversheath;Per share described insulation
Core is made up of conductor and insulating barrier, is filled with inserts between described insulated wire cores, and per share described insulated wire cores is from the inside to the outside
It is sequentially provided with internal shield, external shielding layer, flame-retardant layer, waterproof layer.
Conductor is yellow gold conductor, is made up of following material by weight: copper 98.5 parts;Silver 1.49 parts;Graphene
0.01 part.
Internal shield is preferably proof copper-wire braided screen layer;External shielding layer is preferably copper strips lapped shielding layer.
The present embodiment cable conductor is resistivity about 1.67 Ω m × 10 at 20 DEG C-8, resistivity about 1.98 at 100 DEG C
Ω·m×10-8;Resistivity about 1.96 Ω m × 10 at 300 DEG C-8;At 500 DEG C, resistivity is 1.94 Ω m × 10-8.Anti-soft
Changing temperature is 480 DEG C.Room temperature tensile intensity about 502MPa, elongation at break about 25.6%.
Embodiment 2
A kind of yellow gold conductor cable for aerospace, including split conductor core, oversheath;Per share described insulation
Core is made up of conductor and insulating barrier, is filled with inserts between described insulated wire cores, and per share described insulated wire cores is from the inside to the outside
It is sequentially provided with internal shield, external shielding layer, flame-retardant layer, waterproof layer.
Conductor is yellow gold conductor, is made up of following material by weight: copper 99.0 parts;Silver 0.75 part;Graphene
0.25 part.
Internal shield is preferably proof copper-wire braided screen layer;External shielding layer is preferably copper strips lapped shielding layer.
The present embodiment cable conductor is resistivity about 1.67 Ω m × 10 at 20 DEG C-8, resistivity about 1.82 at 100 DEG C
Ω·m×10-8;Resistivity about 1.89 Ω m × 10 at 300 DEG C-8;At 500 DEG C, resistivity is 1.87 Ω m × 10-8.Anti-soft
Changing temperature is 498 DEG C.Room temperature tensile intensity about 502MPa, elongation at break about 26.7%.
Embodiment 3
A kind of yellow gold conductor cable for aerospace, including split conductor core, oversheath;Per share described insulation
Core is made up of conductor and insulating barrier, is filled with inserts between described insulated wire cores, and per share described insulated wire cores is from the inside to the outside
It is sequentially provided with internal shield, external shielding layer, flame-retardant layer, waterproof layer.
Conductor is yellow gold conductor, is made up of following material by weight: copper 99.5 parts;Silver 0.25 part;Graphene
0.25 part.
Internal shield is preferably proof copper-wire braided screen layer;External shielding layer is preferably copper strips lapped shielding layer.
The present embodiment cable conductor is resistivity about 1.62 Ω m × 10 at 20 DEG C-8, resistivity about 1.76 at 100 DEG C
Ω·m×10-8;Resistivity about 1.85 Ω m × 10 at 300 DEG C-88;At 500 DEG C, resistivity is 1.83 Ω m × 10-8.Anti-soft
Changing temperature is 508 DEG C.Room temperature tensile intensity about 521MPa, elongation at break about 25.8%.
Embodiment 4
A kind of yellow gold conductor cable for aerospace, including split conductor core, oversheath;Per share described insulation
Core is made up of conductor and insulating barrier, is filled with inserts between described insulated wire cores, and per share described insulated wire cores is from the inside to the outside
It is sequentially provided with internal shield, external shielding layer, flame-retardant layer, waterproof layer.
Conductor is yellow gold conductor, is made up of following material by weight: copper 99.8 parts;Silver 0.05 part;Graphene
0.15 part.
The present embodiment cable conductor is resistivity about 1.65 Ω m × 10 at 20 DEG C-8, resistivity about 1.76 at 100 DEG C
Ω·m×10-8;Resistivity about 1.85 Ω m × 10 at 300 DEG C-8;At 500 DEG C, resistivity is 1.83 Ω m × 10-8.Anti-soft
Changing temperature is 500 DEG C.Room temperature tensile intensity about 502MPa, elongation at break about 24.1%.
Internal shield is preferably proof copper-wire braided screen layer;External shielding layer is preferably copper strips lapped shielding layer.
Embodiment 5
A kind of yellow gold conductor cable for aerospace, including split conductor core, oversheath;Per share described insulation
Core is made up of conductor and insulating barrier, is filled with inserts between described insulated wire cores, and per share described insulated wire cores is from the inside to the outside
It is sequentially provided with internal shield, external shielding layer, flame-retardant layer, waterproof layer.
Conductor is yellow gold conductor, is made up of following material by weight: copper 99.9 parts;Silver 0.04 part;Graphene
0.06 part.
Internal shield is preferably proof copper-wire braided screen layer;External shielding layer is preferably copper strips lapped shielding layer.
The present embodiment cable conductor is resistivity about 1.68 Ω m × 10 at 20 DEG C-8, resistivity about 1.98 at 100 DEG C
Ω·m×10-8;Resistivity about 1.96 Ω m × 10 at 300 DEG C-8;At 500 DEG C, resistivity is 1.94 Ω m × 10-8.Anti-soft
Changing temperature is 480 DEG C.Room temperature tensile intensity about 502MPa, elongation at break about 25.6%.
Claims (8)
1. a yellow gold conductor cable for aerospace, it is characterised in that include split conductor core, oversheath (7);Often
Insulated wire cores described in Gu is made up of conductor (1) and insulating barrier (2), is filled with inserts, per share institute between described insulated wire cores
State insulated wire cores and be sequentially provided with internal shield (3), external shielding layer (4), flame-retardant layer (5), waterproof layer (6) from the inside to the outside;Described lead
Body is yellow gold conductor, is made up of following material by weight: copper 10-100 part;Silver 0.1-100 part;Graphene 0.01-100
Part.
A kind of yellow gold conductor cable for aerospace the most according to claim 1, it is characterised in that described silver-bearing copper closes
Gold conductor is made up of following material by weight: copper 95-100 part;Silver 0.1-10 part;Graphene 0.01-10 part.
A kind of yellow gold conductor cable for aerospace the most according to claim 1, it is characterised in that described silver-bearing copper closes
Gold conductor is made up of following material by weight: copper 99.5 parts;Silver 0.49 part;Graphene 0.01 part.
A kind of yellow gold conductor cable for aerospace the most according to claim 1, it is characterised in that described silver-bearing copper closes
Gold conductor is made up of following material by weight: copper 90 parts;Silver 9 parts;Graphene 1 part.
A kind of yellow gold conductor cable for aerospace the most according to claim 1, it is characterised in that described inner shield
Layer is proof copper-wire braided screen layer.
A kind of yellow gold conductor cable for aerospace the most according to claim 1, it is characterised in that described external shield
Layer is copper strips lapped shielding layer.
A kind of yellow gold conductor cable for aerospace the most according to claim 1, it is characterised in that described flame-retardant layer
For wrapped Muscovitum belt.
A kind of yellow gold conductor cable for aerospace the most according to claim 1, it is characterised in that by many strand insulations
Total conductor that fibre core is constituted is coated with the total screen layer of proof copper-wire braided.