CN106087576A - A kind of wear-resistant pressure-resistant cop tube paper and preparation method thereof - Google Patents

A kind of wear-resistant pressure-resistant cop tube paper and preparation method thereof Download PDF

Info

Publication number
CN106087576A
CN106087576A CN201610419958.3A CN201610419958A CN106087576A CN 106087576 A CN106087576 A CN 106087576A CN 201610419958 A CN201610419958 A CN 201610419958A CN 106087576 A CN106087576 A CN 106087576A
Authority
CN
China
Prior art keywords
resistant
parts
wear
paper
cop tube
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610419958.3A
Other languages
Chinese (zh)
Inventor
楼柯勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG HUACHUAN INDUSTRIAL GROUP Co Ltd
Original Assignee
ZHEJIANG HUACHUAN INDUSTRIAL GROUP Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG HUACHUAN INDUSTRIAL GROUP Co Ltd filed Critical ZHEJIANG HUACHUAN INDUSTRIAL GROUP Co Ltd
Priority to CN201610419958.3A priority Critical patent/CN106087576A/en
Publication of CN106087576A publication Critical patent/CN106087576A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of wear-resistant pressure-resistant cop tube paper, including following weight ratio: non-bleached sulphate softwood pulp 12～23 parts, 13～33 parts of knot slurry, villus fiber 21～36 parts, U.S.'s first-class waste paper 32～45 parts, remaining is additive；This product has that manufacturing process is simple, resistance to compression wear resistance is good, cost is than the less expensive and advantage of safety and environmental protection.

Description

A kind of wear-resistant pressure-resistant cop tube paper and preparation method thereof
Technical field
The present invention relates to industrial paper field, be specifically related to a kind of wear-resistant pressure-resistant cop tube paper and preparation method thereof.
Background technology
Cop tube paper is mainly used in the making of kernel and pipeline, and industry is managed, ground membrane tube, firework pipe, spinnerule, serpentine pipe, Conical tube, parallel pipe, various corrugated board corner protectors, carton, honeycomb cardboard etc., wear-resistant pressure-resistant cop tube paper is compared to other type of paper Slurry cost ratio required for for is less expensive, and the various secondary stocks of most employing or biological raw material slurry make, it is not necessary to trees are former Slurry, the main uses of its wear-resistant pressure-resistant cop tube paper is not used under high request environment, and therefore, wear-resistant pressure-resistant cop tube paper is for former material From the point of view of material and manufacturing process, requirement is not the highest, and more available waste residues and waste and old paper re-work use, reduce life Produce cost, the consumption of log can be reduced simultaneously, protect environment.
Existing cop tube paper is mainly used in industrial use and uses, most of center connecting shafts as other stationeries, or Use with four corner protectors within a package during packaging, main still for resistance to compression breakage-proof, and as fixing axle, cop tube paper exists Employed in production process, raw material major part is industry waste paper, industry waste paper characteristic of various paper after again reclaiming decomposition Will reduce a lot, then need to add some other additives in process of production to improve the performances such as the wear-resistant resistance to compression of paper, How to improve, be the required problem solved of existing cop tube paper manufacturer.
Summary of the invention
The technical problem to be solved in the present invention is to provide that a kind of manufacturing process is simple, resistance to compression wear resistance is good, cost ratio The less expensive wear-resistant pressure-resistant cop tube paper with safety and environmental protection.
For solving the problems referred to above, the present invention adopts the following technical scheme that a kind of wear-resistant pressure-resistant cop tube paper, including following weight Ratio: non-bleached sulphate softwood pulp 12～23 parts, 13～33 parts of knot slurry, villus fiber 21～36 parts, U.S.'s first-class waste paper 32～45 parts, remaining is additive.
Further, the tensile property >=11kn/m of described wear-resistant pressure-resistant cop tube paper paper, Paper White Degree 6～9ISO, water Points 3～6%, ash 0.5～0.8%, quantitative 75～480g/, thickness 0.08～0.24mm, degree of sizing >=1.5mm, bursting strength 320～450kPa, longitudinal tear degree 610～1200mN, water absorption 25≤g/.
Further, described additive includes mass ratio: wet strength agent 23～34 parts, defoamer 21～28 parts, sizing agent 21 ～28 parts, remaining be Pulvis Talci.
Further, described wet strength agent is that melamine resin, phenolic resin, epoxychloropropane or polyamide are a kind of Thing mixed above, and add amount control per ton 25～32kg.
Further, described sizing agent is one or more combinations of modified starch, gum rosin, paraffin.
Further, described defoamer be polyoxyethylene polyoxypropylene tetramethylolmethane ether, polyoxyethylene polyoxy propanol amidogen ether, Polypropylene glycerol aether and polyoxyethylene polyoxypropylene glycerin ether, wax, one or both combinations of aliphatic amide, the amount of addition Control per ton 3～5kg.
The preparation method of a kind of wear-resistant pressure-resistant cop tube paper, comprises the following steps:
Mix the most in mass ratio first add water with disintegrator and villus fiber 21～36 parts and U.S.'s first-class waste paper 32～ 45 parts of size degradations, size degradation complete after again the slurry obtained and non-bleached sulphate softwood pulp 12～23 parts, knot slurry 13～33 Part join together blender stirring, mixing time is 1～1.5 hour, the most again through filtrations, upper net forming, squeeze, do Dry, press polish, rewinding, the process of packing prepare wear-resistant pressure-resistant cop tube paper.
The invention has the beneficial effects as follows:
The most with low cost, it is main for selecting non-bleached sulphate softwood pulp, knot slurry, villus fiber, U.S.'s first-class waste paper Wanting raw material, it is the most common materials manufacturing wrapping paper, and these manufacture of materials cost ratios are less expensive, and applicable frequency is high, not Bleached sulphate softwood pulp is the most frequently used raw material, can be effectively improved paper performance, and knot slurry, villus fiber, the U.S. one It is all good fibrous raw material in waste paper, can effectively reduce cost；
2. energy-conserving and environment-protective, add knot slurry in slurry, and knot slurry, as discarded raw material, can be used for reclaiming profit again With, effectively reducing discharge capacity, protection surrounding is pollution-free, and can increase factory economy benefit, reduces production cost；
3. performance is good, and the spool paper produced, no matter as industrial cardboard or vanning corner protector, has good Performance, improve paper tensile wear-resistant ability.
Detailed description of the invention
Below the preferred embodiments of the present invention are described in detail so that advantages and features of the invention can be easier to by It will be appreciated by those skilled in the art that thus protection scope of the present invention is made apparent clear and definite defining.
Embodiment one
Including following weight ratio: 13 parts of non-bleached sulphate softwood pulp 12 parts, knot slurry, villus fiber 25 parts, the U.S. First-class 33 parts of waste paper, remaining is additive.
Tensile property >=the 11kn/m of described wear-resistant pressure-resistant cop tube paper paper, Paper White Degree 6ISO, moisture 3%, ash 0.5%, quantitative 125g/, thickness 1mm, degree of sizing >=1.5mm, bursting strength 340kPa, longitudinal tear degree 730mN, water absorption 25 ≤g/㎡。
Described additive includes mass ratio: wet strength agent 23 parts, defoamer 21 parts, sizing agent 21 parts, remaining be Pulvis Talci.
Described wet strength agent is more than one mixing of melamine resin, phenolic resin, epoxychloropropane or polyamide Thing, and add amount control at 26kg per ton.
Sizing agent is one or more combinations of modified starch, gum rosin, paraffin.
Described defoamer is polyoxyethylene polyoxypropylene tetramethylolmethane ether, polyoxyethylene polyoxy propanol amidogen ether, polyoxypropylene Glycerin ether and polyoxyethylene polyoxypropylene glycerin ether, wax, one or both combinations of aliphatic amide, the amount of addition controls often Ton 3kg.
The preparation method of a kind of wear-resistant pressure-resistant cop tube paper, comprises the following steps:
Mixing the most in mass ratio and first add water with disintegrator and villus fiber and U.S.'s first-class repulping of waste paper, size degradation completes After together with the slurry obtained and non-bleached sulphate softwood pulp, knot slurry, join blender stirring again, mixing time is 1 Hour, the most again through filtration, upper net forming, squeeze, be dried, press polish, rewinding, the process of packing prepare wear-resistant pressure-resistant spool Paper.
Embodiment two
Including following weight ratio: 16 parts of non-bleached sulphate softwood pulp 16 parts, knot slurry, villus fiber 24 parts, the U.S. First-class 34 parts of waste paper, remaining is additive.
Tensile property >=the 11kn/m of described wear-resistant pressure-resistant cop tube paper paper, Paper White Degree 7ISO, moisture 3～6%, ash 0.6%, quantitative 160g/, thickness 0.14mm, degree of sizing >=1.5mm, bursting strength 360kPa, longitudinal tear degree 820mN, water suction Property 25≤g/.
Described additive includes mass ratio: wet strength agent 28 parts, defoamer 26 parts, sizing agent 24 parts, remaining be Pulvis Talci.
Described wet strength agent is more than one mixing of melamine resin, phenolic resin, epoxychloropropane or polyamide Thing, and add amount control at 29kg per ton.
Sizing agent is one or more combinations of modified starch, gum rosin, paraffin.
Described defoamer is polyoxyethylene polyoxypropylene tetramethylolmethane ether, polyoxyethylene polyoxy propanol amidogen ether, polyoxypropylene Glycerin ether and polyoxyethylene polyoxypropylene glycerin ether, wax, one or both combinations of aliphatic amide, the amount of addition controls often Ton 3kg.
The preparation method of a kind of wear-resistant pressure-resistant cop tube paper, comprises the following steps:
Mixing the most in mass ratio and first add water with disintegrator and villus fiber and U.S.'s first-class repulping of waste paper, size degradation completes After together with the slurry obtained and non-bleached sulphate softwood pulp, knot slurry, join blender stirring again, mixing time is 1 Hour, the most again through filtration, upper net forming, squeeze, be dried, press polish, rewinding, the process of packing prepare wear-resistant pressure-resistant spool Paper.
Embodiment three
Including following weight ratio: 21 parts of non-bleached sulphate softwood pulp 14 parts, knot slurry, villus fiber 23 parts, the U.S. First-class 35 parts of waste paper, remaining is additive.
Tensile property >=the 11kn/m of described wear-resistant pressure-resistant cop tube paper paper, Paper White Degree 9ISO, moisture 6%, ash 0.7%, quantitative 320g/, thickness 0.18mm, degree of sizing >=1.5mm, bursting strength 390kPa, longitudinal tear degree 800mN, water suction Property 25≤g/.
Described additive includes mass ratio: wet strength agent 30 parts, defoamer 25 parts, sizing agent 26 parts, remaining be Pulvis Talci.
Described wet strength agent is more than one mixing of melamine resin, phenolic resin, epoxychloropropane or polyamide Thing, and add amount control at 26kg per ton.
Sizing agent is one or more combinations of modified starch, gum rosin, paraffin.
Described defoamer is polyoxyethylene polyoxypropylene tetramethylolmethane ether, polyoxyethylene polyoxy propanol amidogen ether, polyoxypropylene Glycerin ether and polyoxyethylene polyoxypropylene glycerin ether, wax, one or both combinations of aliphatic amide, the amount of addition controls often Ton 3kg.
The preparation method of a kind of wear-resistant pressure-resistant cop tube paper, comprises the following steps:
Mixing the most in mass ratio and first add water with disintegrator and villus fiber and U.S.'s first-class repulping of waste paper, size degradation completes After together with the slurry obtained and non-bleached sulphate softwood pulp, knot slurry, join blender stirring again, mixing time is 1.5 hours, the most again through filtration, upper net forming, squeeze, be dried, press polish, rewinding, the process of packing prepare wear-resistant pressure-resistant yarn Pipe paper.
Embodiment four
Including following weight ratio: 18 parts of non-bleached sulphate softwood pulp 21 parts, knot slurry, villus fiber 32 parts, the U.S. First-class 34 parts of waste paper, remaining is additive.
Tensile property >=the 11kn/m of described wear-resistant pressure-resistant cop tube paper paper, Paper White Degree 9ISO, moisture 3～6%, ash 0.8%, quantitative 420g/, thickness 0.21mm, degree of sizing >=1.5mm, bursting strength 380kPa, longitudinal tear degree 1100mN, water suction Property 25≤g/.
Described additive includes mass ratio: wet strength agent 32 parts, defoamer 36 parts, sizing agent 22 parts, remaining be Pulvis Talci.
Described wet strength agent is more than one mixing of melamine resin, phenolic resin, epoxychloropropane or polyamide Thing, and add amount control at 31kg per ton.
Described sizing agent is one or more combinations of modified starch, gum rosin, paraffin.
Described defoamer is polyoxyethylene polyoxypropylene tetramethylolmethane ether, polyoxyethylene polyoxy propanol amidogen ether, polyoxypropylene Glycerin ether and polyoxyethylene polyoxypropylene glycerin ether, wax, one or both combinations of aliphatic amide, the amount of addition controls often Ton 5kg.
The preparation method of a kind of wear-resistant pressure-resistant cop tube paper, comprises the following steps:
Mixing the most in mass ratio and first add water with disintegrator and villus fiber and U.S.'s first-class repulping of waste paper, size degradation completes After together with the slurry obtained and non-bleached sulphate softwood pulp, knot slurry, join blender stirring again, mixing time is 1.5 hours, the most again through filtration, upper net forming, squeeze, be dried, press polish, rewinding, the process of packing prepare wear-resistant pressure-resistant yarn Pipe paper.
The above, the only detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto, and any The change expected without creative work or replacement, all should contain and be as the criterion at the new protection domain of this practicality.

Claims (7)

1. a wear-resistant pressure-resistant cop tube paper, it is characterised in that: include following weight ratio: non-bleached sulphate softwood pulp 12～23 Part, knot starch 13～33 parts, villus fiber 21～36 parts, U.S.'s first-class waste paper 32～45 parts, and remaining is additive.
A kind of wear-resistant pressure-resistant cop tube paper the most according to claim 1, it is characterised in that: described wear-resistant pressure-resistant cop tube paper paper Tensile property >=11kn/m, Paper White Degree 6～9ISO, moisture 3～6%, ash 0.5～0.8%, quantitative 75～480g/, Thickness 0.08～0.24mm, degree of sizing >=1.5mm, bursting strength 320～450kPa, longitudinal tear degree 610～1200mN, water absorption 25≤g/㎡。
A kind of wear-resistant pressure-resistant cop tube paper the most according to claim 1, it is characterised in that: described additive includes mass ratio: Wet strength agent 23～34 parts, defoamer 21～28 parts, sizing agent 21～28 parts, remaining be Pulvis Talci.
A kind of wear-resistant pressure-resistant cop tube paper the most according to claim 1, it is characterised in that: described wet strength agent is tripolycyanamide first More than one mixture of urea formaldehyde, phenolic resin, epoxychloropropane or polyamide, and the amount added controls per ton 25～ 32kg。
A kind of wear-resistant pressure-resistant cop tube paper the most according to claim 1, it is characterised in that: described sizing agent be modified starch, Gum rosin, one or more combinations of paraffin.
A kind of wear-resistant pressure-resistant cop tube paper the most according to claim 1, it is characterised in that: described defoamer is that polyoxyethylene gathers Oxypropylene tetramethylolmethane ether, polyoxyethylene polyoxy propanol amidogen ether, polypropylene glycerol aether and polyoxyethylene polyoxypropylene glycerin ether, Wax, one or both combinations of aliphatic amide, the amount of addition controls per ton 3～5kg.
The preparation method of a kind of wear-resistant pressure-resistant cop tube paper the most according to claim 1, it is characterised in that: the most in mass ratio Mixing first adds water with disintegrator and villus fiber 21～36 parts and U.S.'s first-class waste paper 32～45 parts of size degradations, size degradation complete after again The slurry obtained and non-bleached sulphate softwood pulp 12～23 parts, knot starch 13～33 parts together with join blender and stir Mixing, mixing time is 1～1.5 hour, the most again through filtration, upper net forming, squeeze, be dried, press polish, rewinding, the mistake of packing Journey prepares wear-resistant pressure-resistant cop tube paper.
CN201610419958.3A 2016-06-13 2016-06-13 A kind of wear-resistant pressure-resistant cop tube paper and preparation method thereof Pending CN106087576A (en)