CN106085137A - A kind of novel high rigidity anticorrosive paint - Google Patents
A kind of novel high rigidity anticorrosive paint Download PDFInfo
- Publication number
- CN106085137A CN106085137A CN201610638558.1A CN201610638558A CN106085137A CN 106085137 A CN106085137 A CN 106085137A CN 201610638558 A CN201610638558 A CN 201610638558A CN 106085137 A CN106085137 A CN 106085137A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- anticorrosive paint
- high rigidity
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the preparation method of a kind of novel high rigidity anticorrosive paint: the preparation of (1) nano dispersion fluid: take Nano carbon white, nano alumina powder, nano barium sulfate, make medium with isopropanol and be configured to suspension, high speed dispersion is uniform, then ultrasonic disperse 20min;A certain amount of silane coupler is dissolved in isopropanol medium, high-speed stirred 20min under room temperature.Mix above-mentioned 2 kinds of solution, ultrasonic disperse 25min according to the ratio of weight ratio 1:1, then keep 30 DEG C and stir in thermostatical oil bath, make coupling reaction 2h, prepare nano dispersion fluid with standby;(2) component A is prepared;(3) using cashew shell oil firming agent as B component, under room temperature, both in mass ratio 2: 1 mechanical agitation are to uniformly, obtain novel high rigidity anticorrosive paint.
Description
Technical field
The present invention relates to a kind of novel high rigidity anticorrosive paint, belong to coating manufacture field.
Background technology
Hardware anticorrosion is most effective, one of most common method is to coat anticorrosion organic coating in metal surface,
With isolation metallic matrix and corrosive medium.The domestic research to anticorrosive paint achieves more achievement, but there is also research side
Method falls behind, and corrosion-inhibiting coating thickness is big, has substantial amounts of inflammable, explosive, poisonous organic solvent to escape, has bigger to human body and environment
The deficiency such as harm.At present, anticorrosive coating market used is still based on traditional solvent-borne anticorrosive coating.But in recent years
Come, countries in the world released one after another relevant environmental pollution limit laws and regulations, be directed to coating industry just has in coating
The content of organic volatile and harmful air pollutants two large problems, so account for the molten of All Around The World coating industry 53% by making
The production of dosage form coating is restricted.Therefore, develop low VOC anticorrosive coating necessary, and solvent-free new coating is real
One of approach of the lowest VOC.
Anticorrosive paint refers to play a class high-performance coating of protection base material effect, protection under harsh corrosive environment
Life-span is generally more than 15 years.The kind of anticorrosive paint is more, such as epoxy resin, polyurethanes, chlorinated polyolefin hydro carbons and chlorine
Change rubber-like etc..Epoxy resin owing to having that adhesive force preferable to various grounds, alkali resistance be especially prominent, good toughness, can expire
The foot advantage such as multiple construction requirement and favored.Epoxy coating is used widely at the corrosion-resistant field such as oil, chemical industry, and
Achieved with good anticorrosion ability.
It is desirable to provide a kind of novel high rigidity anticorrosive paint, its natural environmental-protective, there is again good antiseptic property,
The most superpower pencil hardness.
Summary of the invention
The shortcoming that the present invention is directed to prior art, it is provided that a kind of novel high rigidity anticorrosive paint, its natural environmental-protective, again
There is good antiseptic property, the most superpower pencil hardness.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of preparation method of novel high rigidity anticorrosive paint, its step is as follows:
(1) preparation of nano dispersion fluid:
According to parts by weight, take Nano carbon white 2-4 part, nano alumina powder 2 parts, nano barium sulfate 1 part, make to be situated between with isopropanol
Matter is configured to suspension, and high speed dispersion is uniform, then ultrasonic disperse 20min;
A certain amount of silane coupler is dissolved in isopropanol medium, high-speed stirred 20min under room temperature.
Mix above-mentioned 2 kinds of solution, ultrasonic disperse 25min according to the ratio of weight ratio 1:1, then keep 30 DEG C in thermostatical oil
In bath, stirring, makes coupling reaction 2h, prepares nano dispersion fluid with standby;
(2) component A is prepared:
According to parts by weight, 50 parts of epoxy resin liquid adds nano dispersion fluid 10-12 part, zinc phosphate 2 parts, pigment 8 parts, slides
Stone powder 18 parts, calcium silicates 3 parts, mullite part 0.8 part, 0.5 part of mafic spinel brick 200 mesh powder, solvent 20 parts, according to coating
The ratio of 1: 1 adds abrasive media, carries out ball milling with high-speed grinder, until coating fineness is less than 80 μm, prepares component A;
(3) using cashew shell oil firming agent as B component, under room temperature, both in mass ratio 2: 1 mechanical agitation are to uniformly, obtain novel
High rigidity anticorrosive paint.
The invention have benefit that:
The present invention provides a kind of novel high rigidity anticorrosive paint, its natural environmental-protective, has again good antiseptic property and mechanical property
Can, shelf characteric is stable, not free settling, and adhesive force is good, the most also the pencil hardness of superelevation.
Detailed description of the invention
Embodiment 1:
A kind of preparation method of novel high rigidity anticorrosive paint, its step is as follows:
(1) preparation of nano dispersion fluid:
According to parts by weight, take Nano carbon white 2 parts, nano alumina powder 2 parts, nano barium sulfate 1 part, make medium with isopropanol
Being configured to suspension, high speed dispersion is uniform, then ultrasonic disperse 20min;
A certain amount of silane coupler is dissolved in isopropanol medium, high-speed stirred 20min under room temperature.
Mix above-mentioned 2 kinds of solution, ultrasonic disperse 25min according to the ratio of weight ratio 1:1, then keep 30 DEG C in thermostatical oil
In bath, stirring, makes coupling reaction 2h, prepares nano dispersion fluid with standby;
(2) component A is prepared:
According to parts by weight, 50 parts of epoxy resin liquid adds nano dispersion fluid 12 parts, zinc phosphate 2 parts, pigment 8 parts, Talcum
18 parts of powder, calcium silicates 3 parts, mullite part 0.8 part, 0.5 part of mafic spinel brick 200 mesh powder, solvent 20 parts, according to coating 1:
The ratio of 1 adds abrasive media, carries out ball milling with high-speed grinder, until coating fineness is less than 80 μm, prepares component A;
(3) using cashew shell oil firming agent as B component, under room temperature, both in mass ratio 2: 1 mechanical agitation are to uniformly, obtain novel
High rigidity anticorrosive paint.
Embodiment 2:
A kind of preparation method of novel high rigidity anticorrosive paint, its step is as follows:
(1) preparation of nano dispersion fluid:
According to parts by weight, take Nano carbon white 4 parts, nano alumina powder 2 parts, nano barium sulfate 1 part, make medium with isopropanol
Being configured to suspension, high speed dispersion is uniform, then ultrasonic disperse 20min;
A certain amount of silane coupler is dissolved in isopropanol medium, high-speed stirred 20min under room temperature.
Mix above-mentioned 2 kinds of solution, ultrasonic disperse 25min according to the ratio of weight ratio 1:1, then keep 30 DEG C in thermostatical oil
In bath, stirring, makes coupling reaction 2h, prepares nano dispersion fluid with standby;
(2) component A is prepared:
According to parts by weight, 50 parts of epoxy resin liquid adds nano dispersion fluid 10 parts, zinc phosphate 2 parts, pigment 8 parts, Talcum
18 parts of powder, calcium silicates 3 parts, mullite part 0.8 part, 0.5 part of mafic spinel brick 200 mesh powder, solvent 20 parts, according to coating 1:
The ratio of 1 adds abrasive media, carries out ball milling with high-speed grinder, until coating fineness is less than 80 μm, prepares component A;
(3) using cashew shell oil firming agent as B component, under room temperature, both in mass ratio 2: 1 mechanical agitation are to uniformly, obtain novel
High rigidity anticorrosive paint.
Embodiment 3:
A kind of preparation method of novel high rigidity anticorrosive paint, its step is as follows:
(1) preparation of nano dispersion fluid:
According to parts by weight, take Nano carbon white 3 parts, nano alumina powder 2 parts, nano barium sulfate 1 part, make medium with isopropanol
Being configured to suspension, high speed dispersion is uniform, then ultrasonic disperse 20min;
A certain amount of silane coupler is dissolved in isopropanol medium, high-speed stirred 20min under room temperature.
Mix above-mentioned 2 kinds of solution, ultrasonic disperse 25min according to the ratio of weight ratio 1:1, then keep 30 DEG C in thermostatical oil
In bath, stirring, makes coupling reaction 2h, prepares nano dispersion fluid with standby;
(2) component A is prepared:
According to parts by weight, 50 parts of epoxy resin liquid adds nano dispersion fluid 11 parts, zinc phosphate 2 parts, pigment 8 parts, Talcum
18 parts of powder, calcium silicates 3 parts, mullite part 0.8 part, 0.5 part of mafic spinel brick 200 mesh powder, solvent 20 parts, according to coating 1:
The ratio of 1 adds abrasive media, carries out ball milling with high-speed grinder, until coating fineness is less than 80 μm, prepares component A;
(3) using cashew shell oil firming agent as B component, under room temperature, both in mass ratio 2: 1 mechanical agitation are to uniformly, obtain novel
High rigidity anticorrosive paint.
Embodiment 4:
A kind of preparation method of novel high rigidity anticorrosive paint, its step is as follows:
(1) preparation of nano dispersion fluid:
According to parts by weight, take Nano carbon white 2 parts, nano alumina powder 2 parts, nano barium sulfate 1 part, make medium with isopropanol
Being configured to suspension, high speed dispersion is uniform, then ultrasonic disperse 20min;
A certain amount of silane coupler is dissolved in isopropanol medium, high-speed stirred 20min under room temperature.
Mix above-mentioned 2 kinds of solution, ultrasonic disperse 25min according to the ratio of weight ratio 1:1, then keep 30 DEG C in thermostatical oil
In bath, stirring, makes coupling reaction 2h, prepares nano dispersion fluid with standby;
(2) component A is prepared:
According to parts by weight, 50 parts of epoxy resin liquid adds nano dispersion fluid 10 parts, zinc phosphate 2 parts, pigment 8 parts, Talcum
18 parts of powder, calcium silicates 3 parts, mullite part 0.8 part, 0.5 part of mafic spinel brick 200 mesh powder, solvent 20 parts, according to coating 1:
The ratio of 1 adds abrasive media, carries out ball milling with high-speed grinder, until coating fineness is less than 80 μm, prepares component A;
(3) using cashew shell oil firming agent as B component, under room temperature, both in mass ratio 2: 1 mechanical agitation are to uniformly, obtain novel
High rigidity anticorrosive paint.
Embodiment 5:
A kind of preparation method of novel high rigidity anticorrosive paint, its step is as follows:
(1) preparation of nano dispersion fluid:
According to parts by weight, take Nano carbon white 4 parts, nano alumina powder 2 parts, nano barium sulfate 1 part, make medium with isopropanol
Being configured to suspension, high speed dispersion is uniform, then ultrasonic disperse 20min;
A certain amount of silane coupler is dissolved in isopropanol medium, high-speed stirred 20min under room temperature.
Mix above-mentioned 2 kinds of solution, ultrasonic disperse 25min according to the ratio of weight ratio 1:1, then keep 30 DEG C in thermostatical oil
In bath, stirring, makes coupling reaction 2h, prepares nano dispersion fluid with standby;
(2) component A is prepared:
According to parts by weight, 50 parts of epoxy resin liquid adds nano dispersion fluid 12 parts, zinc phosphate 2 parts, pigment 8 parts, Talcum
18 parts of powder, calcium silicates 3 parts, mullite part 0.8 part, 0.5 part of mafic spinel brick 200 mesh powder, solvent 20 parts, according to coating 1:
The ratio of 1 adds abrasive media, carries out ball milling with high-speed grinder, until coating fineness is less than 80 μm, prepares component A;
(3) using cashew shell oil firming agent as B component, under room temperature, both in mass ratio 2: 1 mechanical agitation are to uniformly, obtain novel
High rigidity anticorrosive paint.
Embodiment 6: effect is tested and assessed
According to GB/T 1,727 1992 " paint film is typically prepared method ", brush with hairbrush that economy-combat abrades rust, oil removal treatment is crossed
Tinplate (tinplate) is upper [specification 50mm × 100mm × (0.2-0.3) mm], and thickness is more than 100 μm, treats that coating is complete at 25 DEG C
Relevant rudimentary quantitative measurement is carried out after solidification.
The anticorrosive paint preparing embodiment 1-5 carries out the test of performance according to relevant criterion, result such as table 1 institute
Show:
Table 1
As can be seen here, the present invention provides a kind of novel high rigidity anticorrosive paint, its natural environmental-protective, has again good antiseptic property
And mechanical property, shelf characteric is stable, not free settling, and adhesive force is good, the most also the pencil hardness of superelevation.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto,
Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and
Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.
Claims (4)
1. a preparation method for novel high rigidity anticorrosive paint, its step is as follows:
(1) preparation of nano dispersion fluid:
Take Nano carbon white, nano alumina powder, nano barium sulfate, make medium with isopropanol and be configured to suspension, at a high speed
It is uniformly dispersed, then ultrasonic disperse 20min;
A certain amount of silane coupler is dissolved in isopropanol medium, high-speed stirred 20min under room temperature.
2. mix above-mentioned 2 kinds of solution, ultrasonic disperse 25min according to the ratio of weight ratio 1:1, then keep 30 DEG C in constant temperature oil bath
In pot, stirring, makes coupling reaction 2h, prepares nano dispersion fluid with standby;
(2) component A is prepared:
According to parts by weight, 50 parts of epoxy resin liquid adds nano dispersion fluid 10-12 part, zinc phosphate 2 parts, pigment 8 parts, slides
Stone powder 18 parts, calcium silicates 3 parts, mullite part 0.8 part, 0.5 part of mafic spinel brick 200 mesh powder, solvent 20 parts, according to coating
The ratio of 1: 1 adds abrasive media, carries out ball milling with high-speed grinder, until coating fineness is less than 80 μm, prepares A group
Point;
(3) using cashew shell oil firming agent as B component, under room temperature, both in mass ratio 2: 1 mechanical agitation are to uniformly, to obtain final product
Novel high rigidity anticorrosive paint.
3. the preparation method described in claim 1, it is characterised in that:
Described step (1) is: according to parts by weight, takes Nano carbon white 2-4 part, nano alumina powder 2 parts, nano barium sulfate 1
Part.
4. the novel high rigidity anticorrosive paint that the preparation method described in claim 1 or 2 obtains.