CN106084668A - 汽车制动器的制架的材料组成配方 - Google Patents
汽车制动器的制架的材料组成配方 Download PDFInfo
- Publication number
- CN106084668A CN106084668A CN201610666474.9A CN201610666474A CN106084668A CN 106084668 A CN106084668 A CN 106084668A CN 201610666474 A CN201610666474 A CN 201610666474A CN 106084668 A CN106084668 A CN 106084668A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide
- frame processed
- automotive brake
- graphite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及汽车制动器的制架的材料组成配方，按照重量份比例包括：铜25~45份、铝20~25份、氧化锌10~14份、石墨20~26份、二氧化硅18~28份、碳酸钙5~20份、干性油醇酸树脂10~15份、白炭黑12~15份、氧化钙16~28份、氧化亚铁10~12份和环氧树脂20~28份。本发明提供的配方配比，通过将铜、铝、氧化锌、石墨、二氧化硅、碳酸钙、干性油醇酸树脂、白炭黑、氧化钙、氧化亚铁和环氧树脂按照配比生产出来的制架，能够在高温中长时间使用，其抗热疲劳性能非常好，大大延长其使用寿命，避免影响汽车制动器的正常使用。
Description
技术领域
本发明涉及汽车零部件技术领域，尤其涉及汽车制动器的制架的材料组成配方。
背景技术
现有技术中，汽车制动器的制架，由于制造材料的原因，在使用的过程中，容易发热，导致制架经常处于高温的状态下运行，很容易使制架产生热疲劳现象，导致制架的使用寿命大大降低，从而影响汽车制动器的正常使用。
发明内容
本发明的根据现有技术的不足，本发明提供一种提高制架抗热疲劳的汽车制动器的制架的材料组成配方。
本发明是这样实现的，汽车制动器的制架的材料组成配方，按照重量份比例包括：铜25~45份、铝20~25份、氧化锌10~14份、石墨20~26份、二氧化硅18~28份、碳酸钙5~20份、干性油醇酸树脂10~15份、白炭黑12~15份、氧化钙16~28份、氧化亚铁10~12份和环氧树脂20~28份。
进一步的，按照重量份比例包括：铜25份、铝20份、氧化锌10份、石墨20份、二氧化硅18份、碳酸钙5份、干性油醇酸树脂10份、白炭黑12份、氧化钙16份、氧化亚铁10份和环氧树脂20份。
进一步的，按照重量份比例包括：铜45份、铝25份、氧化锌14份、石墨26份、二氧化硅28份、碳酸钙20份、干性油醇酸树脂15份、白炭黑15份、氧化钙28份、氧化亚铁12份和环氧树脂28份。
进一步的，按照重量份比例包括：铜35份、铝22份、氧化锌12份、石墨24份、二氧化硅25份、碳酸钙14份、干性油醇酸树脂12份、白炭黑13份、氧化钙20份、氧化亚铁11份和环氧树脂24份。
本发明提供的汽车制动器的制架的材料组成配方的优点在于：本发明提供的配方配比，通过将铜、铝、氧化锌、石墨、二氧化硅、碳酸钙、干性油醇酸树脂、白炭黑、氧化钙、氧化亚铁和环氧树脂按照配比生产出来的制架，能够在高温中长时间使用，其抗热疲劳性能非常好，大大延长其使用寿命，避免影响汽车制动器的正常使用。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
实施例一：
所述汽车制动器的制架的材料组成配方，按照重量份比例包括：铜25份、铝20份、氧化锌10份、石墨20份、二氧化硅18份、碳酸钙5份、干性油醇酸树脂10份、白炭黑12份、氧化钙16份、氧化亚铁10份和环氧树脂20份。
实施例二：
所述汽车制动器的制架的材料组成配方，按照重量份比例包括：铜45份、铝25份、氧化锌14份、石墨26份、二氧化硅28份、碳酸钙20份、干性油醇酸树脂15份、白炭黑15份、氧化钙28份、氧化亚铁12份和环氧树脂28份。
实施例三：
所述汽车制动器的制架的材料组成配方，按照重量份比例包括：铜35份、铝22份、氧化锌12份、石墨24份、二氧化硅25份、碳酸钙14份、干性油醇酸树脂12份、白炭黑13份、氧化钙20份、氧化亚铁11份和环氧树脂24份。
本发明提供的汽车制动器的制架的材料组成配方的优点在于：本发明提供的配方配比，通过将铜、铝、氧化锌、石墨、二氧化硅、碳酸钙、干性油醇酸树脂、白炭黑、氧化钙、氧化亚铁和环氧树脂按照配比生产出来的制架，能够在高温中长时间使用，其抗热疲劳性能非常好，大大延长其使用寿命，避免影响汽车制动器的正常使用。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。
Claims (4)
1.汽车制动器的制架的材料组成配方，其特征在于，按照重量份比例包括：铜25~45份、铝20~25份、氧化锌10~14份、石墨20~26份、二氧化硅18~28份、碳酸钙5~20份、干性油醇酸树脂10~15份、白炭黑12~15份、氧化钙16~28份、氧化亚铁10~12份和环氧树脂20~28份。
2.根据权利要求1所述的汽车制动器的制架的材料组成配方，其特征在于，按照重量份比例包括：铜25份、铝20份、氧化锌10份、石墨20份、二氧化硅18份、碳酸钙5份、干性油醇酸树脂10份、白炭黑12份、氧化钙16份、氧化亚铁10份和环氧树脂20份。
3.根据权利要求1所述的汽车制动器的制架的材料组成配方，其特征在于，按照重量份比例包括：铜45份、铝25份、氧化锌14份、石墨26份、二氧化硅28份、碳酸钙20份、干性油醇酸树脂15份、白炭黑15份、氧化钙28份、氧化亚铁12份和环氧树脂28份。
4.根据权利要求1所述的汽车制动器的制架的材料组成配方，其特征在于，按照重量份比例包括：铜35份、铝22份、氧化锌12份、石墨24份、二氧化硅25份、碳酸钙14份、干性油醇酸树脂12份、白炭黑13份、氧化钙20份、氧化亚铁11份和环氧树脂24份。