CN106084513A - A kind of New-style electrical wire insulant - Google Patents
A kind of New-style electrical wire insulant Download PDFInfo
- Publication number
- CN106084513A CN106084513A CN201610433936.2A CN201610433936A CN106084513A CN 106084513 A CN106084513 A CN 106084513A CN 201610433936 A CN201610433936 A CN 201610433936A CN 106084513 A CN106084513 A CN 106084513A
- Authority
- CN
- China
- Prior art keywords
- parts
- plasticizer
- insulant
- new
- electrical wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
nullThe invention discloses a kind of New-style electrical wire insulant,Relate to electrical engineering technical field,Wherein the weight part ratio of insulant is: nano ceramics 40 50 parts、Polyurethane 10 19 parts、Chlorinated polyethylene rubber 20 40 parts、Carborundum 15 22 parts、Blanc fixe 28、Sodium silicate 1.8 4.2 parts、Rubber 25 parts、Xylenols 8 11 parts、Croci 26 parts、1.5 1.9 parts of sulfur、Ethanedioic acid polyester 9 17 parts、Cyclohexane cyclohexanedimethanodibasic 2-glycidyl ester 12 16 parts、Meerschaum 4 12 parts、Colophonium 27 parts and binding agent 48 parts、Plasticizer 6 10 parts,The New-style electrical wire insulant of the present invention is with nano ceramics as primary raw material,Remaining each raw material acts on jointly,Cooperate,The insulant making the present invention has good insulating properties,And intensity is high,High temperature resistant,High-frequency loss is little,Humidity resistance is good,Have excellent fire-retardant、Ageing-resistant performance,Service life is long,It is suitable as electric wire to use.
Description
Technical field
The present invention relates to electrical engineering technical field, particularly relate to a kind of New-style electrical wire insulant.
Background technology
By the definition of standard GB/T 2900.5 regulation insulant it is: " be used for making device at the material electrically insulated
Material ".Namely can stop the material that electric current passes through.Its resistivity is the highest, generally 10^9~10^22 Ω m's
In the range of.As in motor, turn-to-turn isolation the stator core with ground connection are kept apart by the insulant around conductor, to protect
The safe operation of card motor.
Power industry is in the high-speed developing period at present, and electric equipment products have spread to industry-by-industry.Electric equipment products exhausted
It is the highest that edge requires, although on market, existing surface insulation description of materials is a lot, and Performance comparision is single, its purposes specific aim
Very strong, protection against the tide, anticorrosion, high temperature resistant, the requirement of insulation can't be accomplished, the class of insulation of insulant is inadequate, limit electrical equipment,
The development of electromechanics trade.
The Chinese patent application file of Application No. 201510222093.7, relates to a kind of electric wire insulant, is used for
Making up the deficiencies in the prior art, and provide a kind of capacitor film PP composite material, the weight part ratio of described material is:
Nano ceramics 30-40 part, molybdenum dioxide 2-8 part, polyurethane 12-18 part, carborundum 15-22 part, sodium silicate 1.5-
3.2 parts, rubber 1-3 part, xylenols 10-14 part, sulfur 1.2-1.8 part, ethanedioic acid polyester 10-15 part, hexamethylene
Alkane dioctyl phthalate 2-glycidyl ester 10-15 part, Colophonium 2-6 part and binding agent 2-6 part.The insulant of the present invention has
Good insulating properties, and intensity is high, humidity resistance is good.
The Chinese patent application file of Application No. 201310679919.3, relates to a kind of cable insulation material, for existing
With the presence of the deficiency of technology, the technical problem to be solved is to provide that a kind of hot strength is high, high temperature resistant, burning time
The wire-insulating material of two English harmful to biology will not be discharged.The weight part ratio of described material is: chlorinated polyethylene rubber
30~50;Magnesium hydroxide 10~15;Plasticizer 5~8;Blanc fixe 3~6;Croci 4~12;Meerschaum 6~15;
Paraffin hydrocarbon ils 5~7.The hot strength of flame retardant flexible wire cable insulating layer of the present invention or jacket composition is higher, up to
12MPA, uses temperature higher, can be used as 105 DEG C of lines and uses.
But above-mentioned insulant is during manufacturing and using, owing to electric wire intensity height is the most non-moistureproof, good insulating
But non-refractory, both can not get both, and brings the inconvenience in use.
Summary of the invention
The technical problem to be solved of the present invention is to provide a kind of New-style electrical wire insulant, to solve in prior art
Electric wire in use intensity is low, and loss is big, and humidity resistance is bad, the most aging, the defect that service life is short.
In order to realize the purpose of the present invention, the present invention provide a kind of New-style electrical wire insulant, it is characterized in that: described newly
The weight part ratio of type wire-insulating material: nano ceramics 40-50 part, polyurethane 10-19 part, chlorinated polyethylene rubber 20-40
Part, carborundum 15-22 part, blanc fixe 2-8 part, sodium silicate 1.8-4.2 part, rubber 2-5 part, xylenols 8-11
Part, croci 2-6 part, sulfur 1.5-1.9 part, ethanedioic acid polyester 9-17 part, cyclohexane cyclohexanedimethanodibasic 2-glycidyl
Ester 12-16 part, meerschaum 4-12 part, Colophonium 2-7 part and binding agent 4-8 part, plasticizer 6-10 part.
Preferably, described binding agent uses epoxy resin, phenolic resin, acrylic acid, polyvinyl acetate and silane coupled
The mixture of agent.
Preferably, the parts by weight of each component of described binding agent be epoxy resin 8-13 part, phenolic resin 2-5 part,
Acrylic acid 2-4 part, polyvinyl acetate 3-6 part and silane coupler 1-3 part.
Preferably, the production stage of described binding agent: by epoxy resin, phenolic resin with polyvinyl acetate at stirring bar
Add in acrylic acid under part, be to slowly warm up to 35-45 DEG C, after adding silane coupler, be warming up to 55-65 DEG C, keep 5-
6min, binding agent.
Preferably, described plasticizer uses trimellitic acid class plasticizer, PMA class plasticizer and aliphatic plasticizer.
Preferably, the parts by weight of each component of described plasticizer are trimellitic acid class plasticizer 4-6 part, the increasing of PMA class
Mould agent 6-8 part and aliphatic plasticizer 8-10 part.
The beneficial effects of the present invention is:
1, the New-style electrical wire insulant of the present invention is with nano ceramics as primary raw material, and remaining each raw material acts on jointly, phase interworking
Close so that the insulant of the present invention has good insulating properties.
2, this insulant intensity is high, and high temperature resistant, high-frequency loss is little, and humidity resistance is good, has excellent fire-retardant, ageing-resistant
Performance, service life are long, are suitable as electric wire and use.
3, binding agent is epoxy resin, phenolic resin, acrylic acid, polyvinyl acetate acid esters and the mixing of silane coupler
Thing, is mixed by high temperature, has good cohesive.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention is described in further details.
Embodiment 1
A kind of New-style electrical wire insulant, is characterized in that: the weight part ratio of described New-style electrical wire insulant: nano ceramics 40
Part, polyurethane 19 parts, chlorinated polyethylene rubber 40 parts, carborundum 18.5 parts, blanc fixe 2 parts, sodium silicate 1.8 parts, rubber
5 parts of glue, xylenols 11 parts, croci 4 parts, 1.7 parts of sulfur, ethanedioic acid polyester 13 parts, cyclohexane cyclohexanedimethanodibasic
2-glycidyl ester 12 parts, meerschaum 12 parts, Colophonium 4.5 parts and binding agent 8 parts, plasticizer 8 parts.
In the present invention, described binding agent uses epoxy resin, phenolic resin, acrylic acid, polyvinyl acetate and silane
The mixture of coupling agent.
In the present invention, the parts by weight of each component of described binding agent be epoxy resin 8 parts, 2 parts of phenolic resin, third
Olefin(e) acid 2 parts, polyvinyl acetate 3 parts and silane coupler 1 part.
In the present invention, the production stage of described binding agent: epoxy resin, phenolic resin are being stirred with polyvinyl acetate
Add in acrylic acid under the conditions of mixing, be to slowly warm up to 40 DEG C, after adding silane coupler, be warming up to 60 DEG C, keep 5.5min,
Binding agent.
In the present invention, described plasticizer uses trimellitic acid class plasticizer, PMA class plasticizer and aliphatic series plasticising
Agent.
In the present invention, the parts by weight of each component of described plasticizer are trimellitic acid class plasticizer 6 parts, PMA class
Plasticizer 8 parts and aliphatic plasticizer 10 parts.
Wherein, the New-style electrical wire insulant of the present invention is with nano ceramics as primary raw material, and remaining each raw material acts on jointly,
Cooperate so that the insulant of the present invention has good insulating properties, and intensity is high, and high temperature resistant, high-frequency loss is little, anti-
Tide performance is good, has excellent fire-retardant, ageing-resistant performance, service life long, is suitable as electric wire and uses;Binding agent is epoxy
Resin, phenolic resin, acrylic acid, polyvinyl acetate acid esters and the mixture of silane coupler, mixed by high temperature, has good
Cohesive.
Embodiment 2
A kind of New-style electrical wire insulant, is characterized in that: the weight part ratio of described New-style electrical wire insulant: nano ceramics 50
Part, polyurethane 10 parts, chlorinated polyethylene rubber 20 parts, carborundum 15 parts, blanc fixe 8 parts, sodium silicate 3 parts, rubber 2
Part, xylenols 8 parts, croci 6 parts, 1.5 parts of sulfur, ethanedioic acid polyester 17 parts, cyclohexane cyclohexanedimethanodibasic 2-glycidyl
Ester 16 parts, meerschaum 4 parts, Colophonium 2 parts and binding agent 4 parts, plasticizer 6 parts.
In the present invention, described binding agent uses epoxy resin, phenolic resin, acrylic acid, polyvinyl acetate and silane
The mixture of coupling agent.
In the present invention, the parts by weight of each component of described binding agent are epoxy resin 10.5 parts, phenolic resin 3.5
Part, 3 parts of acrylic acid, polyvinyl acetate 4.5 parts and silane coupler 2 parts.
In the present invention, the production stage of described binding agent: epoxy resin, phenolic resin are being stirred with polyvinyl acetate
Add in acrylic acid under the conditions of mixing, be to slowly warm up to 45 DEG C, after adding silane coupler, be warming up to 65 DEG C, keep 6min,
Obtain binding agent.
In the present invention, described plasticizer uses trimellitic acid class plasticizer, PMA class plasticizer and aliphatic series plasticising
Agent.
In the present invention, the parts by weight of each component of described plasticizer are trimellitic acid class plasticizer 4 parts, PMA class
Plasticizer 6 parts and aliphatic plasticizer 8 parts.
Wherein, the New-style electrical wire insulant of the present invention is with nano ceramics as primary raw material, and remaining each raw material acts on jointly,
Cooperate so that the insulant of the present invention has good insulating properties, and intensity is high, and high temperature resistant, high-frequency loss is little, anti-
Tide performance is good, has excellent fire-retardant, ageing-resistant performance, service life long, is suitable as electric wire and uses;Binding agent is epoxy
Resin, phenolic resin, acrylic acid, polyvinyl acetate acid esters and the mixture of silane coupler, mixed by high temperature, has good
Cohesive.
Embodiment 3
A kind of New-style electrical wire insulant, is characterized in that: the weight part ratio of described New-style electrical wire insulant: nano ceramics 45
Part, polyurethane 14.5 parts, chlorinated polyethylene rubber 30 parts, carborundum 22 parts, blanc fixe 5 parts, sodium silicate 4.2 parts, rubber
3.5 parts, xylenols 9.5 parts, croci 2 parts, 1.9 parts of sulfur, ethanedioic acid polyester 9 parts, cyclohexane cyclohexanedimethanodibasic two shrink
Glyceride 14 parts, meerschaum 8 parts, Colophonium 7 parts and binding agent 6 parts, plasticizer 10 parts.
In the present invention, described binding agent uses epoxy resin, phenolic resin, acrylic acid, polyvinyl acetate and silane
The mixture of coupling agent.
In the present invention, the parts by weight of each component of described binding agent be epoxy resin 13 parts, 5 parts of phenolic resin,
4 parts of acrylic acid, polyvinyl acetate 6 parts and silane coupler 3 parts.
In the present invention, the production stage of described binding agent: epoxy resin, phenolic resin are being stirred with polyvinyl acetate
Add in acrylic acid under the conditions of mixing, be to slowly warm up to 35 DEG C, after adding silane coupler, be warming up to 55 DEG C, keep 5min, i.e.
Binding agent can be obtained.
In the present invention, described plasticizer uses trimellitic acid class plasticizer, PMA class plasticizer and aliphatic series plasticising
Agent.
In the present invention, the parts by weight of each component of described plasticizer are trimellitic acid class plasticizer 5 parts, PMA class
Plasticizer 7 parts and aliphatic plasticizer 9 parts.
Wherein, the New-style electrical wire insulant of the present invention is with nano ceramics as primary raw material, and remaining each raw material acts on jointly,
Cooperate so that the insulant of the present invention has good insulating properties, and intensity is high, and high temperature resistant, high-frequency loss is little, anti-
Tide performance is good, has excellent fire-retardant, ageing-resistant performance, service life long, is suitable as electric wire and uses;Binding agent is epoxy
Resin, phenolic resin, acrylic acid, polyvinyl acetate acid esters and the mixture of silane coupler, mixed by high temperature, has good
Cohesive.
As known by the technical knowledge, the present invention can be by other essence without departing from its spirit or the embodiment party of essential feature
Case realizes.Therefore, embodiment disclosed above, for each side, all it is merely illustrative, is not only.Institute
The change within the scope of the present invention or within being equal to the scope of the present invention is had all to be included in the invention.
Claims (6)
1. a New-style electrical wire insulant, is characterized in that: the weight part ratio of described New-style electrical wire insulant: nano ceramics
40-50 part, polyurethane 10-19 part, chlorinated polyethylene rubber 20-40 part, carborundum 15-22 part, blanc fixe 2-8 part,
Sodium silicate 1.8-4.2 part, rubber 2-5 part, xylenols 8-11 part, croci 2-6 part, sulfur 1.5-1.9
Part, ethanedioic acid polyester 9-17 part, cyclohexane cyclohexanedimethanodibasic 2-glycidyl ester 12-16 part, meerschaum 4-12 part, Colophonium 2-7
Part and binding agent 4-8 part, plasticizer 6-10 part.
A kind of New-style electrical wire insulant the most according to claim 1, it is characterised in that: described binding agent uses asphalt mixtures modified by epoxy resin
The mixture of fat, phenolic resin, acrylic acid, polyvinyl acetate and silane coupler.
A kind of New-style electrical wire insulant the most according to claim 2, it is characterised in that: the weight of each component of described binding agent
Amount number is epoxy resin 8-13 part, phenolic resin 2-5 part, acrylic acid 2-4 part, polyvinyl acetate 3-6 part and silicon
Alkane coupling agent 1-3 part.
A kind of New-style electrical wire insulant the most according to claim 3, it is characterised in that: the production step of described binding agent
Rapid: epoxy resin, phenolic resin to be added in acrylic acid under agitation with polyvinyl acetate, is to slowly warm up to 35-45
DEG C, add after silane coupler and be warming up to 55-65 DEG C, keep 5-6min, binding agent.
A kind of New-style electrical wire insulant the most according to claim 1, it is characterised in that: described plasticizer uses inclined benzene three
Acids plasticizer, PMA class plasticizer and aliphatic plasticizer.
A kind of New-style electrical wire insulant the most according to claim 5, it is characterised in that: the weight of each component of described plasticizer
Amount number is trimellitic acid class plasticizer 4-6 part, PMA class plasticizer 6-8 part and aliphatic plasticizer 8-10 part.