CN106084442A - High performance low smoke non-halogen flame-retardant cable - Google Patents
High performance low smoke non-halogen flame-retardant cable Download PDFInfo
- Publication number
- CN106084442A CN106084442A CN201610577279.9A CN201610577279A CN106084442A CN 106084442 A CN106084442 A CN 106084442A CN 201610577279 A CN201610577279 A CN 201610577279A CN 106084442 A CN106084442 A CN 106084442A
- Authority
- CN
- China
- Prior art keywords
- agent
- cable
- high performance
- granule
- halogen flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high performance low smoke non-halogen flame-retardant cable, the formula of this CABLE MATERIALS includes: EVA granule 15 40%, HDPE granule 15 40%, carbon forming agent 5 15%, plasticizer 5 10%, magnesium hydroxide 1 10%, surfactant 1 5%, red phosphorus 2 6%, compatilizer 1 5%, coupling agent 0 2%, anti-irradiation agent 2 6%, anti-dripping agent 0 3%;The low-smoke halogen-free inflaming-retarding cable overall performance using cable material formula of the present invention to produce is higher, will not send toxic smog, has non-shifting and good elasticity and viscosity during burning.
Description
Technical field
The present invention relates to field of cable technology, particularly relate to a kind of high performance fireproofing cable material without halide.
Background technology
CABLE MATERIALS is one of primary raw material producing cable, the CABLE MATERIALS performance fall of existing production low-smoke halogen-free inflaming-retarding cable
Low, general of the service life causing cable is on the low side, and therefore, the problem solving this class is particularly important.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of high performance low smoke non-halogen flame-retardant cable, by improving
The formula of CABLE MATERIALS improves the overall performance of low-smoke halogen-free cable.
In order to solve the problems referred to above, the invention provides a kind of high performance low smoke non-halogen flame-retardant cable, this CABLE MATERIALS
Formula includes: EVA granule 15-40%, HDPE granule 15-40%, carbon forming agent 5-15%, plasticizer 5-10%, magnesium hydroxide 1-
10%, surfactant 1-5%, red phosphorus 2-6%, compatilizer 1-5%, coupling agent 0-2%, anti-irradiation agent 2-6%, anti-dripping agent 0-3%.
Further improvement is that: the formula of this CABLE MATERIALS described is: EVA granule 30%, HDPE granule 30%, carbon forming agent 10%,
Plasticizer 7%, magnesium hydroxide 6%, surfactant 3%, red phosphorus 4%, compatilizer 3%, coupling agent 1%, anti-irradiation agent 4%, anti-dripping agent
2%。
Further improvement is that: described surfactant and coupling agent spread upon the surface of magnesium hydroxide uniformly.
The invention has the beneficial effects as follows: the low-smoke halogen-free inflaming-retarding cable using cable material formula of the present invention to produce is overall
Performance is higher, will not send toxic smog, has non-shifting and good elasticity and viscosity during burning.
Detailed description of the invention
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the present invention is further described, the present embodiment
It is only used for explaining the present invention, is not intended that limiting the scope of the present invention.
Embodiment one
Present embodiments providing a kind of high performance low smoke non-halogen flame-retardant cable, the formula of this CABLE MATERIALS includes: EVA granule
40%, HDPE granule 40%, carbon forming agent 5%, plasticizer 5%, magnesium hydroxide 1%, surfactant 1%, red phosphorus 2%, compatilizer 1%, idol
Connection agent 1%, anti-irradiation agent 3%, anti-dripping agent 1%.Described surfactant and coupling agent spread upon the table of magnesium hydroxide uniformly
Face.
Embodiment two
The formula of this CABLE MATERIALS described is: EVA granule 25%, HDPE granule 25%, carbon forming agent 20%, plasticizer 7%, magnesium hydroxide
6%, surfactant 3%, red phosphorus 4%, compatilizer 3%, coupling agent 1%, anti-irradiation agent 4%, anti-dripping agent 2%.Described surfactant
The surface of magnesium hydroxide is spread upon uniformly with coupling agent.
Embodiment three
Present embodiments providing a kind of high performance low smoke non-halogen flame-retardant cable, the formula of this CABLE MATERIALS includes: EVA granule
20%, HDPE granule 18%, carbon forming agent 15%, plasticizer 10%, magnesium hydroxide 10%, surfactant 5%, red phosphorus 6%, compatilizer 5%,
Coupling agent 2%, anti-irradiation agent 6%, anti-dripping agent 3%.Described surfactant and coupling agent spread upon the table of magnesium hydroxide uniformly
Face.
The low-smoke halogen-free inflaming-retarding cable overall performance using cable material formula of the present invention to produce is higher, will not during burning
Send toxic smog, there is non-shifting and good elasticity and viscosity.
Claims (3)
1. a high performance low smoke non-halogen flame-retardant cable, it is characterised in that: the formula of this CABLE MATERIALS includes: EVA granule 15-
40%, HDPE granule 15-40%, carbon forming agent 5-15%, plasticizer 5-10%, magnesium hydroxide 1-10%, surfactant 1-5%, red phosphorus
2-6%, compatilizer 1-5%, coupling agent 0-2%, anti-irradiation agent 2-6%, anti-dripping agent 0-3%.
2. high performance low smoke non-halogen flame-retardant cable as claimed in claim 1, it is characterised in that: the formula of this CABLE MATERIALS is:
EVA granule 30%, HDPE granule 30%, carbon forming agent 10%, plasticizer 7%, magnesium hydroxide 6%, surfactant 3%, red phosphorus 4%, compatible
Agent 3%, coupling agent 1%, anti-irradiation agent 4%, anti-dripping agent 2%.
3. claim 1-2 arbitrarily as described in high performance low smoke non-halogen flame-retardant cable, it is characterised in that: described surface activity
Agent and coupling agent spread upon the surface of magnesium hydroxide uniformly.