CN106082762A - A kind of PMA MPEG type poly carboxylic acid series water reducer - Google Patents
A kind of PMA MPEG type poly carboxylic acid series water reducer Download PDFInfo
- Publication number
- CN106082762A CN106082762A CN201610401969.9A CN201610401969A CN106082762A CN 106082762 A CN106082762 A CN 106082762A CN 201610401969 A CN201610401969 A CN 201610401969A CN 106082762 A CN106082762 A CN 106082762A
- Authority
- CN
- China
- Prior art keywords
- pma
- parts
- mpeg
- carboxylic acid
- water reducer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of PMA MPEG type poly carboxylic acid series water reducer, belong to chemical field.It is prepared from by following raw material: polymaleic anhydride (PMA) 40 60 parts, poly glycol monomethyl ether (MPEG) 100 110 parts, Polyethylene Glycol (PEG) 10 20 parts, concentrated sulphuric acid 0.06 0.10 parts, toluene 70 80 parts.Synthesis step of the present invention is simple, and product comb shaped structure is obvious, can be greatly increased concrete dispersibility.
Description
Technical field
The present invention relates to chemical field, be specifically related to a kind of PMA-MPEG type poly carboxylic acid series water reducer
Background technology
Polycarboxylic acid series high efficiency water reducing agent be continue with the wood calcium first generation water reducer as representative and with naphthalene system as representative second
For the third generation high-performance water reducing agent grown up after water reducer.The water-reducing mechanism brand-new due to it and distinctive molecule knot
Structure, it has compared with conventional naphthalene system and melamine system second filial generation high efficiency water reducing agent, and volume is low, reinforced effects good, flowing retentivity
Good, loss of slump is low, lower shrinkage, have certain amount of air entrainment and the plurality of advantages such as get along with environmental friendliness, substantially meet
The concrete works particularly high performance concrete performance requirement to water reducer, becomes the representative product of third generation high efficiency water reducing agent
Product.Additionally, polycarboxylate high performance water-reducing agent product has the implication of seriation.Owing to it is mainly existed by unsaturated monomer
Copolymerization under the effect of initiator, by the side chain graft with active group to obtaining on main polymer chain, the most different
Carboxylic unsaturated monomer, the different activated monomers containing functional functional group, and compound mode different between monomer, no
Same synthetic technology route, can obtain the multiple carboxylic acid copolymer with different structure and performance characteristics.
Summary of the invention
For above-mentioned, it is an object of the invention to provide one.
The concrete technical scheme that the present invention takes is:
A kind of PMA-MPEG type poly carboxylic acid series water reducer, it is characterised in that by weight, be made up of following raw material: poly-horse
Come anhydride (PMA) 40-60 part, poly glycol monomethyl ether (MPEG) 100-110 part, Polyethylene Glycol (PEG) 10-20 part, concentrated sulphuric acid
0.06-0.10 part, toluene 70-80 part.
Present invention also offers a kind of PMA-MPEG type poly carboxylic acid series water reducer manufacture method, comprise the following steps:
(1) add in there-necked flask after polymaleic anhydride, poly glycol monomethyl ether and Polyethylene Glycol being weighed in proportion.Gu
Add due to reaction;
(2) in there-necked flask, instill concentrated sulphuric acid, add reflux, wherein add toluene as water entrainer.It is heated to
60 DEG C and stir, isothermal reaction stopped after 5 hours;
(3) taking off reaction bulb, decompression distills out lower tape water preparation and unreacting material, cold goes to room temperature, adds appropriate
Distilled water dissolves, and neutralizing by NaOH solution is PH=7-8.
The invention have the advantage that synthesis step is simple, product comb shaped structure is obvious, can be greatly increased concrete dispersibility.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that thus protection scope of the present invention is made apparent clear and definite defining.
Embodiment 1
A kind of PMA-MPEG type poly carboxylic acid series water reducer, it is characterised in that by weight, be made up of following raw material: poly-horse
Come 40 parts of anhydride (PMA), poly glycol monomethyl ether (MPEG) 100 parts, Polyethylene Glycol (PEG) 10 parts, concentrated sulphuric acid 0.06 part, toluene
70 parts.
Its concrete manufacturing process comprises the steps of
(1) add in there-necked flask after polymaleic anhydride, poly glycol monomethyl ether and Polyethylene Glycol being weighed in proportion.Gu
Add due to reaction;
(2) in there-necked flask, instill concentrated sulphuric acid, add reflux, wherein add toluene as water entrainer.It is heated to
60 DEG C and stir, isothermal reaction stopped after 5 hours;
(3) taking off reaction bulb, decompression distills out lower tape water preparation and unreacting material, cold goes to room temperature, adds appropriate
Distilled water dissolves, and neutralizing by NaOH solution is PH=7-8.
Embodiment 2
A kind of PMA-MPEG type poly carboxylic acid series water reducer, it is characterised in that by weight, be made up of following raw material: poly-horse
Come 50 parts of anhydride (PMA), poly glycol monomethyl ether (MPEG) 105 parts, Polyethylene Glycol (PEG) 15 parts, concentrated sulphuric acid 0.08 part, toluene
75 parts.
Its concrete manufacturing process comprises the steps of
(1) add in there-necked flask after polymaleic anhydride, poly glycol monomethyl ether and Polyethylene Glycol being weighed in proportion.Gu
Add due to reaction;
(2) in there-necked flask, instill concentrated sulphuric acid, add reflux, wherein add toluene as water entrainer.It is heated to
60 DEG C and stir, isothermal reaction stopped after 5 hours;
(3) taking off reaction bulb, decompression distills out lower tape water preparation and unreacting material, cold goes to room temperature, adds appropriate
Distilled water dissolves, and neutralizing by NaOH solution is PH=7-8.
Embodiment 3
A kind of PMA-MPEG type poly carboxylic acid series water reducer, it is characterised in that by weight, be made up of following raw material: poly-horse
Come 60 parts of anhydride (PMA), poly glycol monomethyl ether (MPEG) 110 parts, Polyethylene Glycol (PEG) 20 parts, concentrated sulphuric acid 0.10 part, toluene
80 parts.
Its concrete manufacturing process comprises the steps of
(1) add in there-necked flask after polymaleic anhydride, poly glycol monomethyl ether and Polyethylene Glycol being weighed in proportion.Gu
Add due to reaction;
(2) in there-necked flask, instill concentrated sulphuric acid, add reflux, wherein add toluene as water entrainer.It is heated to
60 DEG C and stir, isothermal reaction stopped after 5 hours;
(3) taking off reaction bulb, decompression distills out lower tape water preparation and unreacting material, cold goes to room temperature, adds appropriate
Distilled water dissolves, and neutralizing by NaOH solution is PH=7-8.
Claims (4)
1. a PMA-MPEG type poly carboxylic acid series water reducer, it is characterised in that be prepared from by following raw material: poly-Malaysia
Anhydride (PMA) 40-60 part, poly glycol monomethyl ether (MPEG) 100-110 part, Polyethylene Glycol (PEG) 10-20 part, concentrated sulphuric acid
0.06-0.10 part, toluene 70-80 part.
PMA-MPEG type poly carboxylic acid series water reducer the most according to claim 1, it is characterised in that by following raw material
It is prepared from: polymaleic anhydride (PMA) 45-55 part, poly glycol monomethyl ether (MPEG) 103-107 part, Polyethylene Glycol (PEG)
13-17 part, concentrated sulphuric acid 0.07-0.09 part, toluene 73-77 part.
PMA-MPEG type poly carboxylic acid series water reducer the most according to claim 1, it is characterised in that by following raw material
It is prepared from: polymaleic anhydride (PMA) 50 parts, poly glycol monomethyl ether (MPEG) 105 parts, Polyethylene Glycol (PEG) 15 parts, dense sulfur
Acid 0.08 part, toluene 75 parts.
4. the preparation method of a PMA-MPEG type poly carboxylic acid series water reducer, it is characterised in that comprise the following steps:
(1) add in there-necked flask after polymaleic anhydride, poly glycol monomethyl ether and Polyethylene Glycol being weighed in proportion.It is fixed on
Reaction adds;
(2) in there-necked flask, instill concentrated sulphuric acid, add reflux, wherein add toluene as water entrainer.It is heated to 60 DEG C
And stir, isothermal reaction stopped after 5 hours;
(3) taking off reaction bulb, decompression distills out lower tape water preparation and unreacting material, cold goes to room temperature, adds appropriate distillation
Water dissolution, neutralizing by NaOH solution is PH=7-8.