CN106076061B - Taste removal agent material for fresh preservation - Google Patents
Taste removal agent material for fresh preservation Download PDFInfo
- Publication number
- CN106076061B CN106076061B CN201610511523.1A CN201610511523A CN106076061B CN 106076061 B CN106076061 B CN 106076061B CN 201610511523 A CN201610511523 A CN 201610511523A CN 106076061 B CN106076061 B CN 106076061B
- Authority
- CN
- China
- Prior art keywords
- solution
- removal agent
- agent material
- taste removal
- solid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of taste removal agent material for fresh preservation, preparation method is:Inorganic matter is obtained into solids A with acid soak;Prepare aqueous slkali B;By solids A and solution B by mixing, it is dehydrated, it is dry, solid C is calcined to obtain in nitrogen atmosphere;Prepare the solution D of citric acid or polyvinyl alcohol;Solid C and solution D are mixed, filtered, it is dry, it is cooling, grind to obtain solid absorbent E;PVA solution is prepared, solid absorbent E is added, suspension is mixed to obtain;Gained suspension is atomized, the droplet drying of atomization, is placed in glutaraldehyde steam reacting drying to obtain the final product.The taste removal agent material of the present invention can adsorb a variety of organic gases and inorganic gas, can be used for adsorbing and eliminate the peculiar smell in fresh cabinet.
Description
Technical field
The invention belongs to new material technology fields, and in particular to a kind of taste removal agent material for fresh preservation.
Background technology
With the continuous improvement of quality of life, people are especially also higher and higher to the quality requirement of food to the consumer goods,
And freezing and refrigeration product can make the raw and fresh food in fresh cabinet generate various smells or peculiar smell due to putting for a long time, some
Smell eliminates the quality that may influence raw and fresh food not in time, causes fruit well-done too early, and raw and fresh food is rotten to rot even to pollute
The problems such as, and still lack the new material eliminated for the peculiar smell in fresh cabinet at present.
Invention content
Problem provides a kind of taste removal agent material can be used for the anti-peculiar smell of fresh cabinet to the present invention for the above-mentioned prior art.
A kind of taste removal agent material of the present invention, is prepared using following methods step:
(1) by inorganic mineral nitric acid dousing 1-2 hours, it is washed to neutrality, obtains solids A;It is 5% to prepare mass concentration
~8% aqueous slkali B;It is 1 in mass ratio by solids A and solution B:2 are mixed, and are dehydrated, dry, in nitrogen atmosphere in
800~1200 DEG C are calcined 10~40 minutes, and solid C is obtained;
(2) solution D that mass concentration is 10%~15% is prepared;The solution D is citric acid or polyvinyl alcohol and water shape
At mixed liquor;Solid C and solution D are pressed 1:1~5 mass ratio is mixed, and is filtered, dry, cooling, grinds solid
Body adsorbent E;
(3) PVA solution for preparing mass concentration 5%~6%, is added solid absorbent E, suspension is mixed to obtain;It will
Gained suspension is atomized, and the droplet drying of atomization is placed in glutaraldehyde steam and react 1~2 hour, dry 2~8h to get.
Preferably, step (1) the nitric acid mass concentration 30%~40%.
It is calcined 20~30 minutes in 800~900 DEG C in nitrogen atmosphere after preferred steps (1) are dry.
Step (2) described solution D is citric acid solution.
Step (2) solid C and solution D mass ratio 1:2.
Step (3) solid absorbent E accounts for the 1%~2% of PVA solution quality.
The present invention ensure that inorganic mine by carrying out organically-modified by inorganic mineral and being handled by effective calcination process
The stabilization porous structure of object at low ambient temperatures makes inorganic mineral be provided with stronger capture to gas molecule by organically-modified
Ability, the taste removal agent material can effectively adsorb a variety of organic gases and inorganic gas in low temperature environment, can be used for inhaling
It echos and eliminates generated peculiar smell in the agricultural product especially raw and fresh food preservations such as vegetable and fruit.
Specific implementation mode
Embodiment 1
(1) preparation of solids A:By attapulgite 40% nitric acid dousing of mass concentration 1 hour, deionized water is then used
It cleans to neutrality;The potassium hydroxide solution of configuration quality a concentration of 5%, ie in solution B;It is 1 in mass ratio by A and B:2 are mixed
It closes, is dehydrated, it is dry, it is then calcined 30 minutes in 860 degrees Celsius in nitrogen atmosphere, obtains solution solids C.
(2) a concentration of 15% citric acid solution of configuration quality, ie in solution D;C and D is pressed 1:2 mass ratio is mixed,
It under 55 degrees Celsius, is stirred to react 2 hours, filters, it is dry, it is then heat-treated 30 minutes under 180 degrees Celsius, cooling, grinding
To 200 mesh, sieving obtains solid absorbent E.
(3) PVA solution for preparing mass concentration 6%, is added solid absorbent E, and solid absorbent accounts for PVA solution quality
2%, suspension is mixed to obtain;Gained suspension is atomized with sprayer, the droplet drying of atomization is subsequently placed in 55 and takes the photograph
Reacted 1 hour in the glutaraldehyde steam of family name's degree, after cross-linking reaction is complete, as 55 degrees Celsius of air drying 4h to get.
Embodiment 2
(1) preparation of solids A:By attapulgite 30% nitric acid dousing of concentration 2 hours, then cleaned with deionized water
To neutrality;;The potassium hydroxide solution of configuration quality a concentration of 8%, ie in solution B;It is 1 in mass ratio by A and B:2 are mixed,
Dehydration, it is dry, it is then calcined 25 minutes in 880 degrees Celsius in nitrogen atmosphere, obtains solution solids C.
(2) configuration concentration is 10% polyvinyl alcohol, ie in solution D;C and D is pressed 1:2 mass ratio is mixed, and is taken the photograph 55
It under family name's degree, is stirred to react 2 hours, filters, it is dry, then it is heat-treated 30 minutes under 180 degrees Celsius, it is cooling, it is ground to 200
Mesh, sieving, obtains solid absorbent E;
(3) PVA solution for preparing 5%, is added solid absorbent E, and solid absorbent accounts for the 1% of PVA solution quality, mixes
Stir to obtain suspension;Gained suspension is atomized with sprayer, the droplet drying of atomization is subsequently placed in the penta of 55 degrees Celsius
Reacted 1 hour in dialdehyde steam, after cross-linking reaction is complete, as 55 degrees Celsius of air drying 4h to get.
Claims (6)
1. a kind of taste removal agent material for fresh preservation is prepared using following methods step:
(1) by inorganic mineral nitric acid dousing 1-2 hours, it is washed to neutrality, obtains solids A;Prepare mass concentration be 5%~
8% aqueous slkali B;It is 1 in mass ratio by solids A and solution B:2 are mixed, and are dehydrated, dry, in 800 in nitrogen atmosphere
~1200 DEG C are calcined 10~40 minutes, and solid C is obtained;
(2) solution D that mass concentration is 10%~15% is prepared;The solution D is that citric acid or polyvinyl alcohol are formed with water
Mixed liquor;Solid C and solution D are pressed 1:1~5 mass ratio is mixed, and is filtered, dry, cooling, grinds to obtain solid suction
Attached dose of E;
(3) PVA solution for preparing mass concentration 5%~6%, is added solid absorbent E, suspension is mixed to obtain;By gained
Suspension is atomized, and the droplet drying of atomization is placed in glutaraldehyde steam and react 1~2 hour, dry 2~8h to get.
2. being used for the taste removal agent material of fresh preservation as described in claim 1, which is characterized in that step (1) the nitric acid quality
Concentration 30%~40%.
3. being used for the taste removal agent material of fresh preservation as described in claim 1, which is characterized in that in nitrogen after step (1) is dry
It is calcined 20~30 minutes in 800~900 DEG C in atmosphere.
4. being used for the taste removal agent material of fresh preservation as described in claim 1, which is characterized in that step (2) described solution D is lemon
Lemon acid solution.
5. being used for the taste removal agent material of fresh preservation as described in claim 1, which is characterized in that step (2) solid C and solution D
Mass ratio 1:2.
6. being used for the taste removal agent material of fresh preservation as described in claim 1, which is characterized in that step (3) solid absorbent E is accounted for
The 1%~2% of PVA solution quality.