CN106065288A - A kind of metal water-repellent preservation antirusting paint - Google Patents
A kind of metal water-repellent preservation antirusting paint Download PDFInfo
- Publication number
- CN106065288A CN106065288A CN201610580184.2A CN201610580184A CN106065288A CN 106065288 A CN106065288 A CN 106065288A CN 201610580184 A CN201610580184 A CN 201610580184A CN 106065288 A CN106065288 A CN 106065288A
- Authority
- CN
- China
- Prior art keywords
- parts
- zinc
- antirusting paint
- paint
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of metal water-repellent preservation antirusting paint, raw material is: Colophonium, deionized water, iron oxide red, zinc phosphate, zinc yellow, zinc oxide, barium sulfate, nitrile rubber, politef and chromium oxide；Film rust, smooth coating, thickness 55 75 μm, viscosity 45 65s, paint film is hard；Fineness 25 45 μm, glossiness 80 120, impact strength 50 90cm；Hardness 0.5 0.9, surface drying 5 25min, do solid work 25 45min, preparation method is simple, and raw material is simple and easy to get, can be with the widespread production not division of history into periods for current material.
Description
Technical field
The present invention relates to electronic technology field, particularly relate to a kind of metal water-repellent preservation antirusting paint.
Background technology
Coating, at the entitled paint of Chinese tradition.So-called coating is to be coated in be protected or decorated body surface, and
Can be with the continuous film of coated article formation firm attachment, it is common that based on resin or oil or emulsion, add or without face
Material, filler, add corresponding additive, with the formulated thick liquid of organic solvent or water.More authoritative " being coated with of China's coating circle
Material technique " book is defined such that " coating is a kind of material, and this material can be coated in thing by different construction technologies
Part surface, formation adheres to firmly, has some strength, continuous print solid film.The film common name film so formed, also known as paint film
Or coating.”
Coating (paint), our the most described paint is one therein.Refer to coat body surface certain
Under the conditions of can form thin film and play protection, decoration or other specific functions (water-repellent preservation is antirust, antirust, mildew-resistant, heat-resisting etc.)
One class I liquid I or solid material.Because coating in early days is mostly with vegetable oil as primary raw material, therefore also referred to as paint.Synthesize now tree
Fat instead of vegetable oil, therefore referred to as coating.Coating non-liquid, powdery paints is the big class of coating variety one.
Coating belongs to organic chemical industry's macromolecular material, and the film formed belongs to macromolecular compound type.According to the modern times
The classification of current chemical products, coating belongs to fine chemical product.It is multi-functional that modern coating the most progressively becomes a class
Engineering material, be an important industry in chemical industry.
Founding of New is over 60 years, along with the development of national economy every profession and trade, as its supporting coatings industry from one
The most unobtrusive individual little industry progressively develops into the requisite important industry of all fields of national economy.Through several generations
Struggle hard, pioneer and keep forging ahead, China has become second-biggest-in-the-world coating material production state and country of consumption, enters into world's coating industry
The main flow of development.
Antirust paint is a kind of chemistry protecting metal surfaces from air, sea water etc. or the coating of electrochemical corrosion.Main
Physical property to be divided into and the big class of chemically antirust paint two.The former is by the suitable cooperation of pigment and paint vehicle, formed fine and close paint film with
Stop the intrusion of corrosive substance, such as peelable rust cleaning, peelable rust cleaning, graphite antirust paint etc.；The latter presses down by the chemistry of rust resisting pigment
Rust effect, such as styrene, zinc chromate anti-rust paint etc..Antirust for metals such as bridge, boats and ships, pipelines.Styrene antirust paint is one
The paint that kind styrene and drying oil mix.Its permeability, wettability are good, and paint film is soft, attachment is strong, but is dried relatively
Slowly.Great additionally, due to styrene ratio, easily precipitate, and stored for a long time can be thickening, brushability is the most poor.
Summary of the invention
The present invention provides a kind of fast drying, moistureproof metal water-repellent preservation antirusting paint, solves existing metal and is coated with
Material is dried the technical problems such as slow and moisture-sensitive.
The present invention is by the following technical solutions: a kind of metal water-repellent preservation antirusting paint, its raw material is joined by mass fraction
Ratio is as follows: Colophonium 100 parts, deionized water 50-70 part, iron oxide red 10-30 part, zinc phosphate 5-25 part, zinc yellow 1-5 part, zinc oxide
1.5-5.5 part, barium sulfate 0.5-4.5 part, nitrile rubber 6-10 part, politef 15-35 part, chromium oxide 4-8 part.
As a preferred technical solution of the present invention: mass parts pressed by the raw material of described metal water-repellent preservation antirusting paint
Number proportioning is as follows: Colophonium 100 parts, deionized water 55-65 part, iron oxide red 15-25 part, zinc phosphate 10-20 part, zinc yellow 2-4 part, oxidation
Zinc 2.5-4.5 part, barium sulfate 1.5-3.5 part, nitrile rubber 7-9 part, politef 20-30 part, chromium oxide 5-7 part.
As a preferred technical solution of the present invention: mass parts pressed by the raw material of described metal water-repellent preservation antirusting paint
Number proportioning is as follows: Colophonium 100 parts, deionized water 55 parts, iron oxide red 15 parts, zinc phosphate 10 parts, zinc yellow 2 parts, zinc oxide 2.5 parts, sulfur
Acid barium 1.5 parts, nitrile rubber 7 parts, politef 20 parts, chromium oxide 5 parts.
As a preferred technical solution of the present invention: mass parts pressed by the raw material of described metal water-repellent preservation antirusting paint
Number proportioning is as follows: Colophonium 100 parts, deionized water 65 parts, iron oxide red 25 parts, zinc phosphate 20 parts, zinc yellow 4 parts, zinc oxide 4.5 parts, sulfur
Acid barium 3.5 parts, nitrile rubber 9 parts, politef 30 parts, chromium oxide 7 parts.
As a preferred technical solution of the present invention: mass parts pressed by the raw material of described metal water-repellent preservation antirusting paint
Number proportioning is as follows: Colophonium 100 parts, deionized water 60 parts, iron oxide red 20 parts, zinc phosphate 15 parts, zinc yellow 3 parts, zinc oxide 3.5 parts, sulfur
Acid barium 2.5 parts, nitrile rubber 8 parts, politef 25 parts, chromium oxide 6 parts.
Beneficial effect
A kind of metal water-repellent preservation antirusting paint of the present invention uses above technical scheme compared with prior art, tool
There is techniques below effect: 1, film rust, smooth coating, thickness 55-75 μm, viscosity 45-65s, paint film is hard；2, fineness
25-45 μm, glossiness 80-120, impact strength 50-90cm；3, hardness 0.5-0.9, surface drying 5-25min, do solid work 25-45min,
Preparation method is simple, and raw material is simple and easy to get, can be with the widespread production not division of history into periods for current material.
Detailed description of the invention
Below in conjunction with example, the invention will be further described, and embodiment is only used for that the present invention will be described, not
Constituting the restriction to right, other alternative means that it may occur to persons skilled in the art that, all in right of the present invention
In claimed range.
Embodiment 1:
The first step: weigh Colophonium 100 parts according to mass fraction proportioning, deionized water 50 parts, iron oxide red 10 parts, zinc phosphate 5 parts,
Zinc yellow 1 part, zinc oxide 1.5 parts, 0.5 part of barium sulfate, nitrile rubber 6 parts, politef 15 parts, chromium oxide 4 parts.
Second step: deionized water, zinc phosphate and zinc oxide are put in reactor, be heated to 100 DEG C, with 150r/min speed
Degree stirring 40min.
3rd step: add zinc yellow and iron oxide red, adds surplus stock at 160 DEG C and puts into grinder grinding after mix homogeneously
4h, packs after filtration.
Film rust, smooth coating, thickness 55 μm, viscosity 45s, paint film is hard；Fineness 45 μm, glossiness 80, impact
Intensity 50cm；Hardness 0.5, surface drying 25min, do solid work 45min, preparation method is simple, and raw material is simple and easy to get, can with widespread production also
Constantly replace current material.
Embodiment 2:
The first step: weigh Colophonium 100 parts, deionized water 70 parts, iron oxide red 30 parts, zinc phosphate 25 according to mass fraction proportioning
Part, zinc yellow 5 parts, zinc oxide 5.5 parts, 4.5 parts of barium sulfate, nitrile rubber 10 parts, politef 35 parts, chromium oxide 8 parts.
Second step: deionized water, zinc phosphate and zinc oxide are put in reactor, be heated to 140 DEG C, with 350r/min speed
Degree stirring 60min.
3rd step: add zinc yellow and iron oxide red, adds surplus stock at 200 DEG C and puts into grinder grinding after mix homogeneously
8h, packs after filtration.
Film rust, smooth coating, thickness 60 μm, viscosity 50s, paint film is hard；Fineness 40 μm, glossiness 90, impact
Intensity 60cm；Hardness 0.6, surface drying 20min, do solid work 40min, preparation method is simple, and raw material is simple and easy to get, can with widespread production also
Constantly replace current material.
Embodiment 3:
The first step: weigh Colophonium 100 parts, deionized water 55 parts, iron oxide red 15 parts, zinc phosphate 10 according to mass fraction proportioning
Part, zinc yellow 2 parts, zinc oxide 2.5 parts, 1.5 parts of barium sulfate, nitrile rubber 7 parts, politef 20 parts, chromium oxide 5 parts.
Second step: deionized water, zinc phosphate and zinc oxide are put in reactor, be heated to 100 DEG C, with 150r/min speed
Degree stirring 40min.
3rd step: add zinc yellow and iron oxide red, adds surplus stock at 160 DEG C and puts into grinder grinding after mix homogeneously
4h, packs after filtration.
Film rust, smooth coating, thickness 65 μm, viscosity 55s, paint film is hard；Fineness 35 μm, glossiness 100, impact
Intensity 70cm；Hardness 0.7, surface drying 15min, do solid work 35min, preparation method is simple, and raw material is simple and easy to get, can with widespread production also
Constantly replace current material.
Embodiment 4:
The first step: weigh Colophonium 100 parts, deionized water 65 parts, iron oxide red 25 parts, zinc phosphate 20 according to mass fraction proportioning
Part, zinc yellow 4 parts, zinc oxide 4.5 parts, 3.5 parts of barium sulfate, nitrile rubber 9 parts, politef 30 parts, chromium oxide 7 parts.
Second step: deionized water, zinc phosphate and zinc oxide are put in reactor, be heated to 140 DEG C, with 350r/min speed
Degree stirring 60min.
3rd step: add zinc yellow and iron oxide red, adds surplus stock at 200 DEG C and puts into grinder grinding after mix homogeneously
8h, packs after filtration.
Film rust, smooth coating, thickness 70 μm, viscosity 60s, paint film is hard；Fineness 30 μm, glossiness 110, impact
Intensity 80cm；Hardness 0.8, surface drying 10min, do solid work 30min, preparation method is simple, and raw material is simple and easy to get, can with widespread production also
Constantly replace current material.
Embodiment 5:
The first step: weigh Colophonium 100 parts, deionized water 60 parts, iron oxide red 20 parts, zinc phosphate 15 according to mass fraction proportioning
Part, zinc yellow 3 parts, zinc oxide 3.5 parts, 2.5 parts of barium sulfate, nitrile rubber 8 parts, politef 25 parts, chromium oxide 6 parts.
Second step: deionized water, zinc phosphate and zinc oxide are put in reactor, be heated to 120 DEG C, with 250r/min speed
Degree stirring 50min.
3rd step: add zinc yellow and iron oxide red, adds surplus stock at 180 DEG C and puts into grinder grinding after mix homogeneously
6h, packs after filtration.
Film rust, smooth coating, thickness 75 μm, viscosity 65s, paint film is hard；Fineness 25 μm, glossiness 120, impact
Intensity 90cm；Hardness 0.9, surface drying 5min, do solid work 25min, preparation method is simple, and raw material is simple and easy to get, can with widespread production also
Constantly replace current material.
Claims (5)
1. a metal water-repellent preservation antirusting paint, it is characterised in that the raw material of described metal water-repellent preservation antirusting paint
As follows by mass fraction proportioning: Colophonium 100 parts, deionized water 50-70 part, iron oxide red 10-30 part, zinc phosphate 5-25 part, zinc yellow 1-5
Part, zinc oxide 1.5-5.5 part, barium sulfate 0.5-4.5 part, nitrile rubber 6-10 part, politef 15-35 part, chromium oxide 4-8
Part.
A kind of metal water-repellent preservation antirusting paint the most according to claim 1, it is characterised in that described metal aqueous
It is as follows that mass fraction proportioning pressed by the raw material of anti-corrosive antirusting paint: Colophonium 100 parts, deionized water 55-65 part, iron oxide red 15-25 part, phosphorus
Acid zinc 10-20 part, zinc yellow 2-4 part, zinc oxide 2.5-4.5 part, barium sulfate 1.5-3.5 part, nitrile rubber 7-9 part, polytetrafluoroethyl-ne
Alkene 20-30 part, chromium oxide 5-7 part.
A kind of metal water-repellent preservation antirusting paint the most according to claim 1, it is characterised in that described metal aqueous
It is as follows that mass fraction proportioning pressed by the raw material of anti-corrosive antirusting paint: Colophonium 100 parts, deionized water 55 parts, iron oxide red 15 parts, zinc phosphate 10
Part, zinc yellow 2 parts, zinc oxide 2.5 parts, 1.5 parts of barium sulfate, nitrile rubber 7 parts, politef 20 parts, chromium oxide 5 parts.
A kind of metal water-repellent preservation antirusting paint the most according to claim 2, it is characterised in that described metal aqueous
It is as follows that mass fraction proportioning pressed by the raw material of anti-corrosive antirusting paint: Colophonium 100 parts, deionized water 65 parts, iron oxide red 25 parts, zinc phosphate 20
Part, zinc yellow 4 parts, zinc oxide 4.5 parts, 3.5 parts of barium sulfate, nitrile rubber 9 parts, politef 30 parts, chromium oxide 7 parts.
A kind of metal water-repellent preservation antirusting paint the most according to claim 1, it is characterised in that: described metal aqueous
It is as follows that mass fraction proportioning pressed by the raw material of anti-corrosive antirusting paint: Colophonium 100 parts, deionized water 60 parts, iron oxide red 20 parts, zinc phosphate 15
Part, zinc yellow 3 parts, zinc oxide 3.5 parts, 2.5 parts of barium sulfate, nitrile rubber 8 parts, politef 25 parts, chromium oxide 6 parts.