CN106065084A - A kind of dip coated formula PE decorating film of plastic substrate surface - Google Patents
A kind of dip coated formula PE decorating film of plastic substrate surface Download PDFInfo
- Publication number
- CN106065084A CN106065084A CN201610394171.6A CN201610394171A CN106065084A CN 106065084 A CN106065084 A CN 106065084A CN 201610394171 A CN201610394171 A CN 201610394171A CN 106065084 A CN106065084 A CN 106065084A
- Authority
- CN
- China
- Prior art keywords
- dip coated
- film
- coating
- decorating film
- plastic substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the dip coated formula PE decorating film of a kind of plastic substrate surface, be PE film outer surface use dip coated mode decorate a layer function coating, the preparation of the coating slurry involved by described functional coating is by coating adhesive, silane, transition metal complex and cross-linking agent add pulping tank, after stirring, with ammonia regulation pH to 8～9 scopes, stand 2～4 hours, then the mode using dip coated is applied to the outer surface of PE film, dry 0.5 hour under 80 DEG C of environment, solidify 1～1.5 hour under 110～140 DEG C of environment, last balance more than 8 hours under field conditions (factors).After crossing dip coating protection, improve surface tactile sensation and the functional strength of PE decorating film, enable this PE decorating film preferably to fit with plastic substrate surface, improve decorative effect.
Description
Technical field
The invention belongs to decorating film technical field, be specifically related to a kind of PE decoration being suitable to be covered in plastic substrate surface
Film.
Background technology
Decorating film has the effects such as heat-insulation and heat-preservation safety anti-explosive, the effect simultaneously also decorated, and transparent decoration
Film does not also interfere with indoor light.Specifically, the advantage of decorating film includes: energy-conserving and environment-protective, reduces air-conditioning, the great number that heating installation brings
The electricity charge；Deadening ultraviolet is invaded, and protection indoor article fades and aging；Filter high light, reduce dazzle, protection skin and vision；
Increase strength of glass, reduce personal injury and protection property, construct invisible protective screens；Single plane fluoroscopy, protects privacy, allows inhabitation
Easiness is enjoyed in space, quiet comfortable；Improve architectural appearance and beautify indoor living environment；Easily fill patch, easy to clean, rub resistance, nothing
Need special maintenance；Economical and practical, colour-fast, not bubble, use the time long.
Decorating film is up to the solar thermal energy of 79% by intercepting, and can be substantially reduced the refrigeration cost of air-conditioning summer；Winter is controlled
The indoor heat of system scatters and disappears through window, indoor occupant not only will not be made not feel well, and decrease unnecessary energy consumption cost,
Thus have become as the most indoor warming a kind of mode that a lot of people can select.
Summary of the invention
It is an object of the invention to provide a kind of damage resistant is applicable to the PE decorating film that plastic substrate surface uses.
The present invention solves the technical scheme that the problems referred to above are used: dip coated formula PE of a kind of plastic substrate surface
Decorating film, be PE film outer surface use dip coated mode decorate a layer function coating, involved by described functional coating
The preparation of coating slurry is that coating adhesive, silane, transition metal complex and cross-linking agent are added pulping tank, after stirring, with ammonia
Water regulation pH to 8～9 scopes, stand 2～4 hours, then use the mode of dip coated to be applied to the outer surface of PE film, in 80
Drying 0.5 hour under DEG C environment, solidify 1～1.5 hour under 110～140 DEG C of environment, balance 8 is little the most under field conditions (factors)
More than time.
Preferably, described transition metal complex is the complex of titanium, aluminum, stannum or zirconium.
Preferably, the molecular weight of silane is between 200～2000.
Preferably, described silane has the polar group suitably forming hydrogen bridge band in organic side chain.
Compared with prior art, it is an advantage of the current invention that: provide the PE decorating film of a kind of dip coated formula, through leaching
Stain coating protection after, improve surface tactile sensation and the functional strength of PE decorating film, enable this PE decorating film preferably with plastics
Substrate surface is fitted, and improves decorative effect.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
Be applicable to the PE decorating film of plastic-substrates, be PE film outer surface use dip coated mode decorate one layer function be coated with
Layer, the preparation of the coating slurry involved by described functional coating is coating adhesive, silane, titanium, the complex of aluminum and cross-linking agent to be added
Pulping tank, after stirring, regulates pH to 8 scope with ammonia, stands 2～4 hours, then use the mode of dip coated to apply
To PE film surface, dry 0.5 hour under 80 DEG C of environment, solidification 1.5 hours under 120 DEG C of environment, the most under field conditions (factors)
Balance more than 8 hours.
Embodiment 2
Be applicable to the PE decorating film of plastic-substrates, be PE film outer surface use dip coated mode decorate one layer function be coated with
Layer, the preparation of the coating slurry involved by described functional coating is coating adhesive, silane, titanium, the complex of stannum and cross-linking agent to be added
Pulping tank, after stirring, regulates pH to 9 scope with ammonia, stands 2～4 hours, then use the mode of dip coated to apply
To PE film surface, dry 0.5 hour under 80 DEG C of environment, solidify 1 hour under 130 DEG C of environment, put down the most under field conditions (factors)
Weigh more than 8 hours.
Embodiment 3
Be applicable to the PE decorating film of plastic-substrates, be PE film outer surface use dip coated mode decorate one layer function be coated with
Layer, the preparation of the coating slurry involved by described functional coating is coating adhesive, silane, aluminum, the complex of zirconium and cross-linking agent to be added
Pulping tank, after stirring, regulates pH to 9 scope with ammonia, stands 2～4 hours, then use the mode of dip coated to apply
To PE film surface, dry 0.5 hour under 80 DEG C of environment, solidify 1 hour under 110 DEG C of environment, put down the most under field conditions (factors)
Weigh more than 8 hours.
Claims (4)
1. the dip coated formula PE decorating film of a plastic substrate surface, it is characterised in that: it is the outer surface employing at PE film
The mode of dip coated decorates a layer function coating, and the preparation of the coating slurry involved by described functional coating is by coating adhesive, silicon
Alkane, transition metal complex and cross-linking agent add pulping tank, after stirring, with ammonia regulation pH to 8～9 scopes, stand 2～
4 hours, then use the mode of dip coated to be applied to the outer surface of PE film, dry 0.5 hour under 80 DEG C of environment, in 110
～solidify under 140 DEG C of environment 1～1.5 hour, balance more than 8 hours the most under field conditions (factors).
The dip coated formula PE decorating film of plastic substrate surface the most according to claim 1, it is characterised in that: described mistake
Cross the complex that metal complex is titanium, aluminum, stannum or zirconium.
The dip coated formula PE decorating film of plastic substrate surface the most according to claim 2, it is characterised in that: described silicon
The molecular weight of alkane is between 200～2000.
The dip coated formula PE decorating film of plastic substrate surface the most according to claim 2, it is characterised in that: described silicon
Alkane has the polar group suitably forming hydrogen bridge band in organic side chain.