CN106048471A - Metal ceramic material - Google Patents
Metal ceramic material Download PDFInfo
- Publication number
- CN106048471A CN106048471A CN201610535567.8A CN201610535567A CN106048471A CN 106048471 A CN106048471 A CN 106048471A CN 201610535567 A CN201610535567 A CN 201610535567A CN 106048471 A CN106048471 A CN 106048471A
- Authority
- CN
- China
- Prior art keywords
- parts
- titanium
- ceramic material
- metal ceramic
- germanium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a metal ceramic material which is prepared from the following raw materials in parts by weight: 10-14 parts of nano molybdenum carbide, 7-9 parts of chromium, 10-15 parts of copper, 5-8 parts of titanium carbonitride, 2-4 parts of titanium powder, 4-9 parts of aluminum oxide fibers, 7-11 parts of platinum, 5-9 parts of germanium, 5-8 parts of thorium dioxide, 9-14 parts of calcium carbonate, 3-6 parts of titanium nitride, 11-16 parts of oleic acid, 3-7 parts of a water reducer, 8-13 parts of hydroxypropyl cellulose, 9-17 parts of illite and 5-10 parts of hexacyclic stones. The metal ceramic material has the beneficial effects of being small in density, high in hardness, resistant to wear, good in toughness, and excellent in high temperature resistance.
Description
Technical field
The present invention relates to a kind of cermet material.
Background technology
The composite that ceramic metal is made up of with metal or alloy Binder Phase ceramic hard phase, ceramic metal both kept
The characteristics such as high intensity, high rigidity, wear-resistant, high temperature resistant, antioxidation and the chemical stability of pottery, have again preferable metal
Toughness and plasticity.Ceramic metal is in order to make the pottery not only can be high temperature resistant but also be not easy to crush, and people are making the clay of pottery
In added a little metal powder, be therefore made for ceramic metal.Due to ceramic-metallic excellent properties, the scope of ceramic metal application is also
Increasingly wider, require more and more higher along with people for ceramic metal simultaneously, existing cermet material needs further
Improvement, improve ceramic-metallic performance.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is to provide a kind of cermet material, density is little,
Hardness is high, wear-resisting, has good toughness simultaneously, and resistance to elevated temperatures is excellent.
For solving prior art problem, the technical scheme that the present invention provides is, a kind of cermet material, it is by following heavy
The raw material of amount number is made:
Nano silicon carbide molybdenum 10-14 part, chromium 7-9 part, copper 10-15 part, titanium carbonitride 5-8 part, titanium valve 2-4 part, alumina fibre 4-9
Part, platinum 7-11 part, germanium 5-9 part, thorium anhydride 5-8 part, calcium carbonate 9-14 part, titanium nitride 3-6 part, oleic acid 11-16 part, water reducer
3-7 part, hydroxypropyl cellulose 8-13 part, illite 9-17 part, hexacyclic ring stone 5-10 part.
The invention has the beneficial effects as follows: the cermet material of the present invention, density is little, hardness is high, wear-resisting, has good simultaneously
Good toughness, and resistance to elevated temperatures is excellent.
Detailed description of the invention
Embodiment 1
A kind of cermet material, it is made up of the raw material of following parts by weight:
Nano silicon carbide molybdenum 10 parts, chromium 7 parts, copper 10 parts, titanium carbonitride 5 parts, titanium valve 2 parts, alumina fibre 4 parts, 7 parts of platinum, germanium 5
Part, thorium anhydride 5 parts, calcium carbonate 9 parts, titanium nitride 3 parts, oleic acid 11 parts, water reducer 3 parts, hydroxypropyl cellulose 8 parts, illite 9
Part, hexacyclic ring stone 5 parts.
Embodiment 2
A kind of cermet material, it is made up of the raw material of following parts by weight:
Nano silicon carbide molybdenum 14 parts, chromium 9 parts, copper 15 parts, titanium carbonitride 8 parts, titanium valve 4 parts, alumina fibre 9 parts, 11 parts of platinum, germanium 9
Part, thorium anhydride 8 parts, calcium carbonate 14 parts, titanium nitride 6 parts, oleic acid 16 parts, water reducer 7 parts, hydroxypropyl cellulose 13 parts, Erie
17 parts of stone, hexacyclic ring stone 10 parts.
Claims (1)
1. a cermet material, it is characterised in that: it is made up of the raw material of following parts by weight:
Nano silicon carbide molybdenum 10-14 part, chromium 7-9 part, copper 10-15 part, titanium carbonitride 5-8 part, titanium valve 2-4 part, alumina fibre 4-9
Part, platinum 7-11 part, germanium 5-9 part, thorium anhydride 5-8 part, calcium carbonate 9-14 part, titanium nitride 3-6 part, oleic acid 11-16 part, water reducer
3-7 part, hydroxypropyl cellulose 8-13 part, illite 9-17 part, hexacyclic ring stone 5-10 part.