CN106046746A - Flame-retarding toughening cable material specially used for soybean milk machine - Google Patents
Flame-retarding toughening cable material specially used for soybean milk machine Download PDFInfo
- Publication number
- CN106046746A CN106046746A CN201610685313.4A CN201610685313A CN106046746A CN 106046746 A CN106046746 A CN 106046746A CN 201610685313 A CN201610685313 A CN 201610685313A CN 106046746 A CN106046746 A CN 106046746A
- Authority
- CN
- China
- Prior art keywords
- parts
- cable material
- flaming
- bean milk
- making machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a flame-retarding toughening cable material specially used for a soybean milk machine. The cable material includes the main raw materials comprising, by weight, 26-32 parts of modified resin, 10-15 parts of polyphenylene sulfide, 3-6 parts of pyridine carboxamide, 0.1-0.5 parts of 3-hydroxyl butyrate, 0.1-0.5 parts of modified silicon dioxide powder, 0.1-0.5 parts of glyceride, 0.1-0.5 parts of carbon black, and 2-6 parts of glass fibers. The cable material has excellent comprehensive performance, and is good in mould processability, high in flame-retarding performance, strong in toughening property and low in cost.
Description
Technical field
The present invention relates to a kind of technical field of polymer materials, specifically a kind of toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming
And preparation method thereof.
Background technology
Soy bean milk making machine is as the indispensable small household appliances of a lot of families breakfast, and simply, convenient, mobility is strong, but due to soy bean milk making machine
Being positioned over kitchen, its cable often accesses high-power insert row, and the toughness of cable is tested the most greatly simultaneously more.The most how
The fire-retardant toughened property utilizing new material to improve the toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming becomes important research topic.
Summary of the invention
It is an object of the invention to provide toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming and preparation method thereof, above-mentioned to solve
The problem proposed in background technology.
For achieving the above object, the present invention provides following technical scheme:
A kind of toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, includes according to the primary raw material of weight portion: modified resin 26-32 part,
Alkylphenol polyoxyethylene 10-15 part, ascorbyl palmitate 3-6 part, 3-hydroxybutyrate ester 0.1-0.5 part, improved silica powder
End 0.1-0.5 part, glyceride 0.1-0.5 part, white carbon black 0.1-0.5 part, glass fibre 2-6 part.
As the further scheme of the present invention: include according to the primary raw material of weight portion: modified resin 30 parts, alkyl phenol gather
Oxygen vinyl Ether 13 parts, ascorbyl palmitate 5 parts, 3-hydroxybutyrate ester 0.2 part, 0.3 part of improved silica powder, glyceride 0.3
Part, white carbon black 0.3 part, glass fibre 4 parts.
As the further scheme of the present invention: the preparation method of described modified resin is: by PTMG, drip
Blue or green and acrylic resin joins reactor, 130 DEG C of constant temperature 1h, is subsequently added fumaric acid stirring, obtains after cooling.
As the further scheme of the present invention: the preparation method of described improved silica powder is: by aluminium oxide, oxidation
Magnesium, polystyrene and SiO 2 powder carry out vortex mixing, are subsequently added dichloroacetic acid, react 30min, after cooling under 3MPa
Drying.
The preparation method of the described toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, concretely comprises the following steps:
(1) first, improved silica powder, white carbon black and glass fibre 80 DEG C are vacuum dried 6h, are subsequently added to modified tree
In fat and stir, it is allowed to dispersion and obtains mixture；Then, mixture is added alkylphenol polyoxyethylene, pyridinecarboxylic
Carry out sucking filtration after amine and 3-hydroxybutyrate ester, fully mixing, put into 32 DEG C of oven drying 12h, obtain mixture I；
(2) then, with glyceride, mixture I being carried out water-bath, the temperature of water-bath is 60 DEG C-70 DEG C, and the time is 15min-
30min, is subsequently added to double screw extruder, and screw speed is set as 268r/min, and through melt extruding, water-cooled pelletizing obtains
Pellet；Then, forced air drying 2h at 110 DEG C, uses injection machine injection mo(u)lding, obtains soy bean milk making machine special-purpose anti-flaming toughness reinforcing cable material
Material.
As the further scheme of the present invention: in step (2), the temperature of water-bath is 65 DEG C, the time is 21min.
Compared with prior art, the invention has the beneficial effects as follows:
Soy bean milk making machine special-purpose anti-flaming toughness reinforcing cable material excellent combination property in the present invention, has that molding processibility is good, fire resistance
The advantages such as height, increasing tougheness are strong, with low cost.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the technical scheme of this patent is described in more detail.
Embodiment 1
A kind of toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, includes according to the primary raw material of weight portion: modified resin 26 parts, alkyl
Phenol polyethenoxy ether 10 parts, ascorbyl palmitate 3 parts, 3-hydroxybutyrate ester 0.1 part, 0.1 part of improved silica powder, glyceride
0.1 part, white carbon black 0.1 part, glass fibre 2 parts；The preparation method of described modified resin is: by PTMG, Colophonium
Reactor is joined with acrylic resin, 130 DEG C of constant temperature 1h, it is subsequently added fumaric acid stirring, obtains after cooling；Described modified two
The preparation method of silicon oxide powder is: with SiO 2 powder, aluminium oxide, magnesium oxide, polystyrene are carried out vortex mixing, with
Rear addition dichloroacetic acid, reacts 30min, cools down post-drying and get final product under 3MPa.
The preparation method of the described toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, concretely comprises the following steps:
(1) first, improved silica powder, white carbon black and glass fibre 80 DEG C are vacuum dried 6h, are subsequently added to modified tree
In fat and stir, it is allowed to dispersion and obtains mixture；Then, mixture is added alkylphenol polyoxyethylene, pyridinecarboxylic
Carry out sucking filtration after amine and 3-hydroxybutyrate ester, fully mixing, put into 32 DEG C of oven drying 12h, obtain mixture I；
(2) then, with glyceride, mixture I being carried out water-bath, the temperature of water-bath is 60 DEG C, and the time is 15min, is subsequently added to
Double screw extruder, screw speed is set as 268r/min, and through melt extruding, water-cooled pelletizing obtains pellet；Then, 110
Forced air drying 2h at DEG C, uses injection machine injection mo(u)lding, obtains the toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming.
The fire-retardant toughened material that above-mentioned technique prepares, records its combustibility and mechanical property parameters is as follows: the limit
Oxygen index (OI) 31.7%, notch impact strength 9.1 KJ/m2, bending strength 23MPa.
Embodiment 2
A kind of toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, includes according to the primary raw material of weight portion: modified resin 30 parts, alkyl
Phenol polyethenoxy ether 13 parts, ascorbyl palmitate 5 parts, 3-hydroxybutyrate ester 0.2 part, 0.3 part of improved silica powder, glyceride
0.3 part, white carbon black 0.3 part, glass fibre 4 parts；The preparation method of described modified resin is: by PTMG, Colophonium
Reactor is joined with acrylic resin, 130 DEG C of constant temperature 1h, it is subsequently added fumaric acid stirring, obtains after cooling；Described modified two
The preparation method of silicon oxide powder is: with SiO 2 powder, aluminium oxide, magnesium oxide, polystyrene are carried out vortex mixing, with
Rear addition dichloroacetic acid, reacts 30min, cools down post-drying and get final product under 3MPa.
The preparation method of the described toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, concretely comprises the following steps:
(1) first, improved silica powder, white carbon black and glass fibre 80 DEG C are vacuum dried 6h, are subsequently added to modified tree
In fat and stir, it is allowed to dispersion and obtains mixture；Then, mixture is added alkylphenol polyoxyethylene, pyridinecarboxylic
Carry out sucking filtration after amine and 3-hydroxybutyrate ester, fully mixing, put into 32 DEG C of oven drying 12h, obtain mixture I；
(2) then, with glyceride, mixture I being carried out water-bath, the temperature of water-bath is 65 DEG C, and the time is 21min, is subsequently added to
Double screw extruder, screw speed is set as 268r/min, and through melt extruding, water-cooled pelletizing obtains pellet；Then, 110
Forced air drying 2h at DEG C, uses injection machine injection mo(u)lding, obtains the toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming.
The fire-retardant toughened material that above-mentioned technique prepares, records its combustibility and mechanical property parameters is as follows: the limit
Oxygen index (OI) 36.9%, notch impact strength 10.4 KJ/m2, bending strength 25MPa.
Embodiment 3
A kind of toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, includes according to the primary raw material of weight portion: modified resin 32 parts, alkyl
Phenol polyethenoxy ether 15 parts, ascorbyl palmitate 6 parts, 3-hydroxybutyrate ester 0.5 part, 0.5 part of improved silica powder, glyceride
0.5 part, white carbon black 0.5 part, glass fibre 6 parts；The preparation method of described modified resin is: by PTMG, Colophonium
Reactor is joined with acrylic resin, 130 DEG C of constant temperature 1h, it is subsequently added fumaric acid stirring, obtains after cooling；Described modified two
The preparation method of silicon oxide powder is: with SiO 2 powder, aluminium oxide, magnesium oxide, polystyrene are carried out vortex mixing, with
Rear addition dichloroacetic acid, reacts 30min, cools down post-drying and get final product under 3MPa.
The preparation method of the described toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, concretely comprises the following steps:
(1) first, improved silica powder, white carbon black and glass fibre 80 DEG C are vacuum dried 6h, are subsequently added to modified tree
In fat and stir, it is allowed to dispersion and obtains mixture；Then, mixture is added alkylphenol polyoxyethylene, pyridinecarboxylic
Carry out sucking filtration after amine and 3-hydroxybutyrate ester, fully mixing, put into 32 DEG C of oven drying 12h, obtain mixture I；
(2) then, with glyceride, mixture I being carried out water-bath, the temperature of water-bath is 70 DEG C, and the time is 30min, is subsequently added to
Double screw extruder, screw speed is set as 268r/min, and through melt extruding, water-cooled pelletizing obtains pellet；Then, 110
Forced air drying 2h at DEG C, uses injection machine injection mo(u)lding, obtains the toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming.
The fire-retardant toughened material that above-mentioned technique prepares, records its combustibility and mechanical property parameters is as follows: the limit
Oxygen index (OI) 36.4%, notch impact strength 10.0 KJ/m2, bending strength 23MPa.
Comparative example 1
A kind of toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, includes according to the primary raw material of weight portion: acrylic resin 30 parts, alkane
Base phenol polyethenoxy ether 13 parts, ascorbyl palmitate 5 parts, 3-hydroxybutyrate ester 0.2 part, SiO 2 powder 0.3 part, glyceride
0.3 part, white carbon black 0.3 part, glass fibre 4 parts.
The preparation method of the described toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, concretely comprises the following steps:
(1) first, SiO 2 powder, white carbon black and glass fibre 80 DEG C are vacuum dried 6h, are subsequently added to acrylic resin
In and stir, be allowed to dispersion and obtain mixture；Then, mixture is added alkylphenol polyoxyethylene, ascorbyl palmitate
Carry out sucking filtration with after 3-hydroxybutyrate ester, fully mixing, put into 32 DEG C of oven drying 12h, obtain mixture I；
(2) then, being stirred uniformly by mixture I with glyceride, be subsequently added to double screw extruder, screw speed sets
For 268r/min, through melt extruding, water-cooled pelletizing obtains pellet；Then, at 110 DEG C, forced air drying 2h, notes with injection machine
Molded, obtain the toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming.
The fire-retardant toughened material that above-mentioned technique prepares, records its combustibility and mechanical property parameters is as follows: the limit
Oxygen index (OI) 10.1%, notch impact strength 4.3KJ/m2, bending strength 8MPa.
Comparative example 2
A kind of toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, includes according to the primary raw material of weight portion: acrylic resin 30 parts, 3-
Butyric ester 0.2 part, SiO 2 powder 0.3 part, glyceride 0.3 part, white carbon black 0.3 part, glass fibre 4 parts.
The preparation method of the described toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, concretely comprises the following steps:
(1) first, SiO 2 powder, white carbon black and glass fibre 80 DEG C are vacuum dried 6h, are subsequently added to acrylic resin
In and stir, be allowed to dispersion and obtain mixture；Then, mixture is added 3-hydroxybutyrate ester, fully carry out after mixing
Sucking filtration, puts into 32 DEG C of oven drying 12h, obtains mixture I；
(2) then, being stirred uniformly by mixture I with glyceride, be subsequently added to double screw extruder, screw speed sets
For 268r/min, through melt extruding, water-cooled pelletizing obtains pellet；Then, at 110 DEG C, forced air drying 2h, notes with injection machine
Molded, obtain the toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming.
The fire-retardant toughened material that above-mentioned technique prepares, records its combustibility and mechanical property parameters is as follows: the limit
Oxygen index (OI) 7.1%, notch impact strength 2.1KJ/m2, bending strength 2MPa.
Comparative example 3
A kind of toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, includes according to the primary raw material of weight portion: modified resin 30 parts, alkyl
Phenol polyethenoxy ether 13 parts, ascorbyl palmitate 5 parts, 3-hydroxybutyrate ester 0.2 part, 0.3 part of improved silica powder, glyceride
0.3 part, white carbon black 0.3 part, glass fibre 4 parts；The preparation method of described modified resin is: by PTMG, Colophonium
Reactor is joined with acrylic resin, 130 DEG C of constant temperature 1h, it is subsequently added fumaric acid stirring, obtains after cooling；Described modified two
The preparation method of silicon oxide powder is: with SiO 2 powder, aluminium oxide, magnesium oxide, polystyrene are carried out vortex mixing, with
Rear addition dichloroacetic acid, reacts 30min, cools down post-drying and get final product under 3MPa.
The preparation method of the described toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, concretely comprises the following steps:
(1) first, improved silica powder, white carbon black and glass fibre 80 DEG C are vacuum dried 6h, are subsequently added to modified tree
In fat and stir, it is allowed to dispersion and obtains mixture；Then, mixture is added alkylphenol polyoxyethylene, pyridinecarboxylic
Carry out sucking filtration after amine and 3-hydroxybutyrate ester, fully mixing, put into 32 DEG C of oven drying 12h, obtain mixture I；
(2) then, being stirred uniformly by mixture I with glyceride, be subsequently added to double screw extruder, screw speed sets
For 268r/min, through melt extruding, water-cooled pelletizing obtains pellet；Then, at 110 DEG C, forced air drying 2h, notes with injection machine
Molded, obtain the toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming.
The fire-retardant toughened material that above-mentioned technique prepares, records its combustibility and mechanical property parameters is as follows: the limit
Oxygen index (OI) 19.1%, notch impact strength 7.8KJ/m2, bending strength 14MPa.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of the spirit or essential attributes of the present invention, it is possible to realize the present invention in other specific forms.Therefore, no matter
From the point of view of which point, all should regard embodiment as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all by fall in the implication of equivalency and scope of claim
Change is included in the present invention.
Although moreover, it will be appreciated that this specification is been described by according to embodiment, but the most each embodiment only wraps
Containing an independent technical scheme, this narrating mode of description is only that for clarity sake those skilled in the art should
Description can also be formed those skilled in the art through appropriately combined as an entirety, the technical scheme in each embodiment
May be appreciated other embodiments.
Claims (6)
1. the toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming, it is characterised in that include according to the primary raw material of weight portion: modified
Resin 26-32 part, alkylphenol polyoxyethylene 10-15 part, ascorbyl palmitate 3-6 part, 3-hydroxybutyrate ester 0.1-0.5 part, change
Property SiO 2 powder 0.1-0.5 part, glyceride 0.1-0.5 part, white carbon black 0.1-0.5 part, glass fibre 2-6 part.
The toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming the most according to claim 1, it is characterised in that according to the master of weight portion
Want raw material to include: modified resin 30 parts, alkylphenol polyoxyethylene 13 parts, ascorbyl palmitate 5 parts, 3-hydroxybutyrate ester 0.2 part,
0.3 part of improved silica powder, glyceride 0.3 part, white carbon black 0.3 part, glass fibre 4 parts.
The toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming the most according to claim 1 and 2, it is characterised in that described modified tree
The preparation method of fat is: with acrylic resin, PTMG, Colophonium are joined reactor, 130 DEG C of constant temperature 1h, with
Rear addition fumaric acid stirs, and obtains after cooling.
The toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming the most according to claim 3, it is characterised in that described modified titanium dioxide
The preparation method of Si powder is: with SiO 2 powder, aluminium oxide, magnesium oxide, polystyrene are carried out vortex mixing, adds subsequently
Enter dichloroacetic acid, react 30min under 3MPa, cool down post-drying and get final product.
5. a preparation method for the toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming as described in claim 1-4 is arbitrary, its feature
It is, concretely comprises the following steps:
(1) first, improved silica powder, white carbon black and glass fibre 80 DEG C are vacuum dried 6h, are subsequently added to modified tree
In fat and stir, it is allowed to dispersion and obtains mixture；Then, mixture is added alkylphenol polyoxyethylene, pyridinecarboxylic
Carry out sucking filtration after amine and 3-hydroxybutyrate ester, fully mixing, put into 32 DEG C of oven drying 12h, obtain mixture I；
(2) then, with glyceride, mixture I being carried out water-bath, the temperature of water-bath is 60 DEG C-70 DEG C, and the time is 15min-
30min, is subsequently added to double screw extruder, and screw speed is set as 268r/min, and through melt extruding, water-cooled pelletizing obtains
Pellet；Then, forced air drying 2h at 110 DEG C, uses injection machine injection mo(u)lding, obtains soy bean milk making machine special-purpose anti-flaming toughness reinforcing cable material
Material.
The toughness reinforcing cable material of soy bean milk making machine special-purpose anti-flaming the most according to claim 5, it is characterised in that water-bath in step (2)
Temperature be 65 DEG C, the time is 21min.