CN106046463A - Bactericidal and mould-proof rubber floor - Google Patents

Abstract

The invention relates to bactericidal and mould-proof rubber floor, prepared from the following raw materials in parts by weight: 21-35 parts of ethylene propylene diene rubber, 6-10 parts of white carbon black, 4-7 parts of anti-static agent, 8-11 parts of zinc oxide, 45-60 parts of neoprene, 6-9 parts of magnesium oxide, 7-11 parts of 2,2'-ditho bisbenzothiazole, 9-14 parts of tribasic lead sulfate, 4-7 parts of barium stearate, 1.2-4 parts of accelerant, 4-7 parts of xylene, 11-17 parts of titanium dioxide, 8-12 parts of magnesium hydroxide, 2-5 parts of antimony trioxide, 7.2-10 parts of tourmaline and 3.5-8 parts of polyvinyl acetate emulsion. The rubber floor provided by the invention has the beneficial effects of having good bactericidal and mould-proof effect, excellent over-all properties and better durability on the basis of having good weather resistance and fire resistance.

Description

A kind of fungus and mildew resistance rubber floor covering

Technical field

The present invention relates to a kind of fungus and mildew resistance rubber floor covering.

Background technology

Rubber floor covering, is natural rubber and other elastomeric floors.In appearance, its color clear is beautiful, texture As rubber soft, be suitable for motion as the place mat of motion occasion.Rubber floor covering is the most flourishing as floor decorative material Country is the most popular many decades, and be widely used.And the most just rise in China.Rubber floor covering has good Resistance to water, air-tightness and excellent adhesive property.But it is existing more and more higher, at present for the requirement of rubber floor covering along with people Rubber floor covering can not meet use demand, need further to improve.

Summary of the invention

For the deficiencies in the prior art, the problem to be solved in the present invention is to provide a kind of rubber floor covering, the most resistance to having On the basis of time property and anti-flammability, there is good bactericidal mould proof effect；Excellent combination property, ruggedness is more preferable.

For solving prior art problem, the technical scheme that the present invention provides is, a kind of fungus and mildew resistance rubber floor covering, its by with The raw material of lower parts by weight is made:

Ethylene propylene diene rubber 21-35 part, white carbon 6-10 part, antistatic additive 4-7 part, zinc oxide 8-11 part, neoprene 45-60 Part, magnesium oxide 6-9 part, 2,2'-dithio-bis-benzothiazole 7-11 parts, tribasic lead sulfate 9-14 part, barium stearate 4-7 part, Accelerator 1.2-4 part, dimethylbenzene 4-7 part, titanium dioxide 11-17 part, magnesium hydroxide 8-12 part, antimony oxide 2-5 part, electrically Stone 7.2-10 part, polyvinyl acetate emulsion 3.5-8 part.

The invention has the beneficial effects as follows: the rubber floor covering of the present invention, on the basis of there is good weatherability properties and anti-flammability, There is good bactericidal mould proof effect；Excellent combination property, ruggedness is more preferable.

Detailed description of the invention

Embodiment 1

A kind of fungus and mildew resistance rubber floor covering, it is made up of the raw material of following parts by weight:

Ethylene propylene diene rubber 21 parts, white carbon 6 parts, 4 parts of antistatic additive, zinc oxide 8 parts, neoprene 45 parts, magnesium oxide 6 parts, 2,2'-dithio-bis-benzothiazoles 7 parts, tribasic lead sulfate 9 parts, barium stearate 4 parts, accelerator 1.2 parts, dimethylbenzene 4 parts, two Titanium oxide 11 parts, 8 parts of magnesium hydroxide, antimony oxide 2 parts, 7.2 parts of tourmaline, polyvinyl acetate emulsion 3.5 parts.

Embodiment 2

A kind of fungus and mildew resistance rubber floor covering, it is made up of the raw material of following parts by weight:

Ethylene propylene diene rubber 35 parts, white carbon 10 parts, 7 parts of antistatic additive, zinc oxide 11 parts, neoprene 60 parts, magnesium oxide 9 Part, 2,2'-dithio-bis-benzothiazoles 11 parts, tribasic lead sulfate 14 parts, barium stearate 7 parts, accelerator 4 parts, dimethylbenzene 7 Part, titanium dioxide 17 parts, 12 parts of magnesium hydroxide, antimony oxide 5 parts, 10 parts of tourmaline, polyvinyl acetate emulsion 8 parts.

Claims (1)

1. a fungus and mildew resistance rubber floor covering, it is characterised in that: it is made up of the raw material of following parts by weight:

Ethylene propylene diene rubber 21-35 part, white carbon 6-10 part, antistatic additive 4-7 part, zinc oxide 8-11 part, neoprene 45-60 Part, magnesium oxide 6-9 part, 2,2'-dithio-bis-benzothiazole 7-11 parts, tribasic lead sulfate 9-14 part, barium stearate 4-7 part, Accelerator 1.2-4 part, dimethylbenzene 4-7 part, titanium dioxide 11-17 part, magnesium hydroxide 8-12 part, antimony oxide 2-5 part, electrically Stone 7.2-10 part, polyvinyl acetate emulsion 3.5-8 part.