CN106042565A - Novel furniture plate and preparation method thereof - Google Patents

Novel furniture plate and preparation method thereof Download PDF

Info

Publication number
CN106042565A
CN106042565A CN201610464365.9A CN201610464365A CN106042565A CN 106042565 A CN106042565 A CN 106042565A CN 201610464365 A CN201610464365 A CN 201610464365A CN 106042565 A CN106042565 A CN 106042565A
Authority
CN
China
Prior art keywords
glue
bio
foaming agent
foaming
sheet material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610464365.9A
Other languages
Chinese (zh)
Inventor
杨先刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUXI TIANJU TECHNOLOGY Co Ltd
Original Assignee
WUXI TIANJU TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI TIANJU TECHNOLOGY Co Ltd filed Critical WUXI TIANJU TECHNOLOGY Co Ltd
Priority to CN201610464365.9A priority Critical patent/CN106042565A/en
Publication of CN106042565A publication Critical patent/CN106042565A/en
Pending legal-status Critical Current

Abstract

The invention discloses a novel furniture plate and a preparation method thereof. The preparation method comprises the following steps that by using a composite pasting process, firstly, high polymer plastic, inorganic flame retardant, biobased materials and foamers are uniformly mixed, so as to extrude a foamed wood-plastic plate as a base material by a plate extruder, then glue is applied to the upper and lower surfaces of the plate as the base material, and decorative films of the same size are pasted on the upper and lower surfaces of the base material. The furniture plate has the advantages of moisture prevention, light weight and environmental friendliness, the mechanical properties and flame retardant property can be obviously increased, the cost can be reduced, and the environmental requirement of sustainable development is satisfied; the preparation method has the advantages of simplicity and easiness in industrialization and can be widely applied to furniture processing plates such as cupboards, ceilings, window sills, door plates and the like.

Description

A kind of novel Furniture panel and preparation method thereof
Technical field
The present invention relates to sheet material field, particularly relate to a kind of novel Furniture panel and preparation method thereof.
Background technology
Traditional Furniture panel has woodwork plate, particieboard, fibre board, solid wood board etc..Need after wherein woodwork plate has made furniture The operations such as paint, work progress is the veryest long and can produce certain abnormal smells from the patient；Containing substantial amounts of adhesive composition in particieboard, also Can discharge, be unfavorable for the requirement of environmental protection；Fibre board, in the furniture course of processing, is difficult to fixing solid；And solid wood boards etc. need Consume a large amount of timber, be unfavorable for the sustainable development of environment
Macromolecular material and bio-based materials are carried out being blended as base material by Furniture panel of the present invention, can be closed by bio-based materials Reason utilizes, and turn avoid the pollution problem to environment in the furniture course of processing, and mechanical performance is obviously improved with fire resistance, anti- Tide, light weight, environmental protection, it is possible to decrease cost and meet the ecological requirements of sustainable development.Its preparation method simply, easily realizes industry Change, can be widely used for the furniture processing sheet materials such as cabinet, ceiling, windowsill, door-plate.
Summary of the invention
In view of this, technical problem solved by the invention is to provide a kind of novel Furniture panel, to improve above-mentioned tradition The defect of Furniture panel
Technical problem solved by the invention adopts the following technical scheme that and realizes:
A kind of novel Furniture panel, including base material and face material, face material is pasted onto substrate surface
Its formula and preparation technology use following steps: step one: by macromolecular material, inorganic combustion inhibitor, foaming agent, bio-based Material mixes in mixer, extrusion foaming sheet material, and as base material, embossed surface processes；Step 2: prepared in step one The upper and lower surface of foaming wood-plastic sheet material be coated with glue, decorating film is pasted on its surface, compacting, edge sealing
Its formula and preparation technology can also use following steps: step one: by macromolecular material, inorganic combustion inhibitor, foaming agent, Bio-based materials mixes in mixer, and extrusion foaming sheet material, as base material；Step 2: foaming prepared in step one The upper and lower surface of Wood plastic boards is coated with glue, and decorating film is pasted on its surface, compacting, edge sealing, and embossed surface processes
Preferably, described face material is decorating film, the upper and lower surface of Pasting foaming wood-plastic base material
Compared with prior art, the furniture-plates that the raw material preparing Furniture panel provided by the present invention and preparation method are obtained Material, mechanical strength can be obviously improved with fire resistance, and sound insulation, protection against the tide, insulation, environmental protection, complies with sustainable development Trend.It addition, this Furniture panel eliminates the process such as follow-up paint, U.S. dress.Additionally, trace or a small amount of functional aid, Such as plasticizer, antioxidant, coloring agent, heat stabilizer etc. do not interfere with basic technology and the performance of this Furniture panel.
Accompanying drawing illustrates: Fig. 1 is Furniture panel sectional schematic diagram；
In figure: 1 is foaming wood-plastic sheet material；2 is decorating film.
Detailed description of the invention: embodiment 1
Weighing polypropylene 10Kg, foaming agent 0.5kg, wood powder 5kg, magnesium powder 1kg according to practical situation, be blended, extrusion 20mm thickness is sent out Bubble sheet material.Thereon, lower surface coating glue.Take two pieces of 2mm thickness decorating films, be pasted on foaming plate two sides respectively.Finally lead to Crossing double roller and carry out suppressing to increase plate adhesion fastness, edge sealing, embossed surface processes.Gained sheet material is cut into square sheet material, Transport with convenient construction
Embodiment 2
Weigh polrvinyl chloride 10Kg, foaming agent 0.4kg, bamboo powder 5kg, magnesium powder 1.5kg according to practical situation, be blended, extrude 10mm Thick foaming plate, embossed surface processes.Thereon, lower surface coating glue.Take two pieces of 1mm thickness decorating films, be pasted on respectively and send out Bubble sheet material two sides.Carry out suppressing to increase plate adhesion fastness, edge sealing finally by double rollers.Gained sheet material is cut into square plate Material, transports with convenient construction
Embodiment 3
Weigh polrvinyl chloride 10Kg, foaming agent 0.5kg, powder of straw 5kg, magnesium powder 1kg according to practical situation, be blended, extrude 10mm Thick foaming plate.Thereon, lower surface coating glue.Take two pieces of 1mm thickness decorating films, be pasted on foaming plate two sides respectively.? Carrying out suppressing to increase plate adhesion fastness, edge sealing by double rollers afterwards, embossed surface processes.Gained sheet material is cut into square plate Material, transports with convenient construction
Embodiment 4
Weighing polrvinyl chloride 10Kg, foaming agent 0.3kg, wood powder 2kg, magnesium powder 2kg according to practical situation, be blended, extrusion 15mm is thick Foaming plate, embossed surface processes.Thereon, lower surface coating glue.Take two pieces of 1mm thickness decorating films, be pasted on foaming respectively Sheet material two sides.Carry out suppressing to increase plate adhesion fastness, edge sealing finally by double rollers.Gained sheet material is cut into square plate Material, transports with convenient construction
As can be seen here, Furniture panel that the present invention provides and preparation method thereof has the advantage that
(1) described Furniture panel, it is not necessary to paint or sticky table facial film etc. strengthen aesthetic property, eliminate the process portion of traditional handicraft
(2) Furniture panel provided by the present invention, both can reach higher mechanical strength, was also equipped with insulation, fire-retardant, sound insulation, anti- The characteristic of tide
(3) Furniture panel provided by the present invention, owing to being foamed by Wood plastic boards, sheet material quality lightens, it is possible to decrease transport Cost
(4) the bio-based materials wide material sources used by the present invention, can be from trees, straw, the wood green plants body such as bran or Cotton Gossypii Interior extraction modification, aboundresources, the adverse consequences that petrochemical material can be avoided to be brought, meet environmental requirement
(5) the Furniture panel customizable that the present invention provides produces, and pastes required decorating film, its preparation method according to actual needs Technique is simple, with short production cycle, it is easy to accomplish industrialization produces, and can be used for the furniture such as cabinet, ceiling, windowsill, door-plate and adds Work sheet material
Those of ordinary skill in the field, and need not it is understood that the foregoing is only the specific embodiment of the present invention In limit the present invention, all within the spirit and principles in the present invention, any modification, equivalent substitution and improvement etc. done, all should wrap Within being contained in protection scope of the present invention.

Claims (11)

1. a novel Furniture panel, it is characterised in that include following each component: high molecule plastic, nothing
Machine fire retardant, bio-based materials, foaming agent, glue, decorating film
Face material amounts of components is:
Decorating film 2 pieces
The each amounts of components of base material (mass fraction):
High molecule plastic 100 parts
Inorganic combustion inhibitor 5 ~ 30 parts
Bio-based materials 10 ~ 100 parts
Foaming agent 3 ~ 8 parts
Glue quantity, depending on sheet material area, is as the criterion with uniformly coating plate surface.
High molecule plastic the most according to claim 1, it is characterised in that described high molecule plastic includes polypropylene (PP), plastics common in the commercial production such as polyethylene (PE), polrvinyl chloride (PVC).
Inorganic combustion inhibitor the most according to claim 1, it is characterised in that described inorganic combustion inhibitor is magnesium hydroxide, hydrogen One or more in the inorganic combustion inhibitors such as aluminium oxide compound.
Bio-based materials the most according to claim 1, it is characterised in that described bio-based materials is wood powder, bamboo powder, straw The bio-based materials such as stalk powder, starch, algae.
Foaming agent the most according to claim 1, it is characterised in that described foaming agent includes azo-compound, N-nitrous Foaming agent common in the commercial production such as based compound, hydrazide kind compound and compounding foaming agent.
Decorating film the most according to claim 1, it is characterised in that described decorating film material is polrvinyl chloride, polypropylene Or polyethylene film.
Glue the most according to claim 1, it is characterised in that described glue includes that PUR glue, double-component glue etc. are each Plant Pasting glue.
8. according to the preparation method of the Furniture panel described in claim 1 ~ 7, it is characterised in that comprise the steps: step one: Macromolecular material, inorganic combustion inhibitor, foaming agent, bio-based materials being mixed in mixer, extrusion foaming sheet material, as base Material, embossed surface processes；Step 2: the upper and lower surface of foaming wood-plastic sheet material prepared in step one is coated with glue, will dress Decorations film is pasted on its surface, compacting, edge sealing.
9. according to the preparation method of the Furniture panel described in claim 1 ~ 7, it is characterised in that comprise the steps: step one: Macromolecular material, inorganic combustion inhibitor, foaming agent, bio-based materials being mixed in mixer, extrusion foaming sheet material, as base Material；Step 2: the upper and lower surface of foaming wood-plastic sheet material prepared in step one is coated with glue, and decorating film is pasted on it Surface, compacting, edge sealing, embossed surface processes.
Furniture panel described in the most according to Claim 8 ~ 9, it is characterised in that described foaming wood-plastic sheet material portions span is 3 ~150mm。
Furniture panel described in 11. according to Claim 8 ~ 9, it is characterised in that the thickness of described decorating film is respectively 0.1 ~ 2mm。
CN201610464365.9A 2016-06-24 2016-06-24 Novel furniture plate and preparation method thereof Pending CN106042565A (en)