CN106019422A - Optical release film - Google Patents
Optical release film Download PDFInfo
- Publication number
- CN106019422A CN106019422A CN201610534412.2A CN201610534412A CN106019422A CN 106019422 A CN106019422 A CN 106019422A CN 201610534412 A CN201610534412 A CN 201610534412A CN 106019422 A CN106019422 A CN 106019422A
- Authority
- CN
- China
- Prior art keywords
- optical
- layer
- release liner
- basement membrane
- thin film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Disclosed is an optical release film characterized by comprising an optical base film coated with an isolation coating layer for blocking the migration of ultraviolet light and harmful substances and a release layer coated on the isolation coating layer. The optical release film provided by the invention can effectively block the injection of ultraviolet rays, effectively block the migration of harmful substances, reduce the storage requirements of a product and ensure the normal use of an optical product while maintaining the traditional performances of a release film.
Description
Technical field
The present invention relates to optical material field, particularly relate to a kind of optical release liner.
Background technology
In prior art, optical release liner is all to be coated with response type silicone-based materials on film substrate surface,
Then traditional mould release membrance is made.And along with constantly furtheing investigate in optical cement field, optical articles is to light
The requirement restriction learning glue becomes increasingly harsher, the mould release membrance used such as ultraviolet secondary solidification glue product, just
Need to avoid the irradiation of storing process middle-ultraviolet lamp, otherwise impact is used.And if Product transport or deposit
Encroached on by hot and humid environment during storage, the harmful substance within thin film can be caused to move to be protected
The glue surface protected, causes optical articles performance bad, affects the normal use of product.
Summary of the invention
Because the drawbacks described above of prior art, the technical problem to be solved is to provide a kind of new
Type optical release liner, under keeping tradition mould release membrance performance, it is also possible to effectively intercepts injecting of ultraviolet,
And can effectively intercept the migration of harmful substance, reduce the storage of product and use requirement, it is ensured that optical articles
Normal use.
For achieving the above object, the invention provides a kind of optical release liner, including optics basement membrane, described
Optics basement membrane upper surface is coated with one layer and is used for intercepting ultraviolet and the barrier coat of harmful substance migration, in resistance
One layer of release layer it is coated with in coating.
Preferably, described optics basement membrane lower surface is also coated with one layer of described barrier coat.According to actual needs,
One layer of barrier coat can also be further added by, in terms of two, intercept ultraviolet irradiation and obstruct harmful substance moves
Move.
Preferably, described barrier coat material includes resin material and ultraviolet isolating material, described resin
Material is epoxylite, polyester resin, acrylic resin, polyurethane based resin, silicone
Resin or organic fluorinated silicone resinoid.The obstruct of ultraviolet is realized, then by introducing ultraviolet isolating material
It is mixed into the resin material of high-crosslinking-degree, utilizes the space structure after its crosslinking can intercept harmful substance
Migrate.
Preferably, described ultraviolet isolating material be salicylate compounds, benzophenone compound,
Benzotriazole compound, group-substituted acrylonitrile compound, compound in triazine class or aliphatic polybasic alcohols
Compound.
Preferably, described optics basement membrane is PET film, PE thin film, PP thin film, PC thin film, PMMA
Thin film or TAC film, thickness is 2~300 microns.
Preferably, described release layer material is silicone or organic fluorinated silicone class mould release.
The method have the advantages that
The present invention is coated with by introducing the obstruct that can intercept ultraviolet and harmful substance migration on optics basement membrane
Layer, on the premise of ensureing basic mould release membrance performance, also has the incidence effectively intercepting ultraviolet, and prevents
Only issuable harmful substance migrates affects protected glue surface, so can guarantee that the normal of optical articles
Use, also reduce mould release membrance transport and storage, the environmental requirement of optical articles use, to a certain extent
Reduce each link cost.
Accompanying drawing explanation
Fig. 1 is the optical release liner structural representation of a preferred embodiment of the present invention;
Fig. 2 is the optical release liner structural representation of another preferred embodiment of the present invention;
In figure, 101 is optics basement membrane, and 102 is barrier coat, and 103 is release layer.
Detailed description of the invention
The optical release liner of structure as shown in Figure 1, including optics basement membrane 101, optics basement membrane 101 is PET
The thin film such as thin film, PE thin film, PP thin film, PC thin film, PMMA thin film or TAC film, thickness is 2~300
Micron.It is coated with one layer for intercepting ultraviolet and the resistance of harmful substance migration at optics basement membrane 101 upper surface
Every coating 102, the material of barrier coat 102 is by by resin material and ultraviolet isolating material mixing system
Becoming, wherein resin material is epoxylite, polyester resin, acrylic resin, polyurethanes tree
Fat, silicone resin or organic fluorinated silicone resinoid, by controlling the crosslinking degree of above-mentioned resin, utilize
The space structure of high-crosslinking-degree resin, it is achieved the obstruct migrating harmful substance, certainly, other possesses this
The resin of 26S Proteasome Structure and Function can also replace use.And ultraviolet isolating material can be salicylate class
Compound, benzophenone compound, benzotriazole compound, group-substituted acrylonitrile compound, triazine
Compounds, aliphatic polybasic alcohol compound or other have intercept ultraviolet material.It is coated with intercepting
Being coated with one layer of release layer 103 on layer 102, mould release is silicone or organic fluorinated silicone class mould release, has
Machine silicon class mould release is applicable to acrylic compounds, epoxies, polyurethanes, rubber-like, organic fluorinated silicone class from
Type agent is the most additionally applicable to organic silica gel..In order to more preferably realize the obstruct to ultraviolet and harmful substance, root
According to actually used needs, it is also possible to the lower surface at optics basement membrane 101 is coated one layer of above-mentioned barrier coat
102, as shown in Figure 2.
It is described further below with reference to specific embodiment, to be fully understood from the purpose of the present invention, spy
Seek peace effect.
Embodiment 1
As it is shown in figure 1, optics basement membrane uses the PE thin film of 20 microns, barrier coat uses acrylic resin
Adding salicylate compounds, release layer uses the silicone release agent of blue star, products obtained therefrom test knot
Fruit is as shown in table 1.
Table 1
Test event | Test value |
Total thickness | 22μm |
Off-type force | 5g/in |
Rate of absorbing UV | 85% |
Harmful substance separates out and reduces | 76% |
Embodiment 2
As it is shown in figure 1, optics basement membrane uses the PET film originating from east material of 100 microns, barrier coat is adopted
Add the mixing material of benzophenone and salicylate compounds with modified organic silicone resin, release layer is adopted
With the silicone release agent of DOW CORNING, products obtained therefrom test result is as shown in table 2.
Table 2
Test event | Test value |
Total thickness | 103μm |
Off-type force | 8g/in |
Rate of absorbing UV | 92% |
Harmful substance separates out and reduces | 83% |
Embodiment 3
As it is shown in figure 1, optics basement membrane uses the PC thin film of 250 microns, barrier coat uses polyester resin to add
Adding benzotriazole compound, release layer uses the silicone release agent of SHIN-ETSU HANTOTAI, products obtained therefrom test result
As shown in table 3.
Table 3
Test event | Test value |
Total thickness | 253μm |
Off-type force | 10g/in |
Rate of absorbing UV | 85% |
Harmful substance separates out and reduces | 78% |
Embodiment 4
As it is shown in figure 1, optics basement membrane uses the PET film originating from east material of 75 microns, barrier coat uses
Polyester resin adds salicylate compounds, and release layer uses the Organic fluoride mould release of SHIN-ETSU HANTOTAI, gained
Product test result is as shown in table 4.
Table 4
Test event | Test value |
Total thickness | 80μm |
Off-type force | 10g/in |
Rate of absorbing UV | 83% |
Harmful substance separates out and reduces | 79% |
Comparative example 1
As it is shown in figure 1, optics basement membrane uses the PET film originating from east material of 75 microns, release layer uses letter
Organic fluoride mould release more, adds ultraviolet absorber in mould release, products obtained therefrom test result is as shown in table 5.
Table 5
Test event | Test value |
Total thickness | 80μm |
Off-type force | 10g/in |
Rate of absorbing UV | 75% |
Harmful substance separates out and reduces | 1% |
The preferred embodiment of the present invention described in detail above.Should be appreciated that the common skill of this area
Art personnel just can make many modifications and variations according to the design of the present invention without creative work.Therefore,
All technical staff in the art are divided by logic the most on the basis of existing technology
Analysis, reasoning or the available technical scheme of limited experiment, all should be defined in the patent claims
Protection domain in.
Claims (6)
1. an optical release liner, it is characterised in that include optics basement membrane (101), described optics basement membrane (101)
Upper surface is coated with one layer and is used for intercepting ultraviolet and the barrier coat (102) of harmful substance migration, is intercepting
Coating (102) one layer of release layer (103) of upper coating.
2. optical release liner as claimed in claim 1, it is characterised in that under described optics basement membrane (101)
Surface is also coated with one layer of described barrier coat (102).
3. optical release liner as claimed in claim 2, it is characterised in that described barrier coat (102) material
Material includes resin material and ultraviolet isolating material, and described resin material is epoxylite, polyesters tree
Fat, acrylic resin, polyurethane based resin, silicone resin or organic fluorinated silicone resinoid.
4. optical release liner as claimed in claim 3, it is characterised in that described ultraviolet isolating material is
Salicylate compounds, benzophenone compound, benzotriazole compound, group-substituted acrylonitrile
Compound, compound in triazine class or aliphatic polybasic alcohol compound.
5. optical release liner as claimed in claim 1, it is characterised in that described optics basement membrane (101) is
PET film, PE thin film, PP thin film, PC thin film, PMMA thin film or TAC film, thickness is
2~300 microns.
6. optical release liner as claimed in claim 1, it is characterised in that described release layer (103) material
For silicone or organic fluorinated silicone class mould release.