CN106009412A - PVC (polyvinyl chloride) cable material - Google Patents
PVC (polyvinyl chloride) cable material Download PDFInfo
- Publication number
- CN106009412A CN106009412A CN201610575795.8A CN201610575795A CN106009412A CN 106009412 A CN106009412 A CN 106009412A CN 201610575795 A CN201610575795 A CN 201610575795A CN 106009412 A CN106009412 A CN 106009412A
- Authority
- CN
- China
- Prior art keywords
- parts
- inorganic filler
- cable material
- pvc cable
- under conditions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a PVC (polyvinyl chloride) cable material which comprises, by weight, 55-65 parts of SG-2PVC resin, 30-45 parts of SG-4PVC resin, 12-15 parts of trioctyl trimellate, 2-3 parts of calcium-zinc stabilizer, 1-2 parts of linseed oil, 1-2 parts of chlorinated paraffin, 7-11 parts of magnesium hydroxide, 5-8 parts of antimonous oxide, 2-4 parts of calcium stearate and 25-30 parts of inorganic filler. The PVC cable material has excellent mechanical performance, excellent flame retardance and cold resistance and high comprehensive performance and is completely supportive of being used in some places with high requirements.
Description
Technical field
The present invention relates to polymeric material field, relate in particular to a kind of PVC cable material.
Background technology
PVC cable material is a kind of based on Corvic, add that various auxiliary agent and filler etc. are blended, pelletize and obtain
A kind of plastic pellet, its be mainly used in electric wire outer layer skin carry out, there is preferable mechanical performance and electrical insulation capability.
At present, existing a variety of PVC cable material on the market, but the existing most mechanical property of these CABLE MATERIALS or flame resistance
Can not be good, can be used only in some common occasions, higher occasion is required for some, then cannot use.
Summary of the invention
The technical problem to be solved is to provide a kind of has excellent mechanical property, fire resistance and cold tolerance
PVC cable material.
In order to solve above-mentioned technical problem, the present invention adopts the following technical scheme that a kind of PVC cable material, by weight, bag
Include following raw material: SG-2PVC resin 55~65, SG-4PVC resin 30~45, trioctyl trimellitate (TOTM) 12~15, calcium
Zinc stabilizer 2~3, Semen Lini oil 1~2, chlorinated paraffin 1~2, magnesium hydroxide 7~11, antimony oxide 5~8, hard
Fat acid calcium 2~4, inorganic filler 25~30.
Further, by weight, described inorganic filler includes the Pulvis Talci of white carbon, 15~25,5~10 of 50~70
Attapulgite.
The preparation method of above-mentioned PVC cable material, comprises the following steps:
(1) each raw material in addition to inorganic filler is put in mixer, mix under conditions of 100~110 DEG C and stir
Mix uniformly, add inorganic filler afterwards, mixing and stirring under conditions of 70~80 DEG C, obtain compound;
(2) double screw extruder is fed the mixture into, extruding pelletization under conditions of 130~150 DEG C, obtain described PVC
CABLE MATERIALS.
The invention have the benefit that
PVC cable material the most of the present invention not only has excellent mechanical property, the most also has excellent fire resistance and tolerance to cold
Can, combination property is high, is fully able to be used in some and requires high occasion.
The preparation method of PVC cable material the most of the present invention is simple, easily implements, is suitable to large-scale industrial production, and it is the best to have
Application prospect.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described:
The various raw materials that following example are used, as being not specifically noted, are commercially available prod well known in the art.Wherein
Calcium zinc stabilizer is calcium zinc stabilizer RUP-108.
Embodiment 1
A kind of PVC cable material, by weight, including following raw material: SG-2PVC resin 60, SG-4PVC resin 38,
Trioctyl trimellitate (TOTM) 13, calcium zinc stabilizer 2.5, Semen Lini oil 1.5, chlorinated paraffin 1.5, magnesium hydroxide 9, three aoxidize
Two antimony 7, calcium stearate 3, inorganic filler 27;
Wherein said inorganic filler, by weight, the white carbon including 60, the Pulvis Talci of 20, the attapulgite of 8, nothing
Machine filler first passes through milled processed in advance.
The preparation method of above-mentioned PVC cable material, comprises the following steps:
(1) each raw material in addition to inorganic filler is put in mixer, mixing and stirring under conditions of 105 DEG C,
Add inorganic filler afterwards, mixing and stirring under conditions of 75 DEG C, obtain compound;
(2) double screw extruder is fed the mixture into, extruding pelletization under conditions of 140 DEG C, obtain described PVC cable
Material.
Embodiment 2
A kind of PVC cable material, by weight, including following raw material: SG-2PVC resin 55, SG-4PVC resin 30,
Trioctyl trimellitate (TOTM) 12, calcium zinc stabilizer 2, Semen Lini oil 1, chlorinated paraffin 1, magnesium hydroxide 7, antimony oxide 5,
Calcium stearate 2, inorganic filler 25;
Wherein said inorganic filler, by weight, the white carbon including 50, the Pulvis Talci of 15, the attapulgite of 5, nothing
Machine filler first passes through milled processed in advance.
The preparation method of above-mentioned PVC cable material, comprises the following steps:
(1) each raw material in addition to inorganic filler is put in mixer, mixing and stirring under conditions of 100 DEG C,
Add inorganic filler afterwards, mixing and stirring under conditions of 70 DEG C, obtain compound;
(2) double screw extruder is fed the mixture into, extruding pelletization under conditions of 130 DEG C, obtain described PVC cable
Material.
Embodiment 3
A kind of PVC cable material, by weight, including following raw material: SG-2PVC resin 65, SG-4PVC resin 45,
Trioctyl trimellitate (TOTM) 15, calcium zinc stabilizer 3, Semen Lini oil 2, chlorinated paraffin 2, magnesium hydroxide 11, antimony oxide 8,
Calcium stearate 4, inorganic filler 30;
Wherein said inorganic filler, by weight, the white carbon including 70, the Pulvis Talci of 25, the attapulgite of 10, nothing
Machine filler first passes through milled processed in advance.
The preparation method of above-mentioned PVC cable material, comprises the following steps:
(1) each raw material in addition to inorganic filler is put in mixer, mixing and stirring under conditions of 110 DEG C,
Add inorganic filler afterwards, mixing and stirring under conditions of 80 DEG C, obtain compound;
(2) double screw extruder is fed the mixture into, extruding pelletization under conditions of 150 DEG C, obtain described PVC cable
Material.
Embodiment 4
The experimental technique specified according to the standard of GB/T8815-2002 and GB/T5470-2008, to embodiment 1 to 3
PVC cable material carries out performance detection, and testing result is as shown in table 1.
Table 1
Embodiment 1 | Embodiment 2 | Embodiment 3 | |
Hot strength Mpa | 17 | 16.5 | 17.3 |
Elongation at break % | 350 | 355 | 340 |
Oxygen index (OI) % | 26.4 | 27 | 26.2 |
Impact brittle temperature DEG C | -45 | -48 | -43 |
200 DEG C of static heat min stabilization time | 150 | 140 | 145 |
From the data of table 1 it can be seen that PVC cable material of the present invention not only has excellent mechanical property, the most also have excellent
Good fire resistance and cold tolerance, combination property is high, is fully able to be used in some and requires high occasion.
Be to be understood that example as herein described and embodiment only for explanation, those skilled in the art can make various according to it
Amendment or change, in the case of without departing from spirit of the invention, broadly fall into protection scope of the present invention.
Claims (3)
1. a PVC cable material, it is characterised in that by weight, including following raw material: SG-2PVC resin 55~65,
SG-4PVC resin 30~45, trioctyl trimellitate (TOTM) 12~15, calcium zinc stabilizer 2~3, Semen Lini oil 1~2, chlorine
Fossil waxes 1~2, magnesium hydroxide 7~11, antimony oxide 5~8, calcium stearate 2~4, inorganic filler 25~30.
2. PVC cable material as claimed in claim 1, it is characterised in that by weight, described inorganic filler include 50~
The attapulgite of the Pulvis Talci of white carbon, 15~25,5~10 of 70.
3. the preparation method of PVC cable material as claimed in claim 1 or 2, it is characterised in that comprise the following steps:
(1) each raw material in addition to inorganic filler is put in mixer, mix under conditions of 100~110 DEG C and stir
Mix uniformly, add inorganic filler afterwards, mixing and stirring under conditions of 70~80 DEG C, obtain compound;
(2) double screw extruder is fed the mixture into, extruding pelletization under conditions of 130~150 DEG C, obtain described PVC
CABLE MATERIALS.