CN106009393A - Power cable special for municipal garden construction - Google Patents

Power cable special for municipal garden construction Download PDF

Info

Publication number
CN106009393A
CN106009393A CN201610486147.5A CN201610486147A CN106009393A CN 106009393 A CN106009393 A CN 106009393A CN 201610486147 A CN201610486147 A CN 201610486147A CN 106009393 A CN106009393 A CN 106009393A
Authority
CN
China
Prior art keywords
parts
powder
power cable
protective jacket
mass fraction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610486147.5A
Other languages
Chinese (zh)
Inventor
王乔
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610486147.5A priority Critical patent/CN106009393A/en
Publication of CN106009393A publication Critical patent/CN106009393A/en
Pending legal-status Critical Current

Abstract

The invention relates to a power cable special for municipal garden construction. The power cable comprises multiple copper alloy wires and protecting jackets, the copper alloy wires are arranged in parallel, and the outer layer of each copper alloy wire is wrapped by one protecting jacket; the protecting jackets are prepared from, by mass, phosphite ester, polyvinyl chloride resin, acrylic emulsion, antimony trioxide powder, tribasic lead sulfate, nano zirconium phosphate silver-carrying antibacterial agent, potassium persulfate, polyvinyl alcohol, sodium ricinoleate, butyl p-hydroxybenzoate, sodium dehydroacetate, oxadixyl, vancomycin, bentonite, potassium carbonate, zinc-oxide powder, pine-soot ink, aluminum nitride powder, hexamethylene tetramine, graphite powder, MBS resin, manganese dioxide powder, silicone oil, methyl ethyl ketoxime, barium sulfate, triaryl phosphate, calcium oxide, titanium dioxide, wollastonite powder, aluminum silicate, bisphenol-A epoxy resin and m-phenylenediamine. The power cable is soft in texture, resistant to abrasion and high temperature, safe and reliable and has good heat dissipation performance.

Description

A kind of municipal administration garden layout specialized power cable
Technical field
The present invention relates to a kind of municipal administration garden layout specialized power cable, belong to field of cable technology.
Background technology
The process of construction of urban afforestation, functional requirement and management objectives, different with forestry, but be all the ingredient of production and construction, one is that to draw materials be main, and one is based on environmental conservation.Urban afforestation is the input to social environment capital, and its economy return is many, and is the abundantest.City is divided into two aspects to the demand in gardens: one be based on facility；Two is as leisure facilities.During municipal administration garden layout, it is necessary to use suitable mode to give construction usage, in order to improve its using effect, conveniently use as required.
Summary of the invention
It is an object of the invention to provide a kind of municipal administration garden layout specialized power cable, in order to the use function of municipal administration garden layout specialized power cable is better achieved.
To achieve these goals, technical scheme is as follows.
nullA kind of municipal administration garden layout specialized power cable，Include many copper alloy wires and protective jacket，Copper alloy wire is parallel to each other placement，Every copper alloy wire outer layer all utilizes protective jacket to be coated with，Protective jacket is made up of the component of following mass fraction: phosphite ester 18～22 parts、Corvic 20～24 parts、Acrylic emulsion 16～20 parts、Antimony oxide powder 14～18 parts、Tribasic lead sulfate 20～24 parts、Nanometer silver-zirconium phosphate antimicrobial 16～20 parts、Potassium peroxydisulfate 14～18 parts、Polyvinyl alcohol 20～24 parts、Sodium ricinoleate 16～20 parts、Butyl p-hydroxybenzoate 14～18 parts、Sodium dehydroacetate 20～24 parts、Sandofan 16～20 parts、Vancomycin 16～20 parts、Bentonite 14～18 parts、Potassium carbonate 20～24 parts、Zinc Oxide 16～20 parts、Pine-soot ink 14～18 parts、Aluminum nitride powder 20～24 parts、Hexamethylenetetramine 16～20 parts、Graphite powder 14～18 parts、MBS resin 20～24 parts、Manganese dioxide powder 16～20 parts、Silicone oil 14～18 parts、Methyl ethyl ketone oxime 20～24 parts、Barium sulfate 16～20 parts、Triaryl phosphate 16～20 parts、Calcium oxide 16～20 parts、Titanium dioxide 16～20 parts、Wollastonite in powder 16～20 parts、Aluminium silicate 16～20 parts、Bisphenol A type epoxy resin 16～20 parts、M-diaminobenzene. 16～20 parts.
nullFurther，Above-mentioned municipal administration garden layout specialized power cable protective jacket，It is made up of the component of following mass fraction: phosphite ester 18 parts、Corvic 20 parts、Acrylic emulsion 16 parts、14 parts of antimony oxide powder、Tribasic lead sulfate 20 parts、Nanometer silver-zirconium phosphate antimicrobial 16 parts、Potassium peroxydisulfate 14 parts、Polyvinyl alcohol 20 parts、Sodium ricinoleate 16 parts、Butyl p-hydroxybenzoate 14 parts、Sodium dehydroacetate 20 parts、Sandofan 16 parts、Vancomycin 16 parts、Bentonite 14 parts、Potassium carbonate 20 parts、Zinc Oxide 16 parts、Pine-soot ink 14 parts、Aluminum nitride powder 20 parts、Hexamethylenetetramine 16 parts、Graphite powder 14 parts、MBS resin 20 parts、Manganese dioxide powder 16 parts、Silicone oil 14 parts、Methyl ethyl ketone oxime 20 parts、16 parts of barium sulfate、Triaryl phosphate 16 parts、Calcium oxide 16 parts、Titanium dioxide 16 parts、Wollastonite in powder 16 parts、Aluminium silicate 16 parts、Bisphenol A type epoxy resin 16 parts、M-diaminobenzene. 16 parts.
nullFurther，Above-mentioned municipal administration garden layout specialized power cable protective jacket，It is made up of the component of following mass fraction: phosphite ester 20 parts、Corvic 22 parts、Acrylic emulsion 18 parts、16 parts of antimony oxide powder、Tribasic lead sulfate 22 parts、Nanometer silver-zirconium phosphate antimicrobial 18 parts、Potassium peroxydisulfate 16 parts、Polyvinyl alcohol 22 parts、Sodium ricinoleate 18 parts、Butyl p-hydroxybenzoate 16 parts、Sodium dehydroacetate 22 parts、Sandofan 18 parts、Vancomycin 18 parts、Bentonite 16 parts、Potassium carbonate 22 parts、Zinc Oxide 18 parts、Pine-soot ink 16 parts、Aluminum nitride powder 22 parts、Hexamethylenetetramine 18 parts、Graphite powder 16 parts、MBS resin 22 parts、Manganese dioxide powder 18 parts、Silicone oil 16 parts、Methyl ethyl ketone oxime 22 parts、18 parts of barium sulfate、Triaryl phosphate 18 parts、Calcium oxide 18 parts、Titanium dioxide 18 parts、Wollastonite in powder 18 parts、Aluminium silicate 18 parts、Bisphenol A type epoxy resin 18 parts、M-diaminobenzene. 18 parts.
nullFurther，Above-mentioned municipal administration garden layout specialized power cable protective jacket，It is made up of the component of following mass fraction: phosphite ester 22 parts、Corvic 24 parts、Acrylic emulsion 20 parts、18 parts of antimony oxide powder、Tribasic lead sulfate 24 parts、Nanometer silver-zirconium phosphate antimicrobial 20 parts、Potassium peroxydisulfate 18 parts、Polyvinyl alcohol 24 parts、Sodium ricinoleate 20 parts、Butyl p-hydroxybenzoate 18 parts、Sodium dehydroacetate 24 parts、Sandofan 20 parts、Vancomycin 20 parts、Bentonite 18 parts、Potassium carbonate 24 parts、Zinc Oxide 20 parts、Pine-soot ink 18 parts、Aluminum nitride powder 24 parts、Hexamethylenetetramine 20 parts、Graphite powder 18 parts、MBS resin 24 parts、Manganese dioxide powder 20 parts、Silicone oil 18 parts、Methyl ethyl ketone oxime 24 parts、20 parts of barium sulfate、Triaryl phosphate 20 parts、Calcium oxide 20 parts、Titanium dioxide 20 parts、Wollastonite in powder 20 parts、Aluminium silicate 20 parts、Bisphenol A type epoxy resin 20 parts、M-diaminobenzene. 20 parts.
Further, above-mentioned municipal administration garden layout specialized power cable preparation method step is as follows:
(1) by the phosphite ester of described mass fraction, Corvic, acrylic emulsion, antimony oxide powder, tribasic lead sulfate, nanometer silver-zirconium phosphate antimicrobial, Sandofan, aluminum nitride powder, hexamethylenetetramine, graphite powder, MBS resin, manganese dioxide powder, silicone oil, methyl ethyl ketone oxime, barium sulfate, triaryl phosphate, calcium oxide, titanium dioxide, wollastonite in powder, aluminium silicate, bisphenol A type epoxy resin, m-diaminobenzene. is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20～40KHz, rate of dispersion 5000～about 5400r/min, jitter time is 30～60min；
(2) adding the vancomycin of described mass fraction, bentonite, potassium carbonate, Zinc Oxide, pine-soot ink, ultrasonic high speed dispersion, ultrasonic frequency is 20～35KHz, rate of dispersion 4800～about 5200r/min, and jitter time is 30～50min；
(3) potassium peroxydisulfate of described mass fraction, polyvinyl alcohol, sodium ricinoleate, butyl p-hydroxybenzoate, sodium dehydroacetate are added, ultrasonic high speed dispersion, ultrasonic frequency is 20～30KHz, rate of dispersion 4600～about 4800r/min, and jitter time is 20～40min；Mixed material is prepared after mix homogeneously；
(4) mixed material that step (3) obtains is given hot melt, hot melting temperature is 280～320 DEG C, and recycling is provided with the mould extrusion of through hole and prepares satisfactory protective jacket, the most at room temperature gives water cooling cooling, and it is dried process at 60 DEG C, i.e. obtain finished product.
nullThis beneficial effect of the invention is: the present invention relates to a kind of municipal administration garden layout specialized power cable，Include many copper alloy wires and protective jacket，Copper alloy wire is parallel to each other placement，Every copper alloy wire outer layer all utilizes protective jacket to be coated with，Protective jacket is made up of the component of following mass fraction: phosphite ester、Corvic、Acrylic emulsion、Antimony oxide powder、Tribasic lead sulfate、Nanometer silver-zirconium phosphate antimicrobial、Potassium peroxydisulfate、Polyvinyl alcohol、Sodium ricinoleate、Butyl p-hydroxybenzoate、Sodium dehydroacetate、Sandofan、Vancomycin、Bentonite、Potassium carbonate、Zinc Oxide、Pine-soot ink、Aluminum nitride powder、Hexamethylenetetramine、Graphite powder、MBS resin、Manganese dioxide powder、Silicone oil、Methyl ethyl ketone oxime、Barium sulfate、Triaryl phosphate、Calcium oxide、Titanium dioxide、Wollastonite in powder、Aluminium silicate、Bisphenol A type epoxy resin、M-diaminobenzene..This invention cable has quality softness, Wear-resistant, high-temperature resistant, safe and reliable and have good heat dispersion, this power cable can be used under rugged environment requiring very much, the present invention has higher weatherability, resistance to deformation, hot strength is high, elongation percentage is big, waterproof, the superior flame retardant property to base-layer contraction and craze and transfiguration strong adaptability, acid-resisting, alkali resistance, anticorrosion, convenient uses as required.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment 1
nullMunicipal garden layout specialized power cable in the present embodiment，Include many copper alloy wires and protective jacket，Copper alloy wire is parallel to each other placement，Every copper alloy wire outer layer all utilizes protective jacket to be coated with，Protective jacket is made up of the component of following mass fraction: phosphite ester 18 parts、Corvic 20 parts、Acrylic emulsion 16 parts、14 parts of antimony oxide powder、Tribasic lead sulfate 20 parts、Nanometer silver-zirconium phosphate antimicrobial 16 parts、Potassium peroxydisulfate 14 parts、Polyvinyl alcohol 20 parts、Sodium ricinoleate 16 parts、Butyl p-hydroxybenzoate 14 parts、Sodium dehydroacetate 20 parts、Sandofan 16 parts、Vancomycin 16 parts、Bentonite 14 parts、Potassium carbonate 20 parts、Zinc Oxide 16 parts、Pine-soot ink 14 parts、Aluminum nitride powder 20 parts、Hexamethylenetetramine 16 parts、Graphite powder 14 parts、MBS resin 20 parts、Manganese dioxide powder 16 parts、Silicone oil 14 parts、Methyl ethyl ketone oxime 20 parts、16 parts of barium sulfate、Triaryl phosphate 16 parts、Calcium oxide 16 parts、Titanium dioxide 16 parts、Wollastonite in powder 16 parts、Aluminium silicate 16 parts、Bisphenol A type epoxy resin 16 parts、M-diaminobenzene. 16 parts.
Above-mentioned municipal administration garden layout specialized power cable preparation method step is as follows:
(1) by the phosphite ester of described mass fraction, Corvic, acrylic emulsion, antimony oxide powder, tribasic lead sulfate, nanometer silver-zirconium phosphate antimicrobial, Sandofan, aluminum nitride powder, hexamethylenetetramine, graphite powder, MBS resin, manganese dioxide powder, silicone oil, methyl ethyl ketone oxime, barium sulfate, triaryl phosphate, calcium oxide, titanium dioxide, wollastonite in powder, aluminium silicate, bisphenol A type epoxy resin, m-diaminobenzene. is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5400r/min, jitter time is 60min；
(2) adding the vancomycin of described mass fraction, bentonite, potassium carbonate, Zinc Oxide, pine-soot ink, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min；
(3) adding the potassium peroxydisulfate of described mass fraction, polyvinyl alcohol, sodium ricinoleate, butyl p-hydroxybenzoate, sodium dehydroacetate, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min；Mixed material is prepared after mix homogeneously；
(4) mixed material that step (3) obtains is given hot melt, hot melting temperature is 280～320 DEG C, and recycling is provided with the mould extrusion of through hole and prepares satisfactory protective jacket, the most at room temperature gives water cooling cooling, and it is dried process at 60 DEG C, i.e. obtain finished product.
Embodiment 2
nullMunicipal garden layout specialized power cable in the present embodiment，Include many copper alloy wires and protective jacket，Copper alloy wire is parallel to each other placement，Every copper alloy wire outer layer all utilizes protective jacket to be coated with，Protective jacket is made up of the component of following mass fraction: phosphite ester 20 parts、Corvic 22 parts、Acrylic emulsion 18 parts、16 parts of antimony oxide powder、Tribasic lead sulfate 22 parts、Nanometer silver-zirconium phosphate antimicrobial 18 parts、Potassium peroxydisulfate 16 parts、Polyvinyl alcohol 22 parts、Sodium ricinoleate 18 parts、Butyl p-hydroxybenzoate 16 parts、Sodium dehydroacetate 22 parts、Sandofan 18 parts、Vancomycin 18 parts、Bentonite 16 parts、Potassium carbonate 22 parts、Zinc Oxide 18 parts、Pine-soot ink 16 parts、Aluminum nitride powder 22 parts、Hexamethylenetetramine 18 parts、Graphite powder 16 parts、MBS resin 22 parts、Manganese dioxide powder 18 parts、Silicone oil 16 parts、Methyl ethyl ketone oxime 22 parts、18 parts of barium sulfate、Triaryl phosphate 18 parts、Calcium oxide 18 parts、Titanium dioxide 18 parts、Wollastonite in powder 18 parts、Aluminium silicate 18 parts、Bisphenol A type epoxy resin 18 parts、M-diaminobenzene. 18 parts.
Above-mentioned municipal administration garden layout specialized power cable preparation method step is as follows:
(1) by the phosphite ester of described mass fraction, Corvic, acrylic emulsion, antimony oxide powder, tribasic lead sulfate, nanometer silver-zirconium phosphate antimicrobial, Sandofan, aluminum nitride powder, hexamethylenetetramine, graphite powder, MBS resin, manganese dioxide powder, silicone oil, methyl ethyl ketone oxime, barium sulfate, triaryl phosphate, calcium oxide, titanium dioxide, wollastonite in powder, aluminium silicate, bisphenol A type epoxy resin, m-diaminobenzene. is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 5200r/min, jitter time is 45min；
(2) adding the vancomycin of described mass fraction, bentonite, potassium carbonate, Zinc Oxide, pine-soot ink, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min；
(3) adding the potassium peroxydisulfate of described mass fraction, polyvinyl alcohol, sodium ricinoleate, butyl p-hydroxybenzoate, sodium dehydroacetate, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min；Mixed material is prepared after mix homogeneously；
(4) mixed material that step (3) obtains is given hot melt, hot melting temperature is 280～320 DEG C, and recycling is provided with the mould extrusion of through hole and prepares satisfactory protective jacket, the most at room temperature gives water cooling cooling, and it is dried process at 60 DEG C, i.e. obtain finished product.
Embodiment 3
nullMunicipal garden layout specialized power cable in the present embodiment，Include many copper alloy wires and protective jacket，Copper alloy wire is parallel to each other placement，Every copper alloy wire outer layer all utilizes protective jacket to be coated with，Protective jacket is made up of the component of following mass fraction: phosphite ester 22 parts、Corvic 24 parts、Acrylic emulsion 20 parts、18 parts of antimony oxide powder、Tribasic lead sulfate 24 parts、Nanometer silver-zirconium phosphate antimicrobial 20 parts、Potassium peroxydisulfate 18 parts、Polyvinyl alcohol 24 parts、Sodium ricinoleate 20 parts、Butyl p-hydroxybenzoate 18 parts、Sodium dehydroacetate 24 parts、Sandofan 20 parts、Vancomycin 20 parts、Bentonite 18 parts、Potassium carbonate 24 parts、Zinc Oxide 20 parts、Pine-soot ink 18 parts、Aluminum nitride powder 24 parts、Hexamethylenetetramine 20 parts、Graphite powder 18 parts、MBS resin 24 parts、Manganese dioxide powder 20 parts、Silicone oil 18 parts、Methyl ethyl ketone oxime 24 parts、20 parts of barium sulfate、Triaryl phosphate 20 parts、Calcium oxide 20 parts、Titanium dioxide 20 parts、Wollastonite in powder 20 parts、Aluminium silicate 20 parts、Bisphenol A type epoxy resin 20 parts、M-diaminobenzene. 20 parts.
Above-mentioned municipal administration garden layout specialized power cable preparation method step is as follows:
(1) by the phosphite ester of described mass fraction, Corvic, acrylic emulsion, antimony oxide powder, tribasic lead sulfate, nanometer silver-zirconium phosphate antimicrobial, Sandofan, aluminum nitride powder, hexamethylenetetramine, graphite powder, MBS resin, manganese dioxide powder, silicone oil, methyl ethyl ketone oxime, barium sulfate, triaryl phosphate, calcium oxide, titanium dioxide, wollastonite in powder, aluminium silicate, bisphenol A type epoxy resin, m-diaminobenzene. is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, jitter time is 30min；
(2) adding the vancomycin of described mass fraction, bentonite, potassium carbonate, Zinc Oxide, pine-soot ink, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min；
(3) adding the potassium peroxydisulfate of described mass fraction, polyvinyl alcohol, sodium ricinoleate, butyl p-hydroxybenzoate, sodium dehydroacetate, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min；Mixed material is prepared after mix homogeneously；
(4) mixed material that step (3) obtains is given hot melt, hot melting temperature is 280～320 DEG C, and recycling is provided with the mould extrusion of through hole and prepares satisfactory protective jacket, the most at room temperature gives water cooling cooling, and it is dried process at 60 DEG C, i.e. obtain finished product.
Carry out performance measurement for the cable in embodiment 1, embodiment 2 and embodiment 3, and with certain commercially available cable as a control group, measured data are as shown in table 1.
Table 1
The above is the preferred embodiment of the present invention; it should be pointed out that, for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.

Claims (5)

  1. null1. a municipal garden layout specialized power cable，Include many copper alloy wires and protective jacket，Copper alloy wire is parallel to each other placement，Every copper alloy wire outer layer all utilizes protective jacket to be coated with，It is characterized in that: protective jacket is made up of the component of following mass fraction: phosphite ester 18～22 parts、Corvic 20～24 parts、Acrylic emulsion 16～20 parts、Antimony oxide powder 14～18 parts、Tribasic lead sulfate 20～24 parts、Nanometer silver-zirconium phosphate antimicrobial 16～20 parts、Potassium peroxydisulfate 14～18 parts、Polyvinyl alcohol 20～24 parts、Sodium ricinoleate 16～20 parts、Butyl p-hydroxybenzoate 14～18 parts、Sodium dehydroacetate 20～24 parts、Sandofan 16～20 parts、Vancomycin 16～20 parts、Bentonite 14～18 parts、Potassium carbonate 20～24 parts、Zinc Oxide 16～20 parts、Pine-soot ink 14～18 parts、Aluminum nitride powder 20～24 parts、Hexamethylenetetramine 16～20 parts、Graphite powder 14～18 parts、MBS resin 20～24 parts、Manganese dioxide powder 16～20 parts、Silicone oil 14～18 parts、Methyl ethyl ketone oxime 20～24 parts、Barium sulfate 16～20 parts、Triaryl phosphate 16～20 parts、Calcium oxide 16～20 parts、Titanium dioxide 16～20 parts、Wollastonite in powder 16～20 parts、Aluminium silicate 16～20 parts、Bisphenol A type epoxy resin 16～20 parts、M-diaminobenzene. 16～20 parts.
  2. nullMunicipal administration garden layout specialized power cable the most according to claim 1，It is characterized in that: described municipal administration garden layout specialized power cable protective jacket is made up of the component of following mass fraction: phosphite ester 18 parts、Corvic 20 parts、Acrylic emulsion 16 parts、14 parts of antimony oxide powder、Tribasic lead sulfate 20 parts、Nanometer silver-zirconium phosphate antimicrobial 16 parts、Potassium peroxydisulfate 14 parts、Polyvinyl alcohol 20 parts、Sodium ricinoleate 16 parts、Butyl p-hydroxybenzoate 14 parts、Sodium dehydroacetate 20 parts、Sandofan 16 parts、Vancomycin 16 parts、Bentonite 14 parts、Potassium carbonate 20 parts、Zinc Oxide 16 parts、Pine-soot ink 14 parts、Aluminum nitride powder 20 parts、Hexamethylenetetramine 16 parts、Graphite powder 14 parts、MBS resin 20 parts、Manganese dioxide powder 16 parts、Silicone oil 14 parts、Methyl ethyl ketone oxime 20 parts、16 parts of barium sulfate、Triaryl phosphate 16 parts、Calcium oxide 16 parts、Titanium dioxide 16 parts、Wollastonite in powder 16 parts、Aluminium silicate 16 parts、Bisphenol A type epoxy resin 16 parts、M-diaminobenzene. 16 parts.
  3. null3. according to the municipal garden layout specialized power cable described in claim 1 to 2，It is characterized in that: described municipal administration garden layout specialized power cable protective jacket is made up of the component of following mass fraction: phosphite ester 20 parts、Corvic 22 parts、Acrylic emulsion 18 parts、16 parts of antimony oxide powder、Tribasic lead sulfate 22 parts、Nanometer silver-zirconium phosphate antimicrobial 18 parts、Potassium peroxydisulfate 16 parts、Polyvinyl alcohol 22 parts、Sodium ricinoleate 18 parts、Butyl p-hydroxybenzoate 16 parts、Sodium dehydroacetate 22 parts、Sandofan 18 parts、Vancomycin 18 parts、Bentonite 16 parts、Potassium carbonate 22 parts、Zinc Oxide 18 parts、Pine-soot ink 16 parts、Aluminum nitride powder 22 parts、Hexamethylenetetramine 18 parts、Graphite powder 16 parts、MBS resin 22 parts、Manganese dioxide powder 18 parts、Silicone oil 16 parts、Methyl ethyl ketone oxime 22 parts、18 parts of barium sulfate、Triaryl phosphate 18 parts、Calcium oxide 18 parts、Titanium dioxide 18 parts、Wollastonite in powder 18 parts、Aluminium silicate 18 parts、Bisphenol A type epoxy resin 18 parts、M-diaminobenzene. 18 parts.
  4. null4. according to the municipal garden layout specialized power cable described in claims 1 to 3，It is characterized in that: described municipal administration garden layout specialized power cable protective jacket is made up of the component of following mass fraction: phosphite ester 22 parts、Corvic 24 parts、Acrylic emulsion 20 parts、18 parts of antimony oxide powder、Tribasic lead sulfate 24 parts、Nanometer silver-zirconium phosphate antimicrobial 20 parts、Potassium peroxydisulfate 18 parts、Polyvinyl alcohol 24 parts、Sodium ricinoleate 20 parts、Butyl p-hydroxybenzoate 18 parts、Sodium dehydroacetate 24 parts、Sandofan 20 parts、Vancomycin 20 parts、Bentonite 18 parts、Potassium carbonate 24 parts、Zinc Oxide 20 parts、Pine-soot ink 18 parts、Aluminum nitride powder 24 parts、Hexamethylenetetramine 20 parts、Graphite powder 18 parts、MBS resin 24 parts、Manganese dioxide powder 20 parts、Silicone oil 18 parts、Methyl ethyl ketone oxime 24 parts、20 parts of barium sulfate、Triaryl phosphate 20 parts、Calcium oxide 20 parts、Titanium dioxide 20 parts、Wollastonite in powder 20 parts、Aluminium silicate 20 parts、Bisphenol A type epoxy resin 20 parts、M-diaminobenzene. 20 parts.
  5. Municipal administration garden layout specialized power cable the most according to claim 1, it is characterised in that: described municipal administration garden layout specialized power cable protective jacket preparation method step is as follows:
    (1) by the phosphite ester of described mass fraction, Corvic, acrylic emulsion, antimony oxide powder, tribasic lead sulfate, nanometer silver-zirconium phosphate antimicrobial, Sandofan, aluminum nitride powder, hexamethylenetetramine, graphite powder, MBS resin, manganese dioxide powder, silicone oil, methyl ethyl ketone oxime, barium sulfate, triaryl phosphate, calcium oxide, titanium dioxide, wollastonite in powder, aluminium silicate, bisphenol A type epoxy resin, m-diaminobenzene. is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20～40KHz, rate of dispersion 5000～about 5400r/min, jitter time is about 30～60min；
    (2) adding the vancomycin of described mass fraction, bentonite, potassium carbonate, Zinc Oxide, pine-soot ink, ultrasonic high speed dispersion, ultrasonic frequency is 20～35KHz, and rate of dispersion 4800～about 5200r/min, jitter time is about 30～50min；
    (3) potassium peroxydisulfate of described mass fraction, polyvinyl alcohol, sodium ricinoleate, butyl p-hydroxybenzoate, sodium dehydroacetate are added, ultrasonic high speed dispersion, ultrasonic frequency is 20～30KHz, and rate of dispersion 4600～about 4800r/min, jitter time is about 20～40min；Mixed material is prepared after mix homogeneously；
    (4) mixed material that step (3) obtains is given hot melt, hot melting temperature is 280～320 DEG C, and recycling is provided with the mould extrusion of through hole and prepares satisfactory protective jacket, the most at room temperature gives water cooling cooling, and it is dried process at 60 DEG C, i.e. obtain finished product.
CN201610486147.5A 2016-06-29 2016-06-29 Power cable special for municipal garden construction Pending CN106009393A (en)