CN106009345A - High-elasticity anti-deformation chlorinated polyethylene rubber - Google Patents
High-elasticity anti-deformation chlorinated polyethylene rubber Download PDFInfo
- Publication number
- CN106009345A CN106009345A CN201610669954.0A CN201610669954A CN106009345A CN 106009345 A CN106009345 A CN 106009345A CN 201610669954 A CN201610669954 A CN 201610669954A CN 106009345 A CN106009345 A CN 106009345A
- Authority
- CN
- China
- Prior art keywords
- parts
- accounts
- chlorinated polyethylene
- deformation
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a high-elasticity anti-deformation chlorinated polyethylene rubber. The high-elasticity anti-deformation chlorinated polyethylene rubber is composed of chlorinated polyethylene plastic, a filler, an impact-resistant modification agent, an antistatic agent, a dispersant and a vulcanizing agent. The filler is quartz powder, the impact-resistant modification agent is EVA rubber, the antistatic agent is fatty alcohol polyoxyethylene ether, the dispersant is tristearin, the vulcanizing agent is toluene diisocyanate, the high-elasticity anti-deformation chlorinated polyethylene rubber comprises the following components in parts by weight: 77-85 parts of chlorinated polyethylene plastic, 24-30 parts of quartz powder, 16-21 parts of EVA rubber, 5-9 parts of fatty alcohol polyoxyethylene ether, 8-11 parts of tristearin, and 9-13 parts of toluene diisocyanate. The product has the characteristics of high elasticity, anti-deformation, high intensity, good quality, good electrical insulating property, and low cost.
Description
Technical field
The present invention relates to rubber and plastic field, be specifically related to a kind of high-elastic resistance to deformation chlorinated polyethylene rubber.
Background technology
Chlorinated polyethylene, for saturated macromolecular material, outward appearance is white powder, nonpoisonous and tasteless, has excellent weatherability, resistance to ozone, chemical-resistant resistance and ageing-resistant performance, has good oil resistivity, anti-flammability and tinctorial property.Toughness is good (still having pliability at-30 DEG C), has the good compatibility with other macromolecular material, and decomposition temperature is higher.But there is poor flexibility, compressibility becomes big shortcoming.
Summary of the invention
It is an object of the invention to provide a kind of there is elastic height, resistance to deformation, intensity height, quality is good, electrical insulating property is good, the high-elastic resistance to deformation chlorinated polyethylene rubber of the feature of low cost.
The technical scheme is that, a kind of high-elastic resistance to deformation chlorinated polyethylene rubber, by chlorinated polyethylene alkene plastics, filler, shock resistance modification agent, antistatic additive, dispersant and vulcanizing agent composition, described filler is silica flour, described shock resistance modification agent is EVA rubber, described antistatic additive is fatty alcohol-polyoxyethylene ether, described dispersant is glyceryl tristearate, described vulcanizing agent is toluene di-isocyanate(TDI), parts by weight shared by the described high-elastic each composition of resistance to deformation chlorinated polyethylene rubber are respectively as follows: described chlorinated polyethylene alkene plastics and account for 77-85 part, described silica flour accounts for 24-30 part, described EVA rubber accounts for 16-21 part, described fatty alcohol-polyoxyethylene ether accounts for 5-9 part, described glyceryl tristearate accounts for 8-11 part, described toluene di-isocyanate(TDI) accounts for 9-13 part.
In a preferred embodiment of the present invention, shared by the described high-elastic each composition of resistance to deformation chlorinated polyethylene rubber, parts by weight are particularly as follows: described chlorinated polyethylene alkene plastics accounts for 78 parts, described silica flour accounts for 25 parts, described EVA rubber accounts for 17 parts, described fatty alcohol-polyoxyethylene ether accounts for 6 parts, described glyceryl tristearate accounts for 9 parts, and described toluene di-isocyanate(TDI) accounts for 10 parts.
In a preferred embodiment of the present invention, shared by the described high-elastic each composition of resistance to deformation chlorinated polyethylene rubber, parts by weight are particularly as follows: described chlorinated polyethylene alkene plastics accounts for 84 parts, described silica flour accounts for 29 parts, described EVA rubber accounts for 20 parts, described fatty alcohol-polyoxyethylene ether accounts for 8 parts, described glyceryl tristearate accounts for 10 parts, and described toluene di-isocyanate(TDI) accounts for 12 parts.
Of the present invention for a kind of high-elastic resistance to deformation chlorinated polyethylene rubber, this product has elastic height, resistance to deformation, intensity height, quality is good, electrical insulating property is good, the feature of low cost.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail, so that advantages and features of the invention can be easier to be readily appreciated by one skilled in the art, thus protection scope of the present invention is made apparent clear and definite defining.
Of the present invention for a kind of high-elastic resistance to deformation chlorinated polyethylene rubber, by chlorinated polyethylene alkene plastics, filler, shock resistance modification agent, antistatic additive, dispersant and vulcanizing agent composition, described filler is silica flour, described shock resistance modification agent is EVA rubber, described antistatic additive is fatty alcohol-polyoxyethylene ether, described dispersant is glyceryl tristearate, described vulcanizing agent is toluene di-isocyanate(TDI), parts by weight shared by the described high-elastic each composition of resistance to deformation chlorinated polyethylene rubber are respectively as follows: described chlorinated polyethylene alkene plastics and account for 77-85 part, described silica flour accounts for 24-30 part, described EVA rubber accounts for 16-21 part, described fatty alcohol-polyoxyethylene ether accounts for 5-9 part, described glyceryl tristearate accounts for 8-11 part, described toluene di-isocyanate(TDI) accounts for 9-13 part.
Further, shared by the described high-elastic each composition of resistance to deformation chlorinated polyethylene rubber, parts by weight are particularly as follows: described chlorinated polyethylene alkene plastics accounts for 78 parts, described silica flour accounts for 25 parts, described EVA rubber accounts for 17 parts, described fatty alcohol-polyoxyethylene ether accounts for 6 parts, described glyceryl tristearate accounts for 9 parts, and described toluene di-isocyanate(TDI) accounts for 10 parts.
Further, shared by the described high-elastic each composition of resistance to deformation chlorinated polyethylene rubber, parts by weight are particularly as follows: described chlorinated polyethylene alkene plastics accounts for 84 parts, described silica flour accounts for 29 parts, described EVA rubber accounts for 20 parts, described fatty alcohol-polyoxyethylene ether accounts for 8 parts, described glyceryl tristearate accounts for 10 parts, and described toluene di-isocyanate(TDI) accounts for 12 parts.
Proportioning is carried out so that the properties of product height obtained differs by each composition Different Weight number.
Of the present invention for a kind of high-elastic resistance to deformation chlorinated polyethylene rubber, this product has elastic height, resistance to deformation, intensity height, quality is good, electrical insulating property is good, the feature of low cost.
The foregoing is only the detailed description of the invention of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the technical scope that disclosed herein; the change can expected without creative work or replacement, all should contain within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims are limited.
Claims (3)
1. a high-elastic resistance to deformation chlorinated polyethylene rubber, it is characterized in that: by chlorinated polyethylene alkene plastics, filler, shock resistance modification agent, antistatic additive, dispersant and vulcanizing agent composition, described filler is silica flour, described shock resistance modification agent is EVA rubber, described antistatic additive is fatty alcohol-polyoxyethylene ether, described dispersant is glyceryl tristearate, described vulcanizing agent is toluene di-isocyanate(TDI), parts by weight shared by the described high-elastic each composition of resistance to deformation chlorinated polyethylene rubber are respectively as follows: described chlorinated polyethylene alkene plastics and account for 77-85 part, described silica flour accounts for 24-30 part, described EVA rubber accounts for 16-21 part, described fatty alcohol-polyoxyethylene ether accounts for 5-9 part, described glyceryl tristearate accounts for 8-11 part, described toluene di-isocyanate(TDI) accounts for 9-13 part.
High-elastic resistance to deformation chlorinated polyethylene rubber the most according to claim 1, it is characterized in that: shared by the described high-elastic each composition of resistance to deformation chlorinated polyethylene rubber, parts by weight are particularly as follows: described chlorinated polyethylene alkene plastics accounts for 78 parts, described silica flour accounts for 25 parts, described EVA rubber accounts for 17 parts, described fatty alcohol-polyoxyethylene ether accounts for 6 parts, described glyceryl tristearate accounts for 9 parts, and described toluene di-isocyanate(TDI) accounts for 10 parts.
High-elastic resistance to deformation chlorinated polyethylene rubber the most according to claim 1, it is characterized in that: shared by the described high-elastic each composition of resistance to deformation chlorinated polyethylene rubber, parts by weight are particularly as follows: described chlorinated polyethylene alkene plastics accounts for 84 parts, described silica flour accounts for 29 parts, described EVA rubber accounts for 20 parts, described fatty alcohol-polyoxyethylene ether accounts for 8 parts, described glyceryl tristearate accounts for 10 parts, and described toluene di-isocyanate(TDI) accounts for 12 parts.