CN106009318A - Preparation method of outer rubber layer of air delivery hose - Google Patents
Preparation method of outer rubber layer of air delivery hose Download PDFInfo
- Publication number
- CN106009318A CN106009318A CN201610441894.7A CN201610441894A CN106009318A CN 106009318 A CN106009318 A CN 106009318A CN 201610441894 A CN201610441894 A CN 201610441894A CN 106009318 A CN106009318 A CN 106009318A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- sodium
- prepared
- mixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of an outer rubber layer of an air delivery hose and belongs to the technical field of rubber accessory manufacturing. The preparation method includes the steps that ethylene propylene diene monomer, nano silicon dioxide, silicone oil, zinc diethyl dithiocarbamate, 2-thiol benzimidazole, dioctyl ester, sulfur, magnesium strengthening powder and paraffin are put into a mixer for mixing, rubber discharge is performed under the rubber temperature condition of 160 DEG C after mixing, masterbatch is prepared and put in the mixer, the petroleum resin, polyurethane, sodium hexametaphosphate, sodium pyrophosphate and sodium tripolyphosphate are added for mixing, and a rubber compound is prepared; the prepared rubber compound is put into an extruder to make a rubber tube blank, and vulcanization treatment is performed. The outer rubber layer is modified mainly by adding the petroleum resin, the polyurethane, the sodium hexametaphosphate, the sodium pyrophosphate, the sodium tripolyphosphate and the nano silicon dioxide to rubber in specific proportion, and thus the elastic properties of the outer rubber layer are improved.
Description
Technical field
The invention belongs to rubber accessory manufacturing technology field, particularly relate to the preparation method of the outer glue-line of a kind of defeated air hose.
Background technology
Defeated air flexible pipe is mainly made up of inner glue layer and outer glue-line, mainly in the conveying gas such as air, oxygen, is widely used in the field such as industry, pharmaceutical sector.
Summary of the invention
The technical problem to be solved is to provide the preparation method of the outer glue-line of the good defeated air hose of a kind of elastic performance.
In order to solve above-mentioned technical problem, the technical solution adopted in the present invention is:
It comprises the following steps:
The most by weight, 100 parts of ethylene propylene diene rubbers, 6 parts~10 parts of nanometer grade silicas, 0.1 part~0.2 part of silicone oil, 1 part~2 parts of tetraethylthiuram disulfides, 5 parts~10 parts of 2 mercapto benzimidazoles, 20 parts~30 parts of dioctyl esters, 0.1 part~0.2 part of sulfur, 15 parts~20 parts of strong powder of magnesium and 15 parts~20 parts of paraffin are put into banbury and are carried out banburying, banburying terminate after binder removal under conditions of glue temperature is 160 DEG C again, prepare masterbatch;
B. prepared masterbatch is put into mixing roll, adds 15 parts~20 parts of Petropols, 5 parts~10 parts of polyurethanes, 1 part~5 parts of sodium hexameta phosphate, 6 parts~10 parts of sodium pyrophosphates and 6 parts~10 parts of sodium tripolyphosphates, carry out mixing, prepare elastomeric compound;
C. prepared elastomeric compound is put into extruder, make rubber tube blank, and carry out vulcanizing treatment.
Owing to using technique scheme, there is advantages that
The present invention mainly carries out changing surname by adding the Petropols of special ratios, polyurethanes, sodium hexameta phosphate, sodium pyrophosphate, sodium tripolyphosphate and nanometer grade silica in rubber, thus improves its elastic performance.
Detailed description of the invention
Below in conjunction with instantiation, the invention will be further described:
Embodiment 1
The outer glue-line of this defeated air hose includes following preparation process:
A.1000g ethylene propylene diene rubber, 100g nanometer grade silica, 2g silicone oil, 10g tetraethylthiuram disulfide, 80g2-mercaptobenzimidazole, 300g dioctyl ester, 2g sulfur, the strong powder of 150g magnesium and 200g paraffin are put into banbury and are carried out banburying, banburying terminate after binder removal under conditions of glue temperature is 160 DEG C again, prepare masterbatch;
B. prepared masterbatch is put into mixing roll, adds 180g Petropols, 100g polyurethanes, 30g sodium hexameta phosphate, 80g sodium pyrophosphate and 60g sodium tripolyphosphate, carry out mixing, prepare elastomeric compound;
C. prepared elastomeric compound is put into extruder, make rubber tube blank, and carry out vulcanizing treatment.
The shrinkage factor (solidifying 10 minutes under 350 (166 DEG C)) of the outer glue-line of the defeated air hose that the present embodiment prepares is 4.0%.
Embodiment 2
The outer glue-line of this defeated air hose includes following preparation process:
A.1000g ethylene propylene diene rubber, 70g nanometer grade silica, 1g silicone oil, 20g tetraethylthiuram disulfide, 50g2-mercaptobenzimidazole, 240g dioctyl ester, 1.5g sulfur, the strong powder of 170g magnesium and 150g paraffin are put into banbury and are carried out banburying, banburying terminate after binder removal under conditions of glue temperature is 160 DEG C again, prepare masterbatch;
B. prepared masterbatch is put into mixing roll, adds 150g Petropols, 50g polyurethanes, 50g sodium hexameta phosphate, 100g sodium pyrophosphate and 80g sodium tripolyphosphate, carry out mixing, prepare elastomeric compound;
C. prepared elastomeric compound is put into extruder, make rubber tube blank, and carry out vulcanizing treatment.
The shrinkage factor (solidifying 10 minutes under 350 (166 DEG C)) of the outer glue-line of the defeated air hose that the present embodiment prepares is 4.2%.
Embodiment 3
The outer glue-line of this defeated air hose includes following preparation process:
A.1000g ethylene propylene diene rubber, 60g nanometer grade silica, 1.5g silicone oil, 15g tetraethylthiuram disulfide, 100g 2 mercapto benzimidazole, 200g dioctyl ester, 1g sulfur, the strong powder of 200g magnesium and 170g paraffin are put into banbury and are carried out banburying, banburying terminate after binder removal under conditions of glue temperature is 160 DEG C again, prepare masterbatch;
B. prepared masterbatch is put into mixing roll, adds 200g Petropols, 70g polyurethanes, 10g sodium hexameta phosphate, 60g sodium pyrophosphate and 100g sodium tripolyphosphate, carry out mixing, prepare elastomeric compound;
C. prepared elastomeric compound is put into extruder, make rubber tube blank, and carry out vulcanizing treatment.
The shrinkage factor (solidifying 10 minutes under 350 (166 DEG C)) of the outer glue-line of the defeated air hose that the present embodiment prepares is 4.1%.
Claims (1)
1. the preparation method of the outer glue-line of defeated air hose, it is characterised in that comprise the following steps:
The most by weight, 100 parts of ethylene propylene diene rubbers, 6 parts~10 parts of nanometer grade silicas, 0.1 part~0.2 part of silicone oil, 1 part~2 parts of tetraethylthiuram disulfides, 5 parts~10 parts of 2 mercapto benzimidazoles, 20 parts~30 parts of dioctyl esters, 0.1 part~0.2 part of sulfur, 15 parts~20 parts of strong powder of magnesium and 15 parts~20 parts of paraffin are put into banbury and are carried out banburying, banburying terminate after binder removal under conditions of glue temperature is 160 DEG C again, prepare masterbatch;
B. prepared masterbatch is put into mixing roll, adds 15 parts~20 parts of Petropols, 5 parts~10 parts of polyurethanes, 1 part~5 parts of sodium hexameta phosphate, 6 parts~10 parts of sodium pyrophosphates and 6 parts~10 parts of sodium tripolyphosphates, carry out mixing, prepare elastomeric compound;
C. prepared elastomeric compound is put into extruder, make rubber tube blank, and carry out vulcanizing treatment.