CN106008859A - Mobile phone liquid crystal displayer rubber frame and production technology thereof - Google Patents
Mobile phone liquid crystal displayer rubber frame and production technology thereof Download PDFInfo
- Publication number
- CN106008859A CN106008859A CN201610541291.4A CN201610541291A CN106008859A CN 106008859 A CN106008859 A CN 106008859A CN 201610541291 A CN201610541291 A CN 201610541291A CN 106008859 A CN106008859 A CN 106008859A
- Authority
- CN
- China
- Prior art keywords
- mixture
- liquid crystal
- glue frame
- mobile phone
- injection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a mobile phone liquid crystal displayer rubber frame and a production technology thereof and belongs to the technical field of mobile phone liquid crystal displayer rubber frames. The mobile phone liquid crystal displayer rubber frame is prepared from, by weight, 75-85 parts of polycarbonate, 4-10 parts of acrylic acid, 5-9 parts of chlorinated polyethylene, 6-7 parts of poly-ammonium polyphosphate, 2-4 parts of phosphate ester, 4-5 parts of calcium carbonate, 7-8 parts of magnesium oxide and 5-6 parts of a reinforcer. The rubber frame is high in strength and not likely to crack under the action of external force; the rubber frame is resistant to corrosion and long in service life; the rubber frame is free of aging, and a liquid crystal displayer is good in display effect.
Description
Technical field
The invention belongs to Mobile phone liquid crystal display glue frame technical field, particularly relate to a kind of mobile phone liquid crystal display
Device glue frame and production technology thereof.
Background technology
The structure of liquid crystal display is placement liquid crystal cell, infrabasal plate glass in the middle of the glass substrate that two panels is parallel
Thin film transistor (TFT) is set on glass, upper substrate glass arranges colored filter, by thin film transistor (TFT)
Signal and voltage change the rotation direction controlling liquid crystal molecule, thus reach to control each pixel polarization
Whether light outgoing reaches to show purpose.In daily life, mobile phone easily falls on the ground, mobile phone liquid crystal
Show that the glue frame of device was easily broken;Mobile phone speckles with steam, time length, and glue frame is easily corroded;And mobile phone
The most under the high temperature conditions, glue frame is the most aging, affects the display effect of liquid crystal display.
Summary of the invention
The technical problem to be solved is to provide a kind of Mobile phone liquid crystal display glue frame and production thereof
Technique.
For solving the problems referred to above, a kind of Mobile phone liquid crystal display glue frame of the present invention, this mobile phone liquid crystal
Display glue frame is to be composed of the following components in parts by weight: Merlon 75~85, acrylic acid 4~10,
Chlorinated polyethylene 5~9, poly-ammonium polyphosphate 6~7, phosphate ester 2~4, calcium carbonate 4~5, magnesium oxide 7~
8 and hardening agent 5~6.
Described hardening agent is to be composed of the following components in parts by weight: aluminium hydroxide 2.2~2.5, butylphenol
1.1~1.3, dibenzylatiooluene 0.8~0.9, oxybenzoic acid phenyl ester 0.6~0.8, hexamethyl
Phosphoric triamide 1.2~1.5 and chlorinated paraffin 2~3.
The production technology of a kind of Mobile phone liquid crystal display glue frame, comprises the following steps that:
(1) by Merlon 75~85, acrylic acid 4~10, chlorinated polyethylene 5~9, poly-ammonium polyphosphate
6~7, phosphate ester 2~4, calcium carbonate 4~5, magnesium oxide 7~8 and hardening agent 5~6 are put in blender
Stir, obtain mixture a;
(2) putting in injection mold by mixture a, mould inside temperature is 280~360 DEG C, then enters
Row insulation, holding temperature is 280~360 DEG C, and temperature retention time is 4~7 minutes, heat preservation pressure be 50~
70MPa, mixture a are molten condition;
(3) the mixture a of molten condition is entered in mold cavity by screw of injection, injection pressure be 90~
130MPa, then cools down, and cool time is 3~5 minutes;
(4) the glue frame of molding is taken out in die sinking.
Compared with prior art, the invention have the advantages that the glue frame intensity of the present invention is high, it is not easy to
Rupture under external force;The glue frame of the present invention is corrosion-resistant, and service life is long;The glue frame of the present invention will not
Aging, the display effect of liquid crystal display is good.
Detailed description of the invention
Embodiment 1
A kind of Mobile phone liquid crystal display glue frame, this Mobile phone liquid crystal display glue frame is by the one-tenth of following weight portion
Be grouped into: Merlon 75, acrylic acid 4, chlorinated polyethylene 5, poly-ammonium polyphosphate 6, phosphate ester 2,
Calcium carbonate 4, magnesium oxide 7 and hardening agent 5.
Hardening agent is to be composed of the following components in parts by weight: aluminium hydroxide 2.2, butylphenol 1.1, two fourth
Base hydroxy-methylbenzene 0.8, oxybenzoic acid phenyl ester 0.6, HMPA 1.2 and chlorinated paraffin 2.
The production technology of a kind of Mobile phone liquid crystal display glue frame, comprises the following steps that:
(1) by Merlon 75, acrylic acid 4, chlorinated polyethylene 5, poly-ammonium polyphosphate 6, phosphate ester 2,
Calcium carbonate 4, magnesium oxide 7 and hardening agent 5 are put in blender and are stirred, and obtain mixture a;
(2) putting in injection mold by mixture a, mould inside temperature is 280 DEG C, then protects
Temperature, holding temperature is 280 DEG C, and temperature retention time is 4 minutes, and heat preservation pressure is 50MPa, mixture a in
Molten condition;
(3) entering in mold cavity by the mixture a of molten condition by screw of injection, injection pressure is
90MPa, then cools down, and cool time is 3 minutes;
(4) the glue frame of molding is taken out in die sinking.
It is demonstrated experimentally that this parameter low glue frame intensity is high, it is not easy to fracture;Glue frame is corrosion-resistant by force, uses the longevity
Life is long;Glue frame will not be aging, and the display effect of liquid crystal display is preferable.
Embodiment 2
A kind of Mobile phone liquid crystal display glue frame, this Mobile phone liquid crystal display glue frame is by the one-tenth of following weight portion
Be grouped into: Merlon 80, acrylic acid 7, chlorinated polyethylene 7, poly-ammonium polyphosphate 6, phosphate ester 3,
Calcium carbonate 5, magnesium oxide 7 and hardening agent 6.
Hardening agent is to be composed of the following components in parts by weight: aluminium hydroxide 2.3, butylphenol 1.2, two fourth
Base hydroxy-methylbenzene 0.8, oxybenzoic acid phenyl ester 0.7, HMPA 1.4 and chlorinated paraffin 3.
The production technology of a kind of Mobile phone liquid crystal display glue frame, comprises the following steps that:
(1) by Merlon 80, acrylic acid 7, chlorinated polyethylene 7, poly-ammonium polyphosphate 6, phosphate ester 3,
Calcium carbonate 5, magnesium oxide 7 and hardening agent 6 are put in blender and are stirred, and obtain mixture a;
(2) putting in injection mold by mixture a, mould inside temperature is 320 DEG C, then protects
Temperature, holding temperature is 320 DEG C, and temperature retention time is 6 minutes, and heat preservation pressure is 60MPa, mixture a in
Molten condition;
(3) entering in mold cavity by the mixture a of molten condition by screw of injection, injection pressure is
110MPa, then cools down, and cool time is 4 minutes;
(4) the glue frame of molding is taken out in die sinking.
It is demonstrated experimentally that this parameter low glue frame intensity is the highest, it is not easy to fracture;Glue frame is corrosion-resistant the strongest, makes
Use longest-lived;Glue frame will not be aging, and the display effect of liquid crystal display is best.
Therefore, the present embodiment is preferred embodiment.
Embodiment 3
A kind of Mobile phone liquid crystal display glue frame, this Mobile phone liquid crystal display glue frame is by the one-tenth of following weight portion
Be grouped into: Merlon 85, acrylic acid 10, chlorinated polyethylene 9, poly-ammonium polyphosphate 7, phosphate ester 4,
Calcium carbonate 5, magnesium oxide 8 and hardening agent 6.
Hardening agent is to be composed of the following components in parts by weight: aluminium hydroxide 2.5, butylphenol 1.3, two fourth
Base hydroxy-methylbenzene 0.9, oxybenzoic acid phenyl ester 0.8, HMPA 1.5 and chlorinated paraffin 3.
The production technology of a kind of Mobile phone liquid crystal display glue frame, comprises the following steps that:
(1) by Merlon 85, acrylic acid 10, chlorinated polyethylene 9, poly-ammonium polyphosphate 7, phosphate ester
4, calcium carbonate 5, magnesium oxide 8 and hardening agent 6 are put in blender and are stirred, and obtain mixture a;
(2) putting in injection mold by mixture a, mould inside temperature is 360 DEG C, then protects
Temperature, holding temperature is 360 DEG C, and temperature retention time is 7 minutes, and heat preservation pressure is 70MPa, mixture a in
Molten condition;
(3) entering in mold cavity by the mixture a of molten condition by screw of injection, injection pressure is
130MPa, then cools down, and cool time is 5 minutes;
(4) the glue frame of molding is taken out in die sinking.
It is demonstrated experimentally that this parameter low glue frame intensity is higher, it is not easy to fracture;Glue frame is corrosion-resistant relatively strong, makes
Use the life-span long;Glue frame will not be aging, and the display effect of liquid crystal display is good.
Claims (6)
1. a Mobile phone liquid crystal display glue frame, it is characterised in that: this Mobile phone liquid crystal display glue frame be by
The one-tenth of following weight portion is grouped into: Merlon 75~85, acrylic acid 4~10, chlorinated polyethylene 5~9,
Poly-ammonium polyphosphate 6~7, phosphate ester 2~4, calcium carbonate 4~5, magnesium oxide 7~8 and hardening agent 5~6.
A kind of Mobile phone liquid crystal display glue frame, it is characterised in that: described by force
Agent is to be composed of the following components in parts by weight: aluminium hydroxide 2.2~2.5, butylphenol 1.1~1.3,
Dibenzylatiooluene 0.8~0.9, oxybenzoic acid phenyl ester 0.6~0.8, HMPA
1.2~1.5 and chlorinated paraffin 2~3.
3. the production technology of a Mobile phone liquid crystal display glue frame, it is characterised in that: include that following technique walks
Rapid:
(1) by Merlon 75~85, acrylic acid 4~10, chlorinated polyethylene 5~9, poly-ammonium polyphosphate
6~7, phosphate ester 2~4, calcium carbonate 4~5, magnesium oxide 7~8 and hardening agent 5~6 are put in blender
Stir, obtain mixture a;
(2) putting in injection mold by mixture a, mould inside temperature is 280~360 DEG C, then enters
Row insulation, holding temperature is 230~320 DEG C, and temperature retention time is 4~7 minutes, heat preservation pressure be 50~
70MPa, mixture a are molten condition;
(3) the mixture a of molten condition is entered in mold cavity by screw of injection, injection pressure be 90~
130MPa, then cools down, and cool time is 3~5 minutes;
(4) the glue frame of molding is taken out in die sinking.
The production technology of a kind of Mobile phone liquid crystal display glue frame, its feature exists
In: comprise the following steps that:
(1) by Merlon 75, acrylic acid 4, chlorinated polyethylene 5, poly-ammonium polyphosphate 6, phosphate ester 2,
Calcium carbonate 4, magnesium oxide 7 and hardening agent 5 are put in blender and are stirred, and obtain mixture a;
(2) putting in injection mold by mixture a, mould inside temperature is 280 DEG C, then protects
Temperature, holding temperature is 280 DEG C, and temperature retention time is 4 minutes, and heat preservation pressure is 50MPa, mixture a in
Molten condition;
(3) entering in mold cavity by the mixture a of molten condition by screw of injection, injection pressure is
90MPa, then cools down, and cool time is 3 minutes;
(4) the glue frame of molding is taken out in die sinking.
The production technology of a kind of Mobile phone liquid crystal display glue frame, its feature exists
In: comprise the following steps that:
(1) by Merlon 80, acrylic acid 7, chlorinated polyethylene 7, poly-ammonium polyphosphate 6, phosphate ester 3,
Calcium carbonate 5, magnesium oxide 7 and hardening agent 6 are put in blender and are stirred, and obtain mixture a;
(2) putting in injection mold by mixture a, mould inside temperature is 320 DEG C, then protects
Temperature, holding temperature is 320 DEG C, and temperature retention time is 6 minutes, and heat preservation pressure is 60MPa, mixture a in
Molten condition;
(3) entering in mold cavity by the mixture a of molten condition by screw of injection, injection pressure is
110MPa, then cools down, and cool time is 4 minutes;
(4) the glue frame of molding is taken out in die sinking.
The production technology of a kind of Mobile phone liquid crystal display glue frame, its feature exists
In: comprise the following steps that:
(1) by Merlon 85, acrylic acid 10, chlorinated polyethylene 9, poly-ammonium polyphosphate 7, phosphate ester
4, calcium carbonate 5, magnesium oxide 8 and hardening agent 6 are put in blender and are stirred, and obtain mixture a;
(2) putting in injection mold by mixture a, mould inside temperature is 360 DEG C, then protects
Temperature, holding temperature is 360 DEG C, and temperature retention time is 7 minutes, and heat preservation pressure is 70MPa, mixture a in
Molten condition;
(3) entering in mold cavity by the mixture a of molten condition by screw of injection, injection pressure is
130MPa, then cools down, and cool time is 5 minutes;
(4) the glue frame of molding is taken out in die sinking.