CN106008805A - Oil well cement retarder and preparing method thereof - Google Patents
Oil well cement retarder and preparing method thereof Download PDFInfo
- Publication number
- CN106008805A CN106008805A CN201610439910.9A CN201610439910A CN106008805A CN 106008805 A CN106008805 A CN 106008805A CN 201610439910 A CN201610439910 A CN 201610439910A CN 106008805 A CN106008805 A CN 106008805A
- Authority
- CN
- China
- Prior art keywords
- solution
- oil well
- well cement
- cement retarder
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an oil well cement retarder and a preparing method thereof. The oil well cement retarder is prepared from, by weight, 20 parts of 2-acrylamide-2-methylpropanesulfonic acid, 8-9 parts of maleic anhydride, 3.5-4.5 parts of fumaric acid, 1.5-2.5 parts of methacrylic acid, 60 parts of water and 1.5-2 parts of an initiator. The preparing method comprises the steps that firstly, all monomers and water are put into a container and prepared into a solution, and a sodium hydrogen carbonate solution with the concentration of 20% is used for regulating the PH value to be 6; then, the solution is transferred into a reactor, the reactor is put into a water bath pot to be heated, and meanwhile the solution is stirred; the temperature of the solution is maintained when increased to 60 DEG C, and nitrogen is introduced into the reactor for 30 min; finally, the initiator is added into the solution, the temperature continues to be maintained and stirring is carried out for 4 h, and the oil well cement retarder is obtained. The oil well cement retarder prepared with the method still can perform a good retarding effect when the temperature is high.
Description
Technical field
The present invention relates to oil well cement additive field, particularly relate to a kind of oil well cement retarder and preparation side thereof
Method.
Background technology
Retarder is can to prevent cement rapid condensation, prolongation cement slurry thickening time, to guarantee the one of construction safety
Class additive, when when burying the exploration and development carrying out oil gas field at oil well deep, that bottom hole temperature (BHT) temperature is high, well
The higher temperature in the end can cause the thickening time of oil-well cement to shorten, and common oil well cement retarder can not meet
Resistant to elevated temperatures use requirement.
Summary of the invention
Present invention seek to address that the deficiencies in the prior art, and provide a kind of high temperature resistant, effective oil-well cement to delay
Solidifying agent and preparation method thereof.
The present invention for achieving the above object, by the following technical solutions: a kind of oil well cement retarder, its feature
It is, is made up of the raw material of following parts by weight:
As preferably, described 2-acrylamido 2-methyl propane sulfonic acid can be replaced Sodium styrene sulfonate.
As preferably, described initiator is Ammonium persulfate..
The preparation method of a kind of oil well cement retarder that the present invention provides, it is characterised in that comprise the following steps:
(1) 2-acrylamido 2-methyl propane sulfonic acid, maleic anhydride, methacrylic acid and water are put into
In container, it is configured to solution;
(2) pH value using the sodium bicarbonate solution regulation solution of 20% is 6, transfers the solution into reaction
In device;
(3) reactor is placed in water-bath heating, solution is stirred simultaneously;
(4) it is incubated after solution is warming up to 60 DEG C, in reactor, is passed through the nitrogen of 30min;
(5) in solution, add initiator, continue to protect gentle agitation 4h, obtain oil well cement retarder.
The invention has the beneficial effects as follows: the oil well cement retarder that the present invention prepares can stop cement granules
Sedimentation, so that cement mortar has good stability, the macromolecular chain of the retarder being configured to has much sulphur
Acid groups and hydroxy-acid group, these polar group dispersibility are strong, and absorption is in the cation position of cement particle surface
Place, makes particle surface band like charges produce mutual repulsion effect, and the cohesion of suppression cement granules, especially at high temperature
Under this effect more intensive, hence in so that retarder remains to when temperature is higher play preferable retarding effect.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described:
Embodiment 1
A kind of oil well cement retarder, it is characterised in that be made up of the raw material of following parts by weight:
Preparation method: a kind of oil well as a example by the oil well cement retarder preparing 94.5g, the present embodiment provided
The preparation method of cement retarder is described below:
(1) by 20g 2-acrylamido 2-methyl propane sulfonic acid, 8g maleic anhydride, the anti-butylene of 3.5g two
Acid, 1.5g methacrylic acid and 60g water are put in container, are configured to solution;
(2) pH value using the sodium bicarbonate solution regulation solution of 20% is 6, transfers the solution into reaction
In device;
(3) reactor is placed in water-bath heating, solution is stirred simultaneously;
(4) it is incubated after solution is warming up to 60 DEG C, in reactor, is passed through the nitrogen of 30min;
(5) in solution, add 1.5g Ammonium persulfate., continue to protect gentle agitation 4h, obtain oil-well cement slow setting
Agent.
Embodiment 2
A kind of oil well cement retarder, it is characterised in that be made up of the raw material of following parts by weight:
Preparation method: a kind of oil well water as a example by the oil well cement retarder preparing 98g, the present embodiment provided
The preparation method of mud retarder is described below:
(1) by 20g Sodium styrene sulfonate, 9g maleic anhydride, 4.5g fumaric acid, 2.5g methyl
Acrylic acid and 60g water are put in container, are configured to solution;
(2) pH value using the sodium bicarbonate solution regulation solution of 20% is 6, transfers the solution into reaction
In device;
(3) reactor is placed in water-bath heating, solution is stirred simultaneously;
(4) it is incubated after solution is warming up to 60 DEG C, in reactor, is passed through the nitrogen of 30min;
(5) in solution, add 2g Ammonium persulfate., continue to protect gentle agitation 4h, obtain oil-well cement slow setting
Agent.
Above the present invention is exemplarily described, it is clear that the present invention implements and do not limited by aforesaid way
System, as long as have employed method design and the various improvement that carry out of technical scheme of the present invention, or the most improved directly
It is applied to other occasion, all within protection scope of the present invention.
Claims (4)
1. an oil well cement retarder, it is characterised in that be made up of the raw material of following parts by weight:
A kind of oil well cement retarder the most according to claim 1, it is characterised in that described 2-third
Acrylamide base 2-methyl propane sulfonic acid can be replaced Sodium styrene sulfonate.
A kind of oil well cement retarder the most according to claim 1, it is characterised in that described initiation
Agent is Ammonium persulfate..
4. the preparation method of an oil well cement retarder as claimed in claim 1, it is characterised in that bag
Include following steps:
(1) 2-acrylamido 2-methyl propane sulfonic acid, maleic anhydride, methacrylic acid and water are put into
In container, it is configured to solution;
(2) pH value using the sodium bicarbonate solution regulation solution of 20% is 6, transfers the solution into reaction
In device;
(3) reactor is placed in water-bath heating, solution is stirred simultaneously;
(4) it is incubated after solution is warming up to 60 DEG C, in reactor, is passed through the nitrogen of 30min;
(5) in solution, add initiator, continue to protect gentle agitation 4h, obtain oil well cement retarder.