CN106003276A - Novel container bottom plate - Google Patents
Novel container bottom plate Download PDFInfo
- Publication number
- CN106003276A CN106003276A CN201610519715.7A CN201610519715A CN106003276A CN 106003276 A CN106003276 A CN 106003276A CN 201610519715 A CN201610519715 A CN 201610519715A CN 106003276 A CN106003276 A CN 106003276A
- Authority
- CN
- China
- Prior art keywords
- veneer
- container bottom
- edge strip
- board
- bottom plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to plywood for container bottom plates and particularly discloses a novel container bottom plate mainly produced from waste edgings produced through edge sawing of the container bottom plates. The container bottom plate comprises a surface plate, a laminate, a central layer and a bottom plate, wherein the surface plate is made of apitong or impregnated paper, poplar veneer or impregnated paper and a bamboo mat; and the laminate is formed by alternately arranging longitudinal veneer and transverse veneer. The novel container bottom plate is produced from the waste edgings produced through edge sawing of the container bottom plates, so that the utilization rate and the practicability of the edgings are greatly improved; and besides, the novel container bottom plate has very high insect prevention performance, and thus the durability and the safety of a container are improved.
Description
Technical field
The invention belongs to a kind of composite board for bottom board of container, particularly a kind of main container bottom board saws limit
The Novel container bottom plate that the discarded edge strip produced produces.
Background technology
Container forms by steel plate, paint with as the shockproof base plate of buffering, thick plywood.Due to container
Base plate is mainly used in transportation, it is necessary to have good antidetonation, impact resistance, weatherability, the property such as ageing-resistant
Energy.Therefore, glue and durability, the quiet song in addition to apparent size, to the plywood for container bottom board
The physical property such as intensity, elastic modelling quantity proposes the highest requirement.For meeting the requirement of product physical performance index,
Container timber apron typically selects high density rigid broadleaf to be raw material.Owing to the growth cycle of such seeds is long,
General at about 100 years, and the needs of the mankind day by day increase, and cause worldwide hard broad-leaved aptitude
Source is drastically reduced.Thus it is multiple by the Deciduous trees a small amount of hard container bottom board of broadleaf of mixing, directional structure board
Close the new material container bottom boards such as the container bottom board of veneer production, bamboo wood composite container baseboard to become
The main product of current container bottom board, but because of saw limit in the container bottom board production process of above-mentioned new varieties
The edge strip produced just accounts for the 6.9% of finished product boxboard amount, and these edge strip major parts are used for burning boiler, and small part is used for
Nail bracket, comprehensive utilization ratio is extremely low.
Summary of the invention
The technical problem to be solved in the present invention is: in order to solve problem present in above-mentioned background technology, it is provided that
The Novel container bottom plate of a kind of improvement, solves in current container bottom board production process because of the generation of saw limit
Edge strip just accounts for the 6.9% of finished product boxboard amount, and these edge strip major parts are used for burning boiler, and small part is used for following closely bracket,
The problem that comprehensive utilization ratio is extremely low.
The technical solution adopted for the present invention to solve the technical problems is: a kind of Novel container bottom plate, including
Panel, laminate, central core and base plate, described panel is for clone's wood or dipping paper+board using poplar board or impregnates paper
+ bamboo mat forms, and described laminate is for being arranged symmetrically with, and described base plate is clone's wood or dipping paper+board using poplar board
Or dipping paper+bamboo mat composition, described laminate is alternately arranged for longitudinal veneer and horizontal veneer, described center
Layer is made up of through the uniform thickness edge strip longitudinal arrangement of fixed thick gang saw sawing container bottom board sawing edge strip, and described is vertical
To the veneer that veneer is 1.2-1.8mm thickness, described horizontal veneer is that the wood of 1.5-1.8mm thickness is single
Plate, described uniform thickness edge strip is multi-deck container base plate, the container of directional structure board composite wood board production
The edge strip produced when base plate and bamboo wood composite container baseboard saw limit is sawed through uniform thickness gang saw mill sawing and other forms
The uniform thickness edge strip cut, described uniform thickness edge strip thickness is 9-21mm, and width is 28mm.
Preferably, in order to promote insect protected, described longitudinal veneer and the whole double spread of horizontal veneer mixed with
The quaternary resin cement of a certain proportion of insect-proof agent.
Preferably, in order to promote safety, described longitudinal veneer and the whole double spread of horizontal veneer mixed with
The phenolic resin adhesive of a certain proportion of insect-proof agent.
The invention has the beneficial effects as follows, a kind of Novel container bottom plate of the present invention is by sawing with container bottom board
The discarded edge strip that limit produces produces so that edge strip utilization rate and practicality are greatly promoted, and insect protected
The highest so that the ruggedness of container and safety improve.
Accompanying drawing explanation
The present invention is further described with embodiment below in conjunction with the accompanying drawings.
Fig. 1 is the structural representation of the present invention.
1, panel, 2, laminate, 3, central core, 4, base plate.
Fig. 2 is the structural representation in the second embodiment of the present invention.
5,1.2mm thickness clone wooden boards, 6,1.5mm thickness longitudinal Marasse veneer, 7,1.8mm
Thickness horizontal Zelkova schneideriana Hand.-Mazz. veneer, 8, by multi-deck container base plate sawing edge strip through fixed thick gang saw sawing etc. webbing
Bar longitudinal arrangement composition central core, 9,1.2mm thickness clone timber apron.
Detailed description of the invention
In conjunction with the accompanying drawings, the present invention is further detailed explanation.These accompanying drawings are the schematic diagram of simplification,
The basic structure of the present invention is described the most in a schematic way, and therefore it only shows the composition relevant with the present invention.
A kind of Novel container bottom plate shown in Fig. 1, including panel 1, laminate 2, central core 3 and base plate 4.
Panel 1 is clone's wood or dipping paper+board using poplar board or dipping paper+bamboo mat composition, laminate 2 for being arranged symmetrically with,
Base plate 4 is clone's wood or dipping paper+board using poplar board or dipping paper+bamboo mat composition, laminate 2 be longitudinal veneer with
Laterally veneer is alternately arranged, and central core 3 is waited webbing by the fixed thick gang saw sawing of container bottom board sawing edge strip warp
Bar longitudinal arrangement forms, and longitudinal veneer is the veneer of 1.2-1.8mm thickness, and horizontal veneer is 1.5-1.8mm
The veneer of thickness, uniform thickness edge strip is multi-deck container base plate, the collection of directional structure board composite wood board production
The edge strip produced when vanning base plate and bamboo wood composite container baseboard saw limit is through uniform thickness gang saw mill sawing and other shapes
The uniform thickness edge strip of formula sawing, uniform thickness edge strip thickness is 9-21mm, width be 28mm (container bottom board
Nominal thickness).
Preferably, in order to promote insect protected, longitudinal veneer and the whole double spread of horizontal veneer are mixed with a definite proportion
The quaternary resin cement of the insect-proof agent of example, it is preferable that in order to promote safety, longitudinal veneer is with the most single
The whole double spread of plate is mixed with the phenolic resin adhesive of a certain proportion of insect-proof agent, and the one of the present invention is novel
Container bottom board is produced by the discarded edge strip produced with container bottom board saw limit so that edge strip utilization rate
It is greatly promoted with practicality, and insect protected is the highest so that the ruggedness of container and safety improve.
Panel as shown in Figure 2 is that 1.2mm thickness clones wooden boards 5, and base plate is the 1.2mm thickness clone wood end
Plate 9, laminate is two-layer 1.5mm thickness longitudinal Marasse veneer 6 and two-layer 1.8mm thickness horizontal Zelkova schneideriana Hand.-Mazz. veneer
7 are alternately arranged, and central core 8 is (thick through the uniform thickness edge strip of fixed thick gang saw sawing by multi-deck container base plate sawing edge strip
Degree 16mm, width 28mm) (uniform thickness edge strip is side close-packed arrays along face bottom to longitudinal arrangement composition, if going out
Existing gap must install lateral device for exerting additional, it is ensured that uniform thickness edge strip fits tightly), longitudinal veneer and horizontal veneer
All double spread is mixed with the quaternary resin cement of a certain proportion of insect-proof agent, assembly thickness 31.6mm.Warp
The fixed thick molding of hot pressing, then through sanding (overlay film face product is not required to sanding), saw limit, mortise, chamfering, one-tenth product examine
Test etc. and to form.Embodiment container bottom board trimmed size is 2400*1160*28mm, after testing its every physics and chemistry
Performance indications entirely reach GB/T19536-2015 standard-required, and the use being entirely capable of meeting container bottom board is wanted
Ask.
With the above-mentioned desirable embodiment according to the present invention for enlightenment, by above-mentioned description, related work
Personnel can carry out various change and amendment completely in the range of without departing from this invention technological thought.
The content that the technical scope of this invention is not limited in description, it is necessary to according to right
Determine its technical scope.
Claims (3)
1. a Novel container bottom plate, including panel (1), laminate (2), central core (3) and base plate
(4), it is characterized in that: described panel (1) is for clone's wood or dipping paper+board using poplar board or impregnates paper+bamboo mat
Composition, described laminate (2) is for being arranged symmetrically with, and described base plate (4) is clone's wood or dipping paper+poplar
Veneer or dipping paper+bamboo mat composition, described laminate (2) is alternately arranged for longitudinal veneer and horizontal veneer,
Described central core (3) is by the uniform thickness edge strip longitudinal arrangement of the fixed thick gang saw sawing of container bottom board sawing edge strip warp
Composition, the described veneer that longitudinal veneer is 1.2-1.8mm thickness, described horizontal veneer is 1.5-1.8mm
The veneer of thickness, described uniform thickness edge strip is multi-deck container base plate, the life of directional structure board composite wood board
The edge strip produced when the container bottom board produced and bamboo wood composite container baseboard saw limit through uniform thickness gang saw mill sawing and
The uniform thickness edge strip of other form sawings, described uniform thickness edge strip thickness is 9-21mm, and width is 28mm.
A kind of Novel container bottom plate the most according to claim 1, is characterized in that: described is the most single
Plate and the whole double spread of horizontal veneer are mixed with the quaternary resin cement of a certain proportion of insect-proof agent.
A kind of Novel container bottom plate the most according to claim 1, is characterized in that: described is the most single
Plate and the whole double spread of horizontal veneer are mixed with the phenolic resin adhesive of a certain proportion of insect-proof agent.