CN105996164A - Travel garment and dyeing and drying process thereof - Google Patents
Travel garment and dyeing and drying process thereof Download PDFInfo
- Publication number
- CN105996164A CN105996164A CN201610378808.2A CN201610378808A CN105996164A CN 105996164 A CN105996164 A CN 105996164A CN 201610378808 A CN201610378808 A CN 201610378808A CN 105996164 A CN105996164 A CN 105996164A
- Authority
- CN
- China
- Prior art keywords
- sample
- yarn
- wool
- fiber
- garment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a travel garment and a dyeing and drying process of the travel garment. With the travel garment, a user can conveniently check the time but can not feel painful, therefore, great convenience and comfort are brought to the user, and when a clock is not needed, sleeves can be detached, and the travel garment is worn as a short-sleeve shirt. After wearing the travel garment, a presbyopia patient can hang presbyopic glasses on the travel garment and does not need to carry a spectacle case, and therefore, the presbyopia patient can conveniently read the literal information or sign the name and write letters. Fabrics can be dyed simultaneously, therefore, the time of the dyeing process is shortened, and thus the dyeing cost is reduced; meanwhile, the dry performance testing can be completed within a short time, a testing result is rapid and timely, and therefore, the checking on the production and the technology of a water-absorbing fabric by an enterprise is benefited; a testing method is simple and practical, a special testing device does not need to be arranged, and therefore, the testing cost is low.
Description
Technical field
The present invention relates to tourist garment dye with it and drying process, belong to garment material technical field.
Background technology
People are away from home and like having on wrist-watch, in order to can check the time at any time, but wrist-watch has on meeting for a long time to arm
On leave mark, and bring a little pain, additionally some people does not wears wrist-watch tightly, and such wrist-watch will be with the swing of arm
Moving up and down, bring sense of discomfort to people equally, especially old people often gos out without wrist-watch due to the reason such as forgetful, causes
Can not accurately understand the time.
Would generally there is the problem of eyes presbyopia in old people simultaneously in various degree, and presbyopia is inevitable after people step into person in middle and old age
The visual problem occurred, the eye regulating power of patient is gradually reduced thus causes and regard nearly difficulty.And the presbyopia in the year of some cycle of sixty years
Eye patient usually also needs to see written historical materials, does some things of writing of signing, the most just give this group uncomfortable carry constantly old
The people of presbyopic glasses brings puzzlement.
The most just old people is caused to have above all inconvenience when going out or travel.
The blend fabric of different materials needs to make each component obtain essentially identical color, reduces aberration, just can obtain height
The product of quality.Dyeing to blended yarn weaved fabric at present, the method generally used is to dye fabric respectively, dyes identical dyeing
After dyed yarn, obtain the preferable blended yarn weaved fabric of homochromatism through blending;Or it is good that the repeatedly resisdye of blending grey cloth is obtained homochromatism
Blended yarn weaved fabric.No matter but use which kind of method, its process is the most complicated, and production cost is higher.
Simultaneously as wool fabric has water repellency, moisture content cannot be carried out inside fabric, and many major generals of water suction directly affect survey
The correctness of test result, so its drying property is not tested by conventional wool fabric, also cannot ensure wool fabric
Dehumidifying performance.
Summary of the invention
It is an object of the invention to overcome above-mentioned deficiency, it is provided that one can accurately understand the time, and provides presbyopic glasses for oneself,
Can shorten dyeing time, the tourist garment reducing dyeing cost dyes with it and drying process.
The object of the present invention is achieved like this:
A kind of tourist garment, includes garment body, described garment body has two coat-sleeves, said two coat-sleeve by slide fastener with
Garment body connects, and described coat-sleeve is at the outer STH of front end arm and arranges transparent plastic, sets below described transparent plastic
Being equipped with interlayer, be placed with clock and watch in described interlayer, described garment body top is collar, described garment body is additionally provided with and hangs
Chain, described chain sling has two sections, and one end of every section is all fixed with at collar, and the other end is equipped with cuff link.
The dyeing of a kind of tourist garment and drying process, specifically comprise the following steps that
1) wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre are selected, to wool fiber, cashmere fiber, bamboo charcoal
Polyster fibre and stainless steel fibre carry out anti pilling process, ferment treatment and soft treatment, and anti pilling processes selects phosphate ester three oxygen
Changing two antimony mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, at enzyme
Reason system uses protease to process, and protease consumption is the 0.1-0.2% of wool fiber weight, the softness that soft treatment is selected
Agent is water-soluble organic silicon softening agent, and water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight;
2) wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre recombing are made wool top, more premenstrual spin-thin
Yarn-winder-doubling-double twisting-yarn steaming makes yarn, and wherein preparing its number of spun yarn is 81Nm, twist 780Z twist/m;Prepare
Yarn its be the double strand yarn of number 80Nm, twist 810S twist/m of pooling capital;Anti-transparent terylene weight percent in warp thread with weft yarn
It is 30 than content;
3) fabric after blending being carried out reducing bleach process, the bleach of reducing bleach is sodium hydrosulfite 0.5 ~ 5g/L, stabilizer
For sodium pyrophosphate 0.5 ~ 1.5g/L, bleaching temperature is 85 ~ 95 DEG C, and bleaching time is 0.5 ~ 1h;
4) with vinyl-sulfone reactive dyes, the blended yarn weaved fabric processed through reducing bleach is dyeed, first add in dye bath
Paregal O (alkyl polyoxyethylene ether) 0.3 ~ 0.6g/L, vinyl-sulfone reactive dyes 5 ~ 8%, Matrii Sulfas Exsiccatus 30 ~ 50 g/L, then with
1 ~ 1.5 DEG C/min is warming up to 75 ~ 85 DEG C, adds soda 1 ~ 8 g/L, and dye 0.5 ~ 1h;
5) through washing, soap, obtain homochromy blended yarn weaved fabric;
6) drying property of wool fabric is tested:
Step one: lead at 40cm and take two pieces of the sample of 10cm × 20cm on the woolen sample of width as test sample;
Step 2: being placed on by sample in washing appearance device, addition 300ml tetrachloroethylene, as Dry Cleaners, is put into dry-cleaning after sealing
In instrument, take out after dry-cleaning 30min, then repeated washing twice.
Step 3: the loose wool yarn of sample selvedge after cracking-off dry-cleaning, is flat on temperature 20 ± 2 DEG C by sample, and humidity 65 ±
In the environment of 3%, it is put on balance after balancing 12 hours and weighs, claim to obtain the front weight of sample leaching;
Step 4: add reagent 500ml(preparation of reagents method in beaker: add 0.5ml penetrating agent in 499.5ml distilled water
FFA), the sample after dry-cleaning is placed in beaker fully moisture absorption 1 minute;
Step 5: be two to be hung on airer for clothes by the folding along its length of the sample after moisture absorption, is placed in the airer for clothes hanging with sample
Temperature 20 ± 2 DEG C, under the environmental condition of humidity 65 ± 3%, and records the time, measures sample weight after 30 minutes, until
Till sample recovers the front weight of leaching;
Step 6: record sample recovers the time of the front weight of leaching, is the fabric natural drying time.
Compared with prior art, the invention has the beneficial effects as follows:
This tourist garment dyes with it and drying process is by arranging transparent plastic at arm, and is placed under it by clock and watch, thus
Can check the time easily, without feeling pain, thus bringing many convenient and comfort, coat-sleeve is detachable simultaneously
Formula, can unload coat-sleeve when without clock and watch and wear when cotta.Clothes is provided with chain sling simultaneously, and chain sling has two sections, one end of every section
Fixing with at collar, the other end is equipped with cuff link, and described cuff link is similar to key chain, closes for the mirror climbers with presbyopic glasses, from
And fix presbyopic glasses.After using this clothes, presbyopic glasses just can be hung on clothes without carrying eye by Presbyopia patient
Mirror case, facilitates them and sees written historical materials, or signature writes.
Fabric can be made simultaneously to dye, shorten the time of dyeing, reduce dyeing cost;Drying property test simultaneously
Can complete in short time, test result is quickly timely, and water absorption fabric is produced and technology g uarantee, test side by beneficially enterprise
Method is simple and practical, it is not necessary to configuring special detection equipment, testing cost is low.
Detailed description of the invention
The present invention relates to a kind of tourist garment, include garment body, described garment body has two coat-sleeves, said two
Coat-sleeve is connected with garment body by slide fastener, and described coat-sleeve is at the outer STH of front end arm and arranges transparent plastic, described
Bright plastics interlayer is provided below, described interlayer is placed with clock and watch, described garment body top is collar, described clothes this
Being additionally provided with chain sling on body, described chain sling has two sections, and one end of every section is all fixed with at collar, and the other end is equipped with cuff link, described
Cuff link is similar to key chain, and it closes for the mirror climbers with presbyopic glasses, thus fixes presbyopic glasses.
The dyeing of a kind of tourist garment and drying process, specifically comprise the following steps that
1) wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre are selected, to wool fiber, cashmere fiber, bamboo charcoal
Polyster fibre and stainless steel fibre carry out anti pilling process, ferment treatment and soft treatment, and anti pilling processes selects phosphate ester three oxygen
Changing two antimony mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, at enzyme
Reason system uses protease to process, and protease consumption is the 0.1-0.2% of wool fiber weight, the softness that soft treatment is selected
Agent is water-soluble organic silicon softening agent, and water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight;
2) wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre recombing are made wool top, more premenstrual spin-thin
Yarn-winder-doubling-double twisting-yarn steaming makes yarn, and wherein preparing its number of spun yarn is 81Nm, twist 780Z twist/m;Prepare
Yarn its be the double strand yarn of number 80Nm, twist 810S twist/m of pooling capital;Anti-transparent terylene weight percent in warp thread with weft yarn
It is 30 than content;
3) fabric after blending being carried out reducing bleach process, the bleach of reducing bleach is sodium hydrosulfite 0.5 ~ 5g/L, stabilizer
For sodium pyrophosphate 0.5 ~ 1.5g/L, bleaching temperature is 85 ~ 95 DEG C, and bleaching time is 0.5 ~ 1h;
4) with vinyl-sulfone reactive dyes, the blended yarn weaved fabric processed through reducing bleach is dyeed, first add in dye bath
Paregal O (alkyl polyoxyethylene ether) 0.3 ~ 0.6g/L, vinyl-sulfone reactive dyes 5 ~ 8%, Matrii Sulfas Exsiccatus 30 ~ 50 g/L, then with
1 ~ 1.5 DEG C/min is warming up to 75 ~ 85 DEG C, adds soda 1 ~ 8 g/L, and dye 0.5 ~ 1h;
5) through washing, soap, obtain homochromy blended yarn weaved fabric;
6) drying property of wool fabric is tested:
Step one: lead at 40cm and take two pieces of the sample of 10cm × 20cm on the woolen sample of width as test sample;
Step 2: being placed on by sample in washing appearance device, addition 300ml tetrachloroethylene, as Dry Cleaners, is put into dry-cleaning after sealing
In instrument, take out after dry-cleaning 30min, then repeated washing twice.
Step 3: the loose wool yarn of sample selvedge after cracking-off dry-cleaning, is flat on temperature 20 ± 2 DEG C by sample, and humidity 65 ±
In the environment of 3%, it is put on balance after balancing 12 hours and weighs, claim to obtain the front weight of sample leaching;
Step 4: add reagent 500ml(preparation of reagents method in beaker: add 0.5ml penetrating agent in 499.5ml distilled water
FFA), the sample after dry-cleaning is placed in beaker fully moisture absorption 1 minute;
Step 5: be two to be hung on airer for clothes by the folding along its length of the sample after moisture absorption, is placed in the airer for clothes hanging with sample
Temperature 20 ± 2 DEG C, under the environmental condition of humidity 65 ± 3%, and records the time, measures sample weight after 30 minutes, until
Till sample recovers the front weight of leaching;
Step 6: record sample recovers the time of the front weight of leaching, is the fabric natural drying time.
Claims (2)
1. a tourist garment, it is characterised in that: include garment body, described garment body has two coat-sleeves, said two
Coat-sleeve is connected with garment body by slide fastener, and described coat-sleeve is at the outer STH of front end arm and arranges transparent plastic, described
Bright plastics interlayer is provided below, described interlayer is placed with clock and watch, described garment body top is collar, described clothes this
Being additionally provided with chain sling on body, described chain sling has two sections, and one end of every section is all fixed with at collar, and the other end is equipped with cuff link.
The dyeing of a kind of tourist garment the most according to claim 1 and drying process, it is characterised in that: specifically comprise the following steps that
1) wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre are selected, to wool fiber, cashmere fiber, bamboo charcoal
Polyster fibre and stainless steel fibre carry out anti pilling process, ferment treatment and soft treatment, and anti pilling processes selects phosphate ester three oxygen
Changing two antimony mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, at enzyme
Reason system uses protease to process, and protease consumption is the 0.1-0.2% of wool fiber weight, the softness that soft treatment is selected
Agent is water-soluble organic silicon softening agent, and water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight;
2) wool fiber, cashmere fiber, bamboo carbon dacron fiber and stainless steel fibre recombing are made wool top, more premenstrual spin-thin
Yarn-winder-doubling-double twisting-yarn steaming makes yarn, and wherein preparing its number of spun yarn is 81Nm, twist 780Z twist/m;Prepare
Yarn its be the double strand yarn of number 80Nm, twist 810S twist/m of pooling capital;Anti-transparent terylene weight percent in warp thread with weft yarn
It is 30 than content;
3) fabric after blending being carried out reducing bleach process, the bleach of reducing bleach is sodium hydrosulfite 0.5 ~ 5g/L, stabilizer
For sodium pyrophosphate 0.5 ~ 1.5g/L, bleaching temperature is 85 ~ 95 DEG C, and bleaching time is 0.5 ~ 1h;
4) with vinyl-sulfone reactive dyes, the blended yarn weaved fabric processed through reducing bleach is dyeed, first add in dye bath
Paregal O (alkyl polyoxyethylene ether) 0.3 ~ 0.6g/L, vinyl-sulfone reactive dyes 5 ~ 8%, Matrii Sulfas Exsiccatus 30 ~ 50 g/L, then with
1 ~ 1.5 DEG C/min is warming up to 75 ~ 85 DEG C, adds soda 1 ~ 8 g/L, and dye 0.5 ~ 1h;
5) through washing, soap, obtain homochromy blended yarn weaved fabric;
6) drying property of wool fabric is tested:
Step one: lead at 40cm and take two pieces of the sample of 10cm × 20cm on the woolen sample of width as test sample;
Step 2: being placed on by sample in washing appearance device, addition 300ml tetrachloroethylene, as Dry Cleaners, is put into dry-cleaning after sealing
In instrument, take out after dry-cleaning 30min, then repeated washing twice.
Step 3: the wool yarn that after cracking-off dry-cleaning, sample selvedge is loose, is flat on temperature 20 ± 2 DEG C by sample, humidity 65 ± 3%
Under environment, it is put on balance after balancing 12 hours and weighs, claim to obtain the front weight of sample leaching;
Step 4: add reagent 500ml(preparation of reagents method in beaker: add 0.5ml penetrating agent in 499.5ml distilled water
FFA), the sample after dry-cleaning is placed in beaker fully moisture absorption 1 minute;
Step 5: be two to be hung on airer for clothes by the folding along its length of the sample after moisture absorption, is placed in the airer for clothes hanging with sample
Temperature 20 ± 2 DEG C, under the environmental condition of humidity 65 ± 3%, and records the time, measures sample weight after 30 minutes, until
Till sample recovers the front weight of leaching;
Step 6: record sample recovers the time of the front weight of leaching, is the fabric natural drying time.