CN105983686A - 一种自润滑金属材料 - Google Patents
一种自润滑金属材料 Download PDFInfo
- Publication number
- CN105983686A CN105983686A CN201510049335.7A CN201510049335A CN105983686A CN 105983686 A CN105983686 A CN 105983686A CN 201510049335 A CN201510049335 A CN 201510049335A CN 105983686 A CN105983686 A CN 105983686A
- Authority
- CN
- China
- Prior art keywords
- powder
- powder accounts
- self
- accounts
- metal material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种自润滑金属材料,其特征在于:所述的自润滑金属材料中各成分所占重量百分比分别为:所述的铁粉为基础成分其占98%-99%,所述的电解铜粉占0.1%-0.3%,所述的球磨铬粉占0.1%-0.2%,所述的电解锰粉占0.1%-0.2%,所述的钼粉占0.2%-0.3%,所述的钴粉占0.1%-0.3%,所述的石墨粉占0.2%-0.3%、所述的二硫化钼粉0.05%-0.1%,所述的WS2占0.1%-0.3%。本发明提供的一种自润滑金属材料具有优良的摩擦性能,摩擦系数较低,磨损小,并有很好的热强性。
Description
技术领域
本发明涉及一种金属材料领域,具体涉及一种自润滑金属材料。
背景技术
金属材料通常分为黑色金属、有色金属和特种金属材料。黑色金属又称钢铁材料,包括含碳小于2.11%的钢,含碳2.11%~6.67%的铸铁,以及各种用途的结构钢、不锈钢、耐热钢、高温合金 不锈钢等;广义的黑色金属还包括铬、锰及其合金。有色金属是指除铁、铬、锰以外的所有金属及其合金,通常分为轻金属、重金属、贵金属、半金属、稀有金属和稀土金属等。有色合金的强度和硬度一般比纯金属高,并且电阻大、电阻温度系数小; 用金属材料制成的各种机械零件在使用的过程中,往往要受到各种形式的外力作用,作用的结果使其可能受到冲击、拉力、压力、弯曲、扭转等等;为了保证机械零件能正常工作,要求金属材料必须具有一定的抵抗外力的作用而不产生变形或破坏的能力。金属材料抵抗外力的作用所表现出的性能称为金属材料的力学性能,其常用的指标主要包括强度、塑性、硬度、冲击韧度、疲劳强度、蠕变及松弛等。目前所用的固体润滑方法主要有 :石墨、二硫化钼、聚四氟乙烯、尼龙等。但这些材料极易磨损,同时不耐高温。
发明内容
针对上述技术中存在不足之处,本发明的目的在于提供一种自润滑金属材料, 具有优良的摩擦性能, 摩擦系数较低, 磨损小, 并有很好的热强性等优点。
实现本发明目的的技术方案如下 :
一种自润滑金属材料, 其特征在于:所述的自润滑金属材料中各成分所占重量百分比分别为:所述的铁粉为基础成分其占98%-99%,所述的电解铜粉占0.1%-0.3%, 所述的球磨铬粉占0.1%-0.2%, 所述的电解锰粉占0.1%-0.2%, 所述的钼粉占0.2%-0.3%, 所述的钴粉占0.1%-0.3%, 所述的石墨粉占0.2%-0.3%、所述的二硫化钼粉0.05%-0.1%,所述的 WS2占0.1%-0.3%。
在本发明一个较佳实施例中,所述的自润滑金属材料中各成分所占重量百分比具体比例为 :所述的铁粉为基础成分其占98.5%,所述的电解铜粉占0.2%, 所述的球磨铬粉占0.15%, 所述的电解锰粉占0.15%, 所述的钼粉占0.3%, 所述的钴粉占0.15%, 所述的石墨粉占0.25%、所述的二硫化钼粉0.05%、 所述的WS2占0.25%。
在本发明一个较佳实施例中,所述的自润滑金属材料中各成分所占重量百分比具体比例为 :所述的铁粉为基础成分其占98.2%,所述的电解铜粉占0.23%, 所述的球磨铬粉占0.17%, 所述的电解锰粉占0.13%, 所述的钼粉占0.25%, 所述的钴粉占0.1%, 所述的石墨粉占0.23%、所述的二硫化钼粉0.06%、 所述的WS2占0.26%。
本发明具有以下优点和有益效果 :本发明提供的一种自润滑金属材料优良的摩擦性能, 摩擦系数较低, 磨损小, 并有很好的热强性。
具体实施方式
下面结合实施例对本发明作进一步说明:
实施例:一种自润滑金属材料, 其特征在于:所述的自润滑金属材料中各成分所占重量百分比分别为:所述的铁粉为基础成分其占98%-99%,所述的电解铜粉占0.1%-0.3%, 所述的球磨铬粉占0.1%-0.2%, 所述的电解锰粉占0.1%-0.2%, 所述的钼粉占0.2%-0.3%, 所述的钴粉占0.1%-0.3%, 所述的石墨粉占0.2%-0.3%、所述的二硫化钼粉0.05%-0.1%,所述的 WS2占0.1%-0.3%。
优选实施例:所述的自润滑金属材料中各成分所占重量百分比具体比例为 :所述的铁粉为基础成分其占98.5%,所述的电解铜粉占0.2%, 所述的球磨铬粉占0.15%, 所述的电解锰粉占0.15%, 所述的钼粉占0.3%, 所述的钴粉占0.15%, 所述的石墨粉占0.25%、所述的二硫化钼粉0.05%、 所述的WS2占0.25%。
优选实施例:所述的自润滑金属材料中各成分所占重量百分比具体比例为 :所述的铁粉为基础成分其占98.2%,所述的电解铜粉占0.23%, 所述的球磨铬粉占0.17%, 所述的电解锰粉占0.13%, 所述的钼粉占0.25%, 所述的钴粉占0.1%, 所述的石墨粉占0.23%、所述的二硫化钼粉0.06%、 所述的WS2占0.26%。
本材料具有优良的摩擦性能, 摩擦系数较低, 磨损小, 并有很好的热强性, 可广泛用于冶金、化工、窑业等高温作业机械及装备。例如连铸机, 它是处于高温作业的大型装备, 由于润滑十分困难, 轴承等摩擦副损坏较频繁, 影响连铸作业率。对此, 采用本耐热耐磨自润滑材料制成的结晶器足辊轴承、二冷夹辊轴承、拉矫辊轴承、输迭辊道轴承, 以及高逸线材轧钢机侧轮轴套等, 均取得良好的实际应用。
以上详细描述了本发明的较佳具体实施例。应当理解,本领域的普通技术人员无需创造性劳动就可以根据本发明的构思作出诸多修改和变化。因此,凡本技术领域中技术人员依本发明的构思在现有技术的基础上通过逻辑分析、推理或者有限的实验可以得到的技术方案,皆应在由权利要求书所确定的保护范围内。
Claims (3)
1.一种自润滑金属材料, 其特征在于:所述的自润滑金属材料中各成分所占重量百分比分别为:所述的铁粉为基础成分其占98%-99%,所述的电解铜粉占0.1%-0.3%, 所述的球磨铬粉占0.1%-0.2%, 所述的电解锰粉占0.1%-0.2%, 所述的钼粉占0.2%-0.3%, 所述的钴粉占0.1%-0.3%, 所述的石墨粉占0.2%-0.3%、所述的二硫化钼粉0.05%-0.1%,所述的 WS2占0.1%-0.3%。
2.根据权利要求 1 所述的一种自润滑金属材料,其特征在于 :所述的自润滑金属材料中各成分所占重量百分比具体比例为 :所述的铁粉为基础成分其占98.5%,所述的电解铜粉占0.2%, 所述的球磨铬粉占0.15%, 所述的电解锰粉占0.15%, 所述的钼粉占0.3%, 所述的钴粉占0.15%, 所述的石墨粉占0.25%、所述的二硫化钼粉0.05%、 所述的WS2占0.25%。
3. 根据权利要求 1 所述的一种自润滑金属材料,其特征在于 :所述的自润滑金属材料中各成分所占重量百分比具体比例为
:所述的铁粉为基础成分其占98.2%,所述的电解铜粉占0.23%, 所述的球磨铬粉占0.17%, 所述的电解锰粉占0.13%, 所述的钼粉占0.25%, 所述的钴粉占0.1%, 所述的石墨粉占0.23%、所述的二硫化钼粉0.06%、 所述的WS2占0.26%。