CN105970091A - Steel being low in raw material cost - Google Patents
Steel being low in raw material cost Download PDFInfo
- Publication number
- CN105970091A CN105970091A CN201610366549.1A CN201610366549A CN105970091A CN 105970091 A CN105970091 A CN 105970091A CN 201610366549 A CN201610366549 A CN 201610366549A CN 105970091 A CN105970091 A CN 105970091A
- Authority
- CN
- China
- Prior art keywords
- steel
- converter
- cerium
- manganese
- phosphorus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses steel being low in raw material cost. The steel comprises the following raw material components in percentage by weight: not more than 0.235% of carbon, not more than 0.57% of cerium, not more than 0.389% of silicon, not more than 0.027% of phosphorus, not more than 1.13% of manganese, not more than 0.035% of titanium, not more than 0.0145% of surplus, and the balance of iron and impurities. A converter steelmaking craft is adopted during a smelting process of the steel; firebricks are arranged on the inner wall of a converter; a plurality of holes are formed in the side wall of the converter; and through the holes, air is blown into the converter for side-blown converter steelmaking. By adoption of the above technical scheme, the steel disclosed by the invention has the advantages that the adopted raw materials are wide in source, so that the consumption of precious metal can be effectively reduced, the whole cost can be reasonably controlled, and a lot of cost can be saved for an enterprise; and accordingly, large-scale popularization and application are facilitated.
Description
Technical field
The present invention relates to Steel material field, particularly relate to a kind of steel with low cost of material.
Background technology
Steel is a kind of iron-carbon alloy.Steel is processed into steel, and steel can be divided into type, plate, pipe and the big class of silk four.Shaped steel class divides again simple and compound section two kinds by its section configuration difference, and the former includes round steel, square steel, band steel, hexagonal steel and angle steel, and the latter includes rail, I-steel, channel-section steel, casement section steel and deformed steel etc..Steel plate class divides thin plate, middle plate and slab three kinds by thickness difference, and steel band is included in steel plate class.Steel pipe class can cyclotomy pipe, rectangular tube, hexagon pipe and various odd-shaped cross section steel pipe by its cross sectional shape difference.Steel wire class is by shape difference cyclotomy steel wire, flat wire and triangular wire etc..The cost of material that existing steel needs is high, originates the most extensive, it is impossible to enough use on a large scale.
Summary of the invention
The technical problem that present invention mainly solves is to provide a kind of steel with low cost of material, can meet modern's demand to steel.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide a kind of steel with low cost of material, the material composition of described steel includes carbon, cerium, silicon, phosphorus, manganese, titanium, sulfur, ferrum and impurity, described steel is by weight percentage, including material composition have: carbon≤0.235%, cerium≤0.57%, silicon≤0.389%, phosphorus≤0.027%, manganese≤1.13%, titanium≤0.035%, sulfur≤0.0145%, ferrum and impurity: surplus, the smelting process of described steel uses converter steelmaking process, the inwall of described converter is provided with refractory brick, the side of described converter is provided with several holes, air is blown in stove from described hole and realizes side-blown converter.
In a preferred embodiment of the present invention, the material composition of described steel also includes that niobium and vanadium, the total weight percent of described niobium and described vanadium are≤0.05%.
In a preferred embodiment of the present invention, described steel by weight percentage, including material composition have: carbon 0.224%, cerium 0.366%, silicon 0.276%, phosphorus 0.016%, manganese 1.04%, titanium 0.028%, sulfur 0.0135%, ferrum and impurity: surplus.
In a preferred embodiment of the present invention, the described converter steelmaking process persistent period is 10-20 minute.
The invention has the beneficial effects as follows: the steel with low cost of material of the present invention, the raw material sources that this steel uses are extensive, it is possible to the effective use reducing noble metal, reasonably control the cost of entirety well, substantial amounts of cost can be saved, it is simple to large-scale popularization and application for enterprise.
Detailed description of the invention
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, all other embodiments that those of ordinary skill in the art are obtained under not making creative work premise, broadly fall into the scope of protection of the invention.
Embodiment one:
A kind of steel with low cost of material is provided, the material composition of described steel includes carbon, cerium, silicon, phosphorus, manganese, titanium, sulfur, niobium, vanadium, ferrum and impurity, described steel is by weight percentage, including material composition have: carbon 0.224%, cerium 0.366%, silicon 0.276%, phosphorus 0.016%, manganese 1.04%, titanium 0.028%, sulfur 0.0135%, ferrum and impurity: surplus, the total weight percent of described niobium and described vanadium is 0.045%, the smelting process of described steel uses converter steelmaking process, the inwall of described converter is provided with refractory brick, the side of described converter is provided with several holes, air is blown in stove from described hole and realizes side-blown converter.The described converter steelmaking process persistent period is 10 minutes.
Embodiment two:
A kind of steel with low cost of material is provided, the material composition of described steel includes carbon, cerium, silicon, phosphorus, manganese, titanium, sulfur, niobium, vanadium, ferrum and impurity, described steel is by weight percentage, including material composition have: carbon 0.225%, cerium 0.54%, silicon 0.379%, phosphorus 0.024%, manganese 1.04%, titanium 0.032%, sulfur 0.0126%, ferrum and impurity: surplus, the total weight percent of described niobium and described vanadium is 0.033%, the smelting process of described steel uses converter steelmaking process, the inwall of described converter is provided with refractory brick, the side of described converter is provided with several holes, air is blown in stove from described hole and realizes side-blown converter.The described converter steelmaking process persistent period is 15 minutes.
Embodiment three:
A kind of steel with low cost of material is provided, the material composition of described steel includes carbon, cerium, silicon, phosphorus, manganese, titanium, sulfur, niobium, vanadium, ferrum and impurity, described steel is by weight percentage, including material composition have: carbon 0.235%, cerium 0.57%, silicon 0.389%, phosphorus 0.027%, manganese 1.13%, titanium 0.035%, sulfur 0.0145%, ferrum and impurity: surplus, the total weight percent of described niobium and described vanadium is 0.05%, the smelting process of described steel uses converter steelmaking process, the inwall of described converter is provided with refractory brick, the side of described converter is provided with several holes, air is blown in stove from described hole and realizes side-blown converter.The described converter steelmaking process persistent period is 20 minutes.
The invention has the beneficial effects as follows:
One, there are the raw material sources that the steel of low cost of material uses extensive described in, it is possible to the effective use reducing noble metal, reasonably control the cost of entirety well;
The steel described in two, with low cost of material can save substantial amounts of cost for enterprise, it is simple to large-scale popularization and application.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalent structure utilizing description of the invention content to be made or equivalence flow process conversion; or directly or indirectly it is used in other relevant technical field, the most in like manner it is included in the scope of patent protection of the present invention.
Claims (4)
1. a steel with low cost of material, it is characterized in that, the material composition of described steel includes carbon, cerium, silicon, phosphorus, manganese, titanium, sulfur, ferrum and impurity, described steel is by weight percentage, including material composition have: carbon≤0.235%, cerium≤0.57%, silicon≤0.389%, phosphorus≤0.027%, manganese≤1.13%, titanium≤0.035%, sulfur≤0.0145%, ferrum and impurity: surplus, the smelting process of described steel uses converter steelmaking process, the inwall of described converter is provided with refractory brick, the side of described converter is provided with several holes, air is blown in stove from described hole and realizes side-blown converter.
The steel with low cost of material the most according to claim 1, it is characterised in that the material composition of described steel also includes that niobium and vanadium, the total weight percent of described niobium and described vanadium are≤0.05%.
The steel with low cost of material the most according to claim 1, it is characterised in that described steel by weight percentage, including material composition have: carbon
0.224%, cerium 0.366%, silicon 0.276%, phosphorus 0.016%, manganese 1.04%, titanium
0.028%, sulfur 0.0135%, ferrum and impurity: surplus.
The steel with low cost of material the most according to claim 1, it is characterised in that the described converter steelmaking process persistent period is 10-20 minute.