CN105969175A - Antistatic silica gel material - Google Patents
Antistatic silica gel material Download PDFInfo
- Publication number
- CN105969175A CN105969175A CN201610585393.6A CN201610585393A CN105969175A CN 105969175 A CN105969175 A CN 105969175A CN 201610585393 A CN201610585393 A CN 201610585393A CN 105969175 A CN105969175 A CN 105969175A
- Authority
- CN
- China
- Prior art keywords
- silica gel
- gel material
- parts
- die cavity
- wood powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of silica gel sheets, in particular to an antistatic silica gel material. The material is prepared in the mode that by weight, 10-15 parts of silica gel, 1-2 parts of PC, 0.5 part of wood powder, 0.01 part of POE, 0.5-1 part of silicon oil and 0.5 part of antistatic agent are mixed, melted, injected into a mould cavity and cooled. By adding the wood powder, the antistatic performance is improved. Various components are combined, so that mechanical properties are improved.
Description
Technical field
The present invention relates to silica gel piece field, be specifically related to a kind of anti-static silica gel material.
Background technology
Silica gel material improves antistatic property by adding antistatic additive at present, and adds antistatic additive and too much understand shadow
Ring material property, it is therefore necessary to provide a kind of novel anti-static silica gel material.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, it is provided that a kind of improve antistatic property, do not affect product mechanical property
Anti-static silica gel material.
In order to realize foregoing invention purpose, the present invention by the following technical solutions: a kind of anti-static silica gel material, its feature
It is, by 10-15 part silica gel, 1-2 part PC, 0.5 part of wood powder, 0.01 part of POE, 0.5-1 part silicone oil, 0.5 part of antistatic additive mixing
In melting afterwards and injecting die cavity, cooling afterwards obtains, and described number is parts by weight.
Aforesaid a kind of anti-static silica gel material, by 15 parts of silica gel, 2 parts of PC, 0.5 part of wood powder, 0.01 part of POE, 1 part of silicon
In melting and inject die cavity after oil, 0.5 part of antistatic additive mixing, cooling afterwards obtains.
Aforesaid a kind of anti-static silica gel material, temperature time melted after mixing is 250-255 degree Celsius.
Aforesaid a kind of anti-static silica gel material, cools down then die sinking with cooling fan after injecting die cavity.
The present invention, by adding wood powder, improves antistatic property；By the combination of various ingredients, improve mechanical property.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further described in detail.
Embodiment 1
A kind of anti-static silica gel material, by 15 parts of silica gel, 2 parts of PC, 0.5 part of wood powder, 0.01 part of POE, 1 part of silicone oil, 0.5 part anti-quiet
In melting after electricity agent mixing and injecting die cavity, cooling afterwards obtains.Temperature when melting after mixing is 250 degrees Celsius.Inject die cavity
Then die sinking is cooled down afterwards with cooling fan.Surface resistivity carries out test by ISO3915 and passes judgment on, and surface resistivity is 2*1010Ω·
m。
Comparative example 1
A kind of anti-static silica gel material, after 15 parts of silica gel, 2 parts of PC, 0.01 part of POE, 1 part of silicone oil, 0.5 part of antistatic additive mixing
In melting and injecting die cavity, cooling afterwards obtains.Temperature when melting after mixing is 250 degrees Celsius.Cooling fan is used after injecting die cavity
Cool down then die sinking.Surface resistivity carries out test by ISO3915 and passes judgment on, and surface resistivity is 5*109Ω·m。
It should be noted that the foregoing is only embodiments of the invention, not thereby limit the scope of the claims of the present invention,
Every equivalent structure utilizing description of the invention content to be done or equivalence flow process conversion, or directly or indirectly it is used in other phases
Close technical field, be the most in like manner included in the scope of patent protection of the present invention.
Claims (4)
1. an anti-static silica gel material, it is characterised in that by 10-15 part silica gel, 1-2 part PC, 0.5 part of wood powder, 0.01 part
In melting and inject die cavity after POE, 0.5-1 part silicone oil, 0.5 part of antistatic additive mixing, cooling afterwards obtains, and described number is
Parts by weight.
A kind of anti-static silica gel material the most according to claim 1, it is characterised in that by 15 parts of silica gel, 2 parts of PC, 0.5 part
In melting and inject die cavity after wood powder, 0.01 part of POE, 1 part of silicone oil, 0.5 part of antistatic additive mixing, cooling afterwards obtains.
A kind of anti-static silica gel material the most according to claim 1, it is characterised in that temperature time melted after mixing is
250-255 degree Celsius.
A kind of anti-static silica gel material the most according to claim 1, it is characterised in that cool down with cooling fan after injecting die cavity
Then die sinking.