CN105969027A - Heat and corrosion resisting paint for communication equipment - Google Patents
Heat and corrosion resisting paint for communication equipment Download PDFInfo
- Publication number
- CN105969027A CN105969027A CN201610458497.0A CN201610458497A CN105969027A CN 105969027 A CN105969027 A CN 105969027A CN 201610458497 A CN201610458497 A CN 201610458497A CN 105969027 A CN105969027 A CN 105969027A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- communication equipment
- organobentonite
- proof coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses heat and corrosion resisting paint for communication equipment. The paint comprises the following raw materials in parts by weight: 40 to 90 parts of modified vinyl ester resin, 20 to 40 parts of epoxy resin, 10 to 30 parts of phenolic resin, 5 to 15 parts of hydroxymethyl cellulose, 2 to 8 parts of boron nitride nanopowder, 1 to 9 parts of sea-foam stone powder, 2 to 5 parts of organobentonite, 3 to 6 parts of nano aluminum nitride, 4 to 8 parts of organobentonite, 1 to 5 parts of sodium laurylsulfate, 2 to 4 parts of dimethyl phthalate, 1 to 3 parts of antimonous oxide, 2 to 4 parts of xylene, 1 to 5 parts of a drying agent, 2 to 6 parts of pigment, 1 to 4 parts of a flexibilizer, 2 to 4 parts of a defoamer, 3 to 5 parts of a leveling agent, and 1 to 3 parts of a mildew preventive. The paint has excellent heat and corrosion resisting performances.
Description
Technical field
The present invention relates to paint field, particularly relate to a kind of Communication Equipment heat resisting corrosion-proof coating.
Background technology
Communication Equipment refers to be arranged on the most geographically in order to transmit the general designation of the communication apparatus of wave information.Main
Wire communication equipment to be divided into and wireless telecommunications system.Wire communication equipment is mainly introduced and is solved industry spot
Serial communication, the communication of specialty bus-type, turning between communication and the various communications protocol of EPA
Exchange device.Wireless telecommunications system is mainly wireless aps, wireless bridge, wireless network card, wireless lightning arrester, sky
The equipment such as line.
Communication Equipment in use, shines upon the erosion of rainwater, it is easy to corrosion, because of
This wraps up a coating and makes Communication Equipment have the corrosion-resistant and heat-resisting of excellence in the periphery of Communication Equipment housing
Performance, is the currently available technology problem of needing solution badly.
Summary of the invention
For solving technical problem present in background technology, the present invention proposes a kind of Communication Equipment heat resisting corrosion-proof
Coating, has the heat-resisting and decay resistance of excellence.
A kind of Communication Equipment heat resisting corrosion-proof coating that the present invention proposes, its raw material includes by weight: modified
Vinyl ester resin 40-90 part, epoxy resin 20-40 part, phenolic resin 10-30 part, hydroxylmethyl cellulose
Element 5-15 part, nm-class boron nitride 2-8 part, sepiolite powder 1-9 part, organobentonite 2-5 part, nanometer nitrogen
Change aluminum 3-6 part, organobentonite 4-8 part, sodium laurylsulfate 1-5 part, dimethyl phthalate 2-4
Part, antimony oxide 1-3 part, dimethylbenzene 2-4 part, drier 1-5 part, pigment 2-6 part, toughener
1-4 part, defoamer 2-4 part, advection agent 3-5 part, antifungus agent 1-3 part.
Preferably, modified ethenyl resin is prepared by following technique: vinylite is added methyl
In dodecafluorhe-ptylacrylate, it is stirring evenly and then adding into dibenzoyl peroxide, stirs 5-15min, put into true
Deaeration of bleeding in empty van obtains modified ethenyl resin.
Preferably, the weight ratio of vinylite, dodecafluoroheptyl methacrylate and dibenzoyl peroxide
For 3-9:1-3:2-5.
Preferably, the mass fraction of dodecafluoroheptyl methacrylate is 3-9%.
Preferably, the mass fraction of dibenzoyl peroxide is 0.5-1.5%.
Preferably, its raw material includes by weight: modified ethenyl resin 45-85 part, epoxy resin 25-35
Part, phenolic resin 15-25 part, hydroxymethyl cellulose 8-12 part, nm-class boron nitride 3-7 part, sepiolite powder
2-8 part, organobentonite 3-4 part, nano aluminum nitride 4-5 part, organobentonite 5-7 part, lauryl alcohol sulfur
Acid sodium 2-4 part, dimethyl phthalate 2.5-3.5 part, antimony oxide 1.5-2.5 part, dimethylbenzene
2.5-3.5 part, drier 2-4 part, pigment 3-5 part, toughener 2-3 part, defoamer 2.5-3.5 part,
Advection agent 3.5-4.5 part, antifungus agent 1.5-2.5 part.
Preferably, its raw material includes by weight: modified ethenyl resin 65 parts, epoxy resin 30 parts,
20 parts of phenolic resin, hydroxymethyl cellulose 10 parts, nm-class boron nitride 5 parts, sepiolite powder 5 parts, organic
Bentonite 3.5 parts, nano aluminum nitride 4.5 parts, organobentonite 6 parts, sodium laurylsulfate 3 parts, neighbour
Dimethyl phthalate 3 parts, antimony oxide 2 parts, dimethylbenzene 3 parts, drier 3 parts, pigment 4 parts,
Toughener 2.5 parts, defoamer 3 parts, advection agent 4 parts, antifungus agent 2 parts.
A kind of Communication Equipment heat resisting corrosion-proof coating in the present invention, its raw material include modified ethenyl resin,
Epoxy resin, phenolic resin, hydroxymethyl cellulose, nm-class boron nitride, sepiolite powder, organobentonite,
Nano aluminum nitride, organobentonite, sodium laurylsulfate, dimethyl phthalate, antimony oxide,
Dimethylbenzene, drier, pigment, toughener, defoamer, advection agent and antifungus agent, with modified ethenyl
Resin is major ingredient, and auxiliary adds epoxy resin and phenolic resin so that the Communication Equipment of the present invention is with heat-resisting resistance to
Rotten coating has the heat-resisting and decay resistance of excellence;The hydroxymethyl cellulose of interpolation, nm-class boron nitride, sea
Afrodite powder, organobentonite, nano aluminum nitride and organobentonite, as filler, are effectively increased the present invention
The Communication Equipment decay resistance of heat resisting corrosion-proof coating and heat resistance;Add sodium laurylsulfate,
Dimethyl phthalate, antimony oxide, dimethylbenzene, drier, pigment, toughener, defoamer,
Advection agent and antifungus agent are as auxiliary agent so that the Communication Equipment heat resisting corrosion-proof coating of the present invention has excellence
Decay resistance and heat resistance.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in detail, it should be appreciated that embodiment is served only for
The bright present invention rather than be used for limiting the invention, any made on the basis of the present invention amendment,
Equivalents etc. are the most within the scope of the present invention.
In detailed description of the invention, the weight portion of modified ethenyl resin can be 40 parts, 45 parts, 50 parts,
55 parts, 60 parts, 65 parts, 70 parts, 75 parts, 80 parts, 85 parts, 90 parts;The weight portion of epoxy resin
It can be 20 parts, 25 parts, 30 parts, 35 parts, 40 parts;The weight portion of phenolic resin can be 10 parts,
15 parts, 20 parts, 25 parts, 30 parts;The weight portion of hydroxymethyl cellulose can be 5 parts, 6 parts, 7 parts,
8 parts, 9 parts, 10 parts, 11 parts, 12 parts, 13 parts, 14 parts, 15 parts;The weight portion of nm-class boron nitride
It can be 2 parts, 3 parts, 4 parts, 5 parts, 6 parts, 7 parts, 8 parts;The weight portion of sepiolite powder can be 1
Part, 2 parts, 3 parts, 4 parts, 5 parts, 6 parts, 7 parts, 8 parts, 9 parts;Bentonite weight portion can
Think 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of nano aluminum nitride can
Think 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts, 5.5 parts, 6 parts;Bentonite weight portion can
Think 4 parts, 4.5 parts, 5 parts, 5.5 parts, 6 parts, 6.5 parts, 7 parts, 7.5 parts, 8 parts;Lauryl alcohol
The weight portion of sodium sulfate can be 1 part, 2 parts, 3 parts, 4 parts, 5 parts;The weight of dimethyl phthalate
Amount part can be 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts;The weight portion of antimony oxide can be 1
Part, 1.5 parts, 2 parts, 2.5 parts, 3 parts;The weight portion of dimethylbenzene can be 2 parts, 2.5 parts, 3 parts,
3.5 parts, 4 parts;The weight portion of drier can be 1 part, 2 parts, 3 parts, 4 parts, 5 parts;The weight of pigment
Amount part can be 2 parts, 3 parts, 4 parts, 5 parts, 6 parts;The weight portion of toughener can be 1 part, 2 parts,
3 parts, 4 parts;The weight portion of defoamer can be 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts;Advection agent
Weight portion can be 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of antifungus agent can be 1
Part, 1.5 parts, 2 parts, 2.5 parts, 3 parts.
Embodiment 1
A kind of Communication Equipment heat resisting corrosion-proof coating that the present invention proposes, its raw material includes by weight: modified
Vinyl ester resin 65 parts, epoxy resin 30 parts, 20 parts of phenolic resin, hydroxymethyl cellulose 10 parts,
Nm-class boron nitride 5 parts, sepiolite powder 5 parts, organobentonite 3.5 parts, nano aluminum nitride 4.5 parts, have
Machine bentonite 6 parts, sodium laurylsulfate 3 parts, dimethyl phthalate 3 parts, antimony oxide 2 parts,
Dimethylbenzene 3 parts, drier 3 parts, pigment 4 parts, toughener 2.5 parts, defoamer 3 parts, advection agent 4
Part, antifungus agent 2 parts.
Modified ethenyl resin is prepared by following technique: by weight 6 parts of vinylites are added 2
Part mass fraction is in the dodecafluoroheptyl methacrylate of 6%, is stirring evenly and then adding into 3.5 parts of mass fractions
It is the dibenzoyl peroxide of 1.0%, stirs 10min, put into deaeration of bleeding in vacuum tank and obtain ethene improved
Base ester resin.
Embodiment 2
A kind of Communication Equipment heat resisting corrosion-proof coating that the present invention proposes, its raw material includes by weight: modified
Vinyl ester resin 40 parts, epoxy resin 40 parts, 10 parts of phenolic resin, hydroxymethyl cellulose 15 parts,
Nm-class boron nitride 2 parts, sepiolite powder 9 parts, organobentonite 2 parts, nano aluminum nitride 6 parts, organic bentonite
Profit soil 4 parts, sodium laurylsulfate 5 parts, dimethyl phthalate 2 parts, antimony oxide 3 parts, two
Toluene 2 parts, drier 5 parts, pigment 2 parts, toughener 4 parts, defoamer 2 parts, advection agent 5 parts,
Antifungus agent 1 part.
Modified ethenyl resin is prepared by following technique: by weight 3 parts of vinylites are added 3
Part mass fraction is that in the dodecafluoroheptyl methacrylate of 3%, being stirring evenly and then adding into 5 parts of mass fractions is
The dibenzoyl peroxide of 0.5%, stirs 15min, puts into deaeration of bleeding in vacuum tank and obtain modified ethenyl
Resin.
Embodiment 3
A kind of Communication Equipment heat resisting corrosion-proof coating that the present invention proposes, its raw material includes by weight: modified
Vinyl ester resin 90 parts, epoxy resin 20 parts, 30 parts of phenolic resin, hydroxymethyl cellulose 5 parts, receive
Rice boron nitride 8 parts, sepiolite powder 1 part, organobentonite 5 parts, nano aluminum nitride 3 parts, organic swelling
8 parts of soil, sodium laurylsulfate 1 part, dimethyl phthalate 4 parts, antimony oxide 1 part, diformazan
Benzene 4 parts, drier 1 part, pigment 6 parts, toughener 1 part, defoamer 4 parts, advection agent 3 parts, anti-
Mould dose 3 parts.
Modified ethenyl resin is prepared by following technique: by weight 9 parts of vinylites are added 1
Part mass fraction is that in the dodecafluoroheptyl methacrylate of 9%, being stirring evenly and then adding into 2 parts of mass fractions is
The dibenzoyl peroxide of 1.5%, stirs 5min, puts into deaeration of bleeding in vacuum tank and obtain modified ethenyl
Resin.
Embodiment 4
A kind of Communication Equipment heat resisting corrosion-proof coating that the present invention proposes, its raw material includes by weight: modified
Vinyl ester resin 45 parts, epoxy resin 35 parts, 15 parts of phenolic resin, hydroxymethyl cellulose 12 parts,
Nm-class boron nitride 3 parts, sepiolite powder 8 parts, organobentonite 3 parts, nano aluminum nitride 5 parts, organic bentonite
Profit soil 5 parts, sodium laurylsulfate 4 parts, dimethyl phthalate 2.5 parts, antimony oxide 2.5 parts,
Dimethylbenzene 2.5 parts, drier 4 parts, pigment 3 parts, toughener 3 parts, defoamer 2.5 parts, advection agent
4.5 parts, antifungus agent 1.5 parts.
Modified ethenyl resin is prepared by following technique: added by 4 parts of vinylites by weight
2.5 parts of mass fractions are in the dodecafluoroheptyl methacrylate of 4%, are stirring evenly and then adding into 4 parts of quality and divide
Number is the dibenzoyl peroxide of 0.8%, stirs 12min, puts into deaeration of bleeding in vacuum tank and obtains modified second
Alkenyl esters resin.
Embodiment 5
A kind of Communication Equipment heat resisting corrosion-proof coating that the present invention proposes, its raw material includes by weight: modified
Vinyl ester resin 85 parts, epoxy resin 25 parts, 25 parts of phenolic resin, hydroxymethyl cellulose 8 parts, receive
Rice boron nitride 7 parts, sepiolite powder 2 parts, organobentonite 4 parts, nano aluminum nitride 4 parts, organic swelling
Soil 7 parts, sodium laurylsulfate 2 parts, dimethyl phthalate 3.5 parts, antimony oxide 1.5 parts,
Dimethylbenzene 3.5 parts, drier 2 parts, pigment 5 parts, toughener 2 parts, defoamer 3.5 parts, advection agent
3.5 parts, antifungus agent 2.5 parts.
Modified ethenyl resin is prepared by following technique: added by 4 parts of vinylites by weight
2.5 parts of mass fractions are in the dodecafluoroheptyl methacrylate of 4%, are stirring evenly and then adding into 4 parts of quality and divide
Number is the dibenzoyl peroxide of 0.8%, stirs 12min, puts into deaeration of bleeding in vacuum tank and obtains modified second
Alkenyl esters resin.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention not office
Being limited to this, any those familiar with the art is in the technical scope that the invention discloses, according to this
The technical scheme of invention and inventive concept thereof in addition equivalent or change, all should contain the protection in the present invention
Within the scope of.
Claims (7)
1. a Communication Equipment heat resisting corrosion-proof coating, it is characterised in that its raw material includes by weight: change
Sex ethylene base ester resin 40-90 part, epoxy resin 20-40 part, phenolic resin 10-30 part, methylol fibre
Dimension element 5-15 part, nm-class boron nitride 2-8 part, sepiolite powder 1-9 part, organobentonite 2-5 part, nanometer
Aluminium nitride 3-6 part, organobentonite 4-8 part, sodium laurylsulfate 1-5 part, dimethyl phthalate
2-4 part, antimony oxide 1-3 part, dimethylbenzene 2-4 part, drier 1-5 part, pigment 2-6 part, increasing
Tough dose of 1-4 part, defoamer 2-4 part, advection agent 3-5 part, antifungus agent 1-3 part.
Communication Equipment heat resisting corrosion-proof coating the most according to claim 1, it is characterised in that modified second
Alkenyl esters resin is prepared by following technique: added by vinylite in dodecafluoroheptyl methacrylate,
It is stirring evenly and then adding into dibenzoyl peroxide, stirs 5-15min, put into deaeration of bleeding in vacuum tank and obtain
Modified ethenyl resin.
Communication Equipment heat resisting corrosion-proof coating the most according to claim 2, it is characterised in that vinyl
The weight ratio of resin, dodecafluoroheptyl methacrylate and dibenzoyl peroxide is 3-9:1-3:2-5.
4. according to the Communication Equipment heat resisting corrosion-proof coating described in any one of claim 1-3, it is characterised in that
The mass fraction of dodecafluoroheptyl methacrylate is 3-9%.
5. according to the Communication Equipment heat resisting corrosion-proof coating described in any one of claim 1-4, it is characterised in that
The mass fraction of dibenzoyl peroxide is 0.5-1.5%.
6. according to the Communication Equipment heat resisting corrosion-proof coating described in any one of claim 1-5, it is characterised in that
Its raw material includes by weight: modified ethenyl resin 45-85 part, epoxy resin 25-35 part, phenolic aldehyde
Resin 15-25 part, hydroxymethyl cellulose 8-12 part, nm-class boron nitride 3-7 part, sepiolite powder 2-8 part,
Organobentonite 3-4 part, nano aluminum nitride 4-5 part, organobentonite 5-7 part, sodium laurylsulfate 2-4
Part, dimethyl phthalate 2.5-3.5 part, antimony oxide 1.5-2.5 part, dimethylbenzene 2.5-3.5
Part, drier 2-4 part, pigment 3-5 part, toughener 2-3 part, defoamer 2.5-3.5 part, advection agent
3.5-4.5 part, antifungus agent 1.5-2.5 part.
7. according to the Communication Equipment heat resisting corrosion-proof coating described in any one of claim 1-6, it is characterised in that
Its raw material includes by weight: modified ethenyl resin 65 parts, epoxy resin 30 parts, phenolic resin 20
Part, hydroxymethyl cellulose 10 parts, nm-class boron nitride 5 parts, sepiolite powder 5 parts, organobentonite 3.5 parts,
Nano aluminum nitride 4.5 parts, organobentonite 6 parts, sodium laurylsulfate 3 parts, dimethyl phthalate
3 parts, antimony oxide 2 parts, dimethylbenzene 3 parts, drier 3 parts, pigment 4 parts, toughener 2.5 parts,
Defoamer 3 parts, advection agent 4 parts, antifungus agent 2 parts.