CN105968671A - High molecular compound liquid colloid as well as preparation method and application thereof - Google Patents
High molecular compound liquid colloid as well as preparation method and application thereof Download PDFInfo
- Publication number
- CN105968671A CN105968671A CN201610317858.XA CN201610317858A CN105968671A CN 105968671 A CN105968671 A CN 105968671A CN 201610317858 A CN201610317858 A CN 201610317858A CN 105968671 A CN105968671 A CN 105968671A
- Authority
- CN
- China
- Prior art keywords
- liquid colloid
- mass ratio
- accounts
- complex liquid
- colloid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high molecular compound liquid colloid as well as a preparation method and application thereof, and relates to the technical field of the production and the application of colloidal materials. Polyvinyl acetate is dissolved in a solvent; afterwards, propanediol, ethyl acetate, dibutyl phthalate, n-butyl acetate, Tween 80 and a solvent are added into an obtained first mixture; an obtained second mixture is agitated uniformly, so as to obtain the high molecular compound liquid colloid. The method provided by the invention is simple and convenient; a made product is good in stability, is nontoxic and harmless, has no corrosiveness, is non-greasy and does not volatilize; the product does not show bioadhesiveness when moisture does not exist, quickly shows the adhesiveness to an organism once meeting water, and forms a uniform thin film within several seconds to cover a water surface; the thin film can last for as long as several months; if the thin film is agitated, a colloidal block mass with the adhesiveness is formed in water; the high molecular compound liquid colloid can be applied to the formation of an isolating film on the water surface, and is used for occasions of packing, the adhering of a micron-scale fine particle, the removal of oil contamination, hemostasis and the like.
Description
Technical field
The present invention relates to production and the applied technical field of a kind of colloidal materials, be directed to civilian, environmental protection, health, medical treatment, anti-smelting insect etc. multi-field.
Background technology
Existing film product is approved product, is membrane product when making, and membrane product does not separates or decomposes, and is unfavorable for extensively applying.
Silicon
Polymer and Oil Film investigated a kind of colloid, its can in water surface film forming, but they film forming speeds are slow, the film poor ductility of formation, the continuable time is short, is difficult to remove after film forming, to environmentally undesirable.
Summary of the invention
One of the object of the invention is that invention one meets that MJPZ is fast, the later stage removes easy polymer composite liquid colloid.
Polymer composite liquid colloid is mainly made up of polyvinyl acetate, propylene glycol, ethyl acetate, Dibutyl phthalate, n-butyl acetate, POLYSORBATE 80 and solvent;It is 2~80% that described polyvinyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.2% that propylene glycol accounts for the mass ratio of complex liquid colloid;It is 0.1~5% that ethyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.1~2% that Dibutyl phthalate accounts for the mass ratio of complex liquid colloid;It is 0.1~5% that n-butyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.1% that POLYSORBATE 80 accounts for the mass ratio of complex liquid colloid.
The present invention is with polyvinyl acetate as macromolecular material, with propylene glycol and Dibutyl phthalate as plasticizer, with ethyl acetate as binding agent, with n-butyl acetate as cosolvent, with POLYSORBATE 80 as surfactant, above each raw material coexists in solvent, and forms the gel-like prod of mix homogeneously.The present invention is nontoxic, harmless, non-corrosiveness, and non-greasy is non-volatile;When not having moisture, product does not show bioadhesive, convenient long-term preservation, transport.But, after product once meets water, can quickly show biological adhesiveness, and within the several seconds, form the uniform thin film covering water surface, thin film can maintain the several months long, if be stirred thin film, i.e. forms the colloid agglomerate with adhesiveness in water.
It addition, solvent of the present invention can use the mixed liquor of acetone or acetone and ethanol, can regulate and control the viscosity of liquid colloid and control to meet the thickness of the thickness viscosity high film forming of MJPZ greatly, the thickness of viscosity low filming is little.
Further, polyvinyl acetate of the present invention accounts for the mass ratio of complex liquid colloid is 10~20%;It is 1% that ethyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.5% that Dibutyl phthalate accounts for the mass ratio of complex liquid colloid;It is 0.9% that n-butyl acetate accounts for the mass ratio of complex liquid colloid;It is 7.7~97.5% that acetone accounts for the mass ratio of complex liquid colloid;It is 0~75% that ethanol accounts for the mass ratio of complex liquid colloid.The excellent results of the most each composition accounting is: thing liquid colloid viscosity is suitable, it is easy to sprays and uses.Film forming is rapid, and the thickness of film is suitable, has excellent elastic extensibility and persistency.
The ratio increasing organic solvent increases bioadhesive by prolonging and delays the formation of plastic films.
POLYSORBATE 80 makes the plastic films of final form more persistently in order to the elasticity and connection improving resin and plasticizer, the most even high resilience.
The two of the object of the invention are the preparation methoies proposing above polymer composite liquid colloid.
Method is: be dissolved in solvent by polyvinyl acetate, after 10~15 hours, adding propylene glycol, ethyl acetate, Dibutyl phthalate, n-butyl acetate and POLYSORBATE 80 while stirring, solubilizer is to volume required the most again, stirring, i.e. secure satisfactory grades sub-complex liquid colloid;When feeding intake, it is 2~80% that described polyvinyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.2% that propylene glycol accounts for the mass ratio of complex liquid colloid;It is 0.1~5% that ethyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.1~2% that Dibutyl phthalate accounts for the mass ratio of complex liquid colloid;It is 0.1~5% that n-butyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.1% that POLYSORBATE 80 accounts for the mass ratio of complex liquid colloid.
The inventive method is simple, convenient, and the product stability made is good, it is simple to preserve.
The three of the object of the invention are to provide the purposes of polymer composite liquid colloid.
One of purposes: for forming isolating membrane on the water surface.
The two of purposes: after mixing with water, form the thin film for packaging.
The three of purposes: after mixing with water, sparge in air, are used for adhering to micron order fine particle.
The four of purposes: this polymer composite liquid colloid is formed bioadhesive agglomerate with degreaser bonding, is used for degreasing.
The five of purposes: be used for stopping blooding.
The present invention has convenient multiple use at multiple fields, introduces the most one by one.
Detailed description of the invention
One, polymer composite liquid colloid is prepared:
Being dissolved in solvent by polyvinyl acetate, after 10~15 hours, add propylene glycol, ethyl acetate, Dibutyl phthalate, n-butyl acetate and POLYSORBATE 80, the most again solubilizer while stirring, stir, i.e. secure satisfactory grades sub-complex liquid colloid.
All material compositions all meet GRAS(and are commonly considered as safe) row requirement.
It is below the weighing example table (unit: g) of each raw material:
Polyvinyl acetate | Propylene glycol | POLYSORBATE 80 | N-butyl acetate | Ethyl acetate | Dibutyl phthalate | Acetone | Ethanol | |
Example 1 | 20 | 0.2 | 0.1 | 0.9 | 1 | 0.5 | 77.3 | 0 |
Example 2 | 15 | 0.2 | 0.1 | 0.9 | 1 | 0.5 | 82.3 | 0 |
Example 3 | 10 | 0.2 | 0.1 | 0.9 | 1 | 0.5 | 87.3 | 0 |
Example 4 | 20 | 0.2 | 0.1 | 0.9 | 1 | 0.5 | 38.65 | 38.65 |
Example 5 | 20 | 0.2 | 0.1 | 0.9 | 1 | 0.5 | 52.3 | 25 |
Two, product attribute:
The present invention is nontoxic, harmless, non-corrosiveness, and non-greasy is non-volatile.When not having moisture, product does not show bioadhesive, and storage life reaches 5 years.
Three, application:
1, for mosquito control:
The breeding cycle of mosquito needs to carry out on the surface of static shallow water, and before adult mosquito, mosquito ovum swims in the surface of water to obtain air with mosquito larvae and tumbler cluster.
The present invention has an effect with 3 kinds of forms:
1) product of the present invention is directly dripped it is sprinkled upon the water surface, it quickly extends, and form thin film at the water surface, by its bioadhesive and set up a physical barriers and wrap up and suffocate mosquito ovum and mosquito larvae and tumbler, make mosquito ovum, mosquito larvae and tumbler because of anoxia can not adult mosquito, therefore interrupt the reproductive process of mosquito and control mosquito.
2) product of the present invention it is added to the water and quickly stirs, being formed during fast setting and there is bioadhesive agglomerate, adsorbable sticking mosquito ovum and mosquito larvae and tumbler, then by removed together to agglomerate and adsorbate and control mosquito.
3) present invention can control mosquito as the carrying release platform of mosquito killing medicine by strengthening and extend the drug effect of mosquito killing medicine.
2, for the WC pans water surface:
Directly being dripped by product of the present invention and be sprinkled upon the toilet water surface, within the several seconds, the water surface i.e. forms plastic film, carries Excreta and together wash away with current after using.
Effect:
1) prevent the Excreta in toilet from splashing sewage, stop because splashing the infection that sewage causes.
2) prevent Excreta contact nightstool wall from forming spot.
3) the anti-taste of deodorization.
4) cut down when going to toilet and send the sound.
3, for water source purifying:
Being directly added into by product of the present invention in muddy water or contaminated water, and quickly stir, it is formed during fast setting has bioadhesive agglomerate, adsorbable impurity and the pollutant be stained with, then by removed together to agglomerate and adsorbate and water purification.
4, the water yield is kept:
Being directly added in water body by product of the present invention, it forms protecting film at the water surface, prevents the moisture under thin film from evaporating.
5, it is used for covering sewer outlet:
Product of the present invention directly drips the water surface being sprinkled upon sewer outlet, and it quickly extends and forms thin film, and by its bioadhesive and set up a physical barriers, prevent the breeding of flies and mosquitoes capping muddy water abnormal flavour simultaneously.
6, for oil removing:
The degreaser bonding of product of the present invention with aluminium silicate one class is formed bioadhesive agglomerate, therefore degreaser and greasy dirt can be removed jointly.
7, except haze:
After product of the present invention is mixed with water, sparge in air, be used for adhering to micron order fine particle, such as haze.
8, hemostasis:
Product of the present invention is directly injected into blood vessel, meets water this product solidification in blood, blood vessel can be blocked and stop rapidly blood circulation, therefore can stop blooding or block the blood supply of certain tissue.
9, packaging:
Product of the present invention is directly dripped and is sprinkled upon in water body, pull the thin film formed at the water surface out, use thin film that object is formed parcel and close.
In sum, product of the present invention meets after water solidification rapidly and can to form the polymer composite liquid colloid of the uniform thin film with bioadhesive nontoxic and have multi-functional, can be widely used in many fields.
Claims (10)
1. a polymer composite liquid colloid, it is characterised in that be mainly made up of polyvinyl acetate, propylene glycol, ethyl acetate, Dibutyl phthalate, n-butyl acetate, POLYSORBATE 80 and solvent;It is 2~80% that described polyvinyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.2% that propylene glycol accounts for the mass ratio of complex liquid colloid;It is 0.1~5% that ethyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.1~2% that Dibutyl phthalate accounts for the mass ratio of complex liquid colloid;It is 0.1~5% that n-butyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.1% that POLYSORBATE 80 accounts for the mass ratio of complex liquid colloid.
Polymer composite liquid colloid the most according to claim 1, it is characterised in that described solvent is acetone or acetone and the mixed liquor of ethanol.
Polymer composite liquid colloid the most according to claim 2, it is characterised in that it is 10~20% that described polyvinyl acetate accounts for the mass ratio of complex liquid colloid;It is 1% that ethyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.5% that Dibutyl phthalate accounts for the mass ratio of complex liquid colloid;It is 0.9% that n-butyl acetate accounts for the mass ratio of complex liquid colloid;It is 7.7~97.5% that acetone accounts for the mass ratio of complex liquid colloid;It is 0~75% that ethanol accounts for the mass ratio of complex liquid colloid.
4. the preparation method of polymer composite liquid colloid as claimed in claim 1, it is characterized in that being dissolved in solvent polyvinyl acetate, after 10~15 hours, add propylene glycol, ethyl acetate, Dibutyl phthalate, n-butyl acetate and POLYSORBATE 80 while stirring, solubilizer the most again, stirring, i.e. secure satisfactory grades sub-complex liquid colloid;When feeding intake, it is 2~80% that described polyvinyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.2% that propylene glycol accounts for the mass ratio of complex liquid colloid;It is 0.1~5% that ethyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.1~2% that Dibutyl phthalate accounts for the mass ratio of complex liquid colloid;It is 0.1~5% that n-butyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.1% that POLYSORBATE 80 accounts for the mass ratio of complex liquid colloid.
The most according to claim 4, the preparation method of polymer composite liquid colloid, it is characterised in that when feeding intake, it is 10~20% that described polyvinyl acetate accounts for the mass ratio of complex liquid colloid;It is 1% that ethyl acetate accounts for the mass ratio of complex liquid colloid;It is 0.5% that Dibutyl phthalate accounts for the mass ratio of complex liquid colloid;It is 0.9% that n-butyl acetate accounts for the mass ratio of complex liquid colloid;It is 7.7~97.5% that acetone accounts for the mass ratio of complex liquid colloid;It is 0~75% that ethanol accounts for the mass ratio of complex liquid colloid.
6. the purposes of polymer composite liquid colloid as claimed in claim 1, for forming isolating membrane on the water surface.
7. the purposes of polymer composite liquid colloid as claimed in claim 1, after mixing with water, forms the thin film for packaging.
8. the purposes of polymer composite liquid colloid as claimed in claim 1, after mixing with water, sparges in air, is used for adhering to micron order fine particle.
9. the purposes of polymer composite liquid colloid as claimed in claim 1, forms bioadhesive agglomerate by this polymer composite liquid colloid with degreaser bonding, is used for degreasing.
10. the purposes of polymer composite liquid colloid as claimed in claim 1, is used for stopping blooding.