CN105964893A - 一种含蔗渣浆的水溶性型芯及其制备方法 - Google Patents
一种含蔗渣浆的水溶性型芯及其制备方法 Download PDFInfo
- Publication number
- CN105964893A CN105964893A CN201610090144.XA CN201610090144A CN105964893A CN 105964893 A CN105964893 A CN 105964893A CN 201610090144 A CN201610090144 A CN 201610090144A CN 105964893 A CN105964893 A CN 105964893A
- Authority
- CN
- China
- Prior art keywords
- water
- parts
- bagasse pulp
- soluble
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含蔗渣浆的水溶性型芯,其是由下述重量份的原料制得:高岭土30‑40,白云石粉10‑15,蔗渣浆5‑10,氯化钠5‑10,水玻璃5‑10,异丙醇铝0.1‑0.15,聚乙二醇辛基苯基醚0.1‑0.2,羟基硅油0.5‑1,苯甲酸钠0.1‑0.2,明矾0.5‑1,粘结助剂10‑15。本发明的水溶性型芯具有良好的强度、稳定性和低吸湿性,不易发生开裂、缺陷,水溶溃散性好,易于清除,绿色环保,经济耐用,实用价值高。
Description
技术领域
本发明涉及铸造技术领域,尤其涉及一种含蔗渣浆的水溶性型芯及其制备方法。
背景技术
在制造工业中存在大量构件,其内壁呈薄壁复杂的结构,部分内腔几乎封闭,有的连成一体。目前常用的树脂芯、金属芯等溃散性能差,铸件浇注后内腔很难清理,影响铸件内表面的光洁度和尺寸精度,无法满足此类铸件铸造的需求。因此,开发高性能的水溶性型芯十分必要。
水溶性型芯是指以水溶性材料为粘结剂并添加填料,然后通过浇注、压制烧结成型等不同的成型方式制成的型芯。铸件浇注后,该型芯能在水中溶解溃散,达到清理型芯的效果。水溶性型芯具有不发气,可降低铸件缺陷、容易清除等特点,清理时不损伤铸件,尤其适用于带有复杂内腔及弯曲孔道的铸件。并且,水溶性型芯容易再回收利用,节能环保,是一种较为先进的制芯技术,有着良好的应用前景。目前,水溶性型芯的综合性能不佳,尚存在型芯强度差、易变形开裂、水溶溃散性不理想等缺陷,因此限制了其广泛应用。蔗渣浆是由甘蔗制糖废料制成的浆料,主要成分是纤维,具有良好的韧性和粘结作用,其相容性好,通过合理的添加和处理,能有效改善水溶性型芯的性能,并且节能环保,降低成本。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种高强度、低吸湿、抗裂性能好的含蔗渣浆的水溶性型芯及其制备方法。
本发明是通过以下技术方案实现的:
一种含蔗渣浆的水溶性型芯,其是由下述重量份的原料制得:
高岭土30-40,白云石粉10-15,蔗渣浆5-10,氯化钠5-10,水玻璃5-10,异丙醇铝0.1-0.15,聚乙二醇辛基苯基醚0.1-0.2,羟基硅油0.5-1,苯甲酸钠0.1-0.2,明矾0.5-1,粘结助剂10-15;
所述粘结助剂由下列重量份的原料制成:瓜尔胶3-5,丙烯酸0.5-1,烯基琥珀酸酐0.3-0.5,过硫酸铵0.01-0.015,木质素磺酸钙1-2,硅烷偶联剂KH-570 0.1-0.2,水40-60;粘结助剂的制备方法是将瓜尔胶、烯基琥珀酸酐和木质素磺酸钙加入水中80-90℃搅拌1-2h,然后加入其余原料60-70℃、1000-1500r/min搅拌1-2h,冷却后即得。
一种含蔗渣浆的水溶性型芯的制备方法,包括以下步骤:
(1)按重量称取原料,先将高岭土、白云石粉和明矾共同研磨1-2h,再与水玻璃、氯化钠共同加入混料机高速混合10-15min,然后于600-700℃烧结1-2h,冷却后研磨至200-300目,得A组分;
(2)将异丙醇铝加入60-80倍重量的水中,将pH调至3-4后加入聚乙二醇辛基苯基醚和羟基硅油并于85-95℃搅拌2-4h,然后将温度调至40-60℃并加入其余原料搅拌1-2h,冷却后得B组分;
(3)将A组分与B组分加入混料机后高速混合10-20min,然后装填到模具中压实,待其固化后脱模,于200-250℃下烘干12-24h,最后根据需要对其外形进行机械加工,即得含蔗渣浆的水溶性型芯。
本发明的优点是:
本发明通过瓜尔胶、烯基琥珀酸酐、丙烯酸、木质素磺酸钙和硅烷偶联剂KH-570之间的复配及反应制得粘结助剂,有利于型芯的成型,并能有效改善型芯的抗拉性能和抗吸湿性;同时通过蔗渣浆等原料的添加,使制得的水溶性型芯具有良好的强度、稳定性和低吸湿性,不易发生开裂、缺陷,水溶溃散性好,易于清除,绿色环保,经济耐用,实用价值高。
具体实施方式
一种含蔗渣浆的水溶性型芯,其是由下述重量份的原料制得:
高岭土30,白云石粉10,蔗渣浆5,氯化钠5,水玻璃5,异丙醇铝0.1,聚乙二醇辛基苯基醚0.1,羟基硅油0.5,苯甲酸钠0.1,明矾0.5,粘结助剂10;
所述粘结助剂由下列重量份的原料制成:瓜尔胶3,丙烯酸0.5,烯基琥珀酸酐0.3,过硫酸铵0.01,木质素磺酸钙1,硅烷偶联剂KH-570 0.1,水40;粘结助剂的制备方法是将瓜尔胶、烯基琥珀酸酐和木质素磺酸钙加入水中80℃搅拌1h,然后加入其余原料60℃、1000r/min搅拌1h,冷却后即得。
一种含蔗渣浆的水溶性型芯的制备方法,包括以下步骤:
(1)按重量称取原料,先将高岭土、白云石粉和明矾共同研磨1h,再与水玻璃、氯化钠共同加入混料机高速混合10min,然后于600℃烧结1h,冷却后研磨至200目,得A组分;
(2)将异丙醇铝加入60倍重量的水中,将pH调至3后加入聚乙二醇辛基苯基醚和羟基硅油并于85℃搅拌2h,然后将温度调至40℃并加入其余原料搅拌1h,冷却后得B组分;
(3)将A组分与B组分加入混料机后高速混合10min,然后装填到模具中压实,待其固化后脱模,于200℃下烘干12h,最后根据需要对其外形进行机械加工,即得含蔗渣浆的水溶性型芯。
经检验,上述制得的水溶性型芯性能如下:
抗拉强度:4.7MPa;
溃散性能:在水中完全溃散时间≤10min;
抗吸湿性能:空气湿度80%的条件下放置24h,抗拉强度降低6.8%。
Claims (2)
1.一种含蔗渣浆的水溶性型芯,其特征在于,其是由下述重量份的原料制得:
高岭土30-40,白云石粉10-15,蔗渣浆5-10,氯化钠5-10,水玻璃5-10,异丙醇铝0.1-0.15,聚乙二醇辛基苯基醚0.1-0.2,羟基硅油0.5-1,苯甲酸钠0.1-0.2,明矾0.5-1,粘结助剂10-15;
所述粘结助剂由下列重量份的原料制成:瓜尔胶3-5,丙烯酸0.5-1,烯基琥珀酸酐0.3-0.5,过硫酸铵0.01-0.015,木质素磺酸钙1-2,硅烷偶联剂KH-570 0.1-0.2,水40-60;粘结助剂的制备方法是将瓜尔胶、烯基琥珀酸酐和木质素磺酸钙加入水中80-90℃搅拌1-2h,然后加入其余原料60-70℃、1000-1500r/min搅拌1-2h,冷却后即得。
2.根据权利要求1所述的一种含蔗渣浆的水溶性型芯的制备方法,其特征在于,包括以下步骤:
(1)按重量称取原料,先将高岭土、白云石粉和明矾共同研磨1-2h,再与水玻璃、氯化钠共同加入混料机高速混合10-15min,然后于600-700℃烧结1-2h,冷却后研磨至200-300目,得A组分;
(2)将异丙醇铝加入60-80倍重量的水中,将pH调至3-4后加入聚乙二醇辛基苯基醚和羟基硅油并于85-95℃搅拌2-4h,然后将温度调至40-60℃并加入其余原料搅拌1-2h,冷却后得B组分;
(3)将A组分与B组分加入混料机后高速混合10-20min,然后装填到模具中压实,待其固化后脱模,于200-250℃下烘干12-24h,最后根据需要对其外形进行机械加工,即得含蔗渣浆的水溶性型芯。