CN105951501A - Preparation method of bobbin paper - Google Patents
Preparation method of bobbin paper Download PDFInfo
- Publication number
- CN105951501A CN105951501A CN201610421998.1A CN201610421998A CN105951501A CN 105951501 A CN105951501 A CN 105951501A CN 201610421998 A CN201610421998 A CN 201610421998A CN 105951501 A CN105951501 A CN 105951501A
- Authority
- CN
- China
- Prior art keywords
- parts
- paper
- preparation
- pulp
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of bobbin paper. The preparation method comprises the steps that the bobbin paper is prepared from, by weight, 15-26 parts of bagasse pulp, 8-15 parts of villus fiber and 28-39 parts of banana stem pulp; then, the 15-26 parts of bagasse pulp, the 8-15 parts of villus fiber and the 28-39 parts of banana stem pulp are placed into a stirrer for sufficient stirring, the temperature is increased to 60 DEG C, internal cellulose is activated, mesh screen separation, filtering screening, fiber grinding, dehydration by the dehydration separator are performed, then, by weight, 17-32 parts of the United States waste paper and 35-52 parts of national waste paper are added, water is added for dilution, and the ratio of slurry to water is 3-8:5-12, a papermaking additive and padding are added, warming stirring is performed, warming is performed to 70 DEG C, and then papermaking, drying and shearing are performed to obtain needed bobbin paper. The preparation method of the bobbin paper has the advantages of being low in production cost and good in product quality and improving the paper pulp value.
Description
Technical field
The present invention relates to industrial paper field, be specifically related to the preparation method of a kind of cop tube paper.
Background technology
Cop tube paper is mainly used in the making of kernel and pipeline, and industry is managed, ground membrane tube, firework pipe, spinnerule,
Serpentine pipe, Conical tube, parallel pipe, various corrugated board corner protectors, carton, honeycomb cardboard etc., cop tube paper compared to
Slurry cost ratio required for other type of paper is less expensive, the various secondary stocks of most employing or biology
Raw material slurry makes, it is not necessary to trees oleo stock, and the main uses of its cop tube paper is not used under high request environment,
Therefore, cop tube paper is not the highest for requirement from the point of view of raw material and manufacturing process, more available waste residues and
Waste and old paper re-works use, reduces production cost, can reduce the consumption of log simultaneously, protects environment.
The slurry that existing cop tube paper is used mainly waste paper size degradation again forms, and material cost is relatively
Low, but some manufacturer is in order to further reduce cost, can add various filling out in the slurry in fierceness
Material, such as stone powder, china clay, calcium carbonate, titanium dioxide and ferric oxide yellow pigment etc., filler controls in certain requirement
In the range of be the performance in order to improve paper, and paper quality is ignored for cost by some producers, arbitrarily by than
Example is added, and brings up the cop tube paper quality produced and becomes excessively poor, class step-down, and at papermaking row
Industry field, the price harmful competition of each enterprise, cause vicious cycle, make the quality of paper worse and worse, greatly
Destruction industry rule, disrupts the market and continues, accordingly, it would be desirable to a kind of low price and reasonably succedaneum substitute
Filler, makes the quality of cop tube paper grow steadily.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of low production cost, good product quality, paper pulp valency
The preparation method of the cop tube paper that value improves.
For solving the problems referred to above, the present invention adopts the following technical scheme that a kind of cop tube paper, including following weight
Ratio: bagasse pulp 15～26 parts, villus fiber 8～15 parts, 28～39 parts of banana stem slurry, then sugarcane
Slurry 15～26 parts, villus fiber 8～15 parts, banana stem starch 28～39 parts, and to put into blender abundant
Stirring, and is increased to 60 DEG C temperature, activation internal fiber element, then separate through mesh screen, filter clean,
Fiber grind, dehydration seperator dehydration step, be subsequently adding and include following weight ratio: American waste paper 17～
32 parts, domestic waste paper 35～52 parts, and the ratio of dilute, slurry and water is 3～8:5～12, then
Add additive for paper making and filler, and carry out the stirring that heats up, be warming up to 70 DEG C, be then passed through manufacturing paper with pulp, drying
And cut into required cop tube paper.
Further, described bagasse pulp 15～26 parts, villus fiber 8～15 parts, banana stem slurry 28～39
Part tensile property >=8kn/m after stirring, Paper White Degree 10～15ISO, beating consistency 4%～6.5%,
Beating degree 23～26 ° of SR.
Further, described American waste paper includes following weight ratio: useless No. 1 8～15 parts of U.S., U.S. give up No. 5
12～23 parts, U.S. useless No. 11 9～15 parts, wherein, foreign material are less than 1%, and described domestic waste paper is enterprise
Or life use secondary corrugating material wrapping paper.
Further, described additive for paper making includes following weight ratio: sizing agent 25～42 parts, wet strength agent 28～
35 parts, brightening agent 13～18 parts, remaining be Pulvis Talci.
Further, described sizing agent is cationic starch, and described wet strength agent Polyamide Epoxy is described
Brightening agent is calcium carbonate.
The invention has the beneficial effects as follows:
1, with low cost, raw material uses bagasse pulp, villus fiber, banana stem slurry, and bagasse pulp is by Caulis Sacchari sinensis
Obtaining after squeezing, and villus fiber is industrial waste raw material, banana stem slurry is to be ground by banana stem squeezing
Corpus fibrosum, be all industry or life waste material, and add American waste paper and domestic waste paper mixed slurry,
Cheap relative to ecosystem wood pulp several times of cost.
2, raw material is sufficient, and Caulis Sacchari sinensis, discarded fine hair and banana stem are all relatively common life or Industry Waste
Material, in addition to Caulis Sacchari sinensis needs to hoard, other material the most all can be purchased, and waste paper includes that the U.S. gives up
Paper and domestic waste paper, the most all can purchase.
3, environmental protection and energy saving, without log wood pulp, all use castoff regenerative to produce, reduce further and cause environment
Injury, raw material uses plant and fiber product effectively to combine, and reduces chemicals to the destruction of environment and pollution,
And formed after cop tube paper uses more degradable, protect environment.
4, Caulis Sacchari sinensis, discarded fine hair and banana stem all contain abundant fiber, can make full use of, and fiber
Various physical propertys as the performances such as resistance to compression tension, bending degree, water proofing property all than material good, be deeply subject to
Liking of papermaking enterprise.
Bagasse pulp is made up of bagasse that bleaching, the Caulis Sacchari sinensis processing operation of bagasse torrid areas and subtropical zone
In the middle of, the most probably can produce the by-product from sugarcane about more than 1,000,000 tons.And the by-product from sugarcane bleached is also
It is attributed to one of less expensive energy source raw material, because the per unit demand needed for its energy harvest is ploughed
Plant area the lowest.Therefore, utilized by increasing papermaking enterprise, and bagasse pulp contains abundant
Fiber, can one of the big raw material of papermaking the most, bagasse typically contains the moisture content and about of 10---30%
The lignin of 15% and abundant glucide, can be effectively improved microbial degradation rate.
Villus fiber intensity is high.Chopped fiber intensity is 2.6～5.7cN/dtex, high-tenacity fiber be 5.6～
8.0cN/dtex.Owing to hygroscopicity is relatively low, its wet strength is essentially identical with dry strength.Impact resistance is strong
Spend higher 4 times than chinlon, higher 20 times than viscose rayon；Good springiness.Elastic close to Pilus Caprae seu Ovis, when elongation 5%～6%
Time, almost can recover completely.Crease resistance exceedes other fibers, i.e. fabric not wrinkle, good stability of the dimension.
Modulus of elasticity is 22～141cN/dtex, higher 2～3 times than chinlon, heat-resist, and has corrosion-resistant, resistance to
The characteristics such as mill.
Banana stem slurry is the stem stalk that Fructus Musae connects, general all at its stem stalk of Fructus Musae of the most once receiving
Discarding and rot voluntarily, show through research, its stem stalk contains abundant fiber, can carry out the industries such as papermaking
Application, to be increasingly widely used in paper industry.
U.S. useless No. 1, U.S. useless No. 5, U.S. useless No. 11, being American waste paper, the various performance of its paper is above
Domestic paper, and few containing the impurity rate of exchange, repeatable utilization rate is high.
Detailed description of the invention
Below the preferred embodiments of the present invention are described in detail, so that advantages and features of the invention can be more
It is prone to be readily appreciated by one skilled in the art, thus protection scope of the present invention is made apparent clear and definite boundary
Fixed.
Embodiment one
The preparation method of a kind of cop tube paper includes following weight ratio: bagasse pulp 15 parts, villus fiber 8 parts, fragrant
Any of several broadleaf plants stem stalk starches 28 parts, then bagasse pulp 15 parts, villus fiber 8 parts, 28 parts of banana stem slurry is put into and is stirred
It is sufficiently stirred in mixing machine, and temperature is increased to 60 DEG C, activation internal fiber element, then separate through mesh screen,
Filter cleaning, fiber grinds, the step of dehydration seperator dehydration, is subsequently adding and includes following weight ratio: be beautiful
17 parts of state's waste paper, domestic waste paper 35 parts, and the ratio of dilute, slurry and water is 3:5, adds
Additive for paper making and filler, and carry out the stirring that heats up, it is warming up to 70 DEG C, is then passed through manufacturing paper with pulp, dry and cutting
It is cut into required cop tube paper.
Described bagasse pulp 15 parts, villus fiber 8 parts, banana stem starch 28 parts of pull resistances after stirring
Energy >=8kn/m, Paper White Degree 10ISO, beating consistency 4%, 23 ° of SR of beating degree.
Described American waste paper includes following weight ratio: U.S. useless No. 18 parts, U.S. useless No. 5 12 parts, U.S. useless 11
Numbers 9 parts, wherein, foreign material are less than 1%, and described domestic waste paper is enterprise or life secondary corrugating material is packed
Paper.
Described additive for paper making includes following weight ratio: sizing agent 25 parts, wet strength agent 28 parts, brightening agent 13,
Remaining is Pulvis Talci.
Further, described sizing agent is cationic starch, described wet strength agent Polyamide Epoxy, described in brighten
Agent is calcium carbonate.
Embodiment two
The preparation method of a kind of cop tube paper includes following weight ratio: bagasse pulp 18 parts, villus fiber 11 parts,
Banana stem starches 31 parts, then bagasse pulp 18 parts, villus fiber 11 parts, banana stem 31 parts of parts of slurry
Put into blender to be sufficiently stirred for, and temperature is increased to 60 DEG C, activation internal fiber element, then through net
Sieve separate, filter clean, fiber grind, dehydration seperator dehydration step, be subsequently adding include following heavy
Amount ratio: the ratio of American waste paper 24 parts, domestic waste paper 39 parts, and dilute, slurry and water is 4:7,
Add additive for paper making and filler, and carry out the stirring that heats up, be warming up to 70 DEG C, be then passed through manufacturing paper with pulp, drying
Do and cut into required cop tube paper.
Described bagasse pulp 18 parts, villus fiber 11 parts, banana stem starch 31 parts of pull resistances after stirring
Energy >=8kn/m, Paper White Degree 12ISO, beating consistency 4.8%, 24 ° of SR of beating degree.
Described American waste paper includes following weight ratio: useless No. 1 8～15 parts of U.S., useless No. 5 16 parts of U.S., U.S. give up
No. 11 12 parts, wherein, foreign material are less than 1%, and described domestic waste paper is enterprise or life secondary corrugating material
Wrapping paper.
Described additive for paper making includes following weight ratio: sizing agent 32 parts, wet strength agent 33 parts, brightening agent 15
Part, remaining be Pulvis Talci.
Further, described sizing agent is cationic starch, described wet strength agent Polyamide Epoxy, described in brighten
Agent is calcium carbonate.
Embodiment three
The preparation method of a kind of cop tube paper includes following weight ratio: bagasse pulp 21 parts, villus fiber 12 parts,
Banana stem starches 32 parts, then bagasse pulp 21 parts, villus fiber 12 parts, 32 parts of banana stem slurry is put
It is sufficiently stirred in entering blender, and temperature is increased to 60 DEG C, activation internal fiber element, then through mesh screen
Separate, filter cleaning, fiber grinding, the step of dehydration seperator dehydration, be subsequently adding and include following weight
Ratio: the ratio of American waste paper 25 parts, domestic waste paper 46 parts, and dilute, slurry and water is 6:9, then
Add additive for paper making and filler, and carry out the stirring that heats up, be warming up to 70 DEG C, be then passed through manufacturing paper with pulp, drying
And cut into required cop tube paper.
Described bagasse pulp 21 parts, villus fiber 12 parts, banana stem starch 32 parts of pull resistances after stirring
Energy >=8kn/m, Paper White Degree 10～15ISO, beating consistency 5%, 25 ° of SR of beating degree.
Described American waste paper includes following weight ratio: U.S. useless No. 1 12 parts, U.S. useless No. 5 20 parts, U.S. useless 11
Numbers 13 parts, wherein, foreign material are less than 1%, and described domestic waste paper is enterprise or life secondary corrugating material bag
Dress paper.
Described additive for paper making includes following weight ratio: sizing agent 36 parts, wet strength agent 32 parts, brightening agent 16
Part, remaining be Pulvis Talci.
Further, described sizing agent is cationic starch, described wet strength agent Polyamide Epoxy, described in brighten
Agent is calcium carbonate.
Embodiment four
The preparation method of a kind of cop tube paper includes following weight ratio: bagasse pulp 26 parts, villus fiber 15 parts,
Banana stem starches 39 parts, then bagasse pulp 26 parts, villus fiber 15 parts, 39 parts of banana stem slurry is put
It is sufficiently stirred in entering blender, and temperature is increased to 60 DEG C, activation internal fiber element, then through mesh screen
Separate, filter cleaning, fiber grinding, the step of dehydration seperator dehydration, be subsequently adding and include following weight
Ratio: the ratio of American waste paper 32 parts, domestic waste paper 52 parts, and dilute, slurry and water is 8:12,
Add additive for paper making and filler, and carry out the stirring that heats up, be warming up to 70 DEG C, be then passed through manufacturing paper with pulp, drying
Do and cut into required cop tube paper.
Described bagasse pulp 26 parts, villus fiber 15 parts, banana stem starch 39 parts of pull resistances after stirring
Energy >=8kn/m, Paper White Degree 15ISO, beating consistency 6.5%, 26 ° of SR of beating degree.
Described American waste paper includes following weight ratio: U.S. useless No. 1 15 parts, U.S. useless No. 5 23 parts, U.S. useless 11
Numbers 15 parts, wherein, foreign material are less than 1%, and described domestic waste paper is enterprise or life secondary corrugating material bag
Dress paper.
Described additive for paper making includes following weight ratio: sizing agent 42 parts, wet strength agent 35 parts, brightening agent 18
Part, remaining be Pulvis Talci.
Further, described sizing agent is cationic starch, described wet strength agent Polyamide Epoxy, described in brighten
Agent is calcium carbonate.
The above, the only detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto,
Any change expected without creative work or replacement, all should contain and be as the criterion at the new protection domain of this practicality.
Claims (5)
1. the preparation method of a cop tube paper, it is characterised in that: include following weight ratio: bagasse pulp 15～26
Part, villus fiber 8～15 parts, banana stem starch 28～39 parts, then bagasse pulp 15～26 parts, floss
Wool fibre 8～15 parts, banana stem are starched 28～39 parts and are put into blender and be sufficiently stirred for, and temperature liter
Up to 60 DEG C, activation internal fiber is plain, then grinds through mesh screen separation, filtration cleaning, fiber, be dehydrated and divide
Disembark the step of dehydration, be subsequently adding and include following weight ratio: American waste paper 17～32 parts, domestic waste paper 35～
The ratio of 52 parts, and dilute, slurry and water is 3～8:5～12, adds additive for paper making and fills out
Material, and carry out the stirring that heats up, it is warming up to 70 DEG C, is then passed through manufacturing paper with pulp, dry and cut into required yarn
Pipe paper.
The preparation method of a kind of cop tube paper the most according to claim 1, it is characterised in that: described bagasse
Starch 15～26 parts, villus fiber 8～15 parts, banana stem starches 28～39 parts of pull resistances after stirring
Energy >=8kn/m, Paper White Degree 10～15ISO, beating consistency 4%～6.5%, beating degree 23～26 ° of SR.
The preparation method of a kind of cop tube paper the most according to claim 1, it is characterised in that: the described U.S.
Waste paper includes following weight ratio: U.S. useless No. 1 8～15 parts, U.S. useless No. 5 12～23 parts, U.S. useless No. 11 9～
15 parts, wherein, foreign material are less than 1%, and described domestic waste paper is enterprise or life secondary corrugating material is packed
Paper.
The preparation method of a kind of cop tube paper the most according to claim 1, it is characterised in that: described papermaking
Additive includes following weight ratio: sizing agent 25～42 parts, wet strength agent 28～35 parts, brightening agent 13～18
Part, remaining be Pulvis Talci.
The preparation method of a kind of cop tube paper the most according to claim 4, it is characterised in that: described applying glue
Agent is cationic starch, described wet strength agent Polyamide Epoxy, and described brightening agent is calcium carbonate.