CN105924093A - Chlorite bronze-imitating sculpture powder - Google Patents
Chlorite bronze-imitating sculpture powder Download PDFInfo
- Publication number
- CN105924093A CN105924093A CN201610277326.8A CN201610277326A CN105924093A CN 105924093 A CN105924093 A CN 105924093A CN 201610277326 A CN201610277326 A CN 201610277326A CN 105924093 A CN105924093 A CN 105924093A
- Authority
- CN
- China
- Prior art keywords
- chlorite
- bronze
- powder
- sculpture powder
- antique copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a chlorite bronze-imitating sculpture powder. The main points of a technical scheme of the invention are as follows: the chlorite bronze-imitating sculpture powder is composed of chlorite, zeolite, attapulgite clay, white cement, white carbon black, bronze powder, iron oxide orange, iron oxide red, iron oxide green, ferriferrous oxide, rock wool, bronze pearlescent powder and glitter powder. The chlorite bronze-imitating sculpture powder is prepared through the following steps: subjecting ingredients of a semi-finished chlorite bronze-imitating sculpture powder to stirring and carrying out milling, then carrying out co-mixing with the ingredients of the chlorite bronze-imitating sculpture powder under stirring, and carrying out packaging so as to obtain the chlorite bronze-imitating sculpture powder. By adopting the chlorite bronze-imitating sculpture powder to manufacture a bronze-imitating sculpture, a bronze-imitating sculpture craft with pure color is obtained after maintenance and hardening; the obtained bronze-imitating sculpture craft has the characteristics of good smooth finish, brightness, high strength, small shrinkage rate, wear resistance and corrosion resistance, can be placed at a variety of places like outdoors, squares, gardens or indoors for a long term, is adaptable to weather exposure, and does not deform under exposure to wind and rain; meanwhile, the chlorite bronze-imitating sculpture powder is applicable to manufacturing of a variety of bronze-imitating sculpture crafts.
Description
Technical field
The present invention relates to sculpture, be specifically related to a kind of chlorite antique copper sculpture powder.
Background technology
Various ancient times and the imitative bronze sculpture of modern personage, child or animal is had in numerous parks, welcome by traveller very much, due to hold up touch, ride carry on the arm, weather exposure and exposing to wind and rain, these imitative bronze sculptures all can be by than more serious infringement from color to moulding.
Summary of the invention
It is an object of the invention to overcome weak point in prior art, it is provided that a kind of chlorite antique copper sculpture powder.
Chlorite antique copper sculpture powder is made up of the zeolite granular after chlorite, acidifying, Concave-convex clay rod, white cement, white carbon, bronze powder, iron oxide orange pigments, iron oxide red, iron oxide green, ferroso-ferric oxide, rock wool, bronze-colored pearl essence and glitter powder after weathering.
The production method of chlorite antique copper sculpture powder: first the dispensing of chlorite antique copper sculpture powder semi-finished product is stirred and abrasive dust, then it is packaged as chlorite antique copper sculpture powder by after the common mix and blend of dispensing of chlorite antique copper sculpture powder.
The quality of chlorite is fine and glossy and smooth, color is glossy dark green mulberry, it is rich in refined gas, type stone, picture stone, prehnite, plum blossom stone, green glaze stone etc. can be divided into several, overall mellow and full beautiful, there is isochrome light green, yellowish green, dark green, type line combines, like sky, carving god moulds, and the present invention selects the chlorite after pulverizing, granularity≤2 millimeter of chlorite.
Zeolite has powerful adsorption function, to polar molecule such as H2O、NH3、H2S、CO2Etc. there being the highest affinity, even if remaining to effectively adsorb under low relative humidity, low concentration, higher temperature conditions, therefore it is stable performance, adsorbent that adsorption effect is good, it is adaptable to exhaust-gas treatment and air cleaning.
Zeolite granular after acidifying be zeolite is pulverized laggard row roasting, be acidified, dry and sieve after for acidifying after zeolite granular.
Attapulgite has another name called palygorskite or Palygorskite, be a kind of layer of chain structure containing Shuifu County's zeopan clay mineral, Concave-convex clay rod have uniqueness layer chain structure feature, crystal is needle-like, threadiness or fiber collection shape.Concave-convex clay rod has the dispersion of uniqueness, good colloidal nature and the higher adsorption capacity such as saline and alkaline high temperature resistant, anti-, and has certain plasticity and cohesive force.
Concave-convex clay rod after weathering is by Concave-convex clay rod raw ore time weathering more than two winters, Concave-convex clay rod after the raw ore of large block compact is disintegrated for the weathering of fine particle, picking and be evident that barren rock block, string and other earth impurity, the present invention selects granularity≤5 millimeter of the Concave-convex clay rod after weathering.
White portland cement is called for short white cement, it is to be added gypsum, the levigate hydraulic cementing materials made by white portland cement clinker, is typically characterised by and there is the highest whiteness, bright color, quality needs to meet the standard of " GB/T2015-2005 white portland cement ".
White carbon is a kind of ultra tiny inorganic porous property material, owing to its particle diameter is the least, has the special performances such as the stability that specific surface area is big, superficial attractive forces is strong, chemical purity is high, dispersive property is good, superior, reinforcing, thickening property, adhesive force and thixotropy.
Bronze powder is a kind of floating type flake pigment, and by a certain proportion of copper, zinc and aluminium alloy, smelting, ball milling, classification form to required specification and effect, and pure color is beautiful, metal sense extra-heavy.
Iron oxide orange pigments is shallow salmon pink powder to be had to the various coloured light of deep salmon pink powder, has the features such as opaque is fine and smooth, bright-colored, tinting strength, tinting power is high, dispersed, fast light, weather-proof, acidproof, alkaline resistance properties is excellent.
Iron oxide red is also referred to as become rusty red, is red oxidization iron powder, has fast light, high temperature resistant, acidproof, alkaline-resisting, the rust-preventing characteristic of excellence, and good dispersion, tinting strength, tinting power and covering power are the strongest.
Iron oxide green has good dispersion, strongly absorbs ultraviolet, the superperformance such as fast light, corrosion-resistant.
Ferroso-ferric oxide, is commonly called as iron oxide black, magnet, magnet, black iron, has saturated blue ink light black, strong coloring force, the features such as covering power is the highest, and light resistance is good.
Rock wool is with natural rock such as basalt, gabbro, dolomite, iron ore, chlorite etc. as primary raw material, the inorganic fibre made through high temperature melting, fibrillatable, and the present invention selects the length 5 of rock wool fibers～8 millimeters.
Pearl essence is the nacreous novel pigment covering metal oxide outside natural mica thin skin and producing, it can reproduce the gorgeous and color that nature pearl, shell, coral and metal are had, the present invention selects bronze-colored pearl essence, granularity≤0.044 millimeter of bronze-colored pearl essence.
Glitter powder, by PET, PVC, OPP metallic aluminium film material plating of the essence high different-thickness of brightness, is coated with and forms through precision cutting.Glitter powder bright in color, to weather, the mild corrosion chemicals of temperature has certain resistance and temperature tolerance, and the present invention selects golden glitter powder, granularity≤0.044 millimeter of glitter powder.
The technical scheme is that:
1, the dispensing of chlorite antique copper sculpture powder is made up of following component by weight percentage: chlorite antique copper sculpture powder semi-finished product 25～60%, zeolite granular after acidifying 5～25%, white cement 20～45%, rock wool 1～10%, bronze-colored pearl essence 0.5～5% and glitter powder 0.5～5%.
2, the dispensing of chlorite antique copper sculpture powder semi-finished product is made up of following component by weight percentage: chlorite 30～60%, Concave-convex clay rod after weathering 10～40%, white carbon 1～20%, bronze powder 1～20%, iron oxide orange pigments 1～10%, iron oxide red 0～5%, iron oxide green 0～5% and ferroso-ferric oxide 0～5%.
3, the production method of chlorite antique copper sculpture powder: (1) the dispensing of chlorite antique copper sculpture powder semi-finished product inputs stirrer for mixing stirring, inputting abrasive dust in grinding machine after stirring is chlorite antique copper sculpture powder semi-finished product, granularity≤0.044 millimeter；(2) the dispensing of chlorite antique copper sculpture powder is inputted stirrer for mixing stirring, after stirring, is packaged as chlorite antique copper sculpture powder.
4, the production method of the zeolite granular after acidifying: the most first carrying out zeolite pulverizing and screening for the first time, the Task-size Controlling of the zeolite granular after screening is at 0.149～0.42 millimeter；2. by the zeolite granular input revolution roasting in kilns after screening, sintering temperature controls at 420～480 DEG C, and roasting time controlled at 60～120 minutes；3. being inputted in dilute sulfuric acid pond by the zeolite granular after roasting and carry out acidification, the preparation of dilute sulfuric acid includes following component by weight percentage: the sulfuric acid 6～10% of concentration 98, water 90～94%, and the acidification time controlled at 4～12 hours；4. the zeolite granular after acidified process is taken out and drain away the water, zeolite granular semi-finished product after drying as acidifying in input rotary dryer, drying temperature and control at 150～250 DEG C, drying time controls at 30～60 minutes, and the zeolite granular semi-finished product water content after acidifying is less than 2.0%；5. carrying out after second time is sieved being the zeolite granular after being acidified by the zeolite granular semi-finished product after acidifying, the Task-size Controlling of the zeolite granular after acidifying is at 0.125～0.42 millimeter.
Zeolite granular after acidifying is to use by " having the zeolite colour-wash powder of air purification function " filed in 14 days November in 2015 of the present inventor, and China Patent Publication No. is: CN 105272114A, publication date: on 01 27th, 2016.
Concave-convex clay rod after chlorite, weathering, white carbon, bronze powder, iron oxide orange pigments, iron oxide red, iron oxide green and ferroso-ferric oxide are stirred together for rear abrasive dust, be conducive to sufficiently being disperseed the dispensing of chlorite antique copper sculpture powder semi-finished product, promote that white carbon, bronze powder, iron oxide orange pigments, iron oxide red, iron oxide green and ferroso-ferric oxide will be supported on the surface of chlorite and Concave-convex clay rod uniformly.
Adjust bronze powder, iron oxide orange pigments, iron oxide red, iron oxide green, ferroso-ferric oxide, bronze-colored pearl essence and the dispensing percentage of glitter powder, to guarantee that chlorite antique copper sculpture powder is the sculpture powder of a kind of pure coppery modelled after an antique.
Zeolite granular after acidifying uses to be pulverized, screening for the first time, roasting, is acidified, drains, dries and technological process that second time is sieved, substantially increase acidifying quality and the acidification rate of zeolite, strengthen the absorption of chlorite antique copper sculpture powder and purify the efficiency of air, the Task-size Controlling of the zeolite granular after acidifying is at 0.125～0.42 millimeter, the function of aggregate can be played, be conducive to increasing the intensity of antique copper sculpture products.
Zeolite is after 420～480 DEG C of roastings, then carries out acidification, and zeolite has obtained further activation, forms loose porous cavernous body, and its adsorption effect is in optimum value.
Rock wool plays the effect increasing tensile strength in the dispensing of chlorite antique copper sculpture powder, it can be ensured that will not crack when making antique copper sculpture products.
After zeolite granular, rock wool, bronze-colored pearl essence and glitter powder after chlorite antique copper sculpture powder semi-finished product, white cement, acidifying is carried out mix and blend, chlorite antique copper sculpture powder finished product is the powder of a kind of coppery modelled after an antique.
The using method of chlorite antique copper sculpture powder: making scene, first chlorite antique copper sculpture powder is added in the mixer operated, slowly spray into spray water, input after stirring in vacuum-extruder, extruding a kind of sculpture clay for making antique copper sculpture, antique copper sculpture clay quality softness plasticity is good.
Chlorite antique copper sculpture powder is used to make antique copper sculpture, after maintenance hardening, it it is the carving handicraft product of the pure coppery modelled after an antique of a kind of color, have that fineness is good, bright, intensity high, shrinkage factor is little, rub resistance and corrosion resistant feature, can be placed on the places such as open air, square, park or indoor for a long time, beautify the environment, appreciate for traveller, adapt to weather exposure and expose to wind and rain indeformable.
The carving handicraft product of coppery modelled after an antique is placed on indoor, not only there is higher art appreciation and classical collection is worth, moreover it is possible to the air in absorption and clean room.
Chlorite antique copper sculpture powder is applicable to make various antique copper carving handicraft product.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described:
1, the dispensing of chlorite antique copper sculpture powder is made up of following component by weight percentage: zeolite granular 8%, white cement 32%, rock wool 4%, bronze-colored pearl essence 4% and the glitter powder 1% after chlorite antique copper sculpture powder semi-finished product 51%, acidifying.
2, the dispensing of chlorite antique copper sculpture powder semi-finished product is made up of following component by weight percentage: Concave-convex clay rod 26%, white carbon 4%, bronze powder 9%, iron oxide orange pigments 2%, iron oxide red 2%, iron oxide green 0.5% and the ferroso-ferric oxide 0.5% after chlorite 56%, weathering.
3, the production method of chlorite antique copper sculpture powder: (1) the dispensing of chlorite antique copper sculpture powder semi-finished product inputs stirrer for mixing stirring, inputting abrasive dust in grinding machine after stirring is chlorite antique copper sculpture powder semi-finished product, granularity≤0.044 millimeter；(2) the dispensing of chlorite antique copper sculpture powder is inputted stirrer for mixing stirring, after stirring, is packaged as chlorite antique copper sculpture powder.
Claims (4)
1. a chlorite antique copper sculpture powder, it is characterized in that, the dispensing of chlorite antique copper sculpture powder is made up of following component by weight percentage: chlorite antique copper sculpture powder semi-finished product 25～60%, zeolite granular after acidifying 5～25%, white cement 20～45%, rock wool 1～10%, bronze-colored pearl essence 0.5～5% and glitter powder 0.5～5%；
The dispensing of described chlorite antique copper sculpture powder semi-finished product is made up of following component by weight percentage: chlorite 30～60%, Concave-convex clay rod after weathering 10～40%, white carbon 1～20%, bronze powder 1～20%, iron oxide orange pigments 1～10%, iron oxide red 0～5%, iron oxide green 0～5% and ferroso-ferric oxide 0～5%；
The production method of the zeolite granular after described acidifying: the most first carrying out zeolite pulverizing and screening for the first time, the Task-size Controlling of the zeolite granular after screening is at 0.149～0.42 millimeter；2. by the zeolite granular input revolution roasting in kilns after screening, sintering temperature controls at 420～480 DEG C, and roasting time controlled at 60～120 minutes；3. being inputted in dilute sulfuric acid pond by the zeolite granular after roasting and carry out acidification, the preparation of dilute sulfuric acid includes following component by weight percentage: the sulfuric acid 6～10% of concentration 98, water 90～94%, and the acidification time controlled at 4～12 hours；4. the zeolite granular after acidified process is taken out and drain away the water, zeolite granular semi-finished product after drying as acidifying in input rotary dryer, drying temperature and control at 150～250 DEG C, drying time controls at 30～60 minutes, and the zeolite granular semi-finished product water content after acidifying is less than 2.0%；5. carrying out after second time is sieved being the zeolite granular after being acidified by the zeolite granular semi-finished product after acidifying, the Task-size Controlling of the zeolite granular after acidifying is at 0.125～0.42 millimeter.
Chlorite antique copper sculpture powder the most according to claim 1, it is characterized in that, the production method of chlorite antique copper sculpture powder: (1) the dispensing of chlorite antique copper sculpture powder semi-finished product is inputted stirrer for mixing stirring, inputting abrasive dust in grinding machine after stirring is chlorite antique copper sculpture powder semi-finished product, granularity≤0.044 millimeter；(2) the dispensing of chlorite antique copper sculpture powder is inputted stirrer for mixing stirring, after stirring, is packaged as chlorite antique copper sculpture powder.
Chlorite antique copper sculpture powder the most according to claim 1, it is characterized in that, Concave-convex clay rod after weathering is by Concave-convex clay rod raw ore time weathering more than two winters, Concave-convex clay rod after the raw ore of large block compact is disintegrated for the weathering of fine particle, pick and be evident that barren rock block, string and other earth impurity, granularity≤5 millimeter of the Concave-convex clay rod after weathering.
Chlorite antique copper sculpture powder the most according to claim 1, it is characterised in that granularity≤2 millimeter of chlorite, the length 5 of rock wool fibers～8 millimeters, granularity≤0.044 millimeter of bronze-colored pearl essence, granularity≤0.044 millimeter of glitter powder.