CN105908162A - Antirust chain type conveyor - Google Patents
Antirust chain type conveyor Download PDFInfo
- Publication number
- CN105908162A CN105908162A CN201610288744.7A CN201610288744A CN105908162A CN 105908162 A CN105908162 A CN 105908162A CN 201610288744 A CN201610288744 A CN 201610288744A CN 105908162 A CN105908162 A CN 105908162A
- Authority
- CN
- China
- Prior art keywords
- consumption
- antirust
- weight portion
- linked conveyer
- chain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antirust chain type conveyor. The antirust chain type conveyor is obtained by conducting antirust treatment on a metal body. An antirust treatment method includes the steps that firstly, Chinese medicinal herbs are put into an organic solvent to be decocted and then filtered, and filter liquor is taken out; secondly, alpha-pinene, kieselguhr, simethicone, potassium fluozirconate, fatty acid, sodium molybdate, morpholine, methylbenzotriazole, a macromolecule film-forming agent, a surfactant and the filter liquor are mixed to form an antirust agent; and thirdly, the metal body is put into the antirust agent to be soaked and then taken out to be dried, and the antirust chain type conveyor is obtained. The Chinese medicinal herbs comprise lentinus edodes, lignum sappan, reed rhizome, cassia twig, caltrop, alangium chinense, equisetum flowers and boenninghausenia sessilicarpa. The antirust chain type conveyor has the excellent antirust characteristic.
Description
Technical field
The present invention relates to conveying device, in particular it relates to a kind of antirust chain-linked conveyer.
Background technology
Chain-linked conveyer is commonly used to the conveying of the raw material of industry, as the easily fluidization such as cement, flyash
The conveying of granular material.The agent structure of chain-linked conveyer is processed by metalwork, although metalwork
There is the mechanical property of excellence, but extremely get rusty easily after long-time use, especially cement,
The raw materials such as flyash can further speed up the speed of getting rusty of chain-linked conveyer, and then result in chain conveying
The decline of the mechanical property of machine, the most even can cause the avalanche of antirust chain-linked conveyer.
Summary of the invention
It is an object of the invention to provide a kind of antirust chain-linked conveyer, this antirust chain-linked conveyer has excellence
Rust-preventing characteristic.
To achieve these goals, the invention provides a kind of antirust chain-linked conveyer, this antirust chain type is defeated
Sending machine to obtain by metal master is carried out antirust treatment, the method for antirust treatment is:
1) Chinese herbal medicine is placed in organic solvent decocts, then cross leaching filtrate;
2) by australene, diatomite, dimethicone, potassium fluorozirconate, aliphatic acid, sodium molybdate,
Coffee quinoline, tolyl-triazole, macromolecule film former, surfactant and filtrate are mixed to form antirust agent;
3) metal master is placed in antirust agent immersion, then takes out and be dried to prepare antirust chain conveying
Machine;
Wherein, Chinese herbal medicine be perfume (or spice) eat, bush, reed rhizome, cassia twig, puncture vine, alangium, scouring rush Hua Heshi
Green pepper grass.
Preferably, in step 1) in, decoct and at least meet following condition: decoction temperature is 110-125
DEG C, decocting time is 3-5h.
Preferably, in step 1) in, organic solvent selected from ethanol, acetone, chloroform, carbon tetrachloride,
One or more in benzene and toluene.
Preferably, in step 1) in, relative to the organic solvent of 1000 weight portions, the consumption that perfume (or spice) is eaten is
75-88 weight portion, the consumption of bush is 64-79 weight portion, and the consumption of reed rhizome is 35-47 weight portion, osmanthus
The consumption of branch is 65-78 weight portion, and the consumption of puncture vine is 42-58 weight portion, and the consumption of alangium is
118-127 weight portion, the consumption that scouring rush spends is 45-66 weight portion, and the consumption of boenninghausenia sessilicarpa is 25-37 weight
Part.
Preferably, during macromolecule film former is selected from polyethylene glycol, CMS or polyvinyl alcohol
Plant or multiple.
Preferably, surfactant is selected from neopelex, dioctyl succinate disulfonate acid and ten
One or more in tetrol APEO.
Preferably, in step 2) in, relative to the australene of 100 weight portions, diatomaceous consumption is
50-72 weight portion, the consumption of dimethicone is 120-135 weight portion, and the consumption of potassium fluorozirconate is 14-32
Weight portion, the consumption of aliphatic acid is 200-241 weight portion, and the consumption of sodium molybdate is 21-36 weight portion,
The consumption of morpholine is 17-25 weight portion, and the consumption of tolyl-triazole is 9-15 weight portion, and macromolecule becomes
The consumption of film is 3-7 weight portion, and the consumption of surfactant is 5-8 weight portion, and the consumption of filtrate is
82-95 weight portion.
Preferably, in step 3) in, soak and at least meet following condition: soaking temperature is 40-60 DEG C,
Soak time is 8-12h.
Preferably, in step 3) in, it is dried and at least meets following condition: baking temperature is 115-130
DEG C, drying time is 5-7h.
By technique scheme, the present invention first pass through perfume (or spice) eat, bush, reed rhizome, cassia twig, puncture vine,
Alangium, Mu Zeihua, boenninghausenia sessilicarpa and organic solvent prepare extracts of Chinese herbal medicine, followed by australene,
Diatomite, dimethicone, potassium fluorozirconate, aliphatic acid, sodium molybdate, morpholine, tolyl-triazole,
Macromolecule film former, surfactant prepare antirust agent with the synergy of extracts of Chinese herbal medicine, finally will
Immersion it is placed in antirust agent so that metal master for preparing the metal master of antirust chain-linked conveyer
Surface forms antirust coat, and then makes the chain-linked conveyer prepared have the rust-preventing characteristic of excellence.
Other features and advantages of the present invention will be described in detail in detailed description of the invention part subsequently.
Detailed description of the invention
Hereinafter the detailed description of the invention of the present invention is described in detail.It should be appreciated that this place is retouched
The detailed description of the invention stated is merely to illustrate and explains the present invention, is not limited to the present invention.
The invention provides a kind of antirust chain-linked conveyer, this antirust chain-linked conveyer is by by metal master
Carrying out antirust treatment and obtain, the method for antirust treatment is:
1) Chinese herbal medicine is placed in organic solvent decocts, then cross leaching filtrate;
2) by australene, diatomite, dimethicone, potassium fluorozirconate, aliphatic acid, sodium molybdate,
Coffee quinoline, tolyl-triazole, macromolecule film former, surfactant and filtrate are mixed to form antirust agent;
3) metal master is placed in antirust agent immersion, then takes out and be dried to prepare antirust chain conveying
Machine;
Wherein, Chinese herbal medicine be perfume (or spice) eat, bush, reed rhizome, cassia twig, puncture vine, alangium, scouring rush Hua Heshi
Green pepper grass.
In the present invention, the actual conditions of decoction can select in wide scope, but in order to make to prepare
Chain-linked conveyer there is more excellent rustless property, it is preferable that in step 1) in, decoct the fullest
Be enough to lower condition: decocting temperature and be 110-125 DEG C, decocting time is 3-5h.
In the present invention, the concrete kind of organic solvent can select in wide scope, but in order to make
The chain-linked conveyer prepared has more excellent rustless property, it is preferable that in step 1) in, You Jirong
One or more in ethanol, acetone, chloroform, carbon tetrachloride, benzene and toluene of agent.
Step 1 in the present invention) in, the consumption of each material can select in wide scope, but is
The chain-linked conveyer prepared is made to have more excellent rustless property, it is preferable that in step 1) in, phase
For the organic solvent of 1000 weight portions, the consumption that perfume (or spice) is eaten is 75-88 weight portion, and the consumption of bush is
64-79 weight portion, the consumption of reed rhizome is 35-47 weight portion, and the consumption of cassia twig is 65-78 weight portion, puncture
The consumption of lamb's-quarters is 42-58 weight portion, and the consumption of alangium is 118-127 weight portion, the consumption that scouring rush spends
For 45-66 weight portion, the consumption of boenninghausenia sessilicarpa is 25-37 weight portion.
Step 2 in the present invention) in, the concrete kind of macromolecule film former can be selected in wide scope
Select, but in order to make the chain-linked conveyer prepared have more excellent rustless property, it is preferable that macromolecule
One or more in polyethylene glycol, CMS or polyvinyl alcohol of film forming agent.
Step 2 in the present invention) in, the concrete kind of surfactant can select in wide scope,
But in order to make the chain-linked conveyer prepared have more excellent rustless property, it is preferable that surfactant
One in neopelex, dioctyl succinate disulfonate acid and tetradecyl alchohol APEO
Or it is multiple.
Step 2 in the present invention) in, the concrete consumption of each material can select in wide scope, but
It is to make the chain-linked conveyer prepared have more excellent rustless property, it is preferable that in step 2) in,
Relative to the australene of 100 weight portions, diatomaceous consumption is 50-72 weight portion, dimethicone
Consumption is 120-135 weight portion, and the consumption of potassium fluorozirconate is 14-32 weight portion, and the consumption of aliphatic acid is
200-241 weight portion, the consumption of sodium molybdate is 21-36 weight portion, and the consumption of morpholine is 17-25 weight
Part, the consumption of tolyl-triazole is 9-15 weight portion, and the consumption of macromolecule film former is 3-7 weight portion,
The consumption of surfactant is 5-8 weight portion, and the consumption of filtrate is 82-95 weight portion.
Step 3 in the present invention) in, the actual conditions of immersion can select in wide scope, but
In order to make the chain-linked conveyer prepared have more excellent rustless property, it is preferable that in step 3) in,
Soak and at least meet following condition: soaking temperature is 40-60 DEG C, and soak time is 8-12h.
Step 3 in the present invention) in, the actual conditions being dried can select in wide scope, but
In order to make the chain-linked conveyer prepared have more excellent rustless property, it is preferable that in step 3) in,
It is dried and at least meets following condition: baking temperature is 115-130 DEG C, and drying time is 5-7h.
Hereinafter will be described the present invention by embodiment.
Embodiment 1
1) perfume (or spice) is eaten, bush, reed rhizome, cassia twig, puncture vine, alangium, Mu Zeihua, boenninghausenia sessilicarpa and have
Machine solvent (carbon tetrachloride) is according to the weight of 78:69:37:68:48:124:49:27:1000
Than mixing, at 115 DEG C, then decoct 4h, then cross leaching filtrate;
2) at 25 DEG C, by australene, diatomite, dimethicone, potassium fluorozirconate, aliphatic acid,
Sodium molybdate, morpholine, tolyl-triazole, macromolecule film former (CMS), surfactant
(dioctyl succinate disulfonate acid) and filtrate are according to 100:62:125:19:231:26:19:11:
The weight ratio of 5:6:85 is mixed to form antirust agent;
3) metal master is placed in the antirust agent of 50 DEG C immersion 10h, then takes out and be dried at 120 DEG C
6h is to prepare antirust chain-linked conveyer A1.
Embodiment 2
1) perfume (or spice) is eaten, bush, reed rhizome, cassia twig, puncture vine, alangium, Mu Zeihua, boenninghausenia sessilicarpa and have
Machine solvent (ethanol) mixes according to the weight ratio of 75:64:35:65:42:118:45:25:1000
Close, at 110 DEG C, then decoct 3h, then cross leaching filtrate;
2) at 25 DEG C, by australene, diatomite, dimethicone, potassium fluorozirconate, aliphatic acid,
Sodium molybdate, morpholine, tolyl-triazole, macromolecule film former (polyethylene glycol), surfactant (ten
Dialkyl benzene sulfonic acids sodium) with filtrate according to 100:50:120:14:200:21:17:9:3:5:
The weight ratio of 82 is mixed to form antirust agent;
3) metal master is placed in the antirust agent of 40 DEG C immersion 8h, then takes out and be dried at 115 DEG C
5h is to prepare antirust chain-linked conveyer A2.
Embodiment 3
1) perfume (or spice) is eaten, bush, reed rhizome, cassia twig, puncture vine, alangium, Mu Zeihua, boenninghausenia sessilicarpa and have
Machine solvent (toluene) mixes according to the weight ratio of 88:79:47:78:58:127:66:37:1000
Close, at 125 DEG C, then decoct 5h, then cross leaching filtrate;
2) at 25 DEG C, by australene, diatomite, dimethicone, potassium fluorozirconate, aliphatic acid,
Sodium molybdate, morpholine, tolyl-triazole, macromolecule film former (polyvinyl alcohol), surfactant (ten
Tetradecyl alchohol APEO) with filtrate according to 100:72:135:32:241:36:25:15:7:
The weight ratio of 8:95 is mixed to form antirust agent;
3) metal master is placed in the antirust agent of 60 DEG C immersion 12h, then takes out and be dried at 130 DEG C
7h is to prepare antirust chain-linked conveyer A3.
Comparative example 1
Carry out preparing chain-linked conveyer B1, except for the difference that, step 1 according to the method for embodiment 1) in not
Perfume (or spice) is used to eat.
Comparative example 2
Carry out preparing chain-linked conveyer B2, except for the difference that, step 1 according to the method for embodiment 1) in not
Use bush.
Comparative example 3
Carry out preparing chain-linked conveyer B3, except for the difference that, step 1 according to the method for embodiment 1) in not
Use reed rhizome.
Comparative example 4
Carry out preparing chain-linked conveyer B4, except for the difference that, step 1 according to the method for embodiment 1) in not
Use cassia twig.
Comparative example 5
Carry out preparing chain-linked conveyer B5, except for the difference that, step 1 according to the method for embodiment 1) in not
Use puncture vine.
Comparative example 6
Carry out preparing chain-linked conveyer B6, except for the difference that, step 1 according to the method for embodiment 1) in not
Use alangium.
Comparative example 7
Carry out preparing chain-linked conveyer B7, except for the difference that, step 1 according to the method for embodiment 1) in not
Scouring rush is used to spend.
Comparative example 8
Carry out preparing chain-linked conveyer B8, except for the difference that, step 1 according to the method for embodiment 1) in not
Use boenninghausenia sessilicarpa.
Comparative example 9
Carry out preparing chain-linked conveyer B9, except for the difference that, step 2 according to the method for embodiment 1) in not
Use filtrate.
Detection example 1
Above-mentioned chain-linked conveyer is placed in the environment that air humidity is 70% standing 30 days, then detects
Rust staining number (individual/the dm of the unit are on the surface of chain-linked conveyer2), concrete outcome is shown in Table 1.
Table 1
Rust staining number (individual/the dm of unit are2) | |
A1 | 0 |
A2 | 0 |
A3 | 0 |
B1 | 5 |
B2 | 4 |
B3 | 6 |
B4 | 3 |
B5 | 4 |
B6 | 2 |
B7 | 4 |
B8 | 3 |
B9 | 11 |
By above-mentioned detection example, the chain-linked conveyer that the present invention provides has the rust-preventing characteristic of excellence.
The preferred embodiment of the present invention described in detail above, but, the present invention is not limited to above-mentioned reality
Execute the detail in mode, in the technology concept of the present invention, can be to the technical side of the present invention
Case carries out multiple simple variant, and these simple variant belong to protection scope of the present invention.
It is further to note that each the concrete technology described in above-mentioned detailed description of the invention is special
Levy, in the case of reconcilable, can be combined by any suitable means, in order to avoid need not
The repetition wanted, various possible combinations are illustrated by the present invention the most separately.
Additionally, can also be combined between the various different embodiment of the present invention, as long as its
Without prejudice to the thought of the present invention, it should be considered as content disclosed in this invention equally.
Claims (9)
1. an antirust chain-linked conveyer, it is characterised in that described antirust chain-linked conveyer is by by gold
Owner's body carries out antirust treatment and obtains, and the method for described antirust treatment is:
1) Chinese herbal medicine is placed in organic solvent decocts, then cross leaching filtrate;
2) by australene, diatomite, dimethicone, potassium fluorozirconate, aliphatic acid, sodium molybdate,
Coffee quinoline, tolyl-triazole, macromolecule film former, surfactant and described filtrate are mixed to form antirust agent;
3) described metal master is placed in described antirust agent immersion, then takes out and be dried with prepared described
Antirust chain-linked conveyer;
Wherein, described Chinese herbal medicine be perfume (or spice) eat, bush, reed rhizome, cassia twig, puncture vine, alangium, Mu Zeihua
And boenninghausenia sessilicarpa.
Antirust chain-linked conveyer the most according to claim 1, wherein, in step 1) in, described
Decoct and at least meet following condition: decocting temperature and be 110-125 DEG C, decocting time is 3-5h.
Antirust chain-linked conveyer the most according to claim 2, wherein, in step 1) in, like institute
State one or more in ethanol, acetone, chloroform, carbon tetrachloride, benzene and toluene of organic solvent.
4. according to the antirust chain-linked conveyer described in any one in claim 1-3, wherein, in step
Rapid 1) in, relative to the described organic solvent of 1000 weight portions, the consumption that described perfume (or spice) is eaten is 75-88 weight
Amount part, the consumption of described bush is 64-79 weight portion, and the consumption of described reed rhizome is 35-47 weight portion,
The consumption of described cassia twig is 65-78 weight portion, and the consumption of described puncture vine is 42-58 weight portion, described eight
The consumption of angle maple is 118-127 weight portion, and the consumption that described scouring rush spends is 45-66 weight portion, described stone
The consumption of green pepper grass is 25-37 weight portion.
Antirust chain-linked conveyer the most according to claim 4, wherein, described macromolecule film former
One or more in polyethylene glycol, CMS or polyvinyl alcohol.
Antirust chain-linked conveyer the most according to claim 4, wherein, described surfactant selects
One in neopelex, dioctyl succinate disulfonate acid and tetradecyl alchohol APEO or
Multiple.
7. according to the antirust chain-linked conveyer described in claim 5 or 6, wherein, in step 2) in,
Relative to the described australene of 100 weight portions, described diatomaceous consumption is 50-72 weight portion, described
The consumption of dimethicone is 120-135 weight portion, and the consumption of described potassium fluorozirconate is 14-32 weight portion,
The consumption of described aliphatic acid is 200-241 weight portion, and the consumption of described sodium molybdate is 21-36 weight portion,
The consumption of described morpholine is 17-25 weight portion, and the consumption of described tolyl-triazole is 9-15 weight portion,
The consumption of described macromolecule film former is 3-7 weight portion, and the consumption of described surfactant is 5-8 weight
Part, the consumption of described filtrate is 82-95 weight portion.
Antirust chain-linked conveyer the most according to claim 7, wherein, in step 3) in, described
Soak and at least meet following condition: soaking temperature is 40-60 DEG C, and soak time is 8-12h.
Antirust chain-linked conveyer the most according to claim 8, wherein, in step 3) in, described
It is dried and at least meets following condition: baking temperature is 115-130 DEG C, and drying time is 5-7h.