CN105907194A - Outdoor fitness equipment paint with high scratch resistance - Google Patents
Outdoor fitness equipment paint with high scratch resistance Download PDFInfo
- Publication number
- CN105907194A CN105907194A CN201610464793.1A CN201610464793A CN105907194A CN 105907194 A CN105907194 A CN 105907194A CN 201610464793 A CN201610464793 A CN 201610464793A CN 105907194 A CN105907194 A CN 105907194A
- Authority
- CN
- China
- Prior art keywords
- scratch resistance
- fitness equipment
- paint
- modified
- outdoor fitness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses outdoor fitness equipment paint with high scratch resistance. The outdoor fitness equipment paint is prepared from hydroxymethyl acrylic resin, carboxyl modified ternary vinyl chloride-vinyl acetate resin, polyacrylate latex, modified fly ash, pigment, lanolin alcohol, rice bran oil, palygorskite powder, ethyl maltol, sodium alginate, polyether modified organic siloxane, nano-silica and cerium oxide. Compared with the prior art, the outdoor fitness equipment paint has the following advantages that the two kinds of resin are used as main raw materials, and the abrasion and scratch resistance of the paint is improved; polyacrylate latex, lanolin alcohol, rice bran oil and ethyl maltol take synergistic effect, and therefore combinability between the paint and metal is improved; the modified fly ash is added and beneficial for enhancing scratch resistance after the paint using; a compact and hard coating is formed after the paint is used on the surface of metal and is smooth in surface, resistant to water and abrasion, good in scratch resistance and long in service life.
Description
Technical field
The invention belongs to the correlative technology field of body-building apparatus, be specifically related to a kind of outdoor fitness equipment coating with high scratch resistance.
Background technology
Raising along with people's living standard, people increasingly pursue the health of health, outdoor fitness equipment is widely used in park, square, the public places such as residential quarter, it is suitable for men and women, old and young to take exercise, increasing resident joins in various outdoor body-building, but outdoor it is arranged at for a long time due to body-building apparatus, long-term acceptance is exposed to the sun and rain, gradually cause coating aging, the adhesion strength of body-building apparatus face coat is poor at present, the most easily scratch, and after being scratched, easily cause full wafer coating shedding, the problem such as cause that equipment gets rusty, and then affect the use of body-building apparatus.
Summary of the invention
It is an object of the invention to for existing problem, it is provided that a kind of outdoor fitness equipment coating with high scratch resistance.
The present invention is achieved by the following technical solutions: a kind of outdoor fitness equipment coating with high scratch resistance, it is made up of the raw material of following weight portion: hydroxymethylacrylate resin 20-25 part, carboxy-modified ternary chlorine vinegar resin 18-24 part, polyacrylic ester latex 20-25 part, modified coal ash 5-8 part, pigment 2-6 part, lanolin alcohol 1-2 part, Testa oryzae oil 3-6 part, Paligorskite powder 4-6 part, ethylmaltol 2-4 part, sodium alginate 1-2 part, organic silicon modified by polyether oxygen alkane 2-4 part, nano silicon 3-6 part, cerium oxide 1-2 part；
Wherein, the preparation method of modified coal ash is: is put into by flyash in the drying plant that temperature is 120-150 DEG C and processes 5-6 hour, dried flyash water-bath heated and stirred is processed 3 hours by the hydrochloric acid solution then using mass concentration to be 16% under conditions of 75 DEG C, with deionized water rinsing until pH value is neutral after having processed；Adding and be equivalent to its weight 2-3% sodium molybdate, the Petiolus Trachycarpi oil of 1-2% and the silane coupler of 2-3%, stir 2-5 minute with high speed 1800-2000 rev/min, ovendry power is broken into superfines and get final product.
As further improvement of these options, the particle diameter of described Paligorskite powder is 20-40 μm, and the particle diameter of nano silicon is 60-80nm, and the particle diameter of cerium oxide is 8-15 μm.
The preparation method of a kind of outdoor fitness equipment coating with high scratch resistance comprises the following steps:
(1) hydroxymethylacrylate resin, carboxy-modified ternary chlorine vinegar resin, Paligorskite powder, nano silicon and cerium oxide are added in the water being equivalent to its weight portion 3 times, it is stirred until homogeneous dispersion, process 30-40 minute under conditions of supersonic frequency 26KHz, power 120W, obtain mixed material；
(2) process 8-15 minute under microwave frequency 2000MHz, power 800W after adding modified coal ash, sodium alginate and organic silicon modified by polyether oxygen alkane in said mixture material I, obtain mixed material II；
(3) in said mixture material II, add polyacrylic ester latex, lanolin alcohol, Testa oryzae oil and ethylmaltol mix and blend 15-20 minute under conditions of 75-85 DEG C, add pigment after being cooled to room temperature, after stirring 5-10 minute, obtain mixed material III；
(4) said mixture material III is put into ACM flour mill carries out classification pulverizing, cross 180 mesh sieves, get product.
In the present invention, the film forming thickness of the coating of preparation is 120-150 μm.
The present invention has the advantage that with two kinds of resins as primary raw material in the present invention compared to existing technology, improves the wear-resisting scratch-resistant performance of coating；Polyacrylic ester latex, lanolin alcohol, Testa oryzae oil and ethylmaltol synergism, strengthen the associativity of coating and metal；The interpolation of modified coal ash, contributes to strengthening the raising of resistance to marring after coating uses；This coating forms fine and close hard coating behind metal surface, and smooth surface, water proof and wearable, resistance to marring is good, and service life is long.
Detailed description of the invention
Embodiment 1
A kind of outdoor fitness equipment coating with high scratch resistance, is made up of the raw material of following weight portion: hydroxymethylacrylate resin 21 parts, carboxy-modified ternary chlorine vinegar resin 22 parts, polyacrylic ester latex 20 parts, modified coal ash 7 parts, pigment 4 parts, lanolin alcohol 2 parts, Testa oryzae oil 5 parts, 6 parts of Paligorskite powder, ethylmaltol 3 parts, sodium alginate 1 part, 4 parts of organic silicon modified by polyether oxygen alkane, nano silicon 3 parts, cerium oxide 2 parts；
Wherein, the preparation method of modified coal ash is: is put into by flyash in the drying plant that temperature is 120-150 DEG C and processes 5-6 hour, dried flyash water-bath heated and stirred is processed 3 hours by the hydrochloric acid solution then using mass concentration to be 16% under conditions of 75 DEG C, with deionized water rinsing until pH value is neutral after having processed；Adding and be equivalent to its weight 2-3% sodium molybdate, the Petiolus Trachycarpi oil of 1-2% and the silane coupler of 2-3%, stir 2-5 minute with high speed 1800-2000 rev/min, ovendry power is broken into superfines and get final product.
Wherein, the particle diameter of described Paligorskite powder is 20-40 μm, and the particle diameter of nano silicon is 60-80nm, and the particle diameter of cerium oxide is 8-15 μm.
The preparation method of a kind of outdoor fitness equipment coating with high scratch resistance comprises the following steps:
(1) hydroxymethylacrylate resin, carboxy-modified ternary chlorine vinegar resin, Paligorskite powder, nano silicon and cerium oxide are added in the water being equivalent to its weight portion 3 times, it is stirred until homogeneous dispersion, process 30-40 minute under conditions of supersonic frequency 26KHz, power 120W, obtain mixed material；
(2) process 8-15 minute under microwave frequency 2000MHz, power 800W after adding modified coal ash, sodium alginate and organic silicon modified by polyether oxygen alkane in said mixture material I, obtain mixed material II；
(3) in said mixture material II, add polyacrylic ester latex, lanolin alcohol, Testa oryzae oil and ethylmaltol mix and blend 15-20 minute under conditions of 75-85 DEG C, add pigment after being cooled to room temperature, after stirring 5-10 minute, obtain mixed material III；
(4) said mixture material III is put into ACM flour mill carries out classification pulverizing, cross 180 mesh sieves, get product.
In the present embodiment, the film forming thickness of the coating of preparation is 140 μm, and after testing, the highest resistible mass loading is 5N.
Embodiment 2
A kind of outdoor fitness equipment coating with high scratch resistance, is made up of the raw material of following weight portion: hydroxymethylacrylate resin 24 parts, carboxy-modified ternary chlorine vinegar resin 18 parts, polyacrylic ester latex 24 parts, modified coal ash 5 parts, pigment 4 parts, lanolin alcohol 2 parts, Testa oryzae oil 4 parts, 6 parts of Paligorskite powder, ethylmaltol 3 parts, sodium alginate 2 parts, 4 parts of organic silicon modified by polyether oxygen alkane, nano silicon 3 parts, cerium oxide 1 part；
Wherein, the preparation method of modified coal ash is: is put into by flyash in the drying plant that temperature is 120-150 DEG C and processes 5-6 hour, dried flyash water-bath heated and stirred is processed 3 hours by the hydrochloric acid solution then using mass concentration to be 16% under conditions of 75 DEG C, with deionized water rinsing until pH value is neutral after having processed；Adding and be equivalent to its weight 2-3% sodium molybdate, the Petiolus Trachycarpi oil of 1-2% and the silane coupler of 2-3%, stir 2-5 minute with high speed 1800-2000 rev/min, ovendry power is broken into superfines and get final product.
Its preparation method is in the same manner as in Example 1.
In the present embodiment, the film forming thickness of the coating of preparation is 150 μm, and after testing, the highest resistible mass loading is 5N.
Embodiment 3
A kind of outdoor fitness equipment coating with high scratch resistance, is made up of the raw material of following weight portion: hydroxymethylacrylate resin 22 parts, carboxy-modified ternary chlorine vinegar resin 22 parts, polyacrylic ester latex 20 parts, modified coal ash 6 parts, pigment 5 parts, lanolin alcohol 3 parts, Testa oryzae oil 4 parts, 4 parts of Paligorskite powder, ethylmaltol 3 parts, sodium alginate 1 part, 2 parts of organic silicon modified by polyether oxygen alkane, nano silicon 6 parts, cerium oxide 2 parts；
Wherein, the preparation method of modified coal ash is: is put into by flyash in the drying plant that temperature is 120-150 DEG C and processes 5-6 hour, dried flyash water-bath heated and stirred is processed 3 hours by the hydrochloric acid solution then using mass concentration to be 16% under conditions of 75 DEG C, with deionized water rinsing until pH value is neutral after having processed；Adding and be equivalent to its weight 2-3% sodium molybdate, the Petiolus Trachycarpi oil of 1-2% and the silane coupler of 2-3%, stir 2-5 minute with high speed 1800-2000 rev/min, ovendry power is broken into superfines and get final product.
Its preparation method is in the same manner as in Example 1.
In the present embodiment, the film forming thickness of the coating of preparation is 120 μm, and after testing, the highest resistible mass loading is 4.5N.
Claims (4)
1. an outdoor fitness equipment coating with high scratch resistance, it is characterised in that be made up of the raw material of following weight portion: hydroxymethylacrylate resin 20-25 part, carboxy-modified ternary chlorine vinegar resin 18-24 part, polyacrylic ester latex 20-25 part, modified coal ash 5-8 part, pigment 2-6 part, lanolin alcohol 1-2 part, Testa oryzae oil 3-6 part, Paligorskite powder 4-6 part, ethylmaltol 2-4 part, sodium alginate 1-2 part, organic silicon modified by polyether oxygen alkane 2-4 part, nano silicon 3-6 part, cerium oxide 1-2 part；
Wherein, the preparation method of modified coal ash is: is put into by flyash in the drying plant that temperature is 120-150 DEG C and processes 5-6 hour, dried flyash water-bath heated and stirred is processed 3 hours by the hydrochloric acid solution then using mass concentration to be 16% under conditions of 75 DEG C, with deionized water rinsing until pH value is neutral after having processed；Adding and be equivalent to its weight 2-3% sodium molybdate, the Petiolus Trachycarpi oil of 1-2% and the silane coupler of 2-3%, stir 2-5 minute with high speed 1800-2000 rev/min, ovendry power is broken into superfines and get final product.
A kind of outdoor fitness equipment coating with high scratch resistance, it is characterised in that the particle diameter of described Paligorskite powder is 20-40 μm, the particle diameter of nano silicon is 60-80nm, and the particle diameter of cerium oxide is 8-15 μm.
A kind of outdoor fitness equipment coating with high scratch resistance, it is characterised in that its preparation method comprises the following steps:
(1) hydroxymethylacrylate resin, carboxy-modified ternary chlorine vinegar resin, Paligorskite powder, nano silicon and cerium oxide are added in the water being equivalent to its weight portion 3 times, it is stirred until homogeneous dispersion, process 30-40 minute under conditions of supersonic frequency 26KHz, power 120W, obtain mixed material；
(2) process 8-15 minute under microwave frequency 2000MHz, power 800W after adding modified coal ash, sodium alginate and organic silicon modified by polyether oxygen alkane in said mixture material I, obtain mixed material II；
(3) in said mixture material II, add polyacrylic ester latex, lanolin alcohol, Testa oryzae oil and ethylmaltol mix and blend 15-20 minute under conditions of 75-85 DEG C, add pigment after being cooled to room temperature, after stirring 5-10 minute, obtain mixed material III；
(4) said mixture material III is put into ACM flour mill carries out classification pulverizing, cross 180 mesh sieves, get product.
A kind of outdoor fitness equipment coating with high scratch resistance, it is characterised in that the film forming thickness of coating is 120-150 μm.