CN105906993A - PVC (Polyvinyl Chloride) flame-retardant sheathing material - Google Patents
PVC (Polyvinyl Chloride) flame-retardant sheathing material Download PDFInfo
- Publication number
- CN105906993A CN105906993A CN201610501546.4A CN201610501546A CN105906993A CN 105906993 A CN105906993 A CN 105906993A CN 201610501546 A CN201610501546 A CN 201610501546A CN 105906993 A CN105906993 A CN 105906993A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame
- pvc
- retardant
- sheathing material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a PVC (Polyvinyl Chloride) flame-retardant sheathing material and relates to the technical field of cables. The PVC flame-retardant sheathing material is prepared from the following raw materials in parts by weight: 100 parts of PVC, 22 parts of DOP (Dioctyl-Phthalate), 5-10 parts of aluminum oxide, 2-15 parts of magnesium hydroxide and 1-5 parts of an anti-ageing agent. The cable material has the properties that the cable material is difficult to combust and can stop combustion; the flame-retardant grade can reach grade V-0; and in a combustion process, toxic substances containing halogen are not easy to generate and smoke dust is also not easy to generate, so that the PVC flame-retardant sheathing material is suitable for high-voltage and low-voltage power cables.
Description
Technical field
The invention belongs to field of cable technology, be specifically related to a kind of PVC flame-retardant sheath material.
Background technology
The most all flame-retardant sheath material can be increased at outer layer when power cable uses; to prevent cable breaking out of fire at accumulation amount of heat; and the cigarette that material produces when burning just; these cigarettes not only produce substantial amounts of noxious substance; and people can be caused to suffocate; this is only the principal element of death because of fire, and therefore research has the cable protective sleeve of good flame-retardance energy is the important topic preventing power cable fire.
Summary of the invention
It is an object of the invention to provide a kind of PVC flame-retardant sheath material.
In order to solve the problem in the presence of background technology, the present invention uses technical scheme as follows: it is that PVC100 part, DOP22 part, aluminium oxide 5-10 part, magnesium hydroxide 2-15 part, age resister 1-5 part are formulated by raw material.
The present invention has a following beneficial effect:
CABLE MATERIALS of the present invention have being difficult to burning can stop simultaneously burning performance, flame retardant rating, up to V-0 level, is not likely to produce halogen-containing noxious substance during burning, be not easy to produce flue dust, is applicable to high-low pressure power cable and uses.
Detailed description of the invention
Embodiment 1
By raw material be PVC100 part, DOP22 part, aluminium oxide 5 parts, 8 parts of magnesium hydroxide, age resister 1 part mixing after form by the uniform mixed preparing of double screw extruder, carry out pelletize through comminutor the most again.
Embodiment 2
By raw material be PVC100 part, DOP22 part, aluminium oxide 10 parts, 2 parts of magnesium hydroxide, age resister 5 parts mixing after form by the uniform mixed preparing of double screw extruder, carry out pelletize through comminutor the most again.
Embodiment 3
By raw material be PVC100 part, DOP22 part, aluminium oxide 9 parts, 15 parts of magnesium hydroxide, age resister 4 parts mixing after form by the uniform mixed preparing of double screw extruder, carry out pelletize through comminutor the most again.
Claims (4)
1. a PVC flame-retardant sheath material, it is characterised in that it is that PVC100 part, DOP22 part, aluminium oxide 5-10 part, magnesium hydroxide 2-15 part, age resister 1-5 part are formulated by raw material.
A kind of PVC flame-retardant sheath material the most according to claim 1, it is characterised in that described aluminium oxide is 9 parts.
A kind of PVC flame-retardant sheath material the most according to claim 1, it is characterised in that described magnesium hydroxide is 8 parts.
A kind of PVC flame-retardant sheath material the most according to claim 1, it is characterised in that described age resister is 4 parts.