CN105906271A - Cement foaming insulation plate - Google Patents

Cement foaming insulation plate Download PDF

Info

Publication number
CN105906271A
CN105906271A CN201610272505.2A CN201610272505A CN105906271A CN 105906271 A CN105906271 A CN 105906271A CN 201610272505 A CN201610272505 A CN 201610272505A CN 105906271 A CN105906271 A CN 105906271A
Authority
CN
China
Prior art keywords
parts
cement
decoction
foaming insulation
clear water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610272505.2A
Other languages
Chinese (zh)
Inventor
王秀银
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Huaipan New Building Material Technology Co Ltd
Original Assignee
Anhui Huaipan New Building Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Huaipan New Building Material Technology Co Ltd filed Critical Anhui Huaipan New Building Material Technology Co Ltd
Priority to CN201610272505.2A priority Critical patent/CN105906271A/en
Publication of CN105906271A publication Critical patent/CN105906271A/en
Pending legal-status Critical Current

Abstract

The invention provides a cement foaming insulation plate, and relates to the technical field of processing and production of walls. The cement foaming insulation plate is characterized by being prepared from the following materials in parts by weight: 60 parts of quick-setting cement, 14 parts of Portland cement, 1 part of hexabromocyclododecane, 3 parts of simethicone, 1 part of vinyl succinate, 8 parts of chromium slags, 4 parts of S95 mineral powder, 8 parts of 2mm pottery sand, 6 parts of industrial bone glue, 8 parts of quartz sand, 2 parts of methyl ethoxyl cellulose ether, 4 parts of orthoclase, 20 parts of an inorganic water-retaining agent, and 200 parts of clear water. A method is reasonable, operation is facilitated, and matching is reasonable.

Description

A kind of cement foaming insulation board
Technical field:
The present invention relates to body of wall processing technical field, be specifically related to a kind of cement foaming insulation board.
Background technology:
Warming plate say easy-to-understand be exactly insulation to building plank.And the cement in cement heat preserving plate is main raw material, typically it is used in body of wall, makes wallboard；The building structure of bearing system it is made up of wall and floor.Supporting member both made by wall, made again the partition in room, was the most frequently used in residential architecture and the version of less expensive.Shortcoming is that the motility that indoor plane is arranged is poor, for overcoming this shortcoming, currently develops to large bay direction.Panel structure is used for house, apartment, can also be used for the utilities building such as office building, school.The load bearing wall of panel structure can be made with brick, building block, prefabricated or cast-in-place concrete.Floor prefabricated reinforced concrete or prefabricated concrete hollow slab, trough plate, solid slab；Prefabricated with cast-in-place superposed type floor；Full cast-type floor.
And present production technology production is cumbersome, and the impurity in wallboard may be the most, and the life-span of use is not the longest, easily brings harm to inhabitation.
Summary of the invention:
The technical problem to be solved is to overcome existing technological deficiency to provide, and a kind of method is reasonable, easy to operate, a kind of cement foaming insulation board of reasonable mixture ratio.
The technical problem to be solved uses following technical scheme to realize:
A kind of cement foaming insulation board, it is characterised in that: it is made up of the material of following weight portion,
Quick hardening cement 60 parts, portland cement 14 parts, HBCD 1 part, dimethicone 3 parts, alkenyl succinic acid ester 1 part, chromium slag 8 parts, S95 breeze 4 parts, 2mm 8 parts of sand of pottery, industry 6 parts of osseocolla, quartz sand 8 parts, 2 parts of methyl hydroxyethylcellulose ether, potassium feldspar 4 parts, inorganic water-retaining agent 20 parts, 200 parts of clear water；
Including following preparation process,
Step one, first production equipment is carried out repair and maintenance, first no-load running 2min-3min, confirm normal after can use, it is ensured that the person and equipment safety；
Step 2, prepare raw material as requested, should ensure that raw material quality meets technological requirement；
Step 3, before production and processing, staff protected by preparation protection decoction, prevents intoxication conditions from occurring, oral first 50 minutes of work；
Step 4, arrangement pedestal, remove foreign material, brushing interleaving agent；
Step 5, the upper and lower reinforcing bar of stretch-draw, and extruder is in place；
Step 6, above-mentioned material is put into blender through metering, first put into other material, then put into two kinds of cement, dry stirring 2-3 minute, add water stirring 3-5 minute；
Step 7, by dumper, mix is added in forming machine hopper, extruded；
Step 8, on-the-spot maintenance, periodically should sprinkle water according to weather condition during maintenance.
Step 9, when reaching to have cut plate intensity, carry out fixed length cutting.
After step 10, cutting should on every block of wallboard the information such as labeling production date, specification, size, and make a record.
Step 11, it is taken up in order of priority batten one end is lifted gently the mobile demoulding when playing plate, then uniformly that plate is edge-on in side.
Step 12, should by edge-on for the plate of same production time, same specification winch to wooden handcart packing.
Step 13, product natural curing 28 days, can dispatch from the factory through after the assay was approved；
Described protection decoction is made up of the material of following weight portion,
Radix Et Rhizoma Rhei 1 part, 2 parts of Semen Armeniacae Amarum, 3 parts of Poria, CORTEX ZINGIBERIS RHIZOMAE 3 parts, Herba Lobeliae Chinensis 5 parts, Herba Leonuri 6 parts, Radix Cynanchi Atrati 7 parts, Herba Pteridis Multifidae 8 parts, Semen Arecae 9 parts, Radix Et Rhizoma Nardostachyos 10 parts, Rhizoma Cyperi 8 parts, the Fructus Sophorae 7 parts.Lignum Sappan 6 parts, Eupolyphaga Seu Steleophaga 5 parts, 8 parts of catechu, 3 parts of Radix Glycyrrhizae；
Preparation method: rinsed well by above-mentioned material clear water, be then placed in materials decoction device, the clear water of add quantity of material 2.5 times is cooked into decoction, and the amount of decoction is the 1/2 of the amount of clear water, and then filtering residue is administered orally.
The invention have the benefit that I material dust is little, processing method is simple；
II has made decoction can play the effect of protection staff, and long-term taking can also protect health；
III product is hard, resistance to compression, corrosion-resistant, curing cycle, length ensure that quality.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, the present invention is further elucidated below.
A kind of cement foaming insulation board, it is characterised in that: it is made up of the material of following weight portion,
Quick hardening cement 60 parts, portland cement 14 parts, HBCD 1 part, dimethicone 3 parts, alkenyl succinic acid ester 1 part, chromium slag 8 parts, S95 breeze 4 parts, 2mm 8 parts of sand of pottery, industry 6 parts of osseocolla, quartz sand 8 parts, 2 parts of methyl hydroxyethylcellulose ether, potassium feldspar 4 parts, inorganic water-retaining agent 20 parts, 200 parts of clear water；
Including following preparation process,
Step one, first production equipment is carried out repair and maintenance, first no-load running 2min-3min, confirm normal after can use, it is ensured that the person and equipment safety；
Step 2, prepare raw material as requested, should ensure that raw material quality meets technological requirement；
Step 3, before production and processing, staff protected by preparation protection decoction, prevents intoxication conditions from occurring, oral first 50 minutes of work；
Step 4, arrangement pedestal, remove foreign material, brushing interleaving agent；
Step 5, the upper and lower reinforcing bar of stretch-draw, and extruder is in place；
Step 6, above-mentioned material is put into blender through metering, first put into other material, then put into two kinds of cement, dry stirring 2-3 minute, add water stirring 3-5 minute；
Step 7, by dumper, mix is added in forming machine hopper, extruded；
Step 8, on-the-spot maintenance, periodically should sprinkle water according to weather condition during maintenance.
Step 9, when reaching to have cut plate intensity, carry out fixed length cutting.
After step 10, cutting should on every block of wallboard the information such as labeling production date, specification, size, and make a record.
Step 11, it is taken up in order of priority batten one end is lifted gently the mobile demoulding when playing plate, then uniformly that plate is edge-on in side.
Step 12, should by edge-on for the plate of same production time, same specification winch to wooden handcart packing.
Step 13, product natural curing 28 days, can dispatch from the factory through after the assay was approved；
Described protection decoction is made up of the material of following weight portion,
Radix Et Rhizoma Rhei 1 part, 2 parts of Semen Armeniacae Amarum, 3 parts of Poria, CORTEX ZINGIBERIS RHIZOMAE 3 parts, Herba Lobeliae Chinensis 5 parts, Herba Leonuri 6 parts, Radix Cynanchi Atrati 7 parts, Herba Pteridis Multifidae 8 parts, Semen Arecae 9 parts, Radix Et Rhizoma Nardostachyos 10 parts, Rhizoma Cyperi 8 parts, the Fructus Sophorae 7 parts.Lignum Sappan 6 parts, Eupolyphaga Seu Steleophaga 5 parts, 8 parts of catechu, 3 parts of Radix Glycyrrhizae；
Preparation method: rinsed well by above-mentioned material clear water, be then placed in materials decoction device, the clear water of add quantity of material 2.5 times is cooked into decoction, and the amount of decoction is the 1/2 of the amount of clear water, and then filtering residue is administered orally.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.Skilled person will appreciate that of the industry; the present invention is not restricted to the described embodiments; the principle that the present invention is simply described described in above-described embodiment and description; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements both fall within scope of the claimed invention.Claimed scope is defined by appending claims and equivalent thereof.

Claims (3)

1. a cement foaming insulation board, it is characterised in that: it is made up of the material of following weight portion,
Quick hardening cement 60 parts, portland cement 14 parts, HBCD 1 part, dimethicone 3 Part, alkenyl succinic acid ester 1 part, chromium slag 8 parts, S95 breeze 4 parts, 2mm 8 parts of sand of pottery, industry osseocolla 6 parts, quartz sand 8 parts, 2 parts of methyl hydroxyethylcellulose ether, potassium feldspar 4 parts, inorganic water-retaining agent 20 Part, 200 parts of clear water.
A kind of cement foaming insulation board the most according to claim 1, it is characterised in that: include following Preparation process,
Step one, first production equipment is carried out repair and maintenance, first no-load running 2min-3min, really Can use after recognizing normally, it is ensured that the person and equipment safety；
Step 2, prepare raw material as requested, should ensure that raw material quality meets technological requirement；
Step 3, before production and processing preparation protection decoction protect staff, prevent intoxication conditions Occur, within first 50 minutes, be administered orally in work；
Step 4, arrangement pedestal, remove foreign material, brushing interleaving agent；
Step 5, the upper and lower reinforcing bar of stretch-draw, and extruder is in place；
Step 6, by above-mentioned material through metering put into blender, first put into other material, then put into two kinds Cement, dry stirring 2-3 minute, add water stirring 3-5 minute；
Step 7, by dumper, mix is added in forming machine hopper, extruded；
Step 8, on-the-spot maintenance, periodically should sprinkle water according to weather condition during maintenance.
Step 9, when reaching to have cut plate intensity, carry out fixed length cutting.
After step 10, cutting should on every block of wallboard the information such as labeling production date, specification, size, and Make a record.
Step 11, it is taken up in order of priority the mobile demoulding is lifted, gently then in side in batten one end when playing plate Plate is the most edge-on.
Step 12, should by edge-on for the plate of same production time, same specification winch to wooden handcart packing.
Step 13, product natural curing 28 days, can dispatch from the factory through after the assay was approved.
A kind of cement foaming insulation board the most according to claim 1, it is characterised in that: described protection Decoction is made up of the material of following weight portion,
Radix Et Rhizoma Rhei 1 part, 2 parts of Semen Armeniacae Amarum, 3 parts of Poria, CORTEX ZINGIBERIS RHIZOMAE 3 parts, Herba Lobeliae Chinensis 5 parts, Herba Leonuri 6 parts, white Common vetch 7 parts, Herba Pteridis Multifidae 8 parts, Semen Arecae 9 parts, Radix Et Rhizoma Nardostachyos 10 parts, Rhizoma Cyperi 8 parts, the Fructus Sophorae 7 parts.Lignum Sappan 6 parts, Eupolyphaga Seu Steleophaga 5 parts, 8 parts of catechu, 3 parts of Radix Glycyrrhizae；
Preparation method: rinsed well by above-mentioned material clear water, be then placed in materials decoction device, adds The clear water of 2.5 times of quantity of material is cooked into decoction, and the amount of decoction is the 1/2 of the amount of clear water, and then filtering residue is administered orally ?.
CN201610272505.2A 2016-04-27 2016-04-27 Cement foaming insulation plate Pending CN105906271A (en)