CN105906021A - Preparing method for polymeric phosphate-ferric chloride water purifying agent - Google Patents
Preparing method for polymeric phosphate-ferric chloride water purifying agent Download PDFInfo
- Publication number
- CN105906021A CN105906021A CN201610461448.2A CN201610461448A CN105906021A CN 105906021 A CN105906021 A CN 105906021A CN 201610461448 A CN201610461448 A CN 201610461448A CN 105906021 A CN105906021 A CN 105906021A
- Authority
- CN
- China
- Prior art keywords
- ferric chloride
- purifying agent
- pyrite cinder
- poly
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparing method for a polymeric phosphate-ferric chloride water purifying agent. Raw materials include pyrite cinder, kieselguhr, hydrochloric acid and disodium hydrogen phosphate. Pyrite cinder is effectively used, waste is turned into wealth, and the problem that pyrite cinder is difficult to dispose is solved; an appropriate amount of phosphate radical is introduced into polymeric ferric chloride and has a polymerization enhancing effect on polymeric ferrum, the purifying effect is good, various pollutant components in water can be effectively treated, and the content of heavy metal and other harmful substances in water is reduced remarkably. The water purifying agent is mainly prepared from pyrite cinder and kieselguhr, is low in cost and free of secondary pollution, and has the advantages of being high in adsorption capacity, good in water purifying effect and high in water purifying speed.
Description
Technical field
The invention belongs to water treatment field, be specifically related to the preparation method of a kind of poly-phosphorus ferric chloride purifying agent.
Background technology
At present China's industrial sulphuric acid produces and mainly becomes sulfur dioxide by pyrite burning, purified, catalysis oxidation,
Absorb and prepare.Producing substantial amounts of pyrite cinder in roasting process, it is mainly composed of the oxide of ferrum, three oxidations two
Aluminum, silicon dioxide, the most also calcium oxide, magnesium oxide, lead, zinc, selenium, arsenic, phosphorus etc., not only land occupation, pollution environment, and
Cause underground water pollution, always one of difficult problem becoming Sulphuric Acid Enterprises.And the oxide of the ferrum in pyrite cinder, be prepare poly-
How one of raw material of phosphorus ferric chloride purifying agent, therefore, utilize pyrite cinder to prepare poly-phosphorus ferric chloride purifying agent, thus become useless
For treasured, it it is a direction of current pyrite cinder research.
Summary of the invention
In order to make up the deficiencies in the prior art, the invention provides a kind of poly-phosphorus ferric chloride purifying agent and preparation method thereof,
This water purification agent solves the reluctant problem of pyrite cinder, and it can effectively remove the pollutant component in water, and
Purification speed is fast, low cost.
The technical solution adopted in the present invention is as follows:
A kind of preparation method of poly-phosphorus ferric chloride purifying agent, produce the raw material of poly-phosphorus ferric chloride purifying agent include pyrite cinder,
Kieselguhr, hydrochloric acid and disodium hydrogen phosphate, concretely comprise the following steps:
(1) pyrite cinder and diatomite in powder are broken to 200~400 mesh, stand-by;
(2) in the reactor that pressure is 0.2~0.6Mpa, add hydrochloric acid, be heated to 45~65 DEG C;
(3) powder step (1) obtained adds in reactor, stirs 1~3 hour, filters and obtains liquor ferri trichloridi;
(4) disodium hydrogen phosphate is added in the liquor ferri trichloridi that step (3) obtains, be heated to 290~350 DEG C, stir 1~3
Hour, stand and cool to 20~30 DEG C, be subsequently adding water stirring and i.e. can get described poly-phosphorus ferric chloride purifying agent.
Further, in step (2), the mass fraction of hydrochloric acid is 25%~35%.
The present invention has a following beneficial effect:
The preparation method of the poly-phosphorus ferric chloride purifying agent of the present invention, it is achieved that the effective utilization to pyrite cinder, turns waste into wealth,
Solve the reluctant problem of pyrite cinder, and this water purification agent is by introducing appropriate phosphoric acid in poly-ferric chloride
Root, has the poly-effect of increasing, good purification, it is possible to be effectively treated the multiple pollutant component in water, significantly reduce to Polyferric Sulfate
The content of the harmful substance such as heavy metal in water, this water purification agent mainly uses pyrite cinder and kieselguhr to make, low cost, no
Can produce secondary pollution, its absorption affinity is strong simultaneously, has purifying water effect good, the fireballing feature of water purification.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described further:
Embodiment 1
According to the following parts by weight poly-phosphorus ferric chloride purifying agent of configuration: pyrite cinder 40 parts, 15 parts of kieselguhr, hydrochloric acid 200 parts,
Disodium hydrogen phosphate 50 parts.
The preparation method of above-mentioned poly-phosphorus ferric chloride purifying agent, comprises the following steps:
(1) pyrite cinder and diatomite in powder are broken to 400 mesh, stand-by;
(2) adding hydrochloric acid in the reactor that pressure is 0.5Mpa, the mass fraction of hydrochloric acid is 35%, is heated to 65 DEG C;
(3) powder step (1) obtained adds in reactor, stirs 2 hours, filters and obtains liquor ferri trichloridi;
(4) disodium hydrogen phosphate is added in the liquor ferri trichloridi that step (3) obtains, be heated to 350 DEG C, stir 1 hour, stand
Cool to 25 DEG C, be subsequently adding water stirring and i.e. can get described poly-phosphorus ferric chloride purifying agent.
Embodiment 2
According to the following parts by weight poly-phosphorus ferric chloride purifying agent of configuration: pyrite cinder 60 parts, 20 parts of kieselguhr, hydrochloric acid 250 parts,
Disodium hydrogen phosphate 70 parts.
The preparation method of above-mentioned poly-phosphorus ferric chloride purifying agent, comprises the following steps:
(1) pyrite cinder and diatomite in powder are broken to 300 mesh, stand-by;
(2) adding hydrochloric acid in the reactor that pressure is 0.3Mpa, the mass fraction of hydrochloric acid is 25%, is heated to 60 DEG C;
(3) powder step (1) obtained adds in reactor, stirs 2 hours, filters and obtains liquor ferri trichloridi;
(4) disodium hydrogen phosphate is added in the liquor ferri trichloridi that step (3) obtains, be heated to 350 DEG C, stir 1 hour, stand
Cool to 25 DEG C, be subsequently adding water stirring and i.e. can get described poly-phosphorus ferric chloride purifying agent.
Embodiment 3
According to the following parts by weight poly-phosphorus ferric chloride purifying agent of configuration: pyrite cinder 80 parts, 30 parts of kieselguhr, hydrochloric acid 350 parts,
Disodium hydrogen phosphate 90 parts.
The preparation method of above-mentioned poly-phosphorus ferric chloride purifying agent, comprises the following steps:
(1) pyrite cinder and diatomite in powder are broken to 200 mesh, stand-by;
(2) adding hydrochloric acid in the reactor that pressure is 0.5Mpa, the mass fraction of hydrochloric acid is 30%, is heated to 65 DEG C;
(3) powder step (1) obtained adds in reactor, stirs 2 hours, filters and obtains liquor ferri trichloridi;
(4) disodium hydrogen phosphate is added in the liquor ferri trichloridi that step (3) obtains, be heated to 300 DEG C, stir 2 hours, stand
Cool to 25 DEG C, be subsequently adding water stirring and i.e. can get described poly-phosphorus ferric chloride purifying agent.
Use the poly-phosphorus ferric chloride purifying agent of the present invention, it is achieved that the effective utilization to pyrite cinder, turn waste into wealth, solve
The reluctant problem of pyrite cinder of having determined, and this water purification agent is by introducing appropriate phosphate radical in poly-ferric chloride,
Polyferric Sulfate is had the poly-effect of increasing, good purification, it is possible to be effectively treated the multiple pollutant component in water, significantly reduce water
The content of the harmful substances such as middle heavy metal, this water purification agent mainly uses pyrite cinder and kieselguhr to make, and low cost, will not produce
Raw secondary pollution, its absorption affinity is strong simultaneously, has purifying water effect good, the fireballing feature of water purification.
Claims (2)
1. the preparation method of a poly-phosphorus ferric chloride purifying agent, it is characterised in that: produce the raw material bag of poly-phosphorus ferric chloride purifying agent
Include pyrite cinder, kieselguhr, hydrochloric acid and disodium hydrogen phosphate, concretely comprise the following steps:
(1) pyrite cinder and diatomite in powder are broken to 200~400 mesh, stand-by;
(2) in the reactor that pressure is 0.2~0.6Mpa, add hydrochloric acid, be heated to 45~65 DEG C;
(3) powder step (1) obtained adds in reactor, stirs 1~3 hour, filters and obtains liquor ferri trichloridi;
(4) disodium hydrogen phosphate is added in the liquor ferri trichloridi that step (3) obtains, be heated to 290~350 DEG C, stir 1~3
Hour, stand and cool to 20~30 DEG C, be subsequently adding water stirring and i.e. can get described poly-phosphorus ferric chloride purifying agent.
The preparation method of poly-phosphorus ferric chloride purifying agent the most according to claim 1, it is characterised in that: hydrochloric acid in step (2)
Mass fraction be 25%~35%.