CN105887263A - High-strength polyester filament and preparation method thereof - Google Patents
High-strength polyester filament and preparation method thereof Download PDFInfo
- Publication number
- CN105887263A CN105887263A CN201410751583.1A CN201410751583A CN105887263A CN 105887263 A CN105887263 A CN 105887263A CN 201410751583 A CN201410751583 A CN 201410751583A CN 105887263 A CN105887263 A CN 105887263A
- Authority
- CN
- China
- Prior art keywords
- polyester filament
- high strength
- filament yarn
- polyester
- strength polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength polyester filament and a preparation method thereof, and belongs to the field of textile materials. The high-strength polyester filament is formed by two layers of polyester filaments and steel wires of a rhombus grid structure arranged between the two layers of polyester filaments. Two strands of the two layers of polyester filaments are twisted to form a strand of high-strength polyester filament. The rhombus grid is formed by weaving the steel wires in a crossed mode. The high-strength polyester filament has the advantages of being high in strength and large in density, the wear-resisting property can be improved remarkably, and the manufacturing cost is low; according to an actual computer test, the service life of the polyester filament can be prolonged by 3-5years, and the polyester filament can be widely applied to the fields of automobile cushions, tents, beach rackets (chairs), shoe fabrics, cases, handbags and the like.
Description
Technical field
The present invention relates to textile material field, in particular, relate to a kind of high strength polyester filament yarn and
Preparation method.
Background technology
Viscose rayon experienced by the development of a century, becomes the important kind of textile fabric, but due to enterprise
Disparate development in terms of technology, product, uses Caustic soda in a large number in production process, therefore solve environment and protect
Problem of protecting occupies highly important position in viscose rayon produces；And the most domestic viscose rayon
Based on cotton pulp, wood pulp, bamboo pulp consumption are less, and domestic pulp yield is less, it is impossible to meet viscose glue enterprise
Demand, and the demand gap of domestic cotton linter is big, and supply presents nervous situation.
Along with the stable development of China's economy and the trend of globalization that day by day strengthens, domestic long filament market of washing needs
Ask powerful.High strength polyester filament yarn have high intensity, low elongation, corrosion-resistant go mouldy, heat stability,
The feature such as light resistance and good air permeability, can be used for automobile cushion, tent, sandy beach bat (chair), footwear face
The fields such as material, case and bag, handbag.
Summary of the invention
The technical problem to be solved is to provide a kind of high strength polyester filament yarn and preparation method thereof,
Realization has high intensity, density is big advantage, anti-wear performance significantly improve, the weaving that manufacturing cost is relatively low
Material.
The technical scheme is that a kind of high strength polyester filament yarn, including:
Described high strength polyester filament yarn uses two-layer polyester filament and is arranged at the Pedicellus et Pericarpium Trapae between two-layer polyester filament
The steel wire of shape network, becomes one high strength polyester filament yarn by bifilar two-layer polyester filament snarl.
Further, described network uses the braiding of described steel wire decussation to form.
Further, elastomeric material it is full of between described Double-layer polyester long filament.
The preparation method of a kind of high strength polyester filament yarn, it is characterised in that this step includes:
S1, employing 50-1100D high strength industrial polyester filament, the terylene preparing different diameters 1mm is long
Silk, nested composition two-layer polyester filament；
S2, steel wire decussation is woven into network structure, embeds Double-layer polyester long filament, and use bullet
Property material fill space；
S3, by two strands formed the Double-layer polyester long filaments containing network high-strength by being wound one
Degree polyester filament；
S4, the high strength polyester filament yarn of formation is smeared polyester material.
Further, described elastomeric material uses foam.
Beneficial effects of the present invention: there is high intensity, advantage that density is big, anti-wear performance significantly improves,
Manufacturing cost is relatively low, and through actual examination with computer, the polyester harness cord of the present invention is 3～5 years service life,
The fields such as automobile cushion, tent, sandy beach bat (chair), footwear coverings, case and bag, handbag can be widely used in.
Accompanying drawing explanation
Fig. 1 is overall structure schematic diagram of the present invention；
In accompanying drawing, the list of parts representated by each label is as follows:
100, polyester filament, 200, steel wire, 300, polyester filament.
Detailed description of the invention
Being described principle and the feature of the present invention below in conjunction with accompanying drawing, example is served only for explaining this
Invention, is not intended to limit the scope of the present invention.
As it is shown in figure 1, a kind of high strength polyester filament yarn, including: described high strength polyester filament yarn uses two
Layer polyester filament and the steel wire of network structure being arranged between two-layer polyester filament, by bifilar
Two-layer polyester filament snarl become one high strength polyester filament yarn.
Further, described network uses the braiding of described steel wire decussation to form.
Further, elastomeric material it is full of between described Double-layer polyester long filament.
The preparation method of a kind of high strength polyester filament yarn, it is characterised in that this step includes:
S1, employing 50-1100D high strength industrial polyester filament, the terylene preparing different diameters 1mm is long
Silk, nested composition two-layer polyester filament；
S2, steel wire decussation is woven into network structure, embeds Double-layer polyester long filament, and use bullet
Property material fill space；
S3, by two strands formed the Double-layer polyester long filaments containing network high-strength by being wound one
Degree polyester filament；
S4, the high strength polyester filament yarn of formation is smeared polyester material.
Further, described elastomeric material uses foam.
Compared with prior art, beneficial effects of the present invention: there is high intensity, advantage that density is big, resistance to
Mill performance significantly improves, manufacturing cost is relatively low, and through actual examination with computer, the polyester harness cord of the present invention uses the longevity
Life be 3～5 years, can be widely used in automobile cushion, tent, sandy beach clap (chair), footwear coverings,
The field such as case and bag, handbag.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all in the present invention
Spirit and principle within, any modification, equivalent substitution and improvement etc. made, should be included in this
Within bright protection domain.
Claims (5)
1. a high strength polyester filament yarn, it is characterised in that described high strength polyester filament yarn uses two-layer
Polyester filament and the steel wire of network structure being arranged between two-layer polyester filament, by bifilar
Two-layer polyester filament snarl becomes one high strength polyester filament yarn.
High strength polyester filament yarn the most according to claim 1, it is characterised in that described rhombus net
Lattice use the braiding of described steel wire decussation to form.
High strength polyester filament yarn the most according to claim 1, it is characterised in that described bilayer is washed
Elastomeric material it is full of between synthetic fibre long filament.
4. the preparation method of a high strength polyester filament yarn, it is characterised in that this step includes:
S1, employing 50-1100D high strength industrial polyester filament, the terylene preparing different diameters 1mm is long
Silk, nested composition two-layer polyester filament；
S2, steel wire decussation is woven into network structure, embeds Double-layer polyester long filament, and use bullet
Property material fill space；
S3, by two strands formed the Double-layer polyester long filaments containing network high-strength by being wound one
Degree polyester filament；
S4, the high strength polyester filament yarn of formation is smeared polyester material.
The preparation method of high strength polyester filament yarn the most according to claim 1, it is characterised in that
Described elastomeric material uses foam.