CN105886080A - Modified nano material lubricating oil - Google Patents
Modified nano material lubricating oil Download PDFInfo
- Publication number
- CN105886080A CN105886080A CN201610270210.1A CN201610270210A CN105886080A CN 105886080 A CN105886080 A CN 105886080A CN 201610270210 A CN201610270210 A CN 201610270210A CN 105886080 A CN105886080 A CN 105886080A
- Authority
- CN
- China
- Prior art keywords
- lubricating oil
- base oil
- oil
- synergist
- graphite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to modified nano material lubricating oil which is prepared from hydrogenated base oil, a compound dispersant, a solid lubricant agent and a synergist. The hydrogenated base oil is 150 N or 250 N base oil, the solid lubricant agent is prepared from graphite below 3 um and molybdenum disulfide, the compound dispersant is prepared from polyisobutylene succinimide, boronized polyisobutylene-bis-succinimide, polyisobutylene, an ethylene-propylene copolymer, synthetic petroleum sodium sulfonate, polymethacrylate and poly-alpha olefin through compounding, and the synergist is an extreme-pressure agent, an oxidation and corrosion inhibitor, a defoaming agent or a tackifier. The lubricating oil contains, in percentage, 50-80% of the hydrogenated base oil, 0.5-1% of graphite, 1-5% of molybdenum disulfide, 6-12% of the compound dispersant and 6-15% of the synergist. The product can reduce the mechanical friction, repair abraded portions and prolong the service life of equipment, and the lubricating oil has the good effect of oil saving rate up to 5-15% when applied to a vehicle engine.
Description
Technical field
The present invention relates to a kind of modified Nano material lubricating oil, belong to technical field of lubricating oil.
Background technology
The most conventional extreme pressure anti-wear additives such as sulfur-bearing, phosphorus, chlorine isoreactivity organic compound and organo-metallic compound is in friction
During intensification, the product of these compounds and decomposition can have corrosiveness to metal bearing, and raise in temperature is to consume to make simultaneously
Performance reduces.Also have the application of new technique organic-molybdenum, because high temperature and high load capacity and decomposition failure, there is no repair.
Solid lubricant such as graphite and molybdenum bisuphide is because the dispersion of granule disaster is promoted the most widely all the time.
Graphite, molybdenum bisuphide are as lube oil additive, to demonstrate good greasy property in friction process, no
The form and the granularity that require nothing more than granule are wanted suitably and it is necessary to can be dispersed stably in lubricating oil, once occur to be separated,
Graphite is easy for being difficult to because of reunion play its greasy property.
Summary of the invention
It is an object of the invention to provide a kind of modified Nano material lubricating oil, main by chemical method and physical method pair
Graphite, molybdenum bisuphide are modified, and use the composite dispersing agent of uniqueness simultaneously, thoroughly solve graphite and go out in allocation process
Existing sedimentation problem.
To achieve these goals, technical scheme is as follows.
A kind of modified Nano material lubricating oil, by hydrogenated base oil, composite dispersing agent, solid lubrication oil preparation and synergist group
Becoming, wherein, hydrogenated base oil is 150N or 250N base oil, solid lubrication oil preparation by the graphite of below 3um and
Molybdenum bisuphide forms, and composite dispersing agent is by polyisobutene succinimide, boronation polyisobutylene-bis-succinimide, poly-different
Butylene, ethylene-propylene copolymer, synthetic petroleum sodium sulfonate, polymethacrylates and polyalphaolefin are composited, and synergist is
Extreme pressure agent, oxidation and corrosion inhibitor, defoamer and viscosifier.
In above-mentioned lubricating oil, its percentage composition is: hydrogenated base oil 50~80%, graphite 0.5~1%, molybdenum bisuphide 1~
5%, composite dispersing agent is 6~12%, and synergist is 6~15%.
The concrete preparation process of above-mentioned lubricating oil is:
(1) solid lubrication mix wetting process: by the hydrogenated base oil of above-mentioned mass percent half, graphite, two sulfur
Changing molybdenum and synergist to utilize and be pumped in agitator tank, speed of agitator is 800~1000r/min, mixing time be 1.5~
2h;
(2) dispersant preprocessing process: by above-mentioned mass percent second half base oil and composite dispersing agent put into super
Carrying out heating dilution in acoustic wave oscillator, temperature stabilization controls at 60 degree;
(3) stable dispersion solves aggregation procedure: material step 1 and 2 handled well utilizes and is pumped to high speed shear breast
Change in tank, emulsification pretreatment 3.5~4h;
(4) filtration cools down and i.e. obtains this product.
The mechanism of action of the present invention: solid lubricant is affected by frictional force produced between sliding surface in lubricating oil,
Its laminated crystalline result is easily sheared, and this is the reason absorbing friction stree.Because solid material physical and chemical performance is each
Variant, the contribution to lubrication is the most different, and name has extremely strong physical and chemical stability in this way, and high temperature lubricating ratio is low
Gentle lubricating oil is good;Molybdenum bisuphide low-temperature lubrication is better than high temperature lubricating.According to different use requirements, the most multiple
Solid constituent, carries out compounded combination in optimum amount ratio, it is possible to obtain the excellent lubrication effect learn from other's strong points to offset one's weaknesses, being mutually improved
Really.
This beneficial effect of the invention is: graphite, molybdenum bisuphide solid wear resistant material in this product, is attached to metal surface,
Play the effect of sufficient lubrication.At present, solid lubrication oil preparation is few in number in the world, and due to its dispersion and base oil
Unstable properties, all can cause precipitating in 15 days, and this product uses unique formula to solve this problem, is it
His any product is irreplaceable.The absorption of this protecting film plays extreme pressure high temperature resistant, anti-and abnormal the most wear-resisting in engine surface,
Therefore have anti-friction, anti-attrition, cooling, noise reduction, energy-saving and cost-reducing, improve power, reduce equipment failure rate, prolonged mechanical
The miraculous effects in service life.Application range of products: automobile, train, steamer and motorcycle engine;Engineering truck,
Winning equipment and there is a need to oil, fat are as the plant equipment of lubricant medium.At bus, truck addition 5-10%,
Individual vehicle add in 6% ratio after DeGrain, or burn oil, obvious waste gas the vehicle of serious wear such as exceeds standard,
Can consider and add 3%-6% again.Plant equipment uses, can first add in lubricating oil in the ratio of 3%-6%, or
Use with grease stirring in proportion.Mechanical friction reparation abrasion and extension device service life can be reduced.Apply to car
Engines fuel-economizing rate reaches the good result of about 5-15%.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
In the following example, being respectively adopted different ratio and carry out dispensing, proportioning is as shown in table 1.
Table 1: the proportioning of different material
The concrete preparation process of above-mentioned lubricating oil is:
(1) solid lubrication mix wetting process: by the hydrogenated base oil of above-mentioned mass percent half, graphite, two sulfur
Changing molybdenum and synergist to utilize and be pumped in agitator tank, speed of agitator is 800~1000r/min, mixing time be 1.5~
2h;
(2) dispersant preprocessing process: by above-mentioned mass percent second half base oil and composite dispersing agent put into super
Carrying out heating dilution in acoustic wave oscillator, temperature stabilization controls at 60 degree;
(3) stable dispersion solves aggregation procedure: material step 1 and 2 handled well utilizes and is pumped to high speed shear breast
Change in tank, emulsification pretreatment 3.5~4h;
(4) filtration cools down and i.e. obtains this product.
Detecting for above-mentioned lubricating oil, testing result is as shown in table 2:
Table 2:
And carry out actual road performance test, result is as shown in table 3:
Table 3:
Vehicle | License plate number | Stroke (kilometer) | Volume read-out (rises) | Hundred kilometers of oil consumptions | Oil consumption reduces |
Liberation 50 | Shandong fv3230 | 11827 | 4299 | 36 | 12% |
Liberation 50 | Shandong fv3047 | 8490 | 3588 | 42 | 6% |
Liberation 50 | Shandong fv3253 | 11517 | 4617 | 40 | 8% |
Great Wall pick up | Shandong f7x21 | 12256 | 796 | 6.5 | 11% |
Visible, the lubricating oil in the present invention shows preferably performance.
The above is the preferred embodiment of the present invention, it is noted that come for those skilled in the art
Saying, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications also regard
For protection scope of the present invention.
Claims (3)
1. a modified Nano material lubricating oil, it is characterised in that: by hydrogenated base oil, composite dispersing agent, solid profit
Lubricating oil agent and synergist composition, wherein, hydrogenated base oil is 150N or 250N base oil, solid lubrication oil preparation by
The graphite of below 3um and molybdenum bisuphide composition, composite dispersing agent is double by polyisobutene succinimide, boronation polyisobutylene
Succimide, polyisobutylene, ethylene-propylene copolymer, synthetic petroleum sodium sulfonate, polymethacrylates and polyalphaolefin are multiple
Conjunction forms, and synergist is extreme pressure agent, oxidation and corrosion inhibitor, defoamer and viscosifier.
Modified Nano material lubricating oil the most according to claim 1, it is characterised in that: in described lubricating oil, its
Percentage composition is: hydrogenated base oil 50~80%, graphite 0.5~1%, molybdenum bisuphide 1~5%, composite dispersing agent be 6~
12%, synergist is 6~15%.
Modified Nano material lubricating oil the most according to claim 1, it is characterised in that: described lubricating oil is specifically made
Standby process is:
(1) solid lubrication mix wetting process: by the hydrogenated base oil of above-mentioned mass percent half, graphite, two sulfur
Changing molybdenum and synergist to utilize and be pumped in agitator tank, speed of agitator is 800~1000r/min, mixing time be 1.5~
2h;
(2) dispersant preprocessing process: by above-mentioned mass percent second half base oil and composite dispersing agent put into super
Carrying out heating dilution in acoustic wave oscillator, temperature stabilization controls at 60 degree;
(3) stable dispersion solves aggregation procedure: material step 1 and 2 handled well utilizes and is pumped to high speed shear breast
Change in tank, emulsification pretreatment 3.5~4h;
(4) filtration cools down and i.e. obtains this product.