CN105885648A - Self-cleaning high-dispersivity powder paint for coiled material and preparation method thereof - Google Patents
Self-cleaning high-dispersivity powder paint for coiled material and preparation method thereof Download PDFInfo
- Publication number
- CN105885648A CN105885648A CN201610305309.0A CN201610305309A CN105885648A CN 105885648 A CN105885648 A CN 105885648A CN 201610305309 A CN201610305309 A CN 201610305309A CN 105885648 A CN105885648 A CN 105885648A
- Authority
- CN
- China
- Prior art keywords
- parts
- coiled material
- powdery paints
- powder paint
- dispersivity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of powder paint, in particular to self-cleaning high-dispersivity powder paint for a coiled material and a preparation method thereof. The self-cleaning high-dispersivity powder paint for the coiled material is prepared from the following raw materials in parts by weight: 45 to 85 parts of low-temperature weather-proof polyester resin, 2 to 8 parts of TGIC (triglycidyl isocyanurate) or HAA (hydroxy-acid amide), 2 to 12 parts of bisphenol A type epoxy resin, 0.2 to 2.4 parts of PVDF (polyvinylidene fluoride) thermoplastic fluorocarbon resin, 0.1 to 1.2 parts of nanometer aluminum oxide, 0.6 to 5.5 parts of nanometer calcium carbonate, 0.6 to 1.5 parts of acrylic ester flatting agents, 0.03 to 0.8 part of quaternary ammonium salt accelerant, 0.5 to 26 parts of pigment, 0 to 45 parts of fillers and 0.1 to 3 parts of other auxiliary agents. The powder paint has the characteristics that the dispersivity is good; caking cannot easily occur; the storage is easy; the coated film of the powder paint has strong anti-staining capability; the cleaning is easy; the adhesion force is strong; the surface is flat.
Description
Technical field
The present invention relates to powder coating technology field, be specifically related to a kind of automatically cleaning polymolecularity coiled material powdery paints and preparation thereof
Method.
Background technology
Powdery paints owing to having the advantage of environmental protection and superior performance, in the past few decades in, it is at metallic article and thermal sensitivity
Material product has obtained Rapid Popularization application.And the application of coiled material surface is owing to requiring application speed fast, its linear velocity exists
About 100m/min, and the inherent character of powdery paints ratio is relatively inaccessible to this requirement, therefore powdery paints answering on coil painting
With being constantly subjected to restriction.In recent years, along with the environmental consciousness of people and improving constantly of government's environmental requirement, find a kind of environmental protection
Application mode replace the process by oil paint application coiled material extremely urgent.Wherein now research more for water paint
Application and powder coating and their application, the inherent character such as its hardness of water paint is difficult to meet the requirement of coil painting, therefore limit its
Application in coil painting.And the research that powdery paints is in this field is broadly divided into powdery paints and the modification of resin used by it
With two aspects of research to coil coating technology and equipment.
Open a kind of pre-coated metal coiled material powdery paints of Chinese patent CN105038525 and its preparation method and application, it is to powder
End coating has carried out modification, makes the popularization and application that powdery paints is more suitable in coil painting.Chinese patent CN103555170 is public
Open a kind of hydroxy resin using isocyanates, organotin and ammonia and coordinate the fast setting coiled material powdery paints and production thereof obtained
Method.Chinese patent CN105273581 is open a kind of former with other by polyester resin and polyester modification fluorocarbon resin and firming agent
High IR fast setting coil powdery paints that material is prepared as and preparation method thereof.Above patent all discloses coiled material powder
Coating and preparation method thereof.Less yet with coiled material powdery paints particle diameter, typically at 15 microns, powdery paints disperses
Bad, easy conglomeration and be difficult to store, therefore, limit its further genralrlization in coil painting application.It addition, volume
Material uses the most out of doors, is easily subject to the pollution of dust rainwater etc., not easy cleaning.
Summary of the invention
It is an object of the invention to provide the automatically cleaning polymolecularity coiled material powdery paints that a kind of stain resistance is strong, solve coiled material powder
End coating less due to particle diameter, disperse bad, easy conglomeration and be difficult to storage technical problem, the powdery paints of the present invention simultaneously
There is stain resistance strong, characteristic easy to clean, solve technical problem the most easy to clean during coiled material uses;Present invention simultaneously provides
Its preparation method.
Automatically cleaning polymolecularity coiled material powdery paints of the present invention, is made up of the raw material of following parts by weight:
The described SJ5700 that low temperature weather polyester resin is Anhui Shen Jian new material company.
Described HAA is the T105 of South Sea chemical company.
Described TGIC is the TGIC of Niu Tang Chemical Co., Ltd..
Described bisphenol A type epoxy resin is the 904H of Hong Chang Electron Material Co., Ltd.
The described PVDF that PVDF fluorocarbon resin is Shandong Dongyue Chemical Co., Ltd..
The preparation method of described automatically cleaning polymolecularity coiled material powdery paints is by addition to nano aluminium oxide and nano-calcium carbonate
All raw material through premixing, melt extrude, cool down tabletting, pulverizing pulverize and separation sieve, control its particle diameter D50 and exist
Between 10-20 micron, be eventually adding nano aluminium oxide, nano-calcium carbonate is sufficiently mixed.
The powdery paints of the present invention has scattered, is difficult to conglomeration and easily stores, and the film of powdery paints has stain resistance simultaneously
By force, easy to clean, adhesive force is good, the characteristic of surfacing, and its main technical principle is as follows:
(1) powdery paints of the present invention with the addition of nano aluminium oxide and nano-calcium carbonate mixed dispersant, nanoscale mixed dispersant
The coiled material powder coating particles that particle diameter is less is played coating function by particle, it is therefore prevented that the interaction force between powder coating particles,
It is achieved thereby that powdery paints is scattered, it is difficult to conglomeration and the characteristic easily stored.And two kinds of nano materials are added by specific proportioning
Add, eliminate its impact on other performances of powdery paints.
(2) with the addition of PVDF thermoplastic fluorocarbon resin in powdery paints of the present invention, in powdery paints, curing system melts laggard
During row crosslinking curing, PVDF is not participate in chemical reaction, and melted PVDF can float to film coated surface,
On the one hand being conducive to the levelling effect of film coated surface, on the other hand, the PVDF floating to surface makes film have relatively low table
Face energy, therefore, it is possible to play preferable automatically cleaning effect, and the PVDF on surface makes film can produce preferable weatherability,
Improve the weather-proof time limit of coating.
(3) with the addition of the epoxy resin of certain proportioning in powdery paints of the present invention, it can melt levelling more quickly, is conducive to
The levelling effect of film coated surface, and epoxy resin and coiled material ground have more preferable adhesion, it is possible to effectively strengthen film and volume
Adhesive force between material.
Beneficial effects of the present invention is as follows:
The powdery paints of the present invention is scattered, is difficult to conglomeration and easily stores, and the film that the powdery paints of the present invention prepares has anti-soil
Ability is strong, characteristic easy to clean, and weather-proof ability is excellent;Attachment between film and coiled material that the powdery paints of the present invention prepares
Power is good, film difficult drop-off;The powdery paints of the present invention has the characteristic that melt temperature is relatively low, viscosity is low, easily realizes coiled material
Surface surpasses the application of levelling effect, and its preparation method is simple, it is easy to accomplish.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described further.
Embodiment 1
Powdery paints in the present embodiment, is made up of the raw material of following parts by weight:
By above-mentioned all raw material in addition to nano aluminium oxide and nano-calcium carbonate through premixing, melt extrude, cool down tabletting,
Pulverizing is pulverized and separation is sieved, and controls its particle diameter D50 at 15 microns, is eventually adding nano aluminium oxide, nano-calcium carbonate abundant
Mix.
Embodiment 2
Powdery paints in the present embodiment, is made up of the raw material of following parts by weight:
By above-mentioned all raw material in addition to nano aluminium oxide and nano-calcium carbonate through premixing, melt extrude, cool down tabletting,
Pulverizing is pulverized and separation is sieved, and controls its particle diameter D50 at 18 microns, is eventually adding nano aluminium oxide, nano-calcium carbonate abundant
Mix.
Embodiment 3
Powdery paints in the present embodiment, is made up of the raw material of following parts by weight:
By above-mentioned all raw material in addition to nano aluminium oxide and nano-calcium carbonate through premixing, melt extrude, cool down tabletting,
Pulverizing is pulverized and separation is sieved, and controls its particle diameter D50 at 13 microns, is eventually adding nano aluminium oxide, nano-calcium carbonate abundant
Mix.
Table 1 embodiment product correlated performance test result
As shown in Table 1, the automatically cleaning polymolecularity coiled material powdery paints that embodiment 1-3 obtains has scattered, be difficult to conglomeration and
The characteristic easily stored, the film of powdery paints has stain resistance by force simultaneously, and easy to clean, adhesive force is good, the characteristic of surfacing.
Combination property meets or is better than national standard.
Claims (5)
1. an automatically cleaning polymolecularity coiled material powdery paints, it is characterised in that: it is made up of the raw material of following parts by weight:
Automatically cleaning polymolecularity coiled material powdery paints the most according to claim 1, it is characterised in that: low temperature weather gathers
Ester resin is SJ5700.
Automatically cleaning polymolecularity coiled material powdery paints the most according to claim 1, it is characterised in that: HAA is T105.
Automatically cleaning polymolecularity coiled material powdery paints the most according to claim 1, it is characterised in that: bisphenol A-type ring
Epoxy resins is 904H.
5. a preparation method for the arbitrary described automatically cleaning polymolecularity coiled material powdery paints of claim 1-4, its feature exists
In: by all raw material in addition to nano aluminium oxide and nano-calcium carbonate through premixing, melt extrude, cool down tabletting, mill
Powder is pulverized and separation is sieved, and controls its particle diameter D50 between 10-20 micron, is eventually adding nano aluminium oxide, nano-calcium carbonate
It is sufficiently mixed.