CN105885314A - Nano cellulose composite packaging film and preparation method thereof - Google Patents
Nano cellulose composite packaging film and preparation method thereof Download PDFInfo
- Publication number
- CN105885314A CN105885314A CN201610334497.XA CN201610334497A CN105885314A CN 105885314 A CN105885314 A CN 105885314A CN 201610334497 A CN201610334497 A CN 201610334497A CN 105885314 A CN105885314 A CN 105885314A
- Authority
- CN
- China
- Prior art keywords
- cellulose composite
- nano
- preparation
- packing film
- composite packing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a nano cellulose composite packaging film and a preparation method thereof. The preparation method comprises the following steps: (1) mixing ramie fiber, bamboo fiber and deionized water, and grinding with a grinder; (2) homogenizing in a high-pressure homogenizer; (3) filtering and discarding large-particle fiber; (4) mixing the filtrate with polyvinyl alcohol, aluminum silicate, hydroxypropyl methyl cellulose, butyl p-hydroxybenzoate, lauramide propyl betaine, alkylphenol polyoxyethylene ether, decabromodiphenyl ether, dibutyl hydroxytoluene, citric acid, sodium dehydroacetate and rosin resin, putting in a water bath and stirring with a stirrer; (5) standing, removing bubbles and slowly stirring and dispersing with the stirrer; (6) performing film casting of the mixed solution on a base material; and (7) drying in a vacuum drying oven. The nano cellulose composite packaging film provided by the invention has relatively good mechanical properties, strong stretch-proof property, good elasticity and toughness and good transparency and can show a product perfectly.
Description
Technical field
The present invention relates to Material Field, be specifically related to a kind of nano-cellulose composite packing film and preparation method thereof.
Background technology
Along with the fast development of economic society, the development of all trades and professions have also been obtained the biggest progress, especially the Internet
Industry, presents a kind of attitude developed by leaps and bounds, meanwhile, the extensive utilization of the Internet, has also driven a lot of other industry
High speed development, such as packaging industry.Simultaneously also with the raising of people's living standard, for product packaging requirement the most increasingly
Height, does not require nothing more than packaging material and has certain defencive function, the most most basic mechanical property, simultaneously for it functionally
Require it is also more and more harsh.And the transparency of packaging material can show product well, consumer can be by concrete
Seeing the profile of product, color and luster judges whether to need to buy.Therefore, the transparency of packaging material extraordinary can show product
The value of product, is of value to sale, so that consumer and seller are the most benefited.
Summary of the invention
Solve the technical problem that: it is an object of the invention to provide a kind of nano-cellulose composite packing film, have relatively
Good mechanical property, stretch resistance is strong, and elasticity and toughness are good, and excellent transparency simultaneously can show product well.
Technical scheme: a kind of nano-cellulose composite packing film, is prepared from weight portion by following component: Boehmeria is fine
Dimension 1-3 part, bamboo fibre 1-2 part, polyvinyl alcohol 15-25 part, aluminium silicate 1-2 part, hydroxypropyl methyl cellulose 2-4 part, to hydroxyl
Butyl benzoate 0.2-0.4 part, lauroylamidopropyl betaine 1-2 part, alkylphenol polyoxyethylene 2-4 part, decabromodiphenyl oxide
1-2 part, dibenzylatiooluene 0.1-0.3 part, citric acid 0.2-0.5 part, dehydroactic acid sodium 0.2-0.5 part, rosin resin
0.2-0.4 part, deionized water 200-300 part.
It is further preferred that described a kind of nano-cellulose composite packing film, following component prepare with weight portion
Form: ramee 1.5-2.5 part, bamboo fibre 1.2-1.8 part, polyvinyl alcohol 17-23 part, aluminium silicate 1.1-1.7 part, hydroxypropyl
Methylcellulose 2.5-3.5 part, butyl p-hydroxybenzoate 0.25-0.35 part, lauroylamidopropyl betaine 1.2-1.8 part,
Alkylphenol polyoxyethylene 2.5-3.5 part, decabromodiphenyl oxide 1.3-1.7 part, dibenzylatiooluene 0.15-0.25 part, Fructus Citri Limoniae
Acid 0.3-0.4 part, dehydroactic acid sodium 0.3-0.4 part, rosin resin 0.25-0.35 part, deionized water 220-280 part.
The preparation method of above-mentioned nano-cellulose composite packing film comprises the following steps:
(1) ramee, bamboo fibre and deionized water are mixed, be ground 10-30 minute with grinder;
(2) loading high pressure homogenizer carries out homogenizing 10-30 minute;
(3) filter, discard bulky grain fiber;
(4) filtrate and remaining ingredient are mixed, put in 80-90 DEG C of water-bath, enter under rotating speed 300-400r/min with blender
Row stirring 20-40 minute;
(5) stand, slough bubble, be slowly stirred dispersion with blender;
(6) mixed solution is carried out on base material casting film-forming;
(7) put in vacuum drying oven, be dried 14-17 hour at temperature 50-60 DEG C and get final product.
It is further preferred that milling time is 15-25 minute in step (1).
It is further preferred that homogenizing time is 15-25 minute in step (2).
It is further preferred that bath temperature is 85 DEG C in step (4), speed of agitator is 350r/min, and mixing time is 25-
35 minutes.
It is further preferred that temperature is 55 DEG C in step (7), drying time is 15-16 hour.
Beneficial effect: the nano-cellulose composite packing film of the present invention has preferable mechanical property, its hot strength
May be up to 146MPa, stretch resistance is strong, and elastic modelling quantity is 7.15GPa, and elasticity and toughness are good, meanwhile, and its printing opacity at 600nm
Rate also in about 84.3-84.4%, excellent transparency, can show product well.
Detailed description of the invention
Embodiment 1
A kind of nano-cellulose composite packing film, is prepared from weight portion by following component: ramee 1 part, bamboo fibre 1
Part, polyvinyl alcohol 15 parts, aluminium silicate 1 part, hydroxypropyl methyl cellulose 2 parts, butyl p-hydroxybenzoate 0.2 part, lauramide
CAB 1 part, alkylphenol polyoxyethylene 2 parts, decabromodiphenyl oxide 1 part, dibenzylatiooluene 0.1 part, citric acid 0.2
Part, 0.2 part of dehydroactic acid sodium, rosin resin 0.2 part, deionized water 200 parts.
The preparation method of above-mentioned nano-cellulose composite packing film is: (1) is by ramee, bamboo fibre and deionized water
Mixing, is ground 10 minutes with grinder;(2) loading high pressure homogenizer carries out homogenizing 10 minutes;(3) filter, discard big
Particulate fibrous;(4) filtrate and remaining ingredient are mixed, put in 80 DEG C of water-baths, carry out under rotating speed 300r/min with blender
Stir 20 minutes;(5) stand, slough bubble, be slowly stirred dispersion with blender;(6) mixed solution is flowed on base material
Prolong film forming;(7) put in vacuum drying oven, be dried 14 hours under temperature 50 C and get final product.
Embodiment 2
A kind of nano-cellulose composite packing film, is prepared from weight portion by following component: ramee 1.5 parts, bamboo fibre
Tie up 1.2 parts, polyvinyl alcohol 17 parts, aluminium silicate 1.1 parts, hydroxypropyl methyl cellulose 2.5 parts, butyl p-hydroxybenzoate 0.25
Part, lauroylamidopropyl betaine 1.2 parts, alkylphenol polyoxyethylene 2.5 parts, decabromodiphenyl oxide 1.3 parts, butylated hydroxy-a
Benzene 0.15 part, citric acid 0.3 part, 0.3 part of dehydroactic acid sodium, rosin resin 0.25 part, deionized water 220 parts.
The preparation method of above-mentioned nano-cellulose composite packing film is: (1) is by ramee, bamboo fibre and deionized water
Mixing, is ground 15 minutes with grinder;(2) loading high pressure homogenizer carries out homogenizing 15 minutes;(3) filter, discard big
Particulate fibrous;(4) filtrate and remaining ingredient are mixed, put in 85 DEG C of water-baths, carry out under rotating speed 350r/min with blender
Stir 25 minutes;(5) stand, slough bubble, be slowly stirred dispersion with blender;(6) mixed solution is flowed on base material
Prolong film forming;(7) put in vacuum drying oven, be dried 15 hours at temperature 55 DEG C and get final product.
Embodiment 3
A kind of nano-cellulose composite packing film, is prepared from weight portion by following component: ramee 2 parts, bamboo fibre
1.5 parts, polyvinyl alcohol 20 parts, aluminium silicate 1.5 parts, hydroxypropyl methyl cellulose 3 parts, butyl p-hydroxybenzoate 0.3 part, Laurel
Amido propyl betaine 1.5 parts, alkylphenol polyoxyethylene 3 parts, decabromodiphenyl oxide 1.5 parts, dibenzylatiooluene 0.2 part,
Citric acid 0.35 part, 0.35 part of dehydroactic acid sodium, rosin resin 0.3 part, deionized water 250 parts.
The preparation method of above-mentioned nano-cellulose composite packing film is: (1) is by ramee, bamboo fibre and deionized water
Mixing, is ground 20 minutes with grinder;(2) loading high pressure homogenizer carries out homogenizing 20 minutes;(3) filter, discard big
Particulate fibrous;(4) filtrate and remaining ingredient are mixed, put in 85 DEG C of water-baths, carry out under rotating speed 350r/min with blender
Stir 30 minutes;(5) stand, slough bubble, be slowly stirred dispersion with blender;(6) mixed solution is flowed on base material
Prolong film forming;(7) put in vacuum drying oven, be dried 15.5 hours at temperature 55 DEG C and get final product.
Embodiment 4
A kind of nano-cellulose composite packing film, is prepared from weight portion by following component: ramee 2.5 parts, bamboo fibre
Tie up 1.8 parts, polyvinyl alcohol 23 parts, aluminium silicate 1.7 parts, hydroxypropyl methyl cellulose 3.5 parts, butyl p-hydroxybenzoate 0.35
Part, lauroylamidopropyl betaine 1.8 parts, alkylphenol polyoxyethylene 3.5 parts, decabromodiphenyl oxide 1.7 parts, butylated hydroxy-a
Benzene 0.25 part, citric acid 0.4 part, 0.4 part of dehydroactic acid sodium, rosin resin 0.35 part, deionized water 280 parts.
The preparation method of above-mentioned nano-cellulose composite packing film is: (1) is by ramee, bamboo fibre and deionized water
Mixing, is ground 25 minutes with grinder;(2) loading high pressure homogenizer carries out homogenizing 25 minutes;(3) filter, discard big
Particulate fibrous;(4) filtrate and remaining ingredient are mixed, put in 85 DEG C of water-baths, carry out under rotating speed 350r/min with blender
Stir 35 minutes;(5) stand, slough bubble, be slowly stirred dispersion with blender;(6) mixed solution is flowed on base material
Prolong film forming;(7) put in vacuum drying oven, be dried 16 hours at temperature 55 DEG C and get final product.
Embodiment 5
A kind of nano-cellulose composite packing film, is prepared from weight portion by following component: ramee 3 parts, bamboo fibre 2
Part, polyvinyl alcohol 25 parts, aluminium silicate 2 parts, hydroxypropyl methyl cellulose 4 parts, butyl p-hydroxybenzoate 0.4 part, lauramide
CAB 2 parts, alkylphenol polyoxyethylene 4 parts, decabromodiphenyl oxide 2 parts, dibenzylatiooluene 0.3 part, citric acid 0.5
Part, 0.5 part of dehydroactic acid sodium, rosin resin 0.4 part, deionized water 300 parts.
The preparation method of above-mentioned nano-cellulose composite packing film is: (1) is by ramee, bamboo fibre and deionized water
Mixing, is ground 30 minutes with grinder;(2) loading high pressure homogenizer carries out homogenizing 30 minutes;(3) filter, discard big
Particulate fibrous;(4) filtrate and remaining ingredient are mixed, put in 90 DEG C of water-baths, carry out under rotating speed 400r/min with blender
Stir 40 minutes;(5) stand, slough bubble, be slowly stirred dispersion with blender;(6) mixed solution is flowed on base material
Prolong film forming;(7) put in vacuum drying oven, be dried 17 hours under temperature 60 C and get final product.
Comparative example 1
The present embodiment is not contain aluminium silicate with the difference of embodiment 5.Specifically:
A kind of nano-cellulose composite packing film, is prepared from weight portion by following component: ramee 3 parts, bamboo fibre 2
Part, polyvinyl alcohol 25 parts, hydroxypropyl methyl cellulose 4 parts, butyl p-hydroxybenzoate 0.4 part, lauroylamidopropyl betaine 2
Part, alkylphenol polyoxyethylene 4 parts, decabromodiphenyl oxide 2 parts, dibenzylatiooluene 0.3 part, citric acid 0.5 part, dehydroactic acid
0.5 part of sodium, rosin resin 0.4 part, deionized water 300 parts.
The preparation method of above-mentioned nano-cellulose composite packing film is: (1) is by ramee, bamboo fibre and deionized water
Mixing, is ground 30 minutes with grinder;(2) loading high pressure homogenizer carries out homogenizing 30 minutes;(3) filter, discard big
Particulate fibrous;(4) filtrate and remaining ingredient are mixed, put in 90 DEG C of water-baths, carry out under rotating speed 400r/min with blender
Stir 40 minutes;(5) stand, slough bubble, be slowly stirred dispersion with blender;(6) mixed solution is flowed on base material
Prolong film forming;(7) put in vacuum drying oven, be dried 17 hours under temperature 60 C and get final product.
Comparative example 2
The present embodiment is to replace bamboo fibre with ramee with the difference of embodiment 5.Specifically:
A kind of nano-cellulose composite packing film, is prepared from weight portion by following component: ramee 5 parts, polyethylene
Alcohol 25 parts, aluminium silicate 2 parts, hydroxypropyl methyl cellulose 4 parts, butyl p-hydroxybenzoate 0.4 part, lauroylamidopropyl betaine
2 parts, alkylphenol polyoxyethylene 4 parts, decabromodiphenyl oxide 2 parts, dibenzylatiooluene 0.3 part, citric acid 0.5 part, dehydrogenation second
Acid 0.5 part of sodium, rosin resin 0.4 part, deionized water 300 parts.
The preparation method of above-mentioned nano-cellulose composite packing film is: ramee and deionized water are mixed by (1), use
Grinder is ground 30 minutes;(2) loading high pressure homogenizer carries out homogenizing 30 minutes;(3) filter, discard bulky grain fine
Dimension;(4) filtrate and remaining ingredient are mixed, put in 90 DEG C of water-baths, under rotating speed 400r/min, be stirred 40 with blender
Minute;(5) stand, slough bubble, be slowly stirred dispersion with blender;(6) mixed solution is carried out on base material casting film-forming;
(7) put in vacuum drying oven, be dried 17 hours under temperature 60 C and get final product.
The property indices of material of the present invention see table, it may be seen that this packing film has preferable mechanical property
Can, its hot strength may be up to 146MPa, and stretch resistance is strong, and elastic modelling quantity is 7.15GPa, elastic and toughness is good, meanwhile, its
Light transmittance at 600nm also in about 84.3-84.4%, excellent transparency, can show product well.
The property indices of table 1 nano-cellulose composite packing film
Name of product | Hot strength (MPa)) | Elastic modelling quantity (GPa) | Light transmittance (%) |
Embodiment 1 | 143 | 7.11 | 84.3 |
Embodiment 2 | 144 | 7.13 | 84.3 |
Embodiment 3 | 145 | 7.14 | 84.4 |
Embodiment 4 | 146 | 7.15 | 84.4 |
Embodiment 5 | 145 | 7.14 | 84.3 |
Comparative example 1 | 141 | 7.01 | 82.1 |
Comparative example 2 | 137 | 7.08 | 81.6 |
Note: light transmittance values is the value at 600nm.
Claims (7)
1. a nano-cellulose composite packing film, it is characterised in that: it is prepared from weight portion by following component: Boehmeria is fine
Dimension 1-3 part, bamboo fibre 1-2 part, polyvinyl alcohol 15-25 part, aluminium silicate 1-2 part, hydroxypropyl methyl cellulose 2-4 part, to hydroxyl
Butyl benzoate 0.2-0.4 part, lauroylamidopropyl betaine 1-2 part, alkylphenol polyoxyethylene 2-4 part, decabromodiphenyl oxide
1-2 part, dibenzylatiooluene 0.1-0.3 part, citric acid 0.2-0.5 part, dehydroactic acid sodium 0.2-0.5 part, rosin resin
0.2-0.4 part, deionized water 200-300 part.
A kind of nano-cellulose composite packing film the most according to claim 1, it is characterised in that: by following component with weight
Amount part is prepared from: ramee 1.5-2.5 part, bamboo fibre 1.2-1.8 part, polyvinyl alcohol 17-23 part, aluminium silicate 1.1-1.7
Part, hydroxypropyl methyl cellulose 2.5-3.5 part, butyl p-hydroxybenzoate 0.25-0.35 part, lauroylamidopropyl betaine
1.2-1.8 part, alkylphenol polyoxyethylene 2.5-3.5 part, decabromodiphenyl oxide 1.3-1.7 part, dibenzylatiooluene 0.15-
0.25 part, citric acid 0.3-0.4 part, dehydroactic acid sodium 0.3-0.4 part, rosin resin 0.25-0.35 part, deionized water 220-
280 parts.
3. the preparation method of a kind of nano-cellulose composite packing film described in any one of claim 1 to 2, its feature exists
In: comprise the following steps:
(1) ramee, bamboo fibre and deionized water are mixed, be ground 10-30 minute with grinder;
(2) loading high pressure homogenizer carries out homogenizing 10-30 minute;
(3) filter, discard bulky grain fiber;
(4) filtrate and remaining ingredient are mixed, put in 80-90 DEG C of water-bath, enter under rotating speed 300-400r/min with blender
Row stirring 20-40 minute;
(5) stand, slough bubble, be slowly stirred dispersion with blender;
(6) mixed solution is carried out on base material casting film-forming;
(7) put in vacuum drying oven, be dried 14-17 hour at temperature 50-60 DEG C and get final product.
The preparation method of a kind of nano-cellulose composite packing film the most according to claim 3, it is characterised in that: described
In step (1), milling time is 15-25 minute.
The preparation method of a kind of nano-cellulose composite packing film the most according to claim 3, it is characterised in that: described
In step (2), homogenizing time is 15-25 minute.
The preparation method of a kind of nano-cellulose composite packing film the most according to claim 3, it is characterised in that: described
In step (4), bath temperature is 85 DEG C, and speed of agitator is 350r/min, and mixing time is 25-35 minute.
The preparation method of a kind of nano-cellulose composite packing film the most according to claim 3, it is characterised in that: described
In step (7), temperature is 55 DEG C, and drying time is 15-16 hour.