CN105885235A - Heat insulation woven bag - Google Patents
Heat insulation woven bag Download PDFInfo
- Publication number
- CN105885235A CN105885235A CN201610485667.4A CN201610485667A CN105885235A CN 105885235 A CN105885235 A CN 105885235A CN 201610485667 A CN201610485667 A CN 201610485667A CN 105885235 A CN105885235 A CN 105885235A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat insulation
- woven bag
- nano
- polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of plastic woven bags, in particular to a heat insulation woven bag. Concrete production steps are described in the specification. The heat insulation woven bag is prepared from the following raw materials in parts by weight: 100-120 parts of polypropylene, 12-15 parts of styrene, 0.5-1.0 part of methyltin mercaptide TM-FS, 1.0-2.0 parts of a silane coupling agent KH550, 0.5-0.8 part of nano graphite, 1-1.5 parts of nano calcium carbonate, 0.8-1.5 parts of molybdenum disulfide, 0.8-1.2 parts of an antioxidant CA and 4-8 parts of an auxiliary, wherein the auxiliary is formed by mixing clay, alum, a crosslinking agent TAC and morpholine. The heat insulation woven bag provided by the invention has heat insulation effect and is solid and durable, no broken package is caused, cost is low, service life is greatly prolonged, and economic benefit is also relatively high.
Description
Technical field
The present invention relates to Polywoven Bag field, a kind of heat insulation woven bag.
Background technology
Polywoven Bag is divided into Polypropylene Bag, Polythene Bag by main material composition;It is divided into seam end bag, seam by method of sewing
Bag at the bottom of limit.It is now widely used for a kind of packaging material of the article such as fertilizer, chemical products.Its main production is to utilize
The extruded thin film of plastic raw materials, cutting, simple tension are flat filament, through obtaining product through knitting device, and commonly referred to as woven bag.
The packaging bag of the polypropylene flat-filament establishment that conventional art produces, weatherability is poor, easily occur hardening at north of china in winter, embrittlement,
The problems such as demoulding, peeling, fracture, in south owing to summer temperature is high, illumination is strong, ultraviolet penetration power is strong, easily lead
The problem such as cause that woven bag is aging, burn into poor toughness, intensity low service life is short, not only wastes resource but also pollute environment.And mesh
Front Polywoven Bag thermal insulation is the most poor.
Summary of the invention
In order to make up the deficiencies in the prior art, the invention provides a kind of good flame resistance, the heat insulation woven bag of durable one.
The technical solution adopted for the present invention to solve the technical problems is: a kind of heat insulation woven bag, and it is former by following weight portion
Material is made: polypropylene 100-120 part, styrene 12-15 part, methyl stannum TM-FS 0.5-1.0, Silane coupling agent KH550
1.0-2.0, nano-graphite 0.5-0.8 part, nano-calcium carbonate 1-1.5 part, molybdenum bisuphide 0.8-1.5 part, antioxidant
CA 0.8-1.2 part, auxiliary agent 4-8 part.
Preferably, it is made up of the raw material of following weight portion: polypropylene 110 parts, styrene 13 parts, methyl stannum TM-FS0.8,
Silane coupling agent KH550 1.2, nano-graphite 0.5 part, nano-calcium carbonate 1.2 parts, molybdenum bisuphide 1.2 parts, antioxygen
Agent CA 1.0 parts, auxiliary agent 5 parts.
Preferably, institute's auxiliary agent is mixed by clay, Alumen, cross-linking agent TAC and morpholine, described clay, Alumen, crosslinking
The mass ratio of agent TAC and morpholine is 3:4:5:3.
Beneficial effect: the heat insulation woven bag of heretofore described one, heat insulating effect, durable, not bale broken, and
With low cost, obtain service life significantly extending, economic benefit is the highest.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with
Embodiment, is expanded on further the present invention.
It is made up of the raw material of following weight portion: polypropylene 100-120 part, styrene 12-15 part, methyl stannum TM-FS
0.5-1.0, Silane coupling agent KH550 1.0-2.0, nano-graphite 0.5-0.8 part, nano-calcium carbonate 1-1.5 part, two
Molybdenum sulfide 0.8-1.5 part, antioxidant CA 0.8-1.2 part, auxiliary agent 4-8 part.
Preferably, it is made up of the raw material of following weight portion: polypropylene 110 parts, styrene 13 parts, methyl stannum TM-FS0.8,
Silane coupling agent KH550 1.2, nano-graphite 0.5 part, nano-calcium carbonate 1.2 parts, molybdenum bisuphide 1.2 parts, antioxygen
Agent CA 1.0 parts, auxiliary agent 5 parts.
Preferably, institute's auxiliary agent is mixed by clay, Alumen, cross-linking agent TAC and morpholine, described clay, Alumen, crosslinking
The mass ratio of agent TAC and morpholine is 3:4:5:3.
The ultimate principle of the present invention, principal character and advantage have more than been shown and described.Skilled person will appreciate that of the industry,
The present invention is not restricted to the described embodiments, the principle that the present invention is simply described of the description in above-described embodiment and description,
Without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these changes and improvements are all
Fall in scope of the claimed invention.Claimed scope is by appending claims and equivalent circle thereof
Fixed.
Claims (3)
1. a heat insulation woven bag, it is characterised in that: it is made up of the raw material of following weight portion: polypropylene 100-120 part,
Styrene 12-15 part, methyl stannum TM-FS 0.5-1.0, silane coupler KH55 01.0-2.0, nano-graphite 0.5-0.8
Part, nano-calcium carbonate 1-1.5 part, molybdenum bisuphide 0.8-1.5 part, antioxidant CA 0.8-1.2 part, auxiliary agent 4-8 part.
The heat insulation woven bag of one the most according to claim 1, it is characterised in that: it is made up of the raw material of following weight portion:
Polypropylene 110 parts, styrene 13 parts, methyl stannum TM-FS 0.8, Silane coupling agent KH550 1.2, nano-graphite 0.5
Part, nano-calcium carbonate 1.2 parts, molybdenum bisuphide 1.2 parts, antioxidant CA 1.0 parts, auxiliary agent 5 parts.
The heat insulation woven bag of one the most according to claim 1 and 2, it is characterised in that: institute's auxiliary agent by clay, Alumen,
Cross-linking agent TAC and morpholine mix, and the mass ratio of described clay, Alumen, cross-linking agent TAC and morpholine is 3:4:5:3.