CN105885215A - 一种抗紫外线聚丙烯材料的制备方法 - Google Patents
一种抗紫外线聚丙烯材料的制备方法 Download PDFInfo
- Publication number
- CN105885215A CN105885215A CN201410745909.XA CN201410745909A CN105885215A CN 105885215 A CN105885215 A CN 105885215A CN 201410745909 A CN201410745909 A CN 201410745909A CN 105885215 A CN105885215 A CN 105885215A
- Authority
- CN
- China
- Prior art keywords
- preparation
- polypropylene material
- muscovitum
- uvioresistant
- mica powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗紫外线聚丙烯材料的制备方法，包括云母粉制备和复合材料制备两步骤。云母是高模量高刚性的无机粉体，添加到聚丙烯树脂中可以有效的提高其抗拉强度、弯由于曲强度和弯曲模量，PP/云母复合材料具有明显抗紫外老化作用。
Description
技术领域
本发明涉及塑料领域，具体涉及一种抗紫外线聚丙烯材料的制备方法。
背景技术
聚丙烯作为一种综合性能优越的热塑性塑料，在工业应用中非常广泛，聚丙烯应用范围广泛，因此人们对聚丙烯增强增韧做了很多研究。一般情况下都是采用无机刚性粉体、纤维和弹性体。现在聚丙烯制成品户外使用率大大的提升，但是其户外使用寿命很短，故对聚丙烯抗老化性能研究也成为现阶段一个研究的重点、热点。云母是一种片层结构的无机粉体，具有耐腐蚀，耐高温等特点，而且对光线有一定反射等作用。目前，利用云母微粒改性聚丙烯还主要集中在界面性能与力学性能的研究上而且是低含量的填充。因此，可以将云母的抗紫外老化功能运用到聚丙烯中。
发明内容
本发明的目的在于克服现有技术中存在的缺陷，提供一种抗紫外老化性能好的抗紫外线聚丙烯材料的制备方法。
为实现上述技术效果，本发明的技术方案为：一种抗紫外线聚丙烯材料的制备方法，其特征在于，所述方法包括以下步骤：
S1：将云母放入干燥箱内在80℃下干燥24h，球磨6～10h，得到云母粉；
S2：将PP树脂，S1所得云母粉和马来酸酐接枝按比例均匀混合，利用挤出机共混挤出，经过水槽冷却后牵引至塑料切粒机切成母粒，制得抗紫外线聚丙烯材料。
其中，所述抗紫外线聚丙烯材料中云母添加量所占百分比为25～40％，所述云母与马来酸酐接枝的添加量之比为(2～2.5)∶1。
其中，所述云母粉的粒度为20～50μm。
本发明的优点和有益效果在于：
云母是高模量高刚性的无机粉体，添加到聚丙烯树脂中可以有效的提高其抗拉强度、弯由于曲强度和弯曲模量，PP/云母复合材料具有明显抗紫外老化作用。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
实施例1
实施例1的抗紫外线聚丙烯材料的制备方法，包括以下步骤：
S1：将云母放入干燥箱内在80℃下干燥24h，球磨6h，得到云母粉；
S2：将PP树脂，S1所得云母粉和马来酸酐接枝按比例均匀混合，利用挤出机共混挤出，经过水槽冷却后牵引至塑料切粒机切成母粒，制得抗紫外线聚丙烯材料。
其中，抗紫外线聚丙烯材料中云母添加量所占百分比为25％，云母与马来酸酐接枝的添加量之比为2∶1。
其中，云母粉的粒度为50μm。
实施例2
实施例2的抗紫外线聚丙烯材料的制备方法，包括以下步骤：
S1：将云母放入干燥箱内在80℃下干燥24h，球磨8h，得到云母粉；
S2：将PP树脂，S1所得云母粉和马来酸酐接枝按比例均匀混合，利用挤出机共混挤出，经过水槽冷却后牵引至塑料切粒机切成母粒，制得抗紫外线聚丙烯材料。
其中，抗紫外线聚丙烯材料中云母添加量所占百分比为32％，云母与马来酸酐接枝的添加量之比为11∶4。
其中，云母粉的粒度为35μm。
实施例3
实施例3的抗紫外线聚丙烯材料的制备方法，包括以下步骤：
S1：将云母放入干燥箱内在80℃下干燥24h，球磨10h，得到云母粉；
S2：将PP树脂，S1所得云母粉和马来酸酐接枝按比例均匀混合，利用挤出机共混挤出，经过水槽冷却后牵引至塑料切粒机切成母粒，制得抗紫外线聚丙烯材料。
其中，抗紫外线聚丙烯材料中云母添加量所占百分比为40％，云母与马来酸酐接枝的添加量之比为5∶2。
其中，云母粉的粒度为20μm。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (3)
1.一种抗紫外线聚丙烯材料的制备方法，其特征在于，所述方法包括以下步骤：
S1：将云母放入干燥箱内在80℃下干燥24h，球磨6～10h，得到云母粉；
S2：将PP树脂，S1所得云母粉和马来酸酐接枝按比例均匀混合，利用挤出机共混挤出，经过水槽冷却后牵引至塑料切粒机切成母粒，制得抗紫外线聚丙烯材料。
2.根据权利要求1所述的抗紫外线聚丙烯材料的制备方法，其特征在于，所述抗紫外线聚丙烯材料中云母添加量所占百分比为25～40％，所述云母与马来酸酐接枝的添加量之比为(2～2.5)∶1。
3.根据权利要求2所述的抗紫外线聚丙烯材料的制备方法，其特征在于，所述云母粉的粒度为20～50μm。