CN105860914A - Repair adhesive tape used for cables and preparation method thereof - Google Patents
Repair adhesive tape used for cables and preparation method thereof Download PDFInfo
- Publication number
- CN105860914A CN105860914A CN201610263431.6A CN201610263431A CN105860914A CN 105860914 A CN105860914 A CN 105860914A CN 201610263431 A CN201610263431 A CN 201610263431A CN 105860914 A CN105860914 A CN 105860914A
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive tape
- cable
- butanone
- carborundum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a repair adhesive tape used for cables and a preparation method thereof. The repair adhesive tape used for cables is prepared from the following raw materials in parts by weight: 40-50 parts of o-toluene isocyanate, 50-60 parts of 1,4-phenylene diisocyanate, 20-30 parts of polyoxyethylene polyol, 30-40 parts of dipropylene glycol, 10-15 parts of carbon fibers, 6-8 parts of methyl silicone oil, 10-15 parts of silicon carbide, 5-15 parts of aluminium trioxide, 0.3-0.6 part of stannous octoate, 0.4-0.8 part of triethylene diamine, 4-6 parts of dibutyl ester, 10-20 parts of butanone, 1-2 parts of dimethylamino ethyl alcohol and 0.3-0.5 part of colorant. The invention also discloses a preparation method. The repair adhesive tape and the preparation method have the beneficial effects that the bonding strength of the material is further improved on the basis of existing technology, the toughness and strength of the material are simultaneously improved, the acid-base resistance of the material is improved, and weakness of properties caused by repair of the cables is reduced.
Description
Technical field
The present invention relates to a kind of repairing adhesive tape, a kind of cable is with repairing adhesive tape and preparation method thereof.
Background technology
Finding in distribution overhauls, the basic reason that cable breaks down is that insulating properties reduces and the breakdown that causes is broken
Bad, and the main cause causing cable covering insulating properties to reduce is more, such as: cable is excessive curved during construction is laid
Bent, the wound of external force is hit or the local excessive caused that rubs stretches and ruptures and causes, and the hidden danger of this kind of mechanicalness damage is relatively big, and first
Phase is easy to be left in the basket;Secondly as the self deterioration of material, corrosion etc. caused by the character of the environment in the external world and material itself;
Furthermore, cable is in operation and also can be frequently encountered by various overvoltage, to such an extent as to the fault occurrence frequency of power cable is relative to it
It is that comparison is many for its electrical equipment.No matter in life or producing, cable fault all has the biggest harm, the most then lead
Cause to have a power failure and stop production, heavy then cause electric shock to cause casualties, even can also cause fire, consequence is the most serious.Therefore, periodically
Power cable is carried out Insulation Test, finds the operation hidden danger of power cable early and eliminated and be to ensure that power cable safety
The important measures running, preventing cable fault from occurring.
At present, the method repairing cable has a hot repair, cable cold repair glue and repair adhesive tape etc., wherein, repair adhesive tape by
In easy to use, simple to operate, safety is higher and can tackle general sudden cable fault, so being widely used.
But, the performance repairing adhesive tape also needs to further improve, such as: owing to the voltage of cable is higher, to repair sheets tape insulation
Have higher requirement, existing repairing adhesive tape, the generation of the secondary cable accident caused due to insulating properties deficiency is more, and
Endanger the biggest;Owing to repairing adhesive tape in use, need the pretension certain to material, and prolongation over time, adhesive tape
Pretension can gradually weaken, the cementing strength of cable adhesive tape also can gradually disappear, and ultimately results in coming off of cable adhesive tape;
The intensity of adhesive tape is relatively low, becomes the weak link of cable;The winding of adhesive tape adds the thickness of cable covering, dispels the heat and conducts heat
Effect reduce, accelerate the aging of cable adhesive tape.
On the basis of existing technology, applicant, through improvement repeatedly and experiment, finally solves this technological deficiency, carries
Gone out a kind of new technical scheme, and provide a kind of intensity height, good toughness, insulating properties strong and have preferable cementing strength and
The cable repairing adhesive tape of radiating effect.
Summary of the invention
The technical problem to be solved is to provide a kind of cable and repairs adhesive tape and preparation method thereof.
For solving above-mentioned technical problem, technical scheme solves the most from the following aspect: (1) is by adding polyoxy
Change ethylene polyhydric alcohol and dipropylene glycol and improve o-toluene diisocyanate and the gumminess of p-phenylene diisocyanate: polyoxyethylene
Alkene polyhydric alcohol and dipropylene glycol with the use of, it is possible to play synergism, and o-toluene diisocyanate and p-benzene two Carbimide.
Ester with the use of can be complementary, and by screening the molecular weight of polyoxyethylated polyols, coordinating other material performances
On the basis of, gumminess is improved further, and has played the decay resistance of material itself.(2) send out in experimentation
Existing, there is certain contradiction between insulating properties and the heat conduction and heat radiation performance of material, as, although the heat conductivility of material is along with metal
The increase of oxide and strengthen, but too much metal-oxide can reduce the insulating properties of material, and the heat conduction and heat radiation of material
Other performances of material can be affected the most again.This programme by strict control carborundum and the proportioning of alchlor and
Usage amount reaches the balance of material conducts heat and insulation.(3) relatively big due to the flexibility of material, and heat distortion temperature is relatively low,
Then affect intensity and the toughness of material, and by adding carbon fiber and alchlor, improve intensity and the toughness of material, with
Time alchlor can work in coordination with carborundum and optimize the heat conductivility of material further;By adding stannous octoate and Sanya in this programme
Ethyldiamine, under identical testing conditions, cementing intensity increases significantly, and when the proportioning of the two is in certain limit
The most more can play the bonding capacity of material, and the speed of solidification the most significantly improves.(4) by adding the polyether-ether-ketone material of resistance to raising
High temperature resistant and the electrical insulation capability of material, and polyether-ether-ketone can with carbon fiber with the use of, the common intensity improving material and toughness,
Serve beyond thought effect.(5) in order to reach the target of design, it is inadequate by assembling of raw material, each raw material
Select to affect the most to a certain extent the overall performance of material, make a formal request people through selecting materials and allocating repeatedly, finally determine
Technical scheme, to reach the balance between design requirement and material property.
Applicant, by experiment repeatedly, has finally made following technical scheme, described a kind of cable repair sheets
Band is made up of the raw material of following weight portion: o-toluene diisocyanate 40-50 part, p-phenylene diisocyanate 50-60 part, polyoxygenated
Ethylene polyhydric alcohol 20-30 part, dipropylene glycol 30-40 part, carbon fiber 10-15 part, methyl-silicone oil 6-8 part, carborundum 10-15 part,
Alchlor 5-15 part, stannous octoate 0.3-0.6 part, triethylenediamine 0.4-0.8 part, polyether-ether-ketone 5-15 part, dibutyl ester
4-6 part, butanone 10-20 part, dimethylaminoethanol 1-2 part, coloring agent 0.3-0.5 part.
As preferably, the proportioning of described stannous octoate and triethylenediamine is 1:1.2.
As preferably, described carborundum and alchlor proportioning are 1-2:1.
As preferably, adhesive tape repaired by described a kind of cable, it is characterised in that be made up of the raw material of following weight portion:
O-toluene diisocyanate 45 parts, p-phenylene diisocyanate 55 parts, polyoxyethylated polyols 25 parts, dipropylene glycol 35 parts, carbon
Fiber 12 parts, methyl-silicone oil 7 parts, carborundum 12 parts, alchlor 8 parts, stannous octoate 0.4 part, triethylenediamine 0.48 part,
Polyether-ether-ketone 10 parts, dibutyl ester 5 parts, butanone 15 parts, dimethylaminoethanol 1.5 parts, coloring agent 0.4 part.
As preferably, the mean molecule quantity of described polyoxyethylated polyols is 750-800.
Present invention also offers above-mentioned manufacture method, comprise the following steps:
(1) weigh each raw material by weight, and carborundum, alchlor are ground standby.
(2) butanone of polyoxyethylated polyols, dipropylene glycol and 2/3rds being put into there-necked flask, nitrogen charging is protected simultaneously
Protect, be sufficiently stirred under conditions of 50-55 DEG C 1-1.5 hour, obtain serosity A.
(3) o-toluene diisocyanate and p-phenylene diisocyanate are put into four-hole bottle, stir at a temperature of 50-60 DEG C
Mix and add serosity A slowly, pouring in agitator after reacting 6-7 hour, and by methyl-silicone oil, stannous octoate, triethylene
Diamidogen, polyether-ether-ketone, dibutyl ester are sequentially added into agitator.
(4) remaining raw material is added in step (3), and add remaining butanone, every with 70 turns under conditions of rushing nitrogen
Minute rotating speed stir and be cooled to room temperature and obtain serosity B.
(5) the serosity B that step (4) obtains is spread upon in fiber cloth uniformly, then pack under conditions of rushing nitrogen, seal
Deposit.
Being described as follows of part material of the present invention:
Dipropylene glycol: improving flexibility, resistance to be full of cracks and weatherability are preferable.
Polyether-ether-ketone: as polymerizer, has the physical and chemical performances such as high temperature resistant, chemical resistance corrosion, can be used as resistance to
High-temperature structural material and electrically insulating material.And insoluble in any solvent and strong acid, highly basic, and hydrolysis, there is the highest change
Learn stability.
Methyl-silicone oil: there is thermostability, electrical insulating property, weatherability, hydrophobicity, physiological inertia and the less surface of brilliance
Tension force, also has low viscosity-temperature coefficient, higher resistance to compression, also acts as the additive of froth breaking, demoulding.
Stannous octoate, triethylenediamine: work in coordination with and play catalytic action.
Owing to have employed technique scheme, a kind of cable, with repairing adhesive tape, is made up of following raw material: o-first
Phenylisocyanate 40-50 part, p-phenylene diisocyanate 50-60 part, polyoxyethylated polyols 20-30 part, dipropylene glycol 30-
40 parts, carbon fiber 10-15 part, methyl-silicone oil 6-8 part, carborundum 10-15 part, alchlor 5-15 part, stannous octoate 0.3-0.6
Part, triethylenediamine 0.4-0.8 part, polyether-ether-ketone 5-15 part, dibutyl ester 4-6 part, butanone 10-20 part, dimethylaminoethyl
Alcohol 1-2 part, coloring agent 0.3-0.5 part;The method have the advantages that and all reached, at properties, the base that design requires
On plinth, further increase the performance of the acid-resistant corrosion of material, cementing strength, heat conduction and heat radiation, extend the use of material
Life-span.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described further.
Embodiment 1
A kind of cable, with repairing adhesive tape, is made up of following raw material: o-toluene diisocyanate 40 parts, p-benzene two Carbimide.
Ester 50 parts, polyoxyethylated polyols 20 parts, dipropylene glycol 30 parts, 10 parts of carbon fiber, methyl-silicone oil 6 parts, carborundum 10 parts, three
Aluminium oxide 5 parts, stannous octoate 0.3 part, triethylenediamine 0.4-0.8 part, polyether-ether-ketone 5 parts, dibutyl ester 4 parts, butanone 10 parts,
Dimethylaminoethanol 1 part, coloring agent 0.3 part.
Above-mentioned manufacture method, comprises the following steps:
(1) weigh each raw material by weight, and carborundum, alchlor are ground standby.
(2) butanone of polyoxyethylated polyols, dipropylene glycol and 2/3rds being put into there-necked flask, nitrogen charging is protected simultaneously
Protect, be sufficiently stirred under conditions of 50-55 DEG C 1-1.5 hour, obtain serosity A.
(3) o-toluene diisocyanate and p-phenylene diisocyanate are put into four-hole bottle, stir at a temperature of 50-60 DEG C
Mix and add serosity A slowly, pouring in agitator after reacting 6-7 hour, and by methyl-silicone oil, stannous octoate, triethylene
Diamidogen, polyether-ether-ketone, dibutyl ester are sequentially added into agitator.
(4) remaining raw material is added in step (3), and add remaining butanone, every with 70 turns under conditions of rushing nitrogen
Minute rotating speed stir and be cooled to room temperature and obtain serosity B.
(5) the serosity B that step (4) obtains is spread upon in fiber cloth uniformly, then pack under conditions of rushing nitrogen, seal
Deposit.
Embodiment 2
A kind of cable, with repairing adhesive tape, is made up of following raw material: o-toluene diisocyanate 45 parts, p-benzene two Carbimide.
Ester 55 parts, mean molecule quantity are the polyoxyethylated polyols 25 parts of 750-800, dipropylene glycol 35 parts, 12 parts of carbon fiber, methyl
Silicone oil 7 parts, carborundum 12 parts, alchlor 8 parts, stannous octoate 0.4 part, triethylenediamine 0.48 part, polyether-ether-ketone 10 parts,
Dibutyl ester 5 parts, butanone 15 parts, dimethylaminoethanol 1.5 parts, coloring agent 0.4 part.
Above-mentioned manufacture method, comprises the following steps:
(1) weigh each raw material by weight, and carborundum, alchlor are ground standby.
(2) butanone of polyoxyethylated polyols, dipropylene glycol and 2/3rds being put into there-necked flask, nitrogen charging is protected simultaneously
Protect, be sufficiently stirred under conditions of 50-55 DEG C 1-1.5 hour, obtain serosity A.
(3) o-toluene diisocyanate and p-phenylene diisocyanate are put into four-hole bottle, stir at a temperature of 50-60 DEG C
Mix and add serosity A slowly, pouring in agitator after reacting 6-7 hour, and by methyl-silicone oil, stannous octoate, triethylene
Diamidogen, polyether-ether-ketone, dibutyl ester are sequentially added into agitator.
(4) remaining raw material is added in step (3), and add remaining butanone, every with 70 turns under conditions of rushing nitrogen
Minute rotating speed stir and be cooled to room temperature and obtain serosity B.
(5) the serosity B that step (4) obtains is spread upon in fiber cloth uniformly, then pack under conditions of rushing nitrogen, seal
Deposit.
Embodiment 3
A kind of cable, with repairing adhesive tape, is made up of following raw material: o-toluene diisocyanate 50 parts, p-benzene two Carbimide.
Ester 60 parts, polyoxyethylated polyols 30 parts, dipropylene glycol 40 parts, 15 parts of carbon fiber, methyl-silicone oil 8 parts, carborundum 15 parts, three
Aluminium oxide 15 parts, stannous octoate 0.6 part, triethylenediamine 0.8 part, polyether-ether-ketone 15 parts, dibutyl ester 6 parts, butanone 20 parts, two
Methyl amino ethanol 2 parts, coloring agent 0.5 part
Above-mentioned manufacture method, comprises the following steps:
(1) weigh each raw material by weight, and carborundum, alchlor are ground standby.
(2) butanone of polyoxyethylated polyols, dipropylene glycol and 2/3rds being put into there-necked flask, nitrogen charging is protected simultaneously
Protect, be sufficiently stirred under conditions of 50-55 DEG C 1-1.5 hour, obtain serosity A.
(3) o-toluene diisocyanate and p-phenylene diisocyanate are put into four-hole bottle, stir at a temperature of 50-60 DEG C
Mix and add serosity A slowly, pouring in agitator after reacting 6-7 hour, and by methyl-silicone oil, stannous octoate, triethylene
Diamidogen, polyether-ether-ketone, dibutyl ester are sequentially added into agitator.
(4) remaining raw material is added in step (3), and add remaining butanone, every with 70 turns under conditions of rushing nitrogen
Minute rotating speed stir and be cooled to room temperature and obtain serosity B.
(5) the serosity B that step (4) obtains is spread upon in fiber cloth uniformly, then pack under conditions of rushing nitrogen, seal
Deposit.
The performance test detection of embodiment 1, embodiment 2 and embodiment 3 is as follows:
Take 1 millimeters thick embodiment 1-3 prepare material 23 DEG C under the conditions of detect, its mechanical performance such as table 1:
Table 1
Group | Embodiment 1 | Embodiment 2 | Embodiment 3 |
Impact strength (J) | 13.8 | 15.2 | 14.5 |
Tensile strength (N/mm2) | 15.5 | 16.0 | 16.4 |
Elongation at break (%) | 490 | 498 | 495 |
Hardness (A) | 75 | 80 | 79 |
Insulating properties (Ω) | ≥1×1013 | ≥1×1013 | ≥1×1013 |
Acid-resistant corrosion (90d) | Unchanged | Unchanged | Unchanged |
To cable cover(ing) peel strength (N/cm2) | 33.7 | 35.6 | 34.5 |
The equipment used in the present invention is the common equipment of this area, does not repeats them here.
The foregoing is only the schematic detailed description of the invention of the present invention, be not limited to the scope of the present invention.Any
Those skilled in the art, equivalent variations done on the premise of without departing from the design of the present invention and principle and amendment, all
The scope of protection of the invention should be belonged to.
Claims (6)
1. a cable is with repairing adhesive tape, it is characterised in that be made up of the raw material of following weight portion: o-toluene diisocyanate 40-
50 parts, p-phenylene diisocyanate 50-60 part, polyoxyethylated polyols 20-30 part, dipropylene glycol 30-40 part, carbon fiber 10-
15 parts, methyl-silicone oil 6-8 part, carborundum 10-15 part, alchlor 5-15 part, stannous octoate 0.3-0.6 part, triethylene two
Amine 0.4-0.8 part, polyether-ether-ketone 5-15 part, dibutyl ester 4-6 part, butanone 10-20 part, dimethylaminoethanol 1-2 part, coloring agent
0.3-0.5 part.
Adhesive tape repaired by a kind of cable the most according to claim 1, it is characterised in that: described stannous octoate and triethylene
The proportioning of diamidogen is 1:1.2.
Adhesive tape repaired by a kind of cable the most according to claim 1, it is characterised in that: described carborundum and alchlor are joined
Ratio is 1-2:1.
Adhesive tape repaired by a kind of cable the most according to claim 1, it is characterised in that by the raw material system of following weight portion
Become: o-toluene diisocyanate 45 parts, p-phenylene diisocyanate 55 parts, polyoxyethylated polyols 25 parts, dipropylene glycol 35 parts,
12 parts of carbon fiber, methyl-silicone oil 7 parts, carborundum 12 parts, alchlor 8 parts, stannous octoate 0.4 part, triethylenediamine 0.48
Part, polyether-ether-ketone 10 parts, dibutyl ester 5 parts, butanone 15 parts, dimethylaminoethanol 1.5 parts, coloring agent 0.4 part.
5. repair adhesive tape according to a kind of cable described in claim 1 or 4, it is characterised in that: described polyethylene glycol oxide is polynary
The mean molecule quantity of alcohol is 750-800.
6. the manufacture method of adhesive tape repaired by a kind of cable as described in claim 1 or 4, it is characterised in that include following step
Rapid:
(1) weigh each raw material by weight, and carborundum, alchlor are ground standby;
(2) butanone of polyoxyethylated polyols, dipropylene glycol and 2/3rds is put into there-necked flask, simultaneously nitrogen filled protection,
It is sufficiently stirred under conditions of 50-55 DEG C 1-1.5 hour, obtains serosity A;
(3) o-toluene diisocyanate and p-phenylene diisocyanate are put into four-hole bottle, stir also at a temperature of 50-60 DEG C
Slowly add serosity A, pour in agitator after reacting 6-7 hour, and by methyl-silicone oil, stannous octoate, triethylenediamine,
Polyether-ether-ketone, dibutyl ester are sequentially added into agitator;
(4) remaining raw material is added in step (3), and add remaining butanone, with 70 rpms under conditions of rushing nitrogen
Rotating speed stir and be cooled to room temperature and obtain serosity B;
(5) the serosity B that step (4) obtains is spread upon in fiber cloth uniformly, then pack under conditions of rushing nitrogen, seal up for safekeeping.