CN105860681A - Heat-insulating waterproof coating and preparation method thereof - Google Patents
Heat-insulating waterproof coating and preparation method thereof Download PDFInfo
- Publication number
- CN105860681A CN105860681A CN201610301829.4A CN201610301829A CN105860681A CN 105860681 A CN105860681 A CN 105860681A CN 201610301829 A CN201610301829 A CN 201610301829A CN 105860681 A CN105860681 A CN 105860681A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic emulsion
- heat
- waterproof coating
- insulating waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A heat-insulating waterproof coating is composed of, by weight, 10-20 parts of water, 50-80 parts of precipitated calcium carbonate, 20-30 parts of diatom ooze, 25-35 parts of adhesive polystyrene particles, 5-15 parts of anti-crack fiber, 30-50 parts of glass beads, 20-30 parts of a pure acrylic emulsion, 25-35 parts of a styrene-acrylic emulsion, 0.2-0.4 part of a preservative, 0.2-04 part of a defoamer and 0.9-5 parts of a cosolvent. Adhesive polystyrene particles have good heat-insulating effect, glass beads have good hydrophobicity and waterproofness, diatom ooze has unique molecular sieve structure and selective adsorption performance, harmful substances like free formaldehyde, benzene and ammonium in air and peculiar smell generated by pets, smoking and garbage can be removed effectively, and indoor air can be purified.
Description
Technical field
The present invention relates to heat-insulating waterproof coating technical field, be specially a kind of heat-insulating waterproof coating and preparation side thereof
Method.
Background technology
Heat-insulating waterproof coating is that the one grown up in recent years has sun-proof, heat insulation, waterproof, energy-conservation, ring
The new type functional coating protected.China is vast in territory, and communal facility is various, the most all kinds of grains, material
The roofing of depot establishment thing needs brushing heat-insulating waterproof coating, forms thick matter rubber-like film, has the highest disconnected
Split elongation percentage, bear expanding with heat and contract with cold of building roof, make up crack, play good waterproof action.But
Existing heat-insulating waterproof coating have containing poisonous accessory ingredient, there is potential safety hazard, or its waterproof and heat-insulating effect
Poor, it is difficult to reach preferable insulating waterproof effect, to this end, we design a kind of heat-insulating waterproof coating and
Preparation method.
Summary of the invention
It is an object of the invention to provide a kind of heat-insulating waterproof coating and preparation method thereof, to solve above-mentioned background skill
The problem proposed in art.
For achieving the above object, the present invention provides following technical scheme:
A kind of heat-insulating waterproof coating, is made up of according to weight portion following raw material: water 10~20 parts, precipitation carbon
Acid calcium 50~80 parts, diatom ooze 20~30 parts, glue powder polyphenyl particle 25~35 parts, anti-crack fiber 5~15
Part, glass microballoon 30~50 parts, pure-acrylic emulsion 20~30 parts, styrene-acrylic emulsion 25~35 parts, preservative 0.2~
0.4 part, defoamer 0.2~0.4 part, cosolvent 0.9~5 parts.
As the further scheme of the present invention: be made up of according to weight portion following raw material: water 12~17 parts, heavy
Shallow lake calcium carbonate 60~70 parts, diatom ooze 23~27 parts, glue powder polyphenyl particle 28~31 parts, anti-crack fiber 8~
12 parts, glass microballoon 35~45 parts, pure-acrylic emulsion 24~27 parts, styrene-acrylic emulsion 28~32 parts, preservative
0.25~0.35 part, defoamer 0.25~0.35 part, cosolvent 2~4 parts.
As the further scheme of the present invention: be made up of according to weight portion following raw material: 15 parts of water, precipitation carbon
Acid calcium 65 parts, diatom ooze 26 parts, glue powder polyphenyl particle 30 parts, anti-crack fiber 10 parts, glass microballoon 40
Part, pure-acrylic emulsion 25 parts, styrene-acrylic emulsion 30 parts, preservative 0.3 part, defoamer 0.3, cosolvent 3 parts.
The preparation method of a kind of heat-insulating waterproof coating, comprises the following steps:
S1: add water in dispersion cylinder, then preservative, defoamer and cosolvent are added thereto, low speed
Stirring (300~400rpm) 2-6min;
S2: winnofil, diatom ooze, glue powder polyphenyl particle, anti-crack fiber and glass microballoon are joined step
In solution in rapid S1, stirring at low speed (300~400rpm) 5-15min;
S3: pure-acrylic emulsion and styrene-acrylic emulsion are joined in the solution in step S2, adds appropriate water,
At 8-45 DEG C, middling speed dispersion (1000~1500rpm) 20-30min.
Compared with prior art, the invention has the beneficial effects as follows: in the present invention, glue powder polyphenyl particle has well
Function of heat insulation, glass microballoon then has good hydrophobic waterproof, and diatom ooze possesses the " molecule of uniqueness
Sieve " structure and selective absorption performance, can effectively remove the free formaldehyde in air, benzene, ammonia etc. harmful
Material and because of abnormal flavour produced by house pet, smoking, rubbish, purifies the air of a room.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the technical scheme of this patent is described in more detail.
Embodiment 1
The present embodiment proposes a kind of heat-insulating waterproof coating, is made up of according to weight portion following raw material: 10 parts of water,
Winnofil 50 parts, diatom ooze 20 parts, glue powder polyphenyl particle 25 parts, anti-crack fiber 5 parts, glass are micro-
Pearl 30, pure-acrylic emulsion 20 parts, styrene-acrylic emulsion 25 parts, preservative 0.2 part, defoamer 0.2 part, hydrotropy
Agent 0.9 part.
Its preparation process needs following steps:
S1: add water in dispersion cylinder, then preservative, defoamer and cosolvent are added thereto, low speed
Stirring (300~400rpm) 3min;
S2: winnofil, diatom ooze, glue powder polyphenyl particle, anti-crack fiber and glass microballoon are joined step
In solution in rapid S1, stirring at low speed (300~400rpm) 7min;
S3: pure-acrylic emulsion and styrene-acrylic emulsion are joined in the solution in step S2, adds appropriate water,
At 8-45 DEG C, middling speed dispersion (1000~1500rpm) 23min.
Embodiment 2
The present embodiment proposes a kind of heat-insulating waterproof coating, is made up of according to weight portion following raw material: 20 parts of water,
Winnofil 80 parts, diatom ooze 30 parts, glue powder polyphenyl particle 35 parts, anti-crack fiber 15 parts, glass
Microballon 50, pure-acrylic emulsion 30 parts, styrene-acrylic emulsion 35 parts, preservative 0.4 part, defoamer 0.4 part, help
Solvent 5 parts.
Its preparation process needs following steps:
S1: add water in dispersion cylinder, then preservative, defoamer and cosolvent are added thereto, low speed
Stirring (300~400rpm) 4min;
S2: winnofil, diatom ooze, glue powder polyphenyl particle, anti-crack fiber and glass microballoon are joined step
In solution in rapid S1, stirring at low speed (300~400rpm) 9min;
S3: pure-acrylic emulsion and styrene-acrylic emulsion are joined in the solution in step S2, adds appropriate water,
At 8-45 DEG C, middling speed dispersion (1000~1500rpm) 24min.
Embodiment 3
The present embodiment proposes a kind of heat-insulating waterproof coating, is made up of according to weight portion following raw material: 15 parts of water,
Winnofil 65 parts, diatom ooze 26 parts, glue powder polyphenyl particle 30 parts, anti-crack fiber 10 parts, glass
Microballon 40 parts, pure-acrylic emulsion 25 parts, styrene-acrylic emulsion 30 parts, preservative 0.3 part, defoamer 0.3, help
Solvent 3 parts.
Its preparation process needs following steps:
S1: add water in dispersion cylinder, then preservative, defoamer and cosolvent are added thereto, low speed
Stirring (300~400rpm) 5min;
S2: winnofil, diatom ooze, glue powder polyphenyl particle, anti-crack fiber and glass microballoon are joined step
In solution in rapid S1, stirring at low speed (300~400rpm) 10min;
S3: pure-acrylic emulsion and styrene-acrylic emulsion are joined in the solution in step S2, adds appropriate water,
At 8-45 DEG C, middling speed dispersion (1000~1500rpm) 25min.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art,
It is appreciated that and these embodiments can be carried out multiple change without departing from the principles and spirit of the present invention
Changing, revise, replace and modification, the scope of the present invention is limited by claims and equivalent thereof.
Claims (4)
1. a heat-insulating waterproof coating, it is characterised in that: be made up of according to weight portion following raw material: water 10~
20 parts, winnofil 50~80 parts, diatom ooze 20~30 parts, glue powder polyphenyl particle 25~35 parts, anti-
Split fiber 5~15 parts, glass microballoon 30~50 parts, pure-acrylic emulsion 20~30 parts, styrene-acrylic emulsion 25~35
Part, preservative 0.2~0.4 part, defoamer 0.2~0.4 part, cosolvent 0.9~5 parts.
Heat-insulating waterproof coating the most according to claim 1, it is characterised in that: by following raw material according to weight
Amount part composition: water 12~17 parts, winnofil 60~70 parts, diatom ooze 23~27 parts, adhesive polystyrene
Granule 28~31 parts, anti-crack fiber 8~12 parts, glass microballoon 35~45 parts, pure-acrylic emulsion 24~27 parts,
Styrene-acrylic emulsion 28~32 parts, preservative 0.25~0.35 part, defoamer 0.25~0.35 part, cosolvent 2~
4 parts.
Heat-insulating waterproof coating the most according to claim 1, it is characterised in that: following raw material is according to weight
Part composition: 15 parts of water, winnofil 65 parts, diatom ooze 26 parts, glue powder polyphenyl particle 30 parts, anti-
Split fiber 10 parts, glass microballoon 40 parts, pure-acrylic emulsion 25 parts, styrene-acrylic emulsion 30 parts, preservative 0.3
Part, defoamer 0.3, cosolvent 3 parts.
4. the preparation method of a heat-insulating waterproof coating as claimed in claim 1, it is characterised in that: include
Following steps:
S1: add water in dispersion cylinder, then preservative, defoamer and cosolvent are added thereto, low speed
Stirring (300~400rpm) 2-6min;
S2: winnofil, diatom ooze, glue powder polyphenyl particle, anti-crack fiber and glass microballoon are joined step
In solution in rapid S1, stirring at low speed (300~400rpm) 5-15min;
S3: pure-acrylic emulsion and styrene-acrylic emulsion are joined in the solution in step S2, adds appropriate water,
At 8-45 DEG C, middling speed dispersion (1000~1500rpm) 20-30min.