CN105858744A - Water treatment agent - Google Patents
Water treatment agent Download PDFInfo
- Publication number
- CN105858744A CN105858744A CN201610306482.2A CN201610306482A CN105858744A CN 105858744 A CN105858744 A CN 105858744A CN 201610306482 A CN201610306482 A CN 201610306482A CN 105858744 A CN105858744 A CN 105858744A
- Authority
- CN
- China
- Prior art keywords
- treatment agent
- water treatment
- mass parts
- solution
- acrylamide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water treatment agent and belongs to the field of environment protection. The water treatment agent is synthesized by, by weight, 20-30 parts of diatomite, 20-30 parts of acrylamide, 4-6 parts of sodium hydroxide, 100 parts of water, acrylic acid, nano-silica, industrial dextrin, glycol and silane coupling agent, wherein the mass ratio of the acrylic acid to the acrylamide is 1:1.5-2, the mass ratio of the nano-silica to the acrylamide is 5-7:20-30, the mass ratio of the industrial dextrin to the acrylic acid is 1:5-8, and the mass ratio of the glycol to the acrylamide is 8-10:20-30. By the water treatment agent, the small-molecule solid in sewage can be effectively filtered and agglutinated on the surface of the water treatment agent.
Description
Technical field
The present invention relates to environmental technology field, particularly to the technical field of water treatment agent.
Background technology
In modern industry, there is large amount of sewage, if the most treated direct discharge of these sewage, environment and human body can be made
Become serious injury.
Summary of the invention
It is an object of the invention to provide and a kind of can effectively the solid impurity in sewage be filtered, and by its coagulation at table
The water treatment agent in face.
Technical scheme is as follows: a kind of water treatment agent, and it is synthesized by following components: mass parts is the silicon of 20 ~ 30
Diatomaceous earth, mass parts is the acrylamide of 20 ~ 30, and mass parts is the sodium hydroxide of 4 ~ 6, and mass parts is the water of 100, with acrylamide
Mass ratio is the acrylic acid of 1:1.5 ~ 2, is the nano silicon of 5 ~ 7:20 ~ 30 with the proportion of acylamide, with acrylic acid
Mass ratio is the industrial dextrin of 1:5 ~ 8, with ethylene glycol and the silane coupler of the proportion of acylamide 8 ~ 10:20 ~ 30.
Preferably: the quality of described silane coupler is the 1% ~ 1.5% of described nano silicon quality.
The preferable following preparation method of this water treatment agent:
1) kieselguhr, acrylamide, sodium hydroxide is soluble in water, obtain the first solution after stirring, this solution is heated up
To 80 ~ 90 DEG C, maintain the reflux under nitrogen atmosphere;
2) adding acrylic acid in the first solution, be uniformly mixed, constant temperature obtains the second solution after refluxing 4 ~ 6 hours;
3) the second solution is cooled to 60 ~ 70 DEG C, is added thereto to silane coupler, be stirring evenly and then adding into nanometer titanium dioxide
Silicon, obtains the 3rd solution after constant temperature stirring 10 ~ 20min;
4) the 3rd solution is cooled to 30 ~ 40 DEG C, is added thereto to industrial dextrin, constant temperature backflow 30 under nitrogen atmosphere ~
60min, obtains the 4th solution;
5) in the 4th solution, add ethylene glycol, after stirring, i.e. obtain described water treatment agent.
The water treatment agent of the present invention may filter that the little molecular solid impurity in sewage, and by its coagulation on surface, processes effect
Rate is high, and dirt-removing power is strong.
Detailed description of the invention
Embodiment 1
The acrylamide that kieselguhr that mass parts is 20, mass parts are 20 is dissolved in mass parts with the sodium hydroxide that mass parts is 4
It is in the water of 100, after stirring, obtains the first solution, be warming up to 90 DEG C, and constant temperature backflow under nitrogen atmosphere, thereafter
Adding mass parts in the first solution is the acrylic acid of 10, and under agitation constant temperature backflow obtains the second solution for 4 hours, the most slowly
Being cooled to 60 DEG C, keep this temperature, adding mass parts in solution is the silane coupler of 0.05, and coupling agent used is kh550,
It is stirring evenly and then adding into the nano silicon that mass parts is 5, after constant temperature stirring 10min, obtains the 3rd solution, by the 3rd solution
Being cooled to after 30 DEG C add the industrial dextrin that mass parts is 2, under nitrogen atmosphere, constant temperature backflow 30min, obtains the 4th solution, to
4th solution adds the ethylene glycol that mass parts is 8 stir and i.e. obtain described water treatment agent.
Embodiment 2
The acrylamide that kieselguhr that mass parts is 30, mass parts are 30 is dissolved in mass parts with the sodium hydroxide that mass parts is 6
It is in the water of 100, after stirring, obtains the first solution, be warming up to 80 DEG C, and constant temperature backflow under nitrogen atmosphere, thereafter
Adding mass parts in the first solution is the acrylic acid of 20, and under agitation constant temperature backflow obtains the second solution for 6 hours, the most slowly
Being cooled to 70 DEG C, keep this temperature, adding mass parts in solution is the silane coupler of 0.105, and coupling agent used is
Kh550, is stirring evenly and then adding into the nano silicon that mass parts is 7, obtains the 3rd solution after constant temperature stirring 20min, by the
Three solution are cooled to after 40 DEG C add the industrial dextrin that mass parts is 2.5, and under nitrogen atmosphere, constant temperature backflow 60min, obtains the
Four solution, add the ethylene glycol that mass parts is 10 in the 4th solution and stir and i.e. obtain described water treatment agent.
Claims (2)
1. a water treatment agent, it is characterised in that: it is synthesized by following components: mass parts is the kieselguhr of 20 ~ 30, and mass parts is
The acrylamide of 20 ~ 30, mass parts is the sodium hydroxide of 4 ~ 6, and mass parts is the water of 100, is 1:1.5 with the proportion of acylamide
The acrylic acid of ~ 2, is the nano silicon of 5 ~ 7:20 ~ 30 with the proportion of acylamide, is 1:5 ~ 8 with acrylic acid mass ratio
Industrial dextrin, with ethylene glycol and the silane coupler of the proportion of acylamide 8 ~ 10:20 ~ 30.
Water treatment agent the most according to claim 1, it is characterised in that: the quality of described silane coupler is described nanometer two
The 1% ~ 1.5% of siliconoxide mass.