CN105858743A - 一种水处理剂的制备方法 - Google Patents
一种水处理剂的制备方法 Download PDFInfo
- Publication number
- CN105858743A CN105858743A CN201610306481.8A CN201610306481A CN105858743A CN 105858743 A CN105858743 A CN 105858743A CN 201610306481 A CN201610306481 A CN 201610306481A CN 105858743 A CN105858743 A CN 105858743A
- Authority
- CN
- China
- Prior art keywords
- solution
- treatment agent
- water treatment
- preparation
- acrylamide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水处理剂的制备方法，属于环保领域。本发明通过将硅藻土、丙烯酰胺、氢氧化钠溶于水后与丙烯酸进行反应，再与纳米二氧化硅进行偶联，其后进行糊精包覆，最后与乙二醇混合的过程可制得成本较低，能有效将污水中的杂质过滤并凝集的水处理剂。
Description
技术领域
本发明涉及环保技术领域，特别涉及水处理剂的技术领域。
背景技术
在现代工业中，存在大量污水，这些污水若不经处理直接排放，会对环境和人体造成严重的伤害。
发明内容
本发明的目的在于提供一种能够有效将污水中的固体杂质过滤，并将其凝集在表面的水处理剂的制备方法。
本发明的技术方案如下：
一种水处理剂的制备方法，包括以下步骤：
1）将丙烯酰胺、氢氧化钠溶于水中，搅拌均匀后得到第一溶液，将该溶液升温至80~90℃，在氮气氛围下保持回流；
2）向第一溶液中加入丙烯酸，搅拌混合均匀，恒温回流4~6小时后得到第二溶液；
3）将第二溶液降温至60~70℃，向其中加入硅烷偶联剂，搅拌均匀后加入纳米二氧化硅，恒温搅拌10~20min后得到第三溶液；
4）将第三溶液降温至30~40℃，向其中加入工业用糊精，在氮气氛围下恒温回流30~60min，得到第四溶液；
5）向第四溶液中加入乙二醇，搅拌均匀后即得到所述水处理剂；
所述糊精与所述丙烯酸的质量比为1:5~8。
其优选实施方案为：所述第一溶液中所述硅藻土、丙烯酰胺、氢氧化钠、水的质量比为20~30：20~30：4~6:100。
其另一优选实施方案为：所述丙烯酰胺与所述丙烯酸的质量比为1.5~2:1。
其另一优选实施方案为：所述丙烯酰胺与所述纳米二氧化硅的质量比为20~30：5~7。
其另一优选实施方案为：所述丙烯酰胺与所述乙二醇的质量比为20~30:8~10。
其另一优选实施方案为：所述硅烷偶联剂的质量为所述纳米二氧化硅质量的1%~1.5%。
本发明制得的水处理剂可过滤污水中的小分子固体杂质，并将其凝集在表面，处理效率高，去污能力强。
具体实施方式
实施例1
将质量份为20的硅藻土、质量份为20的丙烯酰胺与质量份为4的氢氧化钠溶于质量份为100的水中，搅拌均匀后得到第一溶液，将其升温至90℃，并于氮气氛围下恒温回流，其后向第一溶液中加入质量份为10的丙烯酸，在搅拌下恒温回流4小时得到第二溶液，其后缓慢降温至60℃，保持该温度，向溶液中加入质量份为0.05的硅烷偶联剂，所用偶联剂为kh550，搅拌均匀后加入质量份为5的纳米二氧化硅，恒温搅拌10min后得到第三溶液，将第三溶液降温至30℃后加入质量份为8的乙二醇搅拌均匀即得到所述水处理剂。
实施例2
将质量份为30的硅藻土、质量份为30的丙烯酰胺与质量份为6的氢氧化钠溶于质量份为100的水中，搅拌均匀后得到第一溶液，将其升温至80℃，并于氮气氛围下恒温回流，其后向第一溶液中加入质量份为20的丙烯酸，在搅拌下恒温回流6小时得到第二溶液，其后缓慢降温至70℃，保持该温度，向溶液中加入质量份为0.105的硅烷偶联剂，所用偶联剂为kh550，搅拌均匀后加入质量份为7的纳米二氧化硅，恒温搅拌20min后得到第三溶液，将第三溶液降温至40℃后加入质量份为10的乙二醇搅拌均匀即得到所述水处理剂。
Claims (6)
1.一种水处理剂的制备方法，其特征在于：包括以下步骤：
（1）将硅藻土、丙烯酰胺、氢氧化钠溶于水中，搅拌均匀后得到第一溶液，将该溶液升温至80~90℃，在氮气氛围下保持回流；
（2）向第一溶液中加入丙烯酸，搅拌混合均匀，恒温回流4~6小时后得到第二溶液；
（3）将第二溶液降温至60~70℃，向其中加入硅烷偶联剂，搅拌均匀后加入纳米二氧化硅，恒温搅拌10~20min后得到第三溶液；
（4）将第三溶液降温至30~40℃，向其中加入工业用糊精，在氮气氛围下恒温回流30~60min，得到第四溶液；
（5）向第四溶液中加入乙二醇，搅拌均匀后即得到所述水处理剂；
所述糊精与所述丙烯酸的质量比为1:5~8。
2.根据权利要求1所述的水处理剂的制备方法，其特征在于：所述第一溶液中所述硅藻土、丙烯酰胺、氢氧化钠、水的质量比为20~30：20~30：4~6:100。
3.根据权利要求1所述的水处理剂的制备方法，其特征在于：所述丙烯酰胺与所述丙烯酸的质量比为1~1.5:1。
4.根据权利要求1所述的水处理剂的制备方法，其特征在于：所述丙烯酰胺与所述纳米二氧化硅的质量比为20~30：5~7。
5.根据权利要求1所述的水处理剂的制备方法，其特征在于：所述丙烯酰胺与所述乙二醇的质量比为20~30:8~10。
6.根据权利要求1所述的水处理剂的制备方法，其特征在于：所述硅烷偶联剂的质量为所述纳米二氧化硅质量的1%~1.5%。