CN105855212B - A kind of cleaning method of silica gel high polymer material - Google Patents
A kind of cleaning method of silica gel high polymer material Download PDFInfo
- Publication number
- CN105855212B CN105855212B CN201610341127.9A CN201610341127A CN105855212B CN 105855212 B CN105855212 B CN 105855212B CN 201610341127 A CN201610341127 A CN 201610341127A CN 105855212 B CN105855212 B CN 105855212B
- Authority
- CN
- China
- Prior art keywords
- product
- wearing layer
- cleaning
- silica gel
- polymer material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to silica gel polymeric material field, and in particular to a kind of cleaning method of silica gel high polymer material, comprises the following steps：Last layer wearing layer is sprayed by spraying method in product surface；The product for spraying wearing layer is put into steam ambient, vapor (steam) temperature is 100 degrees Celsius and is water, placed 5 10 minutes；It will be put into cleaning machine, cleaning machine is 2cm provided with the flow velocity that 4 delivery ports, each a diameter of 0.5cm of delivery port current, and current direction spray the product of wearing layer3/ s, the product for spraying wearing layer is located at the center of 4 delivery ports, and it is that fulcrum makees lever motion to spray the product of wearing layer with product center；Clean 20 30 minutes；Described delivery port connection cleaning agent bucket, cleaning agent is SDS, acetone and water mixture.The present invention uses above-mentioned cleaning method, is put into steam ambient, loosens impurity, then is cleaned by 4 delivery ports, and causes product to make lever motion, improves cleaning efficiency.
Description
Technical field
The present invention relates to silica gel polymeric material field, and in particular to a kind of cleaning method of silica gel high polymer material.
Background technology
Silica gel high polymer material is mainly that the middleware in electronic product production process can also be final piece, and it is being prepared
During be made up of Multiple components, its surface may residual impurity after the completion of preparation, it is necessary to remove it.
The content of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of cleaning for the silica gel high polymer material for improving cleaning efficiency
Method.
In order to realize foregoing invention purpose, the present invention uses following technical scheme：A kind of cleaning of silica gel high polymer material
Method, it is characterised in that comprise the following steps：
Last layer wearing layer is sprayed by spraying method in product surface；
The product for spraying wearing layer is put into steam ambient, vapor (steam) temperature is 100 degrees Celsius and is water, places 5-10 points
Clock；
It will be put into cleaning machine, cleaning machine sprays provided with 4 delivery ports, each a diameter of 0.5cm of delivery port current, and current direction
The flow velocity of the product of upper wearing layer is 2cm3/ s, the product for spraying wearing layer is located at the center of 4 delivery ports, and sprays wearing layer
Product lever motion is made for fulcrum with product center；Cleaning 20-30 minutes；
Described delivery port connection cleaning agent bucket, cleaning agent is SDS, acetone and water mixture.
By 10-15 parts of methyl phenyl vinyl silicone rubber, 1-5 parts of plasticizer, 0.5-1 parts of platinum catalyst, mica 0.1-0.5
Part, which is mixed and heated 230-260 degrees Celsius in high-speed mixer and is incubated 1-2h, obtains molten mixture, solid at room temperature
Change obtains product, and described number is parts by weight.
Described wearing layer is made up of PTFE.The product for spraying wearing layer is put into steam ambient, vapor (steam) temperature is 100
Degree Celsius and for water, place 8 minutes.Product center is made to refer to during lever motion for fulcrum, and product center is motionless, product two ends alternating
Move up and down.SDS, acetone and water mass ratio are 1:1:20.
The present invention uses above-mentioned cleaning method, is put into steam ambient, loosens impurity, then clear by 4 delivery ports
Wash, and cause product to make lever motion, improve cleaning efficiency.
Embodiment
The present invention is further described in detail with reference to specific embodiment.
Embodiment 1
A kind of cleaning method of silica gel high polymer material, comprises the following steps：
Last layer wearing layer is sprayed by spraying method in product surface；
The product for spraying wearing layer is put into steam ambient, vapor (steam) temperature is 100 degrees Celsius and is water, placed 5 minutes；
It will be put into cleaning machine, cleaning machine sprays provided with 4 delivery ports, each a diameter of 0.5cm of delivery port current, and current direction
The flow velocity of the product of upper wearing layer is 2cm3/ s, the product for spraying wearing layer is located at the center of 4 delivery ports, and sprays wearing layer
Product lever motion is made for fulcrum with product center；Cleaning 20-30 minutes；Described delivery port connection cleaning agent bucket, cleaning
Agent is SDS, acetone and water mixture.
By 10-15 parts of methyl phenyl vinyl silicone rubber, 1-5 parts of plasticizer, 0.5-1 parts of platinum catalyst, mica 0.1-0.5
Part, which is mixed and heated 230-260 degrees Celsius in high-speed mixer and is incubated 1-2h, obtains molten mixture, solid at room temperature
Change obtains product, and described number is parts by weight.
Described wearing layer is made up of PTFE.Product center is made to refer to during lever motion for fulcrum, and product center is motionless, product
Two ends alternately move up and down.SDS, acetone and water mass ratio are 1:1:20.
Embodiment 2
A kind of cleaning method of silica gel high polymer material, comprises the following steps：
Last layer wearing layer is sprayed by spraying method in product surface；
The product for spraying wearing layer is put into steam ambient, vapor (steam) temperature is 100 degrees Celsius and is water, places 10 points
Clock；
It will be put into cleaning machine, cleaning machine sprays provided with 4 delivery ports, each a diameter of 0.5cm of delivery port current, and current direction
The flow velocity of the product of upper wearing layer is 2cm3/ s, the product for spraying wearing layer is located at the center of 4 delivery ports, and sprays wearing layer
Product lever motion is made for fulcrum with product center；Cleaning 20-30 minutes；Described delivery port connection cleaning agent bucket, cleaning
Agent is SDS, acetone and water mixture.
By 10-15 parts of methyl phenyl vinyl silicone rubber, 1-5 parts of plasticizer, 0.5-1 parts of platinum catalyst, mica 0.1-0.5
Part, which is mixed and heated 230-260 degrees Celsius in high-speed mixer and is incubated 1-2h, obtains molten mixture, solid at room temperature
Change obtains product, and described number is parts by weight.
Described wearing layer is made up of PTFE.Product center is made to refer to during lever motion for fulcrum, and product center is motionless, product
Two ends alternately move up and down.SDS, acetone and water mass ratio are 1:1:20.
It should be noted that the foregoing is only embodiments of the invention, it is not intended to limit the scope of the invention,
Equivalent structure or equivalent flow conversion that every utilization present specification is done, or directly or indirectly it is used in other phases
Technical field is closed, is included within the scope of the present invention.
Claims (6)
1. a kind of cleaning method of silica gel high polymer material, it is characterised in that comprise the following steps：
Last layer wearing layer is sprayed by spraying method in product surface；
The product for spraying wearing layer is put into steam ambient, vapor (steam) temperature is 100 degrees Celsius and is water, placed 5-10 minutes；
Product is put into cleaning machine, cleaning machine sprays provided with 4 delivery ports, each a diameter of 0.5cm of delivery port current, and current direction
The flow velocity of the product of upper wearing layer is 2cm3/ s, the product for spraying wearing layer is located at the center of 4 delivery ports, and sprays wearing layer
Product lever motion is made for fulcrum with product center；Cleaning 20-30 minutes；
Described delivery port connection cleaning agent bucket, cleaning agent is SDS, acetone and water mixture.
2. the cleaning method of a kind of silica gel high polymer material according to claim 1, it is characterised in that by aminomethyl phenyl second
10-15 parts of alkenyl silicon rubber, 1-5 parts of plasticizer, 0.5-1 parts of platinum catalyst, 0.1-0.5 parts of mica are mixed in high-speed mixer
And be heated to 230-260 degrees Celsius and be incubated 1-2h to obtain molten mixture, solidification at room temperature obtains product, and number is weight
Number.
3. a kind of cleaning method of silica gel high polymer material according to claim 1, it is characterised in that described wearing layer
It is made up of PTFE.
4. the cleaning method of a kind of silica gel high polymer material according to claim 1, it is characterised in that wearing layer will be sprayed
Product be put into steam ambient, vapor (steam) temperature is 100 degrees Celsius and is water, place 8 minutes.
5. the cleaning method of a kind of silica gel high polymer material according to claim 1, it is characterised in that product center is branch
Point refers to that product center is motionless as lever motion, and product two ends alternately move up and down.
6. the cleaning method of a kind of silica gel high polymer material according to claim 5, it is characterised in that SDS, acetone and water
Mass ratio be 1:1:20.