CN105837964A - High-strength long-life fishing net - Google Patents
High-strength long-life fishing net Download PDFInfo
- Publication number
- CN105837964A CN105837964A CN201610234022.3A CN201610234022A CN105837964A CN 105837964 A CN105837964 A CN 105837964A CN 201610234022 A CN201610234022 A CN 201610234022A CN 105837964 A CN105837964 A CN 105837964A
- Authority
- CN
- China
- Prior art keywords
- fishing net
- zinc oxide
- high intensity
- long life
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-strength long-life fishing net. The fishing net is manufactured from the following raw materials, 150-165 of chlorinated polyethylene, 5-6 of polyacrylamide, 4-5 of hydrogenated castor oil, 3-5 of a plasticizer, 2-3 of modified nanometer zinc oxide, 3-4 of calcium bicarbonate, and 5-6 of auxiliary agents. The fishing net lines are simple in processing technology, and the added modified nanometer zinc oxide and carbon nanotubes match other raw materials for the obvious improvement of properties of the fishing net.
Description
Technical field
The present invention relates to a kind of fishing net, be specially a kind of high intensity long life fishing net.
Background technology
Fishing net is the net of fishing, and it is numb as raw material that men of old uses coarse cloth to add, the method rolled up by bundle makes fishnet.Although this fishing net is perishable, toughness is poor, but its fishing efficiency has been greatly improved.Along with the development of fishery, the object of fishing and hunting is more than fish, and the instrument fished for also grows with each passing hour.It is numb as raw material that men of old uses coarse cloth to add, the method rolled up by bundle makes fishnet.Although this fishing net is perishable, toughness is poor, but its fishing efficiency has been greatly improved.Along with the development of fishery, the object of fishing and hunting is more than fish, and the instrument fished for also grows with each passing hour.Modern fishing net mainly uses polyethylene, the raw materials such as nylon are processed, there are longer use cycle, and higher catching rate, but the mechanical property of polyethylene itself is general, hot strength is relatively low, creep resistance is bad, results in the tradition intensity of fishing net, anti-wear performance, toughness are unsuitable at the bottom of Complex Sea and wind and waves environment fishing operation, reduce the service life of fishing gear, not only waste resource, also directly affect catch.
Summary of the invention
It is an object of the invention to provide a kind of high intensity long life fishing net, be achieved through the following technical solutions:
A kind of high intensity long life fishing net, is made up of following raw material: haloflex 150-165, polyacrylamide 5-6, rilanit special 4-5, plasticizer 3-5, modified nano zinc oxide 2-3, calcium bicarbonate 3-4, auxiliary agent 5-6.
Described plasticizer is made up of organic silicone oil 5-6, dimethyl sulfoxide (DMSO) 3-5, coal tar 2-3.
Described modified nano zinc oxide be the stearic acid of mass fraction 7-8% is mixed with the Zinc oxide powder of 50-100 mesh after, at 50-55 DEG C react 62-75min.
Described auxiliary agent is made up of the raw material of following weight portion: CNT 1-2, the quick lime powder 3-4 of poly-second diester 3-4,80-100 mesh；Above raw material is combined at 60-70 DEG C.
A kind of high intensity long life fishing net, is made up of following steps:
(1) mix at haloflex, polyacrylamide, rilanit special, calcium bicarbonate mixing being placed on 60-70 DEG C, it is subsequently adding plasticizer, modified nano zinc oxide, auxiliary agent, stir at 65-75 DEG C, then mixture is put into extruder extrusion, one section of temperature of extruder is 175-180 DEG C, two sections of temperature are 178-184 DEG C, and three sections of temperature are 181-187 DEG C, and latter end temperature is 183-189 DEG C.
(2) spinneret case is added after extrusion, then spinning appts is used to carry out wire drawing, then drawing-off is carried out, first draw roll pressure is 0.88-0.95bar, the second draw roll pressure is 3.09-3.13bar, then dry at 88-95 DEG C, then take-up roll is used to be wound, first winding roller rotating speed is 3500m/min, second winding roller rotating speed is 3900m/min, 3rd take-up roll rotating speed is 4300m/min, carry out further drawing-off, be then wound obtaining wire rod, then carry out working out and i.e. obtain fishing net.
Beneficial effect: the fishing lines processing technology that the present invention makes is simple, and the modified nano zinc oxide of interpolation, CNT coordinate the various aspects of performance that can significantly improve fishing net with other raw materials.
Detailed description of the invention
Embodiment 1
A kind of high intensity long life fishing net, is made up of following raw material: haloflex 150-165, polyacrylamide 5-6, rilanit special 4-5, plasticizer 3-5, modified nano zinc oxide 2-3, calcium bicarbonate 3-4, auxiliary agent 5-6.
Described plasticizer is made up of organic silicone oil 5.6, dimethyl sulfoxide (DMSO) 3.5, coal tar 2.3.
Described modified nano zinc oxide is by after the stearic acid of mass fraction 7.8% and the Zinc oxide powder mixing of 50 mesh, reacts 67min at 55 DEG C.
Described auxiliary agent is made up of the raw material of following weight portion: CNT 1-2, the quick lime powder 3-4 of poly-second diester 3-4,80-100 mesh；Above raw material is combined at 60-70 DEG C.
A kind of high intensity long life fishing net, is made up of following steps:
(1) haloflex, polyacrylamide, rilanit special, calcium bicarbonate mixing are placed at 67 DEG C and mix, it is subsequently adding plasticizer, modified nano zinc oxide, auxiliary agent, stir at 70 DEG C, then mixture is put into extruder extrusion, one section of temperature of extruder is 177 DEG C, two sections of temperature are 179 DEG C, and three sections of temperature are 184 DEG C, and latter end temperature is 186 DEG C.
(2) spinneret case is added after extrusion, then using spinning appts to carry out wire drawing, then carry out drawing-off, the first draw roll pressure is 0.89bar, the second draw roll pressure is 3.09bar, then dry at 91 DEG C, then using take-up roll to be wound, first winding roller rotating speed is 3400m/min, and second winding roller rotating speed is 3700m/min, 3rd take-up roll rotating speed is 4100m/min, carry out further drawing-off, be then wound obtaining wire rod, then carry out working out and i.e. obtain fishing net.
Claims (5)
1. a high intensity long life fishing net, it is characterised in that be made up of following raw material: haloflex 150-165, polyacrylamide 5-6, rilanit special 4-5, plasticizer 3-5, modified nano zinc oxide 2-3, calcium bicarbonate 3-4, auxiliary agent 5-6.
2. a kind of high intensity long life fishing net as claimed in claim 1, it is characterised in that described plasticizer is made up of organic silicone oil 5-6, dimethyl sulfoxide (DMSO) 3-5, coal tar 2-3.
3. high intensity long life fishing net as claimed in claim 1 a kind of, it is characterised in that described modified nano zinc oxide be the stearic acid of mass fraction 7-8% is mixed with the Zinc oxide powder of 50-100 mesh after, reaction 62-75min at 50-55 DEG C.
4. according to a kind of high intensity long life fishing net described in claim 1, it is characterised in that: described auxiliary agent is made up of the raw material of following weight portion: CNT 1-2, the quick lime powder 3-4 of poly-second diester 3-4,80-100 mesh；Above raw material is combined at 60-70 DEG C.
5. according to a kind of high intensity long life fishing net described in claim 1, it is characterised in that be made up of following steps:
(1) mix at haloflex, polyacrylamide, rilanit special, calcium bicarbonate mixing being placed on 60-70 DEG C, it is subsequently adding plasticizer, modified nano zinc oxide, auxiliary agent, stir at 65-75 DEG C, then mixture is put into extruder extrusion, one section of temperature of extruder is 175-180 DEG C, two sections of temperature are 178-184 DEG C, and three sections of temperature are 181-187 DEG C, and latter end temperature is 183-189 DEG C.
(2) spinneret case is added after extrusion, then spinning appts is used to carry out wire drawing, then drawing-off is carried out, first draw roll pressure is 0.88-0.95bar, the second draw roll pressure is 3.09-3.13bar, then dry at 88-95 DEG C, then take-up roll is used to be wound, first winding roller rotating speed is 3500m/min, second winding roller rotating speed is 3900m/min, 3rd take-up roll rotating speed is 4300m/min, carry out further drawing-off, be then wound obtaining wire rod, then carry out working out and i.e. obtain fishing net.