CN105835490A - A manufacturing method of a high-haze high-viscosity protective film - Google Patents
A manufacturing method of a high-haze high-viscosity protective film Download PDFInfo
- Publication number
- CN105835490A CN105835490A CN201610217434.6A CN201610217434A CN105835490A CN 105835490 A CN105835490 A CN 105835490A CN 201610217434 A CN201610217434 A CN 201610217434A CN 105835490 A CN105835490 A CN 105835490A
- Authority
- CN
- China
- Prior art keywords
- layer
- polyethylene
- polypropylene
- haze
- protective film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A manufacturing method of a high-haze high-viscosity protective film is disclosed. The protective film is manufactured mainly by a three-layer co-extrusion manner, wherein an A layer comprises polypropylene and polyethylene which are blended, a B layer comprises polypropylene and polyethylene which are blended, and a C layer comprises blended polystyrene type elastomers. The method is characterized in that the polypropylene is adopted as a substrate, haze is formed through roughness of the raw material itself and diffuse reflection caused by incompatibility between the polypropylene and the polyethylene so as to avoid precipitation of small molecules, and the C layer is an adhesive layer, is blended through adopting a unique formula, and adsorbs based on static actions of the material itself. The protective film has high-temperature resistance, capability of being not liable to degum, high haze, high viscosity, and other functions. The protective film is high in surface haze, and therefore the protective film is especially easy to uncoil and is not liable to adhere during high-viscosity product manufacturing, and the protective film is particularly suitable for brightening films, light guide plates, steel plates, and other industries requiring high viscosity for adhesion.
Description
Technical field
The present invention is relevant a kind of haze, and full-bodied protecting film is particularly suited for brightness enhancement film, light guide plate, steel plate etc.
Need the viscous industry that could fit of height.
Background technology
The highest viscous adhesive protecting film generally exists, and precipitation is many, or the little patch of viscosity does not goes up, or thickening is the most strict
Evil, causes with affixed object product stick together brokenly ring affixed object product.And good multi-product, such as brightness enhancement film, light guide plate etc. just has
The difference of reverse side, is the most all to distinguish with coloured protecting film, and such cost is high, and color masterbatch has little molecule to separate out wind
Danger, the protecting film of the present invention can substitute coloured protecting film with the protecting film of haze, such that it is able to distinguish positive and negative, and
And noresidue under the protecting film high temperature of present invention making, brilliant point is few, and viscosity stabilized, the surface of haze is conducive to pile.This
Bright protecting film, because Surface haze is higher, is very easy to uncoiling when making the viscous product of height, it is not easy to adhesion.
Summary of the invention
The present invention solves the problems referred to above, it is provided that a kind of haze, full-bodied protecting film.
Technical scheme is summarized as follows
A kind of haze height glues protecting film and is mainly fabricated in the way of three-layer co-extruded, wherein A composition of layer be polypropylene and
Polyethylene blend, B composition of layer be polypropylene with polyethylene blend, C composition of layer is that polystyrene type is elastomer blended.
Preferably, described a kind of haze height glues protecting film, and A layer polypropylene is random copolymerization or block copolymerization
Polypropylene, polyethylene is that low-pressure polyethylene is blended.
Preferably, described a kind of haze height glues protecting film, the random or polypropylene elastic modelling quantity of block copolymerization
Between 1200MPA-1600MPA.Fat melting is between 5-8.
Preferably, described a kind of haze height glues protecting film, the density of low-pressure polyethylene 0.951-0.965 it
Between, fat melting is between 5-7.
Preferably, described a kind of haze height glues protecting film, and in A layer, polyacrylic ratio is at 70%-100%, poly-
Ethylene is 0%-30%.
Preferably, described a kind of haze height glues protecting film, and B layer polypropylene is the polypropylene of random copolymerization, poly-second
Alkene is that polyethylene from high pressure process is blended.
Preferably, described a kind of haze height glues protecting film, and the polypropylene elastic modelling quantity of random copolymerization is at 800MPA-
Between 1200MPA.Fat melting is between 5-8.
Preferably, described a kind of haze height glues protecting film, the density of polyethylene from high pressure process 0.920-0.930 it
Between, fat melting is between 5-7.
Preferably, described a kind of haze height glues protecting film, and in B layer, polyacrylic ratio is at 80%-100%, poly-
Ethylene is 0%-20%.
Preferably, described a kind of haze height glues protecting film, and the elastomer of C strata phenylethylene, mainly with polyphenyl
Ethylene-butylene, polystyrene-pentadiene, Petropols, antioxidant mixing is made.
Preferably, described a kind of haze height glues protecting film, and the composition manufactured by the mixing of C layer is about polyphenyl second
Alkene-butadiene 20%-30%, polystyrene-pentadiene 40%-60%, Petropols 10%-30%, antioxidant 1%-3%.
Preferably, described a kind of haze height glues protecting film, and it is 10%-40%, B layer that A layer accounts for the ratio of whole film
The ratio accounting for whole film is ratio 5%-20% that 30%-60%, C layer accounts for whole film.
Beneficial effects of the present invention:
The protecting film mist degree that the present invention makes relies primarily on the roughness of raw material itself, and polyethylene with polyacrylic not
The diffuse-reflectance that the compatibility causes forms mist degree, is different from other principles (such as by adding matt master), and so make is excellent
Gesture is to avoid the precipitation of little molecule.
The protecting film that the present invention makes is mainly with polypropylene as base material so that the heat resistance of film is superior, it is easy to follow-up mould
Cut.
The protecting film C layer that the present invention makes is viscous layer, is depended on by the electrostatic of raw material own and is different from coating technique and makes
Protecting film, such advantage is film no solvent residue, will not degumming.
C layer viscous layer of the present invention, uses unique formula to be blended, by styrene-butadiene, polystyrene-pentadiene, stone
Oleoresin, antioxidant mixing is made, and hydrogenation degree is than traditional polystyrene-fourth preferentially to select polystyrene-pentadiene advantage to be
Diene (SEBS) is high, and such unsaturated double-bond is little, and the product made is viscosity stabilized, viscosifies little.Add antioxidant and make product
Ageing resistace be improved, extend the use cycle of product with period of storage.Add tackifying resin and make the soft of product
Changing point to improve, the mobility of increase product is with processability, and improves the viscosity of product.
The protecting film that the present invention makes causes film to compare mist because top layer is coarse, can produce other advantage, and film is solving
During volume, the best uncoiling, glues product scope at height especially, often as adhesion coating is with tegillum adhesion, causes film to be difficult to uncoiling.
Specific embodiments
Hereinafter, the present invention is explained in more detail by embodiment, but the present invention is not limited to these embodiments.
A layer is the low-pressure polyethylene of the random copolymerization PP+10% of 80% ratio, and B layer is the random copolymerization PP+10% of 90%
Polyethylene from high pressure process, C layer is the blended viscous layer told above.
Ratio shared by A layer is 30%, and the ratio shared by layer is 60%, and the ratio shared by C layer is 10%.
The thickness of whole film is 50u.
Viscosity determining procedure: film is cut into 25mm width, 200mm length, is affixed on affixed object surface, tests on puller system the most again
Peeling force, puller system speed is 300mm/ minute, and peel angle is 180 degree.
Residue analysis method: will make film and be affixed on affixed object surface, with roller compaction, makees room temperature respectively, 65 degree of high temperature, and 90
Degree high temperature test 24 hours, opens protecting film and sees whether affixed object product have foreign body.
Mist degree method of testing: with reference to GB/T2410
The film properties made such as following table
The viscosity such as following table of the film patch different plates made
The film residue analysis such as following table made
Room temperature | 65 degree | 90 degree | |
Sample | Foreign | Foreign | Foreign |
Find out that the full-bodied protecting film of haze that the present invention makes is viscosity stabilized by above test, can paste different
Product, viscosifies little, and noresidue at a certain temperature, can be widely used in the industries such as light guide plate, brightness enhancement film, steel plate.
Claims (12)
1. a haze height glues protecting film and is mainly fabricated in the way of three-layer co-extruded, and wherein A composition of layer is polypropylene and poly-
Ethylene be blended, B composition of layer be polypropylene with polyethylene blend, C composition of layer is that polystyrene type is elastomer blended.
2., according to the polypropylene that A layer polypropylene is random copolymerization or block copolymerization required by claim 1, polyethylene is low pressure
Polyethylene blend.
3. according to the polypropylene elastic modelling quantity of the random or block copolymerization required by claim 2 1200MPA-1600MPA it
Between.Fat melting is between 5-8.
4. according to required by claim 2 the density of low-pressure polyethylene between 0.951-0.965, fat melting is between 5-7.
5., according to polyacrylic ratio in the A layer required by claim 2 at 70%-100%, polyethylene is 0%-30%.
6., according to the polypropylene that B layer polypropylene is random copolymerization required by claim 1, polyethylene is that polyethylene from high pressure process is blended.
7. according to the polypropylene elastic modelling quantity of the random copolymerization required by claim 6 between 800MPA-1200MPA.Fat melting exists
Between 5-8.
8. according to required by claim 6 the density of polyethylene from high pressure process between 0.920-0.930, fat melting is between 5-7.
9., according to polyacrylic ratio in the B layer required by claim 6 at 80%-100%, polyethylene is 0%-20%.
10. according to the elastomer of the C strata phenylethylene required by claim 1, mainly with styrene-butadiene, polyphenyl second
Alkene-pentadiene, Petropols, antioxidant mixing is made.
11. are about styrene-butadiene 20%-30% according to the composition manufactured by the C layer mixing required by claim 10,
Polystyrene-pentadiene 40%-60%, Petropols 10%-30%, antioxidant 1%-3%.
12. glue protecting film A layer to account for the ratio of whole film according to the height required by claim 1 be that 10%-40%, B layer accounts for whole film
Ratio be ratio 5%-20% that 30%-60%, C layer accounts for whole film.