CN105820443A - Cold-resistant toughened polypropylene material - Google Patents
Cold-resistant toughened polypropylene material Download PDFInfo
- Publication number
- CN105820443A CN105820443A CN201610338339.1A CN201610338339A CN105820443A CN 105820443 A CN105820443 A CN 105820443A CN 201610338339 A CN201610338339 A CN 201610338339A CN 105820443 A CN105820443 A CN 105820443A
- Authority
- CN
- China
- Prior art keywords
- cold
- resistant toughened
- polypropylene material
- resistant
- acicular wollastonite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a cold-resistant toughened polypropylene material .The cold-resistant toughened polypropylene material is prepared from polypropylene, modified needle-like wollastonite, bis(p-ethyldibenzal)sorbitol, a cold-resistant toughening agent, antioxidant, lubricant and optical stabilizer .The low-temperature toughness retention rate of the polypropylene material can be improved obviously by needle-like wollastonite and bis(p-ethyldibenzal)sorbitol, and the low-temperature toughness retention rate, at 30 DEG C, of the polypropylene material reaches 60% or more by using needle-like wollastonite, bis(p-ethyldibenzal)sorbitol and the cold-resistant toughening agent in a compound mode.
Description
Technical field
The present invention relates to polymer modification field, particularly relate to a kind of cold-resistant toughened polypropylene material.
Background technology
Along with the development of modern science and technology, people are more and more higher to the requirement of material property, especially to general-purpose plastics polypropylene
Material.Polypropylene is mainly used in the fields such as automobile, household electrical appliances, tubing, medical treatment, food.Due to polypropylene material low-temperature flexibility relatively
Difference, if being accomplished by it is carried out the toughening modifying low-temperature flexibility with raising polypropylene material for low temperature environment, common changes
The material of kind polypropylene low temperature toughness is ethylene propylene diene rubber (EPDM), based elastomers (POE), styrene-butadiene-benzene
Ethylene elastomer (SBS), SEBS elastomer (SEBS), its consumption is generally polypropylene quality
10wt%~40wt%.As: Chinese patent CN 1221607C utilizes SEBS tenacity-increased profax;Chinese patent CN 102311584 B,
CN 102675745 A, CN 102516663 A be all to utilize POE tenacity-increased profax;Chinese patent CN 1119374 C utilizes
EPDM and SBS tenacity-increased profax.
Summary of the invention
The present invention provides a kind of cold-resistant toughened polypropylene material, has significantly effect to polyacrylic low-temperature flexibility conservation rate
Really.
Technical scheme is as follows:
A kind of cold-resistant toughened polypropylene material, it is made up of by weight percentage following component:
Polypropylene 100 parts
Modified acicular wollastonite 0.5 ~ 1.5 part
Two (to ethyl two benzal) sorbitol 0.3 ~ 1 part
Cold-resistant toughened dose 2 ~ 20 parts
0.2 ~ 0.5 part of antioxidant
Lubricant 0.1 ~ 0.3 part
The steady agent of light 0.1 ~ 0.3 part.
Scheme further, described modified acicular wollastonite is to be carried out surface process by acicular wollastonite through titanate coupling agent
Rear draw ratio is 7:1 ~ 22:1, particle diameter is 600 ~ 1250 mesh.
Scheme further, described titanate coupling agent is isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters.
Scheme further, described antioxidant is four [β-(3,5-di-tert-butyl-hydroxy phenyl) propanoic acid] pentaerythritol ester
Compound with three [2,4-di-tert-butyl-phenyl] phosphite ester.
Described lubricant is ethylene bis stearamide.
The steady agent of described light is 50% hindered amine as light stabilizer 2,2,6,6-tetramethyl-4-piperidine alcohols stearate oligomerisation of propene
Mixture and 2-(2-hydroxyl-5-uncle good fortune base phenyl) compound of benzotriazole.
Scheme further, described cold-resistant toughened dose is hydrogenated polystyrene butadiene styrene triblock copolymer.
Usefulness of the present invention:
1, acicular wollastonite and two (to ethyl two benzal) sorbitol are used, especially by the present invention simultaneously as Polypropylene cold-resistant agent
It is that the holding to HOPP low-temperature flexibility has significant effect.
2, using compounding to acicular wollastonite and traditional polypropylene toughening agent, it keeps effect to polypropylene low temperature toughness
Than both individually using effect good.
3, acicular wollastonite and two (to ethyl two benzal) sorbitol usage amount of the present invention are the least, and typically its consumption is
0.5 ~ the 1.5wt% and 0.3 ~ 1% of polypropylene quality, has broken traditional acicular wollastonite and has used as reclaimed polypropylene charge and use
The amount that amount is also used for inserts use is much smaller, reduces cost and uses.
4, widen acicular wollastonite and the range of two (to ethyl two benzal) sorbitol, break conventional needle-like silicon
Lime stone is filled mainly as polyacrylic enhancing, and dibenzal sorbitol uses mainly as polyacrylic nucleator.
Detailed description of the invention
Below in conjunction with some embodiments, the invention will be further described with comparative example.
Note: following Izod notched impact strength performs GB/T 1843.
Low-temperature flexibility conservation rate=(impact strengths of impact strength/23 DEG C of-30 DEG C) * 100%.
The modification of acicular wollastonite is to add to account for gross mass 1% titanate coupling agent (NDZ-201) and enter in acicular wollastonite
Row surface processes gained.I.e. processed gained by the acicular wollastonite of 1% coupling agent NDZ-201 and 99%.Concrete processing mode is as follows:
First weigh the acicular wollastonite of 99 mass parts in high-speed mixer, then weigh the coupling agent NDZ-201 of 1 mass parts from a high speed
The upper end aperture of mixer is slowly added to and starts mixer carry out mixing to obtain modified acicular wollastonite.
The steady agent of light is 50% hindered amine as light stabilizer 2,2,6,6-tetramethyl-4-piperidine alcohols stearate oligomerisation of propene mixing
Thing and 2-(2-hydroxyl-5-uncle good fortune base phenyl) compound of benzotriazole.
Cold-resistant toughened dose is hydrogenated polystyrene butadiene styrene triblock copolymer.
Embodiment 1
It is 100 parts of polypropylene by weight portion, the modified acicular wollastonite of 0.5 part, 0.3 part of two (to ethyl two benzal) sorbitol,
The antioxidant 1010 of 0.1 part, the irgasfos 168 of 0.1 part, the Lubricate EBS of 0.1 part, the steady agent of light of 0.05 part, cold-resistant toughened dose
2 parts, after high mixer mix homogeneously, through double screw extruder extruding pelletization.
Embodiment 2
By the polypropylene that weight portion is 100 parts, the modified acicular wollastonite of 1.5 parts, 0.8 part of two (to ethyl two benzal) Pyrusussuriensis
Alcohol, the antioxidant 1010 of 0.2 part, the irgasfos 168 of 0.3 part, the Lubricate EBS of 0.3 part, the steady agent of light of 0.3 part, cold-resistant toughened
Agent 5 parts is after high mixer mix homogeneously, through double screw extruder extruding pelletization.
Embodiment 3
By the polypropylene that weight portion is 100 parts, the modified acicular wollastonite of 1.0 parts, 1 part of two (to ethyl two benzal) sorbitol,
The antioxidant 1010 of 0.2 part, the irgasfos 168 of 0.2 part, the Lubricate EBS of 0.2 part, the steady agent of light of 0.25 part, cold-resistant toughened dose
10 parts after high mixer mix homogeneously, through double screw extruder extruding pelletization.
Comparative example 1
By the polypropylene that weight portion is 100 parts, the antioxidant 1010 of 0.1 part, the irgasfos 168 of 0.1 part, the lubricant of 0.1 part
EBS, the steady agent of light of 0.1 part is after high mixer mix homogeneously, through double screw extruder extruding pelletization.
The single screw injection molding machine of material embodiment 1-3 and comparative example 1 prepared is molded into standard batten, is 23 in temperature
DEG C ± 2 DEG C and humidity is to place at least 24 hours under conditions of RH50% ± 5%, then carries out room temperature and the cantilever beam under low temperature state
Notch shock is tested, and its cryogenic conditions is :-30 DEG C, 3 hours.Test result is shown in Table 1.
Table 1 performance test
Can be seen that from the performance comparison of upper table embodiment 1 and comparative example 1, the present invention adds modified acicular wollastonite as cold-resistant agent
And the cold-resistant toughened dose of low-temperature flexibility conservation rate that can make polypropylene material is all more than 60%, and it is resistance to not add acicular wollastonite
Polypropylene material low-temperature flexibility conservation rate ability 30% in the comparative example 1 of cold agent.
Embodiment listed by the present invention is the exemplary embodiments of the present invention, and right protection scope of the present invention is not limited to
This.
Claims (7)
1. a cold-resistant toughened polythene material, it is characterised in that: it is made up of by weight percentage following component:
Polypropylene 100 parts
Modified acicular wollastonite 0.5 ~ 1.5 part
Two (to ethyl two benzal) sorbitol 0.3 ~ 1 part
Cold-resistant toughened dose 2 ~ 20 parts
0.2 ~ 0.5 part of antioxidant
Lubricant 0.1 ~ 0.3 part
The steady agent of light 0.1 ~ 0.3 part.
Cold-resistant toughened polypropylene material the most according to claim 1, it is characterised in that: described modified acicular wollastonite be by
Acicular wollastonite draw ratio after titanate coupling agent carries out surface process is 7:1 ~ 22:1, particle diameter is 600 ~ 1250 mesh.
Cold-resistant toughened polypropylene material the most according to claim 1, it is characterised in that: described titanate coupling agent is isopropyl
Base three (dioctylphyrophosphoric acid acyloxy) titanate esters.
Cold-resistant toughened polypropylene material the most according to claim 1, it is characterised in that: described antioxidant is four [β-(3,5-
Di-tert-butyl-hydroxy phenyl) propanoic acid] pentaerythritol ester and the compound of three [2,4-di-tert-butyl-phenyl] phosphite ester.
Cold-resistant toughened polypropylene material the most according to claim 1, it is characterised in that: described lubricant is that ethylene is double stearic
Amide.
Cold-resistant toughened polypropylene material the most according to claim 1, it is characterised in that: the steady agent of described light is 50% hindered amine
Light stabilizer 2,2,6,6-tetramethyl-4-piperidine alcohols stearate oligomerisation of propene mixture and 2-(2-hydroxyl-5-uncle good fortune base benzene
Base) compound of benzotriazole.
Cold-resistant toughened polypropylene material the most according to claim 1, it is characterised in that: described cold-resistant toughened dose is gathered for hydrogenation
Styrene butadiene styrene triblock copolymer.